Terminal solid solubilities at 900–1000°C in the magnesium oxide-zinc oxide system measured using a magnesium fluoride solid-electrolyte galvanic cell

The terminal solid solubilities of the periclase (MgO-rich) and zincite (ZnO-rich) solid solutions in the MgO---ZnO system have been determined by measuring the activity of MgO using a solid-state galvanic cell of the type 02(g), Pt/MgO, MgF2//MgF2//{χMgO+(1-χ)ZnO}(s, sln), MgF2/Pt, O2(g) in the temperature range 900–1050°C. The ZnO activity was calculated by graphical Gibbs-Duhem integration. The activity-composition plots of both components exhibit a strong positive deviation from ideality and are characterised by a miscibility gap. The terminal solid solubilities of the periclase and zincite solid solutions obtained from the activity-composition plots are found to be in reasonable agreement with those reported in the literature.

Mechanism of gel-to-crystallite conversion process in the synthesis of nanocrystalline multinary oxides

Description of gel-to-crystallite conversion process is made towards the synthesis of nanocrystalline titanates and aluminates. Thermodynamic and kinetic factors governing the conversion of a gel to meta-stable and stable nanocrystalline products(s) are discussed. Correlations between these factors and the preparative conditions employed for the syntheses of titanates and aluminates are arrived at.

A PEFC With Pt-TiO2/C as Oxygen-Reduction Catalyst

Carbon-supported Pt-TiO2 (Pt-TiO2/C) catalyst with varying atomic ratio of Pt to Ti, namely, 1: 1, 2: 1, and 3: 1, is prepared by sol-gel method and its electrocatalytic activity toward oxygen-reduction reaction (ORR) is evaluated for the application in polymer electrolyte fuel cells (PEFCs). The optimum atomic ratio of Pt to Ti in Pt-TiO2/C and annealing temperature are established by cyclic voltammetry and fuel-cell-polarization studies. Pt-TiO2/C annealed at 750 degrees C with Pt and Ti in atomic ratio of 2: 1, namely, 750 Pt-TiO2/C (2: 1), shows enhanced electrocatalytic activity toward ORR. It is found that the incorporation of TiO2 with Pt ameliorates both electrocatalytic activity and stability of cathode in relation to pristine Pt cathode, currently being used in PEFCs. A power density of 0.75 W/cm(2) is achieved at 0.6 V for the PEFC with 750 Pt-TiO2/C (2: 1) as compared with 0.62 W/cm(2) at 0.6 V achieved with the PEFC comprising Pt/C as cathode catalyst while operating under identical conditions. Interestingly, carbon-supported Pt-TiO2 cathode exhibits only 6% loss in electrochemical surface area after 5000 potential cycles while it is as high as 25% for Pt/C. DOI: 10.1115/1.4002466]

Citrate gel processing of the perovskite lanthanide chromites

Chemically pure and stoichiometric lanthanide chromites, LnCrO3, where Ln = La, Pr, Nd, Sm, Gd, Dy, Ho, Yb, Lu and YCrO3 have been prepared by the calcination of the corresponding lanthanide bis(citrato)chromium {Ln[Cr(C6H5O7)2·nH2O} complexes at relatively low temperatures. Formation of the chromites was confirmed by powder X-ray diffraction, infrared and electronic spectra. The citrate gel process is found to be highly economical, time-saving and appropriate for the large-scale production of these ceramic materials at low temperatures compared with other non-conventional methods.

Gradient solid-electrolyte for use with dissimilar gas electrodes

The EMF of a solid-state cell, incorporating a composite solid-electrolyte with gradual variation in composition, and dissimilar gas electrodes, has been studied as a function of temperature and partial pressures at the electrodes. The cell with the configuration: Pt, CO2' + O2' parallel-to Na2CO3\Na(SO4)x(CO3)1-x\Na2SO4 parallel-to SO3'' + SO2'' + O2'', Pt x=0 x=1 was investigated in the temperature range 973 to 1079 K. The solid-electrolyte surface exposed to SO3 + SO2 + O2 gas mixture was doped-Na2SO4, whereas the CO2 + O2 gas mixture was in contact with pure Na2CO3. The composition of the solid solution between the carbonate and sulfate, with hexagonal structure, was varied gradually between the boundary values. It has been found that the EMF of the cell is close to that calculated from thermodynamic data, assuming unit transport number for Na+ ions. The gradient in the concentration of sulfate and carbonate ions in the electrolyte does not give rise to a significant diffusion potential.

