Solubility and activity of oxygen in liquid antimony

The solubility limit of oxygen in liquid antimony has been measured by a novel isopiestic technique in the temperature range 995--1175 deg K. The results can be expressed by the equation log c = --5500/T + 3.754 ( plus/minus 0.04) with c in at.% O and T in deg K. The oxygen potential over Sb + O alloys equilibrium with Sb2O3 has been measured by a solid state cell using a fully stabilized CaO.ZrO2 electrolyte. The cell was designed to contain the Sb + Sb2O3 mixture in a closed volume, that the vaporization of the oxide can be minimized and true equilibrium attained. The Gibbs free energy of the reaction 2 Sb(s) + 3/2 O2 = Sb2O3(s) is Delta G deg = --719560 + 274.51 T( plus/minus 500) and Sb(l) + 3/2 O2 = Sb2O3(l), Delta G deg = --704711 + ( plus/minus 500) ( Delta G deg in J/mole, T in deg K). The combination of these results with Sieverts' law yields the standard free energy of solution of oxygen in liquid antimony according to the reaction 1/2 O2 = \O\Sb,at.% as Delta G deg = --129620 + 14.23 T ( plus/minus 950). The standard enthalopy and entropy of the solution of oxygen in Sb are compared with values for other metal- oyxgen systems, and with the standard enthalpies of formation of corresponding oxides. The resulting correlations permit the estimation of the standard free energy of solution of oxygen in pure metals for which experimental information is lacking. 24 ref.--AA

Experimental evidence of Ga-vacancy induced room temperature ferromagnetic behavior in GaN films

We have grown Ga deficient GaN epitaxial films on (0001) sapphire substrate by plasma-assisted molecular beam epitaxy and report the experimental evidence of room temperature ferromagnetic behavior. The observed yellow emission peak in room temperature photoluminescence spectra and the peak positioning at 300 cm(-1) in Raman spectra confirms the existence of Ga vacancies. The x-ray photoelectron spectroscopic measurements further confirmed the formation of Ga vacancies; since the N/Ga is found to be >1. The ferromagnetism is believed to originate from the polarization of the unpaired 2p electrons of N surrounding the Ga vacancy. (C) 2011 American Institute of Physics. [doi:10.1063/1.3654151]

Solubility and activity of oxygen in liquid manganese

The oxygen concentration of liquid manganese in equilibrium with MnAl2+2xO4+3x and α−Al2O3 has been determined in the temperature range 1520 to 1875 K. The oxygen content of quenched samples, wrapped in oxygen-free nickel foil, was determined by an inert gas fusion technique. The results are combined with accurate data now available on the Gibbs energies of formation of MnO and Al2O3−saturated MnAl2+2xO4+3x to derive the oxygen content of liquid manganese in equilibrium with MnO and the Gibbs energy of solution of diatomic oxygen gas in liquid manganese. The enthalpy and entropy of solution of oxygen in manganese are compared with similar data on other metal-oxygen systems.

Potentiometric determination of the Gibbs energies of formation of lead aluminates

The Gibbs energies of formation of three compounds in the PbO-Al2O3 system—2PbO · Al2O3, PbO · Al2O3, andPbO· 6Al2O3—have been determined from potentiometric measurements on reversible solid-state galvanic cells [dformula Pt, Ir | Pb, alpha-Al[sub 2]O[sub 3], PbO [center-dot] 6Al[sub 2]O[sub 3] | ZrO[sub 2]-CaO | NiO, Ni | Pt] [dformula Pt | NiO, Ni | ZrO[sub 2]-CaO | Pb, PbO [center-dot] 6Al[sub 2]O[sub 3], PbO [center-dot] Al[sub 2]O[sub 3] | Ir, Pt] and [dformula Pt | NiO, Ni | ZrO[sub 2]-CaO | Pb, PbO [center-dot] Al[sub 2]O[sub 3], 2PbO [center-dot] Al[sub 2]O[sub 3] | Ir, Pt] in the temperature range 850–1375 K. The results are discussed in the light of reported phase diagrams for the PbO-Al2O3system. The partial pressures of different lead oxide species, PbnOn, n = 1–6, in the gas phase in equilibrium withthe aluminates are calculated by combining the results of this study with the mass-spectrometric data of Drowart et al.(1) for polymerization equilibria in the gas phase. The concentration of oxygen in lead in equilibrium with the aluminatesare also derived from the results and the literature data on the Gibbs energy of solution of oxygen in liquid lead.

