Nanostructured Copper(II) oxide thin film for alcohol sensing

Nanostructured copper(II) oxide film was deposited using reactive DC magnetron sputtering. It has been characterized using XRD, EDAX, XPS, and FESEM. The grain size of copper oxide film was found to be 40-65 nm with size distribution. The entire study was divided into two parts. In the first part, the film has been studied for its response to alcohol at different temperatures to find the optimum sensing temperature, whereas in the second part, the film sensitivity to different alcohol concentrations were studied at fixed optimum operating temperature. The optimum temperature for the response of ethanol was observed to be 400 C,and the response for different concentrations was found to be almost linear.

Contribution of different physical forces to the disjoining pressure of a thin water film being pressed by an oil droplet

With an objective to understand the nature of forces which contribute to the disjoining pressure of a thin water film on a steel substrate being pressed by an oil droplet, two independent sets of experiments were done. (i) A spherical silica probe approaches the three substrates; mica, PTFE and steel, in a 10 mM electrolyte solution at two different pHs (3 and 10). (ii) The silica probe with and without a smeared oil film approaches the same three substrates in water (pH = 6). The surface potential of the oil film/water was measured using a dynamic light scattering experiment. Assuming the capacity of a substrate for ion exchange the total interaction force for each experiment was estimated to include the Derjaguin-Landau-Verwey-Overbeek (DLVO) force, hydration repulsion, hydrophobic attraction and oil-capillary attraction. The best fit of these estimates to the force-displacement characteristics obtained from the two sets of experiment gives the appropriate surface potentials of the substrates. The procedure allows an assessment of the relevance of a specific physical interaction to an experimental configuration. Two of the principal observations of this work are: (i) The presence of a surface at constant charge, as in the presence of an oil film on the probe, significantly enhances the counterion density over what is achieved when both the surfaces allow ion exchange. This raises the corresponding repulsion barrier greatly. (ii) When the substrate surface is wettable by oil, oil-capillary attraction contributes substantially to the total interaction. If it is not wettable the oil film is deformed and squeezed out. (C) 2010 Elsevier Inc. All rights reserved.

Thin Film Strain Gauges--an Overview

This review gives a brief description of the historical development followed by the origin and the principle of operation of strain gauges. The features of an ideal strain gauge for measurement purposes and the general classes of strain gauges are given. The remaning part is devoted to an important development in strain gauge technology, namely thin film strain gauges. After highlighting the advantages of thin film strain gauges, a review of current data is given. Detailed description of metallic thin film strain gauges is provided and avaliable information on alloy semiconductor and cermet films for their possible use as strain gauge elements has also been included. The importance of ion implantation in tailoring the properties of strain gauges is highlighted. 33 ref.--AA

Stress induced phase transition in monomolecular perfluroalkylsilane film self assembled on aluminium surface

We control the stiffnesses of two dual double cantelevers placed in series to control penetration into a perflurooctyltrichlorosilane monolayer self assembled on aluminium and silicon substrates. The top cantilever which carries the probe is displaced with respect to the bottom cantilever which carries the substrate, the difference in displacement recorded using capacitors gives penetration. We further modulate the input displacement sinusoidally to deconvolute the viscoelastic properties of the monolayer. When the intervention is limited to the terminal end of the molecule there is a strong viscous response in consonance with the ability of the molecule to dissipate energy by the generation of gauche defects freely. When the intervention reaches the backbone, at a contact mean pressure of 0.2GPa the damping disappears abruptly and the molecule registers a steep rise in elastic modulus and relaxation time constant, with increasing contact pressure. We offer a physical explanation of the process and describe this change as due to a phase transition from a liquid like to a solid like state.

