977 resultados para ferroelectric and polymeric precursor
Resumo:
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
Resumo:
NiWO4 and ZnWO4 were synthesized by the polymeric precursor method at low temperatures with zinc or nickel carbonate as secondary phase. The materials were characterized by thermal analysis (TG/DTA), infrared spectroscopy, UV-Vis spectroscopy and X-ray diffraction. NiWO4 was crystalline after calcination at 350 A degrees C/12 h while ZnWO4 only crystallized after calcination at 400 A degrees C for 2 h. Thermal decomposition of the powder precursor of NiWO4 heat treated for 12 h had one exothermic transition, while the precursor heat treated for 24 h had one more step between 600 and 800 A degrees C with a small mass gain. Powder precursor of ZnWO4 presented three exothermic transitions, with peak temperatures and mass losses higher than NiWO4 has indicating that nickel made carbon elimination easier.
Resumo:
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
Resumo:
SrBi2(Ta0.5Nb0.48W0.02)(2)O-9 powders (SBTN-W) were prepared by the polymeric precursor method. The influence of annealing temperature on the phase formation and specific surface area was evaluated. TG/DTA associated with X-ray diffraction (XRD) analyses showed the formation of perovskite phase at around 500-600 degrees C. An orthorhombic structure with A21am space group was identified by Rietveld refinement. BET analysis revealed that the specific surface area reduces with increasing thermal annealing. SEM micrographies showed grains in an almost-spherical morphology with the presence of agglomerates. (C) 2006 Elsevier B.V. All rights reserved.
Resumo:
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Ultrafine ordered and disordered SrZrO3 powders were prepared by the polymeric precursor method. The structural evolution from structural disorder to order was monitored by X-ray diffraction and X-ray absorption near-edge spectroscopy. Complex cluster vacancies [ZrO5 center dot V-O(Z)] and [SrOII center dot V-O(Z)] (where V-O(Z) = V-O(X), V-O(center dot) and V-O(center dot center dot)) were proposed for disordered powders. The intense violet-blue light photoluminescence emission measured at room temperature in the disordered powders was attributed to complex cluster vacancies. High-level quantum mechanical calculations within the density functional theory framework were used to interpret the experimental results. (C) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Resumo:
In this study undoped and Cr, Sb or Mo doped TiO(2) were synthesized by polymeric precursor method and characterized by X-ray diffraction, UV-VIS spectroscopy, infrared spectroscopy and thermogravimetry (TG). The TG curves showed a continuous mass loss assigned to the hydroxyl elimination and Cr(6+) reduction. Doped TiO(2) samples showed a higher mass loss assigned to water and gas elimination at lower temperatures. In these doped materials a decrease in the anatase-rutile phase transition temperature was observed. After calcination at 1,000 A degrees C, rutile was obtained as a single phase material without the presence of Cr(6+).
Resumo:
Nowadays solid state chemists have the possibility of work with low temperature strategies to obtain solid state materials with appropriate physical and chemical properties for useful technological applications. Photonic core shell materials having a core and shell domains composed by a variety of compounds have been synthesized by different methods. In this work we used silica-germania soot prepared by vapor-phase axial deposition as a core where a nanoshell of Eu2O3 was deposited. A new sol-gel like method was used to obtain the Eu2O3 nanoshell coating the SiO2-GeO2 particles, which was prepared by the polymeric precursor method. The photophysical properties of Eu3+ were used to obtain information about the rare earth surrounding in the SiO2-GeO2@Eu2O3 material during the sintering process. The sintering process was followed by the luminescence spectra of Eu3+ and all the samples present the characteristic emission related to the D-5(0) -> F-7(J) (J=0, 1, 2, 3 and 4). The ratios of the D-5(0) -> F-7(2)/D-5(0) -> F-7(1) emission intensity for the SiO2-GeO2@Eu2O3 systems were calculated and it was observed an increase in its values, indicating a low symmetry around the Eu3+ as the temperature increases.
Resumo:
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Intense and broad photoluminescence (PL) emission at room temperature was observed on structurally disordered Ba[Zr0.25Ti0.75]O-3 (BZT) powders synthesized by the polymeric precursor method. BZT powders were annealed at 573 K for different times and at 973 K for 2 h in oxygen atmosphere. The single-phase cubic perovskite structure of the powder annealed at 973 K for 2 It was identified by X-ray diffraction and Fourier transform Raman techniques. PL emission increased with the increase of annealing time, which reached its maximum value in the powder annealed at 573 K for 192 h. First principles quantum mechanical calculations based on density functional theory (B3LYP level) were employed to study the electronic structure of ordered and disordered models. The theoretical calculations and experimental measurements of Ultraviolet-visible absorption spectroscopy indicate that the presence of intermediary energy levels in the band gap is favorable for the intense and broad PL emission at room temperature in disordered BZT powders. The PL behavior is probably due the existence of a charge gradient on the disordered structure, denoted by means of a charge transfer process from [TiO5]-[ZrO6] or [TiO6]-[ZrO5] clusters to [TiO6]-[ZrO6] clusters. (C) 2008 Elsevier Ltd. All rights reserved.
Resumo:
In this work, a SiO2 spherical were prepared by the Stober Method and then recovered with a single layer of Eu2O3 oxide (SiO2@Eu2O3) obtained by the Polymeric Precursor Method. The SiO2@Eu2O3 powder was heated treated at 100, 300, 400, 500 and 800 A degrees C. The samples were characterized by the Scanning Electonic Microscopy (SEM), Thermal Analysis (TGA/DTA), and the luminescent properties of the SiO2@Eu2O3 powders were studied by their emission and excitation spectra as well as by the lifetime measurements of the Eu3+ D-5(0) -> aEuro parts per thousand F-7(2) transition. The SEM analysis shows that the silica prepared by the Stober Method is spherical with a particle size of 460 nm. The emission spectra of the SiO2@Eu2O3 powders presented the Eu3+ characteristics bands related to the D-5(0) -> aEuro parts per thousand F-7(J) (J = 0, 1, 2, 3, 4) transitions at 577, 591, 616, 649 and 695 nm, respectively. The band related to the D-5(0) -> aEuro parts per thousand F-7(2) transition is the most intense in the spectra, and its intensity decreases with the temperature enhancement. The decay curves of the SiO2@Eu2O3 samples presented monoexponential features, and the obtained lifetime values were higher than the Eu2O3 oxide. It was possible to conclude that the D-5(0) -> aEuro parts per thousand F-7(2) hypersensitive transition is strongly dependent on the Eu3+ surrounding.
Resumo:
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Resumo:
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)