Oxygen content of liquid cobalt in equilibrium with CoO.(1+x)Al2O3 and -Al2O3

The oxygen concentration of liquid cobalt in equilibrium with cobalt aluminate and a-alumina has been measured by suction sampling and crucible quenching techniques at temperatures between 1770 and 1975 K. Experiments were made with cobalt of high and low initial oxygen contents, and with and without the addition of cobalt aluminate. The effect of temperature on the equilibrium oxygen content is represented by the equation, log (at.% 0) = -10,4001T(K) + 4.64 (±0.008). The composition of the spinel phase, CoO.(1+x)AI20 3, saturated with alumina, has been determined by electron probe microanalysis. The values of x are 0.22 at 1770 Kand 0.28 at 1975 K. The oxygen potential corresponding to the three-phase equilibrium between cobalt, aluminate and alumina, and the standard Gibbs' energy of formation of nonstoichiometric cobalt aluminate are evaluated by combining the results of this study with recently published data on the activity of oxygen in liquid cobalt. Implications of the present results to aluminium deoxidation of liquid cobalt are discussed.

Gibbs energies of formation of intermetallic phases in the systems Pt Mg, Pt Ca and Pt Ba and some applications

The standard Gibbs energies of formation of platinum-rich intermetallic compounds in the systems Pt-Mg, Pt-Ca, and Pt-Ba have been measured in the temperature range of 950 to 1200 K using solid-state galvanic cells based on MgF2, CaF2, and BaF2 as solid electrolytes. The results are summarized by the following equations: ΔG° (MgPt7) = −256,100 + 16.5T (±2000) J/mol ΔG° (MgPt3) = −217,400 + 10.7T (±2000) J/mol ΔG° (CaPt5) = −297,500 + 13.0T (±5000) J/mol ΔG° (Ca2Pt7) = −551,800 + 22.3T (±5000) J/mol ΔG° (CaPt2) = −245,400 + 9.3T (±5000) J/mol ΔG° (BaPt5) = −238,700 + 8.1T (±4000) J/mol ΔG° (BaPt2) = −197,300 + 4.0T (±4000) J/mol where solid platinum and liquid alkaline earth metals are selected as the standard states. The relatively large error estimates reflect the uncertainties in the auxiliary thermodynamic data used in the calculation. Because of the strong interaction between platinum and alkaline earth metals, it is possible to reduce oxides of Group ILA metals by hydrogen at high temperature in the presence of platinum. The alkaline earth metals can be recovered from the resulting intermetallic compounds by distillation, regenerating platinum for recycling. The platinum-slag-gas equilibration technique for the study of the activities of FeO, MnO, or Cr2O3 in slags containing MgO, CaO, or BaO is feasible provided oxygen partial pressure in the gas is maintained above that corresponding to the coexistence of Fe and “FeO.”

The standard molar Gibbs energy of formation of YbPt3 and LuPt3 intermetallics

The standard molar Gibbs energies of formation of YbPt3 and LuPt3 intermetallic compounds have been measured in the temperature range 880 K to 1100 K using the solid-state cells:View the MathML source and View the MathML source The trifluoride of Yb is not stable in equilibrium with Yb or YbPt3. The results can be expressed by the equations: View the MathML source View the MathML source The standard molar Gibbs energy of formation of LuPt3 is −41.1 kJ · mol−1 more negative than that for YbPt3 at 1000 K. Ytterbium is divalent in the pure metal and trivalent in the intermetallic YbPt3. The energy required for the promotion of divalent Yb to the trivalent state is responsible for the less negative ΔfGmo of YbPt3. The enthalpies of formation of the two intermetallics are in reasonable agreement with Miedema's model. Because of the extraordinary stability of these compounds it is possible to reduce oxides of Yb and Lu with hydrogen in the presence of platinum at View the MathML source. The equilibrium chemical potential of oxygen corresponding to the reduction of Yb2O3 and Lu2O3 by hydrogen in the presence of platinum is presented in the form of an Ellingham diagram.

