Measurement of Gibbs energy of formation of Ca2PbO4 using a solid-state cell with three electrodes

Phase relations in the system Ca-Pb-O at 1100 K have been determined by equilibrating 18 compositions in the ternary and identifying the phases present in quenched samples by X-ray diffraction and energy dispersive X-ray analysis (EDX). Only one ternary compound Ca2PbO4 was found to be present. The compound coexists with CaO and PbO. The intermetallic compounds Ca2Pb, Ca5Pb3 and CaPb and liquid alloys are in equilibrium with CaO. The standard Gibbs energies of formation of Ca2PbO4 (880 - 1100 K) and Pb3O4 (770 - 910 K) were determined using solid-state cells based on yttria-stabilized zirconia as the solid electrolyte. Pure oxygen gas at 0.1 MPa was used as the reference electrode. For measurements on Ca2PbO4, a novel cell design with three electrodes in series, separated by solid electrolyte membranes, was used to avoid polarization of the electrode containing three solid phases. Two three-phase electrodes were used. The first absorbs the electrochemical flux of oxygen from the reference electrode to the measuring electrode. The other three-phase electrode, which is unaffected by the oxygen flux through the solid electrolyte, is used for electromotive force (EMF) measurement. The results from EMF studies were cross-checked using thermogravimetry (TG) under controlled oxygen partial pressures. The stability of Pb3O4 was investigated using a conventional solid-state cell with RuO2 electrodes. The results can be summarized by the following equations: 2CaO + PbO +1/2O(2) --> Ca2PbO4 Delta(r)G degrees/J mol(-1) = (- 128340 + 93.21 T/K) +/- 200 3PbO + 1/2O(2) --> Pb3O4 Delta(r)G degrees/J mol(-1) = (- 70060 + 77.5 T/K) +/- 150

Synthesis and vesicle formation from novel pseudoglyceryl dimeric lipids. Evidence of formation of widely different membrane organizations with exceptional thermotropic properties

Eight new bis-cationic dimeric lipids 2a-h have been synthesized; TEM of their aqueous dispersions confirmed the vesicle formation and from the thermal, spectroscopic, DLS and XRD studies it has been revealed that they form three different kinds of membranous aggregate depending on the m-value.

Metabolic disposition of a monoterpene ketone, piperitenone, in rats: Evidence for the formation of a known toxin, p-cresol

It was shown earlier that the monoterpene ketone, piperitenone (I) is one of the major metabolites of R-(+)-pulegone, a potent hepatotoxin, In the present studies, the metabolic disposition of piperitenone (I) was examined in rats. Piperitenone (I) was administered orally (400 mg/kg of the b. wt./day) to rats for 5 days, The following urinary metabolites were isolated and identified by various spectral analyses: p-cresol (VI), 6,7-dehydromenthofuran (III), p-mentha-1,3,5,8-tetraen-3-ol (IX), p-mentha-1,3, 5-friene-3, 8-diol (X), 5-hydroxypiperitenone (VIII), 7-hydroxypiperitenone (XI), 10-hydroxypiperitenone (XII), and 4-hydroxypiperitenone (VII). Incubation of piperitenone (I) with phenobarbital-induced rat liver microsomes in the presence of NADPH resulted in the formation of five metabolites which have been tentatively identified as metabolites III, VII, VIII, XI, XII, on the basis of gas chromatography retention time and gas chromatography-mass spectrometry analysis. Based on these results, a probable mechanism for the formation of p-cresol from piperitenone (I) via the intermediacy of metabolite III has been proposed.

On the formation of poly(ethyleneoxide)-poly(vinylalcohol) blends

Poly(ethyleneoxide)-poly(vinylalcohol) blends were prepared and characterized using thermal, spectroscopic and structural methods, By all indications the blends appear to be microscopically inhomogeneous with no strong interpolymer bonding. The high degree of crystallinity in PEO regions induces a significant degree of ordering in neighbouring PVA regions, as evident from thermal properties. PVA obtained from solvent evaporation exhibits an irreversible endothermic transition which could be order-disorder type. Both IR and NMR spectroscopies also suggest the presence of subtle structural ordering influence of PEO on PVA. It is found to be possible to prepare self supporting films of the blends which consists of fine dispersion of PEO and PVA in each other. (C) 1999 Elsevier Science Ltd. All rights reserved.

