Textural Characterization of Micro- and Mesoporous Carbons Using Combined Gas Adsorption and n-Nonane Preadsorption

Porous carbon and carbide materials with different structures were characterized using adsorption of nitrogen at 77.4 K before and after preadsorption of n-nonane. The selective blocking of the microporosity with n-nonane shows that ordered mesoporous silicon carbide material (OM-SiC) is almost exclusively mesoporous whereas the ordered mesoporous carbon CMK-3 contains a significant amount of micropores (25%). The insertion of micropores into OM-SiC using selective extraction of silicon by hot chlorine gas leads to the formation of ordered mesoporous carbide-derived carbon (OM-CDC) with a hierarchical pore structure and significantly higher micropore volume as compared to CMK-3, whereas a CDC material from a nonporous precursor is exclusively microporous. Volumes of narrow micropores, calculated by adsorption of carbon dioxide at 273 K, are in linear correlation with the volumes blocked by n-nonane. Argon adsorption measurements at 87.3 K allow for precise and reliable calculation of the pore size distribution of the materials using density functional theory (DFT) methods.

Micro/Mesoporous Activated Carbons Derived from Polyaniline: Promising Candidates for CO2 Adsorption

A series of activated carbons were prepared by carbonization of polyaniline at different temperatures, using KOH or K2CO3 as activating agent. Pure microporous or micro/mesoporous activated carbons were obtained depending on the preparation conditions. Carbonization temperature has been proven to be a key parameter to define the textural properties of the carbon when using KOH. Low carbonization temperatures (400–650 °C) yield materials with a highly developed micro- and mesoporous structure, whereas high temperatures (800 °C) yield microporous carbons. Some of the materials prepared using KOH exhibit a BET surface area superior to 4000 m2/g, with total pore volume exceeding 2.5 cm3/g, which are among the largest found for activated carbons. On the other hand, microporous materials are obtained when using K2CO3, independently of carbonization temperature. Some of the materials were tested for CO2 capture due to their high microporosity and N content. The adsorption capacity for CO2 at atmospheric pressure and 0 °C achieves a value of ∼7.6 mmol CO2/g, which is among the largest reported in the literature. This study provides guidelines for the design of activated carbons with a proper N/C ratio for CO2 capture at atmospheric pressure.

Water characteristics in cooked beef as influenced by ageing and high-pressure treatment -an NMR micro imaging study

The water characteristics in cooked pressure-heat treated (45 degreesC for 45 min prior to pressurisation at 150 MPa for 30 min) and non-pressurised, cooked (control) samples of beef Longissimus aged for 1, 3, 8 or 16 days were studied by nuclear magnetic resonance microscopy. A multi-echo sequence was used to obtain T2 images, and independent of ageing period, the T2 values were found to be lower in pressure-heat treated meat revealing alterations in water characteristics of pressure-treated, cooked meat compared with cooked meat. With increasing ageing duration, the T2 values in both pressure-treated, cooked and cooked meat decreased indicating that the water became more tightly trapped in the protein network. In addition, independent of length of ageing period the relationship between cooking loss in the cooked meat and transverse relaxation differed between non-pressurised and pressure-treated meat. which reveals that the mechanisms changing the water properties in beef during ageing are different from those occuring during pressure-heat treatment of meat. (C) 2003 Elsevier Ltd. All rights reserved.

Bacterial community structure associated with white band disease in the elkhorn coral Acropora palmata determined using culture-independent 16S rRNA techniques

Culture-independent molecular (16S ribosomal RNA) techniques showed distinct differences in bacterial communities associated with white band disease (WBD) Type I and healthy elkhorn coral Acropora palmata. Differences were apparent at all levels, with a greater diversity present in tissues of diseased colonies. The bacterial community associated with remote, non-diseased coral was distinct from the apparently healthy tissues of infected corals several cm from the disease lesion. This demonstrates a whole-organism effect from what appears to be a localised disease lesion, an effect that has also been recently demonstrated in white plague-like disease in star coral Montastraea annularis. The pattern of bacterial community structure changes was similar to that recently demonstrated for white plague-like disease and black band disease. Some of the changes are likely to be explained by the colonisation of dead and degrading tissues by a micro-heterotroph community adapted to the decomposition of coral tissues. However, specific ribosomal types that are absent from healthy tissues appear consistently in all samples of each of the diseases. These ribotypes are closely related members of a group of alpha-proteobacteria that cause disease, notably juvenile oyster disease, in other marine organisms. It is clearly important that members of this group are isolated for challenge experiments to determine their role in the diseases.