Terahertz Spectroscopy of Single-Walled Carbon Nanotubes in a Polymer Film: Observation of Low-Frequency Phonons

We investigate the dielectric response of single-walled carbon nanotubes dispersed in poly(vinyl alcohol) matrix by using terahertz time domain spectroscopy. Frequency-dependent real and imaginary parts of the complex dielectric function are measured experimentally in the terahertz regime. The low-frequency phonons of carbon nanotubes, though predicted theoretically, are directly observed for the first time at frequencies 0.26, 0.60, and 0.85 THz. Further, a broad resonance is observed at 1.15 THz associated with the longitudinal acoustic mode of vibration of straight-chain segments of the long polymeric molecules in the film. The latter is observed at 1.24 THz for a pristine polymer film and has been used to derive the size of crystalline lamellae in the film.

Deformation and failure of a film/substrate system subjected to spherical indentation: Part 1. Experimental validation of stresses and strains derived using Hankel transform technique in an elastic film/substrate system

Our concern here is to rationalize experimental observations of failure modes brought about by indentation of hard thin ceramic films deposited on metallic substrates. By undertaking this exercise, we would like to evolve an analytical framework that can be used for designs of coatings. In Part I of the paper we develop an algorithm and test it for a model system. Using this analytical framework we address the issue of failure of columnar TiN films in Part II [J. Mater. Res. 21, 783 (2006)] of the paper. In this part, we used a previously derived Hankel transform procedure to derive stress and strain in a birefringent polymer film glued to a strong substrate and subjected to spherical indentation. We measure surface radial strains using strain gauges and bulk film stresses using photo elastic technique (stress freezing). For a boundary condition based on Hertzian traction with no film interface constraint and assuming the substrate constraint to be a function of the imposed strain, the theory describes the stress distributions well. The variation in peak stresses also demonstrates the usefulness of depositing even a soft film to protect an underlying substrate.

Direct Writing of Copper Film Patterns by Laser-Induced Decomposition of Copper Acetate

Direct writing of patterns is being widely attempted in the field of microelectronic circuit/device manufacture. Use of this technique eliminates the need for employing photolithographic process. Laser induced direct writing can be achieved by (i) Photochemical reaction [i] , (ii) Evaporation from target material [2], and (iii) decomposition.Micron size features of palladium and copper through decomposition of palladium acetate and copper formate respectively on quartz and silicon using Argon ion laser have been reported [3,4] .In this commuication we report a technique for both single line and large area depositon of copper through decomposition of copper acetate,(CH3COO)2Cu, on alumina substrates.Nd:YAG laser known for its reliability and low maintenance cost as compared to excimer and other gas lasers is used. This technique offers an attractive and economical alternative for manufacture of thin film microcircuits.

Photo induced optical changes in Sb/As2S3 multilayered film and (As2S3)(0.93)Sb-0.07 film of equal thickness

The increase in optical band gap (photo bleaching) due to light illumination was studied at room temperature as well as at low (4.2 K) temperature for Sb/As2S3 multilayered film of 640 nm thickness by Fourier Transform Infrared Technique. The interdiffusion of Sb into As2S3 matrix results the formation of Sb-As2S3 ternary solid solutions which is explained by the change in optical band gap (E-g), absorption coefficient (alpha), Tauc parameter (B-1/2), Urbach edge (E-e). At the same time, photo darkening phenomena was observed in (As2S3)(0.93)Sb-0.07 film of same thickness both at low and room temperatures. From our X-ray Photoelectron Spectroscopy measurements,we are able to show that some of the As-As, S-S and Sb-Sb bonds are converted into As-S and S-Sb bonds in case of multilayers. We found that the energetically favoured heteropolar bond formation take place by a phonon-assisted mechanism using the lone pair pi electrons of S-2(0). But in case of (As2S3)(0.93)Sb-0.02 film, the homopolar bonds are playing a major role. (C) 2010 Elsevier B.V. All rights reserved.

Polycrystalline Lead Tin Chalcogenide Thin Film Grown by Spray Pyrolysis

PbSnS2 thin film has been prepared for the first time by spray pyrolysis technique on FTO substrate at 570K. The preliminary optical and structural characteristics of the film have been reported. The optical studies showed that the value of the fundamental absorption edge lies at 1.47eV and a low energy absorption band tail has been observed. The prepared film is p- type electrical conductivity, polycrystalline in nature and has an orthorhombic crystal structure. The value of an average grain size of the film is 350Å.