Hydrazine carboxylate precursors to fine particle titania, zirconia and zirconium titanate

Titanyl hydrazine carboxylate dihydrate, TiO(N2H3COO)2.2H2O, zirconyl hydrazine carboxylate dihydrate, ZrO(N2H3COO)2.2H2O and their solid solution, ZrTiO2(N2H3COO)4.4H2O have been prepared for the first time and investigated as precursors to fine particle TiO2, ZrO2 and ZrTiO4 respectively. Titania(anatase) formed has a very high surface area of 110 m2/g and zirconium titanate showed very low dielectric loss (4 x 10(-4)).

Low-temperature preparation and characterization of phase-pure lanthanide chromates (V) by the citrate gel process

Phase-pure, crystalline lanthanide chromates LnCrO4 (V), where Ln = La, Pr, Nd, Sm, Gd, Dy, Ho, Yb, Lu and Y, have been prepared by the controlled combustion of the corresponding lanthanide biscitrato chromium (III) complexes at comparatively low temperatures. Formation of chromates (V) was confirmed by X-ray diffraction, infrared and electronic spectroscopy. Phase purity of the materials has also been confirmed by X-ray photoelectron spectroscopy.

Nafion®-bound carbon electrodes containing transitionmetal phthalocyanines for oxygen reduction in solid-polymer-electrolyte fuel cells

Catalytic activities of some transition metal-phthalocyanine complexes towards electroreduction of molecular oxygen are examined on Nafion®-bound and bare porous carbon electrodes in 2.5 M H2SO4 electrolyte. It is found that these metal complexes exhibit better catalytic activities towards oxygen reduction with the Nafion®-bound electrodes.

Strong metal-support interaction in Ni/TiO2 catalysts: in situ EXAFS and related studies

In situ EXAFS and X-ray diffraction investigations of Ni/TiO2 catalysts show that NiTiO3 is formed as an intermediate during calcination of catalyst precursors prepared by the wet-impregnation method; the intermediate is not formed when ion-exchange method is used for the preparation. On hydrogen reduction, NiTiO3 gives rise to Ni particles dispersed in the TiO2(rutile) matrix. The occurrence of the anatase-rutile transformation of the TiO2 support, the formation and subsequent decomposition/reduction of NiTiO3 as well as the unique interface properties of the Ni particles are all factors of importance in giving rise to metal-support interaction. Active TiO2(anatase) prepared from gel route gives an additional species involving Ni3+.

Structural, dielectric and ferroelectric properties of multilayer lithium tantalate thin films prepared by sol-gel technique

Multilayer lithium tantalate thin films were deposited on Pt-Si Si(111)/SiO2/TiO2/Pt(111)]substrates by sol-gel process. The films were annealed at different annealing temperatures (300, 450 and 650 degrees C) for 15 min. The films are polycrystalline at 650 degrees C and at other annealing conditions below 650 degrees C the films are in amorphous state. The films were characterized using X-ray diffraction, atomic force microscopy (AFM) and Raman spectroscopy. The AFM of images show the formation of nanograins of uniform size (50 nm) at 650 degrees C. These polycrystalline films exhibit spontaneous polarization of 1.5 mu C/cm(2) at an application of 100 kV/cm. The dielectric constant of multilayer film is very small (6.4 at 10 kHz) as compared to that of single crystal. (C) 2010 Elsevier B.V. All rights reserved.

Poly-ols Based Sol-Gel Synthesis of Zinc Oxide Thin Films

We demonstrate that the structural and optical properties of a sol-gel deposited zinc oxide thin film can be tuned by varying the composition of the sol, consisting of ethylene glycol and glycerol. A systematic study of the effect of the composition of sol on the mean grain size, thickness, and defect density of the zinc oxide film is presented. About 20% glycerol content in the sol is observed to improve the quality of the film, as evaluated by X-ray diffraction and photoluminescence studies. Thus, optimizing the composition of the sol for about 60 nm thick ZnO film using 20% glycerol resulted in the zinc oxide film that is about 80% transparent in visible spectrum, exhibiting electrical resistivity of about 18 Omega cm and field-effect mobility of 0.78 cm(2)/(V s). (C) 2010 The Electrochemical Society. DOI: 10.1149/1.3515894] All rights reserved.