Gibbs’ energy of formation of YBa2Cu3O7-x (tetragonal)

The high temperature ceramic oxide superconductor YBa2Cu3O7-x (1–2–3 compound) is generally synthesized in an oxygen-rich environment. Hence any method for determining its thermodynamic stability should operate at a high oxygen partial pressure. A solid-state cell incorporating CaF2 as the electrolyte and functioning under pure oxygen at a pressure of 1·01 × 105 Pa has been employed for the determination of the Gibbs’ energy of formation of the 1–2–3 compound. The configuration of the galvanic cell can be represented by: Pt, O2, YBa2Cu3O7−x , Y2BaCuO5, CuO, BaF2/CaF2/BaF2, BaZrO3, ZrO2, O2, Pt. Using the values of the standard Gibbs’ energy of formation of the compounds BaZrO3 and Y2BaCuO5 from the literature, the Gibbs’ energy of formation of the 1–2–3 compound from the constituent binary oxides has been computed at different temperatures. The value ofx at each temperature is determined by the oxygen partial pressure. At 1023 K for O content of 6·5 the Gibbs’ energy of formation of the 1–2–3 compound is −261·7 kJ mol−1.

Variation of the partial thermodynamic properties of oxygen with composition in YBa2Cu3O7−δ

The variation of equilibrium oxygen potential with oxygen concentration inYBa 2Cu3O7-δhas been measured in the temperature range of 773 to 1223 K. For temperatures up to 1073 K, the oxygen content of theYBa 2Cu3O7-δsample, held in a stabilized-zirconia crucible, was altered by coulometric titration. The compound was in contact with the electrolyte, permitting direct exchange of oxygen ions. For measurements above 1073 K, the oxide was contained in a magnesia crucible placed inside a closed silica tube. The oxygen potential in the gas phase above the 123 compound was controlled and measured by a solid-state cell based on yttria-stabilized zirconia, which served both as a pump and sensor. Pure oxygen at a pressure of 1.01 × 105 Pa was used as the reference electrode. The oxygen pressure over the sample was varied from 10-1 to 105 Pa. The oxygen concentrations of the sample equilibrated with pure oxygen at 1.01 × 105 Pa at different temperatures were determined after quenching in liquid nitrogen by hydrogen reduction at 1223 K. The plot of chemical potential of oxygen as a function of oxygen non-stoichiometry shows an inflexion at δ ∼ 0.375 at 873 K. Data at 773 K indicate tendency for phase separation at lower temperatures. The partial enthalpy and entropy of oxygen derived from the temperature dependence of electromotive force (emf ) exhibit variation with composition. The partial enthalpy for °= 0.3, 0.4, and 0.5 also appears to be temperature dependent. The results are discussed in comparison with the data reported in the literature. An expression for the integral free energy of formation of YBa2Cu3O6.5 is evaluated based on measurements reported in the literature. By integration of the partial Gibbs’ energy of oxygen obtained in this study, the variation of integral property with oxygen concentration is obtained at 873 K.