ASSOCIATIVISMO EMPRESARIAL ENTRE MICRO E PEQUENAS EMPRESAS: A EXPERIÊNCIA DO GRANDE ABC COM O PROJETO EMPREENDER (SEBRAE)

O associativismo empresarial aparece como forma de desenvolvimento regional, seja este econômico, social ou cultural, e é grande aliado para o surgimento e crescimento das micro e pequenas empresas. É um tema já vivenciado e estudado por vários países do mundo, entre eles europeus e especificamente italianos, mas ainda pouco estudado e conhecido no Brasil. A presente pesquisa objetivou analisar o associativismo empresarial entre micro e pequenas empresas (MPEs) na região do Grande ABC (GABC) pelo Projeto Empreender (SEBRAE) relacionando seus dados com os publicados do relatório 2003/5 de autoria do Observatório Europeu de estudos sobre pequenas e médias empresas europeias, analisando as formas de associativismo aqui ocorridas, além de identificar o perfil das empresas e empresários envolvidos no projeto. Para tal análise foram coletados dados de um total de 63 empresas do Projeto Empreender, nos núcleos de Santo André, São Caetano do Sul e Ribeirão Pires. Do GABC foram coletados dados utilizando o instrumento desenvolvido pelo Observatório Europeu de estudos sobre pequenas e médias empresas. A análise dos dados coletados no GABC em relação aos dados europeus se fez necessária para que pudessem ser encontrados pontos de divergências e convergências em cada uma das experiências, objetivando o aprendizado e evolução do tema. A escolha do GABC foi motivada pelo fato da região passar por mudanças no seu perfil econômico, passando de berço e grande pólo das grandes indústrias para um grande centro de pequenas empresas prestadoras de serviços. Após coleta e análise dos dados, percebeu-se que a experiência do GABC e a ocorrida na Itália se parecem em muitos aspectos, porém tem grandes diferenças estruturais. Enquanto o projeto europeu é de responsabilidade de um órgão da União Europeia, aqui o projeto é de autoria do SEBRAE e sofre grandes conflitos com as Associações Comerciais e Industriais (ACIs) da região quando o tema é custeio das despesas das pessoas e estrutura que envolve a implantação do projeto. Além disso, conclui-se que é necessária uma maior aproximação dos municípios com o projeto, tendo em vista que isto poderia ser fator de incentivo a entrada de novas empresas além de fator de aumento de seriedade do sistema. Mais dois dados merecem destaque. Primeiro o fato do Projeto Empreender ter pouca visibilidade regional, ou seja, ser muito pouco divulgado, e o fato da agência de desenvolvimento do GABC não ter aproximação alguma com o projeto. Por último, surgem dados no decorrer da pesquisa que rompem a barreira das teorias administrativas conhecidas, tais como a amizade como fator de associativismo. Portanto, os resultados obtidos com essa pesquisa apontam para a influência no incentivo ao desenvolvimento do processo associativista na região do GABC, além de servir como incentivador para a aproximação de outros atores sociais no processo.(AU)

