UV-visible absorption characteristics of TEOS-derived and Cr-doped silica sonogels aged in different pH solutions and heat treated up to 600 degrees C

Cr-doped xerogels were obtained by sol-gel process from the acid-catalyzed and ultrasound-stimulated hydrolysis of tetraethoxysilane (TEOS) with addition of CrCl3.6H(2)O in water solution during the liquid step of the process. The gels were aged immersed in different pH solutions for about 30 days, after that they were allowed to dry. The samples were annealed at temperatures ranging from 40 to 600degreesC and analyzed by UV-visible absorption spectroscopy. Cr3+ is the preferable oxidation state of the chromium ion in the gels annealed up to 250-300degreesC, in the case of aging in solutions of pH=5 and 11. A high UV absorption below similar to320 nm, due to the host gel, and different absorption bands, depending on the temperature, due to the chromium ion were observed in the xerogels at temperatures below similar to250degreesC, in the case of aging in solutions of pH=1 and 2. These absorption bands have not been assigned. Above 300degreesC up to 600degreesC, Cr5+, and possibly Cr6+, are the preferable oxidation states of the chromium ion independent of the pH of the aging solution, so the xerogels turn to a yellowish appearance in all cases.

Functionalized silica synthesized by sol-gel process

This work considers some aspects of the chemistry involved in the preparation and description of silicon oxide functionalized by sol-gel process. In this work we studied the synthesis and measured the properties of silicon oxide functionalized with 3-chloropropyl, through a sol-gel process. Thermogravimetic analysis, infrared spectra, and elemental analyses were measured. The samples were prepared in the following proportions of tetraethylorthosilicate (TEOS): 3-chloropropyl trimethoxisilane molar ratio: 1:0, 1:1, 2:1, 3:1 and 4:1. The thermogravimetric data for the resulting materials established the 'minimum formulae' 2:0, 3:1, 4.1, 7:1 and 11:1, respectively. As expected, the relative amount of water is inversely proportional to the presence of propyl groups. Infrared data show Si-C and -CH2-vibration modes at 1250 to 1280 and 2920 to 2940 cm(-1), respectively. Thermogravimetric data and infrared spectra showed that inorganic polymers contained organic polymers. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Investigation of the systems silica and silica containing chromium in alcohol medium

The purpose of this work is to obtain micrometer sized spherical particles of silica and silica-chromium from sodium silicate. Spherical particles were prepared by sol-gel method from hydrolysis to polycondensation of aqueous sodium silicate in alcohol medium. Chromium was added to the system for some samples. Compositions and morphologies were achieved by changing the precipitation agent. X-ray diffractometry, electrophoretic mobility, infrared spectroscopy and scanning electron microscopies were carried out on these particles to identify phases, determine particle mobility, morphology, particle sizes, shapes and order at short distance. Non-crystalline silica particles with spherical shapes and micrometric size were obtained. The surface potentials of the silica particles differed from that of the silica-chromium particles. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Preparation and characterization of spherical silica-porphyrin catalysts obtained by the sol-gel methodology

This work describes the synthesis of a first-generation iron porphyrin catalyst entrapped in a silica matrix by the sol-gel route, leading to spherical particles. The catalyst was synthesized by the method of Stober, through hydrolysis and condensation of the alkoxysilane TEOS in a mixture of alcohol, water and ammonia, in the presence of the iron porphyrin Fe(TPP)Cl. The relation between particle morphology and catalytic activity of the different Fe(TPP)-SiO2, obtained using different H2O/silane molar ratios and ammonia concentrations in the xerogel syntheses, was studied.The obtained catalysts were characterized by UV-vis spectroscopy, NMR Si-29. thermogravimetric analysis and transmission electron microscopy. Their ability to catalyze (Z)-cyclooctene epoxidation and cyclohexane oxidation was tested using iodosylbenzene as oxygen donor; the oxidation products were analyzed by gas chromatography and the catalysts obtained in a form of particles spherical and monodispersed showed to be a promising catalytic system for selective oxidation. (c) 2005 Elsevier B.V. All rights reserved.

Montmorillonite (MMT) effect on the structure of poly(oxyethylene) (PEO)-MMT nanocomposites and silica-PEO-MMT hybrid materials

In this work we report the effects of incorporation of variable amounts (0.5-25%w/w) of montmorillonite in poly(oxyethylene) based materials in order to decrease the polymer crystallinity. Two different classes of materials were studied: silica-poly(oxyethylene)-montmorillonite hybrids prepared by the sol-gel route and poly(oxyethylene)-montmorillonite nanocomposites prepared by mixing the dry clay or the clay aqueous suspension into the melt poly(oxyethylene). The effects of monternorillonite loading on the poly(oxyethylene) crystallization control and on the nanostructural features were investigated by X-ray powder diffraction, small-angle X-ray scattering and differential scanning calorimetry. Experimental results show that free montmorillonite layers coexist with open aggregates and tactoids in the poly(oxyethylene)-montmorillonite nanocomposites, with different features depending on the filler proportion and preparation route. The intercalation of polymer chains in montmorillonite galleries markedly hinders the crystallization of the poly(oxyethylene) matrix. For hybrids materials the silica phase favors the exfoliation of montmorillonite tactoids, so that samples are predominantly constituted by dispersed platelets. (c) 2006 Elsevier B.V. All rights reserved.