Gibbs energy of formation of CuCrO4 and phase relations in the system Cu-Cr-O below 735 K

A solid state galvanic cell incorporating yttria-stabilized zirconia electrolyte and ruthenium(IV) oxide electrodes has been used to measure the equilibrium chemical potential of oxygen corresponding to the decomposition of CuCrO4 in the range 590–760 K. For the reaction CuO(tenorite) + CuCr2O4(spinel) + 1.5O2(g)→2CuCrO4(orth), ΔGXXX = −183540 + 249.6T(±900) J mol−1. The decomposition temperature of CuCrO4 in pure oxygen at a pressure of 1.01 × 105 Pa is 735(±1) K. By combining the results obtained in this study with data on the Gibbs energy of formation of CuCr2O4 and CuCrO2 reported earlier, the standard Gibbs energy of formation of CuCrO4 and the phase relations in the system Cu-Cr-O at temperatures below 735 K have been deduced. Electron microscopic studies have indicated that the decomposition of CuCrO4 to CuCr2O4 is topotactic.

Gibbs’ free energies of formation of Cu2Ln2O5 (Ln = Tb, Dy, Er, Yb) compounds

The standard Gibbs' free energies of formation of compounds of type Cu2L%05 (Ln = Tb,Dy,Er,Yb) were measured using the solid state cell in the temperature range of 970 to 1323 K For formation of Cu2L?O5 compounds from their binary component oxides according to the reaction 2 CUO (s) + L%03 (s) -, Cu,,L%05 (s),the Gibbs' free energy changes can be represented by the following equations:AGO = 13 080 - 13.70 'I" (+80) J mol-' (Ln = Tb)AGq = 11 480 - 13.51 T (260) J mol-I (Ln = Dy)AGO = 10 750 - 13.99 T (260) J mol-I (Ln = Er)AGO = 9 920 - 13.90 T (260) J mol-' (Ln = Yb) Since formation of the compounds is endothermic, the compounds become thermodynamically unstable with respect to their component oxides below 955 K for Cu2Tb205, 850 K for Cu2Dy205, 768 K for Cu2Er205 and 714 K for Cu2Yb2OS When the oxygen partial pressure over Cu2L%05 is lowered, they decompose according to the scheme, 2 CU,L%O, (s) -r 2 L%03 (s) +2 cu20 (s) + 02(g)The equilibrium chemical potentials of oxygen corresponding to the dissociation reactions are computed from the emf data and auxiliary information on Cu20 and CuO. The computed decomposition temperatures at an oxygen partial pressure of 5.0 x ld Pa are compared with those obtained directly from combined thermogravimetric (TGA) and differential thermal analyses (DTA).The free energy, enthalpy and entropy of formation of Cu2Ln205 compounds show systematic variation with the ionic radius of the trivalent lanthanide ion. The trends obtained in this study are compared with information available in the literature. The staZbility of Cu2Ln205 compounds increases with the decrease in ionic radii of the ~ n ion~. +

Gibbs energy of formation of CaCu3Ti4O12 and phase relations in the system CaO-CUO/CU2O-TiO2

he standard Gibbs energy of formation of CaCu3Ti4O12 (CCTO) from CaTiO3, CuO and TiO2 has been determined as a function of temperature from 925 to 1350 K using a solid-state electrochemical cell with yttria-stabilized zirconia as the solid electrolyte. Combining this result with information in the literature on CaTiO3, the standard Gibbs energy of formation of CCTO from its component binary oxides, CaO, CuO and TiO2, has been obtained: View the MathML source (CaCu3Ti4O12)/J mol−1 (±600) = −125231 + 6.57 (T/K). The oxygen chemical potential corresponding to the reduction of CCTO to CaTiO3, TiO2 and Cu2O has been calculated from the electrochemical measurements as a function of temperature and compared on an Ellingham diagram with those for the reduction of CuO to Cu2O and Cu2O to Cu. The oxygen partial pressures corresponding to the reduction reactions at any chosen temperature can be read using the nomograms provided on either side of the diagram. The effect of the oxygen partial pressure on phase relations in the pseudo-ternary system CaO–CuO/Cu2O–TiO2 at 1273 K has been evaluated. The phase diagrams allow identification of secondary phases that may form during the synthesis of the CCTO under equilibrium conditions. The secondary phases may have a significant effect on the extrinsic component of the colossal dielectric response of CCTO.