Formation of Ce1-xPdxO2-delta solid solution in combustion-synthesized Pd/CeO2 catalyst: XRD, XPS, and EXAFS investigation

Pd/CeO2 (1 at. %) prepared by the solution-combustion method shows a higher catalytic activity for CO oxidation and NO reduction than Pd metal, PdO, and Pd dispersed over CeO2 by the conventional method. To understand the higher catalytic properties, the structure of 1 at. % Pd/CeO2 catalyst material has been investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and extended X-ray absorption fine structure (EXAFS) spectroscopy. The diffraction lines corresponding to Pd or PdO are not observed in the high-resolution XRD pattern of 1 at. % Pd/CeO2. The structure of 1 at. % Pd/CeO2 could be refined for the composition of Ce0.99Pd0.01O1.90 in the fluorite structure with 5% oxide ion vacancy. Pd(3d) peaks in the XPS in I at. % Pd/CeO2 are shifted by 3 eV indicating that Pd is in a highly ionic +2 state. EXAFS studies show the average coordination number of 3 around Pd2+ ion in the first shell of 1 at. % Pd/CeO2 at a distance of 2.02 Angstrom, instead of 4 as in PdO. The second shell at 2.72 Angstrom is due to Pd-Pd correlation which is larger than 2.69 Angstrom in PdO. The third shell at 3.31 Angstrom having 7 coordination is absent either in Pd metal or PdO, which can be attributed to -Pd2+-Ce4+- correlation. Thus, 1 at. % Pd/CeO2 forms the Ce1-xPdxO2-delta type of solid solution having -Pd2+-O-2-Ce4+- kinds of linkages.

Solid state structural and solution studies on the formation of a flexible cavity for anions by copper(I) and 1,2-bis(diphenylphosphino)ethane

Copper(l) complexes of 1,2-bis(diphenylphosphino)ethane (dppe) with a stoichiometry Cu-2(dppe)(3)(X)(2) [X- = CN- (1), SCN- (2), NO3- (3)] are obtained from direct reactions of CuX and dppe. The complexes are structurally and spectroscopically (NMR and IR) characterized. The structure of the [Cu-2(dPPe)(3)](2+) dication is similar to the structural motif observed in many other complexes with a chelating dppe and a bridging dppe connecting two copper centers. In complexes 1 -3, the anions are confined to the cavity formed by the phosphines which force a monodentate coordination mode despite the predominant bidentate/bridging character of the anions. The coordination angles rather than the thermochemical radii dictate the steric requirement of anions. While the solution behavior of 3, with nitrate, is similar to complexes studied earlier, complexes with pseudohalides exhibit new solution behavior. (C) 2002 Elsevier Science Ltd. All rights reserved.

Structural investigation of combustion synthesized Cu/CeO2 catalysts by EXAFS and other physical techniques: Formation of a Ce1-xCuxO2-delta solid solution

The structure and chemical environment of Cu in Cu/CeO2 catalysts synthesized by the solution combustion method have been investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), electron paramagnetic resonance (EPR) spectroscopy, X-ray photoelectron spectroscopy (XPS), cyclic voltammetry (CV), and extended X-ray fine structure (EXAFS) spectroscopy. High-resolution XRD studies of 3 and 5 atom % Cu/CeO2 do not show CuO lines in their respective patterns. The structure could be refined for the composition Ce1-xCuxO2-delta (x = 0.03 and 0.05; delta similar to 0.13 and 0.16) in the fluorite structure with 5-8% oxide ion vacancy. High-resolution TEM did not show CuO particles in 5 atom % Cu/CeO2. EPR as well as XPS studies confirm the presence of Cu2+ species in the CeO2 matrix. Redox potentials of Cu species in the CeO2 matrix are lower than those in CuO. EXAFS investigations of these catalysts show an average coordination number of 3 around the Cu2+ ion in the first shell at a distance of 1.96 Angstrom, indicating the O2- ion vacancy around the Cu2+ ion. The Cu-O bond length also decreases compared to that in CuO. The second and third shell around the Cu2+ ion in the catalysts are attributed to -Cu2+-O2--Cu2+ - at 2.92 Angstrom and -Cu2+-O2--Ce4+- at the distance of 3.15 Angstrom, respectively. The present results provide direct evidence for the formation of a Ce1-xCuxO2-delta type of solid solution phase having -square-Cu2+-O-Ce4+- kind of linkages.

The influence of oxygen impurities on the formation of AlN-Al composites by infiltration of molten Al-Mg

The influence of residual oxygen in nitrogen on the formation of AlN-Al matrix by reactive infiltration has been investigated. Increasing the oxygen content from 10 ppm upwards decreased the nitride content in the matrix from 64 to 6%, Based on the analysis of the availability of oxygen at the Al-melt/gas interface, three distinct scenarios have been proposed (i) at lowest values, oxygen does not interfere with either infiltration or nitridation reaction; (ii) at intermediate values, nitridation is suppressed, however infiltration continues; and (iii) at a critical upper value, the melt passivates without any infiltration. This phenomenon offers control of the AlN/Al ratio in the matrix and the possibility of creation of microstructural gradierits by the appropriate choice of gas mixtures. (C) 2002 Elsevier Science B.V. All rights reserved.

Novel phase-transition behavior near liquid/liquid critical points of aqueous solutions: Formation of a third phase at the interface

We report a novel phase behavior in aqueous solutions of simple organic solutes near their liquid/liquid critical points, where a solid-like third phase appears at the liquid/liquid interface. The phenomenon has been found in three different laboratories. It appears in many aqueous systems of organic solutes and becomes enhanced upon the addition of salt to these solutions.