Sulfation of intrinsic glycoproteins of the rabbit vitreous

The experiments reported here were designed to characterize the intrinsic vitreous glycoproteins and to understand the process of their sulfation. Rabbits were injected intravitreally with S-35-sodium sulfate and killed at several time intervals after injection. In another series of experiments, rabbits were injected either with S-35-sodium sulfate, H-3-fucose or H-3-tyrosine, associated or not associated with tunicamycin administration. Vitreous from the control eyes was also digested with N-glycosidase.. Furthermore, ciliary bodies, the putative source of the intrinsic vitreous glycoproteins, were incubated with S-35-sodium sulfate in the presence or absence of the protein synthesis inhibitor cycloheximide, and the culture media recovered for analysis. These and the vitreous samples of the other experiments were processed for sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE) and fluorography. Except for serum albumin, practically all polypeptide bands of the vitreous and culture media were labeled with radioactive sulfate and were shown to undergo renewal. The experiments using tunicamycin or enzyme treatment suggest that radioactive sulfate was incorporated not only into the carbohydrate side chains of the glycoproteins but also into the amino acid tyrosine of the polypeptide backbone of these glycoproteins. (C) 1998 Academic Press.

Chondroitin sulfate proteoglycans are structural renewable constituents of the rabbit vitreous body

Purpose: To characterize the vitreous intrinsic proteoglycans, investigate their dynamics, and examine their role in the supramolecular organization of the vitreous. Methods: Vitreous from normal rabbits was collected and processed for observation with the transmission electron microscope after treatment with glycosidases. Also, rabbits were injected intravitreally with [S-35]-sodium sulfate and sacrificed at several time intervals after the injection. Proteoglycans (PGs) were assayed in the vitreous supernatant or in whole samples extracted with guanidine hydrochloride by polyacrylamide or agarose gel electrophoresis, followed respectively by fluorography or autoradiography, and ion-exchange chromatography and gel-filtration chromatography, combined with glycolytic treatment of the samples. The sulfated glycosaminoglycans (GAGs) were characterized by agarose gel electrophoresis after treating vitreous samples with protease and specific glycosidases. Results: the electron microscopic study revealed a network with hyaluronic acid ( HA) as thin threads coating and connecting collagen fibrils. The elimination of the HA coat showed chondroitin sulfate granules (8-25 nm) arranged at regular intervals on the fibril surface. The chondroitinase ABC digestion, besides removing the granules, also caused the formation of thicker bundles of the collagen fibrils. The PG and GAG analysis indicated that there are three renewable PGs in the vitreous ( e. g., one heparan-and two chondroitin-sulfate ones). Conclusions: At least one of the chondroitin sulfate PGs is involved in the interactions that occur in the vitreous structure, mainly by providing adequate spacing between the collagen fibrils, a condition that is probably required for the transparency of the vitreous.

A nonisothermal study of the kinetics of the nanoporosity elimination in sonogels-derived silica xerogels

A nonisothermal study of the kinetics of the nanoporosity elimination in monolithic silica xerogels, prepared from acid and ultrasound catalyzed hydrolysis of tetraethylortosilicate (TEOS), has been carried out by means of in situ linear shrinkage measurements performed with different heating rates. The study could be applied up to almost alpha similar to 0.6 of the volume fraction alpha of eliminated pores. The activation energy was found increasing from about 3.2 x 10(2) kJ/mol for alpha similar to 0.06 up to about 4.4 x 10(2) kJ/mol for alpha. similar to 0.44. The sintering process accompanying the nanopore elimination in this set of xerogels is in agreement with a viscous flux sintering process with the hydroxyl content diminishing with the volume fraction of eliminated pores. All the volume fraction of eliminated pores versus temperature (T) curves can be matched onto a unique curve with an appropriate rescaling of the T axis, independent of the heating rate. This scaling property suggests that the path of sintering seems the same, regardless of the heating rate; the difference is that the rate is faster at higher temperature.

Er-doped silica-based waveguides prepared by different techniques: RF-sputtering, sol-gel and ion-exchange

Erbium-activated silica-based planar waveguides were prepared by three different technological routes: RF-sputtering, sol-gel and ion exchange. Various parameters of preparation were varied in order to optimize the waveguides for operation in the NIR region. Particular attention was devoted to the minimization of the losses and the increase of the luminescence efficiency of the metastable I-4(13/2) state of the Er3+ ion. Waveguide properties were determined by m-line spectroscopy and loss measurements. Waveguide Raman and luminescence spectroscopy were used to obtain information about the structure of the prepared films and about the dynamical processes related to the luminescence of the Er3+ ions.