Vibrational dynamics and structure of natural feldspars

The present study gives a contribution to the knowledge on the Na-feldspar and plagioclases, extending the database of the Raman spectra of plagioclases with different chemical compositions and structural orders. This information may be used for the future planetary explorations by “rovers”, for the investigation of ceramics nanocrystal materials and for the mineralogical phase identification in sediments. Na-feldspar and plagioclase solid solution have been investigated by Raman spectroscopy in order to determine the relationships between the vibrational changes and the plagioclase crystal chemistry and structure. We focused on the Raman micro-spectroscopy technique, being a non-destructive method, suited for contactless analysis with high spatial resolution. Chemical and structural analyses have been performed on natural samples to test the usefulness of Raman spectroscopy as a tool in the study of the pressure-induced structural deformations, the disordering processes due to change in the Al-Si distribution in the tetrahedral sites and, finally, in the determination of the anorthitic content (Anx) in plagioclase minerals. All the predicted 39 Ag Raman active modes have been identified and assigned to specific patterns of atomic vibrational motion. A detailed comparison between experimental and computed Raman spectra has been performed and previous assignments have been revised, solving some discrepancies reported in recent literature. The ab initio calculation at the hybrid HF/DFT level with the WC1LYP Hamiltonian has proven to give excellent agreement between calculated and experimentally measured Raman wavenumbers and intensities in triclinic minerals. A short digression on the 36 infrared active modes of Na-feldspar has been done too. The identification of all 39 computed Raman modes in the experimentally measured spectra of the fully ordered Na-feldspar, known as low albite, along with the detailed description of each vibrational mode, has been essential to extend the comparative analysis to the high pressure and high temperature structural forms of albite, which reflect the physical–chemical conditions of the hosting rocks. The understanding of feldspar structure response to pressure and temperature is crucial in order to constrain crustal behaviour. The compressional behaviour of the Na-feldspar has been investigated for the first time by Raman spectroscopy. The absence of phase transitions and the occurrence of two secondary compression mechanisms acting at different pressures have been confirmed. Moreover, Raman data suggest that the internal structural changes are confined to a small pressure interval, localized around 6 GPa, not spread out from 4 to 8 GPa as suggested by previous X-rays studies on elasticity. The dominant compression mechanisms act via tetrahedral tilting, while the T-O bond lengths remain nearly constant at moderate compressional regimes. At the spectroscopic level, this leads to the strong pressure dependencies of T-O-T bending modes, as found for the four modes at 478, 508, 578 and 815 cm-1. The Al-Si distribution in the tetrahedral sites affects also the Raman spectrum of Na-feldspar. In particular, peak broadening is more sensitive than peak position to changes in the degree of order. Raman spectroscopy is found to be a good probe for local ordering, in particular being sensitive to the first annealing steps, when the macroscopic order parameter is still high. Even though Raman data are scattered and there are outliers in the estimated values of the degree of order, the average peak linewidths of the Na-feldspar characteristic doublet band, labelled here as υa and υb, as a function of the order parameter Qod show interesting trends: both peak linewidths linearly increase until saturation. From Qod values lower than 0.6, peak broadening is no more affected by the Al-Si distribution. Moreover, the disordering process is found to be heterogeneous. SC-XRD and Raman data have suggested an inter-crystalline inhomogeneity of the samples, i.e., the presence of regions with different defect density on the micrometric scale. Finally, the influence of Ca-Na substitution in the plagioclase Raman spectra has been investigated. Raman spectra have been collected on a series of well characterized natural, low structural plagioclases. The variations of the Raman modes as a function of the chemical composition and the structural order have been determined. The number of the observed Raman bands at each composition gives information about the unit-cell symmetry: moving away from the C1 structures, the number of the Raman bands enhances, as the number of formula units in the unit cell increases. The modification from an “albite-like” Raman spectrum to a more “anorthite-like” spectrum occurs from sample An78 onwards, which coincides with the appearance of c reflections in the diffraction patterns of the samples. The evolution of the Raman bands υa and υb displays two changes in slope at ~An45 and ~An75: the first one occurs between e2 and e1 plagioclases, the latter separates e1 and I1 plagioclases with only b reflections in their diffraction patterns from I1 and P1 samples having b and c reflections too. The first variation represents exactly the e2→e1 phase transitions, whereas the second one corresponds in good approximation to the C1→I1 transition, which has been determined at ~An70 by previous works. The I1→P1 phase transition in the anorthite-rich side of the solid solution is not highlighted in the collected Raman spectra. Variations in peak broadening provide insights into the behaviour of the order parameter on a local scale, suggesting an increase in the structural disorder within the solid solution, as the structures have to incorporate more Al atoms to balance the change from monovalent to divalent cations. All the information acquired on these natural plagioclases has been used to produce a protocol able to give a preliminary estimation of the chemical composition of an unknown plagioclase from its Raman spectrum. Two calibration curves, one for albite-rich plagioclases and the other one for the anorthite-rich plagioclases, have been proposed by relating the peak linewidth of the most intense Raman band υa and the An content. It has been pointed out that the dependence of the composition from the linewidth can be obtained only for low structural plagioclases with a degree of order not far away from the references. The proposed tool has been tested on three mineralogical samples, two of meteoric origin and one of volcanic origin. Chemical compositions by Raman spectroscopy compare well, within an error of about 10%, with those obtained by elemental techniques. Further analyses on plagioclases with unknown composition will be necessary to validate the suggested method and introduce it as routine tool for the determination of the chemical composition from Raman data in planetary missions.