Equivalent circuit parameters of the film-covered magnesium/electrolyte interface in Mg/MnO2 dry cells from transient and ac impedance measurements

The electrochemical properties of the film-covered anode/solution interface in the magnesium/ manganese dioxide dry cell have been evaluated. The most plausible electrical equivalent circuit description of the Mg/solution interface with the passive film intact, has been identified. These results are based on the analysis of ac impedance and voltage transient measurements made on the dry cell under conditions which cause no damage to the protective passive film on the anode. The study demonstrates the complementary character of impedance and transient measurements when widely different frequency ranges are sampled in each type of investigation. The values and temperature dependence of the anode-film resistance, film capacitance, double-layer capacitance and charge-transfer resistance of the film-covered magnesium/solution interface have been determined. The magnitude of these values and its implications in understanding the important performance aspects of the magnesium/manganese dioxide dry cell are discussed. The study may be extended, in principle, to Li, Al and Ca batteries.

Equivalent circuit parameters of the film-covered magnesium/electrolyte interface in Mg/MnO2 dry cells from transient and ac impedance measurements

The electrochemical properties of the film-covered anode/solution interface in the magnesium/ manganese dioxide dry cell have been evaluated. The most plausible electrical equivalent circuit description of the Mg/solution interface with the passive film intact, has been identified. These results are based on the analysis of ac impedance and voltage transient measurements made on the dry cell under conditions which cause no damage to the protective passive film on the anode. The study demonstrates the complementary character of impedance and transient measurements when widely different frequency ranges are sampled in each type of investigation. The values and temperature dependence of the anode-film resistance, film capacitance, double-layer capacitance and charge-transfer resistance of the film-covered magnesium/solution interface have been determined. The magnitude of these values and its implications in understanding the important performance aspects of the magnesium/manganese dioxide dry cell are discussed. The study may be extended, in principle, to Li, Al and Ca batteries.

Antimicrobial activity of highly stable silver nano particles embedded in agar-agar matrix as a thin film

Highly stable silver nanoparticles (Ag NPs) in agar-agar (Ag/agar) as inorganic-organic hybrid were obtained as free-standing film by in situ reduction of silver nitrate by ethanol. The antimicrobial activity of Ag/agar film on Escherichia coli (E. coil), Staphylococcus aureus (S. aureus), and Candida albicans (C albicans) was evaluated in a nutrient broth and also in saline solution. In particular, films were repeatedly tested for antimicrobial activity after recycling. UV-vis absorption and TEM studies were carried out on films at different stages and morphological studies on microbes were carried out by SEM. Results showed spherical Ag NPs of size 15-25 nm, having sharp surface plasmon resonance (SPR) band. The antimicrobial activity of Ag/agar film was found to be in the order, C. albicans > E. coil > S. aureus, and antimicrobial activity against C. albicans was almost maintained even after the third cycle. Whereas, in case of E. coil and S. aureus there was a sharp decline in antimicrobial activity after the second cycle. Agglomeration of Ag NPs in Ag/agar film on exposure to microbes was observed by TEM studies. Cytotoxic experiments carried out on HeLa cells showed a threshold Ag NPs concentration of 60 mu g/mL, much higher than the minimum inhibition concentration of Ag NPs (25.8 mu g/mL) for E. coli. The mechanical strength of the film determined by nanoindentation technique showed almost retention of the strength even after repeated cycle. (C) 2010 Elsevier Ltd. All rights reserved.

On the uniformity of film thickness on rotating spherical substrates on a planar work holder

Curves for the uniformity in film thickness on spherical substrates are drawn for various geometries. The optimum source-to-substrate height for maximum uniformity of the film thickness is determined. These data are approximated to achieve uniform thickness on a large number of small planar substrates loaded on a large spherical substrate holder, the appropriate geometry being selected on the basis of the radius of curvature of the substrate holder.