Formation of amorphous xenon nanoclusters and microstructure evolution in pulsed laser deposited Ti(62.5)Si(37.5) thin films during Xe ion irradiation

As deposited amorphous and crystallized thin films of Ti 37.5% Si alloy deposited by pulsed laser ablation technique were irradiated with 100 keV Xe(+) ion beam to an ion fluence of about 10(16) ions-cm(-2). Transmission electron microscopy revealed that the implanted Xe formed amorphous nanosized clusters in both cases. The Xe ion-irradiation favors nucleation of a fcc-Ti(Si) phase in amorphous films. However, in crystalline films, irradiation leads to dissolution of the Ti(5)Si(3) intermetallic phase. In both cases, Xe irradiation leads to the evolution of similar microstructures. Our results point to the pivotal role of nucleation in the evolution of the microstructure under the condition of ion implantation.

Propensity of formation of zipper architecture vs. Lincoln log arrangement in solvated molecular complexes of melamine with hydroxybenzoic acids

Molecular complexes of melamine with hydroxy and dihydroxybenzoic acids have been analyzed to assess the collective role of the hydroxyl (OH) and carboxyl (COOH) functionalities in the recognition process. In most cases, solvents of crystallization do play a major role in self-assembly and structure stabilization. Hydrated compounds generate linear chains of melamine molecules with acid molecules pendant resulting in a zipper architecture. However, anhydrous and solvated compounds generate tetrameric units consisting of melamine dimers together with acid molecules. These tetramers in turn interweave to form a Lincoln log arrangement in the crystal. The salt/co-crystal formation in these complexes cannot be predicted apriori on the basis of Delta pK(a) values as there exists a salt-to-co-crystal continuum.

Carbothermal reduction and nitridation reaction of SiOx and preoxidized SiOx: Formation of α-Si3N4 fibers

The chemical composition of amorphous SiOx has been analyzed by oxidation studies and is found to be SiO1.7. SiO1.7 appears to be a monophasic amorphous material on the basis of 29Si nuclear magnetic resonance, high resolution electron microscopy, and comparative behavior of a physical mixture of Si and SiO2. Carbothermal reduction and nitridation reactions have been carried out on amorphous SiO1.7 and on amorphous SiO2 obtained from oxidation of SiO1.7. At 1623 K reactions of SiO1.7 lead exclusively to the formation of Si2N2O, while those of SiO2 lead exclusively to the formation of Si3N4. Formation of copious fibers of α-Si3N4 was observed in the latter reaction. It is suggested that the partial pressure of SiO in equilibrium with reduced SiO1.7 and SiO2 during the reaction is the crucial factor that determines the chemistry of the products. The differences in the structures of SiO2 and SiO1.7 have been considered to be the origin of the differences in the SiO partial pressures of the reduction products formed prior to nitridation. The effect of the ratios, C:SiO1.7 and C:SiO2, in the reaction mixture as well as the effect of the temperature on the course of the reactions have also been investigated.

Standard Gibbs energy of formation of Pb2Ru2O6.5

Lead ruthenate is used as a bifunctional electrocatalyst for both oxygen evolution and reduction and as a conducting component in thick-film resistors. It also has potential applications in supercapacitors and solid oxide fuel cells. However, thermodynamic properties of the compound have not been reported in the literature. The standard Gibbs energy of formation has now been determined in the temperature range from 873 to 1123 K using a solid-state cell incorporating yttria-stabilized zirconia (YSZ) as the electrolyte, a mixture of PbO + Pb2Ru2O6.5 + Ru as the measuring electrode, and Ru + RuO2 as the reference. The design of the measuring electrode is based on a study of phase relations in the ternary system Pb–Ru–O at 1123 K. For the reaction,S0884291400095625_eqnU1 the standard enthalpy of formation and standard entropy at 298.15 K are estimated from the high-temperature measurements. An oxygen potential diagram for the system Pb–Ru–O is composed based on data obtained in this study and auxiliary information from the literature

Formation of amorphous xenon nanoclusters and microstructure evolution in pulsed laser deposited Ti62.5Si37.5 thin films during Xe ion irradiation

As deposited amorphous and crystallized thin films of Ti 37.5% Si alloy deposited by pulsed laser ablation technique were irradiated with 100 keV Xe+ ion beam to an ion fluence of about 1016 ions-cm−2. Transmission electron microscopy revealed that the implanted Xe formed amorphous nanosized clusters in both cases. The Xe ion-irradiation favors nucleation of a fcc-Ti(Si) phase in amorphous films. However, in crystalline films, irradiation leads to dissolution of the Ti5Si3 intermetallic phase. In both cases, Xe irradiation leads to the evolution of similar microstructures. Our results point to the pivotal role of nucleation in the evolution of the microstructure under the condition of ion implantation.