Gibbs Energy of Formation of Ca3Ti8Al12O37 and Phase Relations and Chemical Potentials in the System Al2O3-TiO2-CaO

The quaternary oxide in the system Al2O3-CaO-TiO2 is found to have the composition Ca3Ti8Al12O37 rather than CaTi3Al8O19 as reported in the literature. The standard Gibbs energy of formation of Ca3Ti8Al12O37 from component binary oxides is measured in the temperature range from 900 to 1250 K using a solid-state electrochemical cell incorporating single crystal CaF2 as the solid electrolyte. The results can be represented by the equation: delta G(f(0x))(0) (+/- 70)/J mol(-1) = -248474 - 15.706(T/K). Combining this information with thermodynamic data on calcium aluminates and titanates available in the literature, subsolidus phase relations in the pseudo-ternary system Al2O3-CaO-TiO2 are computed and presented as isothermal sections. The evolution of phase relations with temperature is highlighted. Chemical potential diagrams are computed at 1200 K, showing the stability domains of the various phases in the chemical potential-composition space. In each chemical potential diagram, chemical potential of one component is plotted against the cationic fraction of the other two components. The diagrams are valid at relatively high oxygen potentials where Ti is present in its four-valent state in all the oxide phases.

System Ho-Rh-O: Phase Equilibria, Chemical Potentials and Gibbs Energy of Formation of HoRhO3

The thermodynamic properties of the HoRhO3 were determined in the temperature range from 900 to 1300 K by using a solid-state electrochemical cell incorporating calcia-stabilized zirconia as the electrolyte. The standard Gibbs free energy of formation of orthorhombic perovskite HoRhO3, from Ho2O3 with C-rare earth structure and Rh2O3 with orthorhombic structure, can be expressed by the equation; Delta G(f)degrees((ox)) (+/- 78)/(J/mol) = -50535 + 3.85(T/K) Using the thermodynamic data of HoRhO3 and auxiliary data for binary oxides from the literature, the phase relations in the Ho-Rh-O system were computed at 1273 K. Thermodynamic data for intermetallic phases in the binary Ho-Rh were estimated from experimental enthalpy of formation for three compositions from the literature and Miedema's model, consistent with the phase diagram. The oxygen potential-composition diagram and three-dimensional chemical potential diagram at 1273 K, and temperature-composition diagrams at constant oxygen partial pressures were computed for the system Ho-Rh-O. The decomposition temperature of HoRhO3 is 1717(+/- 2) K in pure O-2 and 1610(+/- 2) K in air at a total pressure p(o) = 0.1 MPa.

Gibbs energy of formation of Ca7V4O17

Thermodynamic properties of Ca7V4O17 are measured for the first time using a solid-state electrochemical cell incorporating single crystal of CaF2 as the electrolyte over the temperature range from (900 to 1175) K. An equimolar mixture of CaO and CaF2 is used as the reference electrode and a mixture of Ca3V2O8, Ca7V4O17 and CaF2 as the measuring electrode. Both the electrodes are placed under flowing oxygen gas at ambient pressure. The standard Gibbs energy change for the reaction: 2Ca(3)V(2)O(8) + CaO -> Ca7V4O17; which is related to the chemical potential of CaO in the two-phase region (Ca3V2O8 + Ca7V4O17) of the pseudo-binary system CaO + V2O5, is obtained from the electromotive force of the cell as: Delta(r)G(o) +/- 127/(J . mol(-1)) = Delta mu(CaO) = -11453 + 8.273(T/K). The derived standard enthalpy of formation of Ca7V4O17 from elements in their normal standard states is ( 8208.97 +/- 8) kJ . mol (1) and its standard entropy is (560.05 +/- 7.5) J . K (1) . mol (1), both at T = 298.15 K. The results indicate that Ca7V4O17 decomposes into Ca3V2O8 and CaO at T = (1384 +/- 3) K.