Highly thermally responsive hybrid in-fiber slab waveguide grating structure with a plastic core and a silica cladding

A 1.2(height)×125(depth)×500(length) micro-slot was engraved along a fiber Bragg grating by chemically assisted femtosecond laser processing. By filling epoxy and UV-curing, waveguide with plastic-core and silica-cladding was created, presenting high thermal responding coefficient of 211pm/°C.

Highly thermally responsive hybrid in-fiber sSlab waveguide grating structure with a plastic core and a silica cladding

A 1.2(height)×125(depth)×500(length) micro-slot was engraved along a fiber Bragg grating by chemically assisted femtosecond laser processing. By filling epoxy and UV-curing, waveguide with plastic-core and silica-cladding was created, presenting high thermal responding coefficient of 211pm/°C.

A comparison of the economic performance of different micro-states, and between micro-states and larger countries

The economic performance of micro-states and those sub-national regions enjoying a high degree of autonomy is a generally under-researched area. This paper builds on earlier research (Armstrong and Read, 1995) by employing quantitative techniques to test: 1. (a) the extent to which the economic performance of micro-states differs, by comparing their GNP per capita with that of the region in which they are located and with the countries to which they are adjacent; 2. (b) whether some micro-states perform better than others as a result of differences in their economic structure; and 3. (c) whether the rates of growth of micro-states have been faster or slower than those of larger countries. Considerable diversity among micro-states is revealed, although most exhibit strong economic performance.

An investigation of thin amorphous carbon-based sputtered coatings for MEMS and micro-engineering applications

The work presented in this thesis describes an investigation into the production and properties of thin amorphous C films, with and without Cr doping, as a low wear / friction coating applicable to MEMS and other micro- and nano-engineering applications. Firstly, an assessment was made of the available testing techniques. Secondly, the optimised test methods were applied to a series of sputtered films of thickness 10 - 2000 nm in order to: (i) investigate the effect of thickness on the properties of coatingslcoating process (ii) investigate fundamental tribology at the nano-scale and (iii) provide a starting point for nanotribological coating optimisation at ultra low thickness. The use of XPS was investigated for the determination of Sp3/Sp2 carbon bonding. Under C 1s peak analysis, significant errors were identified and this was attributed to the absence of sufficient instrument resolution to guide the component peak structure (even with a high resolution instrument). A simple peak width analysis and correlation work with C KLL D value confirmed the errors. The use of XPS for Sp3/Sp2 was therefore limited to initial tentative estimations. Nanoindentation was shown to provide consistent hardness and reduced modulus results with depth (to < 7nm) when replicate data was suitably statistically processed. No significant pile-up or cracking of the films was identified under nanoindentation. Nanowear experimentation by multiple nanoscratching provided some useful information, however the conditions of test were very different to those expect for MEMS and micro- / nano-engineering systems. A novel 'sample oscillated nanoindentation' system was developed for testing nanowear under more relevant conditions. The films were produced in an industrial production coating line. In order to maximise the available information and to take account of uncontrolled process variation a statistical design of experiment procedure was used to investigate the effect of four key process control parameters. Cr doping was the most significant control parameter at all thicknesses tested and produced a softening effect and thus increased nanowear. Substrate bias voltage was also a significant parameter and produced hardening and a wear reducing effect at all thicknesses tested. The use of a Cr adhesion layer produced beneficial results at 150 nm thickness, but was ineffective at 50 nm. Argon flow to the coating chamber produced a complex effect. All effects reduced significantly with reducing film thickness. Classic fretting wear was produced at low amplitude under nanowear testing. Reciprocating sliding was produced at higher amplitude which generated three body abrasive wear and this was generally consistent with the Archard model. Specific wear rates were very low (typically 10-16 - 10-18 m3N-1m-1). Wear rates reduced exponentially with reduced film thickness and below (approx.) 20 nm, thickness was identified as the most important control of wear.

A study of the micro-mechanics of granular media

The development of more realistic constitutive models for granular media, such as sand, requires ingredients which take into account the internal micro-mechanical response to deformation. Unfortunately, at present, very little is known about these mechanisms and therefore it is instructive to find out more about the internal nature of granular samples by conducting suitable tests. In contrast to physical testing the method of investigation used in this study employs the Distinct Element Method. This is a computer based, iterative, time-dependent technique that allows the deformation of granular assemblies to be numerically simulated. By making assumptions regarding contact stiffnesses each individual contact force can be measured and by resolution particle centroid forces can be calculated. Then by dividing particle forces by their respective mass, particle centroid velocities and displacements are obtained by numerical integration. The Distinct Element Method is incorporated into a computer program 'Ball'. This program is effectively a numerical apparatus which forms a logical housing for this method and allows data input and output, and also provides testing control. By using this numerical apparatus tests have been carried out on disc assemblies and many new interesting observations regarding the micromechanical behaviour are revealed. In order to relate the observed microscopic mechanisms of deformation to the flow of the granular system two separate approaches have been used. Firstly a constitutive model has been developed which describes the yield function, flow rule and translation rule for regular assemblies of spheres and discs when subjected to coaxial deformation. Secondly statistical analyses have been carried out using data which was extracted from the simulation tests. These analyses define and quantify granular structure and then show how the force and velocity distributions use the structure to produce the corresponding stress and strain-rate tensors.

Schematic structure and the modulation of propositions in economics forecasting text

Working within the framework of the branch of Linguistics known as discourse analysis, and more specifically within the current approach of genre analysis, this thesis presents an analysis of the English of economic forecasting. The language of economic forecasting is highly specialised and follows certain conventions of structure and style. This research project identifies these characteristics and explains them in terms of their communicative function. The work is based on a corpus of texts published in economic reports and surveys by major corporate bodies. These documents are targeted at an international expert readership familiar with this genre. The data is analysed at two broad levels: firstly, the macro-level of text structure which is described in terms of schema-theory, a currently influential model of analysis, and, secondly, the micro-level of authors' strategies for modulating the predictions which form the key move in the forecasting schema. The thesis aims to contribute to the newly developing field of genre analysis in a number of ways: firstly, by a coverage of a hitherto neglected but intrinsically interesting and important genre (Economic Forecasting); secondly, by testing the applicability of existing models of analysis at the level of schematic structure and proposing a genre-specific model; thirdly by offering insights into the nature of modulation of propositions which is often broadly classified as `hedging' or `modality', and which has been recently described as lq`an area for prolonged fieldwork'. This phenomenon is shown to be a key feature of this particular genre. It is suggested that this thesis, in addition to its contribution to the theory of genre analysis, provides a useful basis for work by teachers of English for Economics, an important area of English for Specific Purposes.

Highly thermally responsive hybrid in-fiber slab waveguide grating structure with a plastic core and a silica cladding

A 1.2(height)×125(depth)×500(length) micro-slot was engraved along a fiber Bragg grating by chemically assisted femtosecond laser processing. By filling epoxy and UV-curing, waveguide with plastic-core and silica-cladding was created, presenting high thermal responding coefficient of 211pm/°C.

Highly thermally responsive hybrid in-fiber sSlab waveguide grating structure with a plastic core and a silica cladding

A 1.2(height)×125(depth)×500(length) micro-slot was engraved along a fiber Bragg grating by chemically assisted femtosecond laser processing. By filling epoxy and UV-curing, waveguide with plastic-core and silica-cladding was created, presenting high thermal responding coefficient of 211pm/°C.

Fabry-Perot micro-structured polymer optical fibre sensors for opto-acoustic endoscopy

Opto-Acoustic Endoscopy (OAE) requires sensors with a high sensitivity and small physical dimensions in order to facilitate integration into an endoscope of less than 1mm in diameter. We present fibre Bragg grating (FBG) and Fabry- Perot intrinsic fibre sensors for ultrasound detection. We present a structure profile characterisation setup to analyse tune the fibre sensors in preparation for ultrasonic detection. We evaluate the suitability of the different structures and grating parameters for ultrasonic sensing. By analysing the prepared gratings, we enable the optimisation of the profile and a simplification of the detection regime for an optimal interferometric OAE configuration.