SAXS study of gelation, aging and drying of silica-polypropyleneglycol hybrid materials

New silica-polypropyleneglycol ormosils (organically modified silicates) with covalent bends between the organic (polymer) and inorganic (silica) phases have been prepared by the sol-gel process. Their structural evolution during sol formation, sol-gel transition, gel aging and drying has been studied in situ by small-angle X-ray scattering (SAXS). The experimental SAXS curves corresponding to sols and gels exhibit features expected from fractal objects. Clusters of size around 55 Angstrom with an initial fractal dimension D = 2.4 are formed in the sol. They are constituted of small primary silica particles chemically crosslinked at the end of the polymer chains. A strong liquid-like spatial correlation between the silica particles develops during drying due to the shrinkage of the polymeric network induced by water and ethanol evaporation. The continuous increase in SAXS intensity during drying, while the interparticle distance remains constant, is a consequence of the progressive growth of the dry fraction of the total volume. After drying, the gel structure consists of a rather compact arrangement of silica particles embedded in the polypropyleneglycol matrix.

Effects of different treatments on purity of silica from soluble sodium silicate

Noncrystalline silica was obtained with low iron, sodium, and nitrate ions concentrations from soluble sodium silicate (water glass) and nitric acid solution. Extractions with nitric acid solution and/or deionized water and/or dialysis were carried out to eliminate soluble metal ions. Products were dried in a microwave oven and characterized by chemical analysis, XRD, and IR. Dialysis seems to be the best treatment for the elimination of sodium and nitrate ions. Silica purified by nitric acid and water extractions followed by dialysis yields the purest silica sample.

Spectroscopic and thermal characterization in poly(p-phenylene vinylene)/sol-gel silica sample

The absorption and luminescence spectra for the poly(p-phenylene vinylene)/sol-gel silica with different thermal treatments were measured. A considerable increase in the luminescence was observed for the polymer introduced into SiO2 matrix with thermal treatment at 120 degreesC. The thermal diffusivity of these samples was measured using the thermal lens technique, and the obtained value 3.3 x 10(-5) cm(2)/s (sample treated at 37 degreesC) is practically independent of the thermal treatment (37-150 degreesC). (C) 2003 Elsevier B.V. All rights reserved.

Blue cooperative luminescence properties in Yb3+ doped GeO2-PbO-Bi2O3 vitreous system for the production of thin films

Germanate glasses are of interest for optoelectronic applications because they combine high mechanical strength, high chemical durability and temperature stability with a large transmission window (400 to 4500 nm) and high refractive index (2.0). GeO2-PbO-Bi2O3 glasses doped with Y-b(3+) were fabricated by melting powders in a crucible and then pouring them in a brass mold. Energy Dispersive Spectroscopy showed that the glass composition has a high spatial uniformity and that the Yb concentration in the solid sample is proportional to the Yb concentration in the melt, what was confirmed by absorption measurements. Intense blue emission at 507 nm was observed, corresponding to half of the wavelength of the near infrared region (NIR) emission; besides, a decay lifetime of 0.25 ms was measured and this corresponds to half of the decay lifetime in the infrared region; these are very strong indications of the presence of blue cooperative luminescence. Larger targets have been produced to be sputtered, resulting in thin films for three dimensional (3D) display and waveguide applications. (c) 2006 Elsevier B.V. All rights reserved.

Silica-PEG hybrid ormolytes: structure and properties

The effect of lithium salt doping on the structure and ionic conduction properties of silica-polyethyleneglycol composites is reported. These materials, so called ormolytes (organically modified electrolytes), were obtained by the sol-gel process. They have chemical stability due to the covalent bonds between the inorganic (silica) and organic (polymer) phase. The structure of these hybrid materials was investigated by small-angle X-ray scattering (SAXS) as a function of lithium concentration [O]/[Li] (O being the oxygens of the ether type). The spectra have a well-defined peak attributed to the existence of a liquid-like spatial correlation of silica clusters. The ionic conductivity was studied by AC impedance spectroscopy and is maximum for [O]/[Li] = 15. This result is consistent with SAXS and thermo-mechanical analysis measurements and is due to the formation of cross-linking between the polymer chains for the larger lithium concentrations. These materials are solid, transparent, flexible and have an ionic conductivity up to 10(-4) S/cm. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Laserlike emission from silica inverse opals infiltrated with rhodamine 6G

Monodisperse latex spheres were obtained by a surfactant free styrene polymerization method and used to obtain colloidal crystals by controlled centrifugation settling. Silica inverse opals were then prepared by using the colloidal crystals as templates and TEOS/ethanol solution. The inverse opals were infiltrated with Rhodamine 6G and laserlike emission was observed at 590 nm under 532 nm pump wavelength. The data show line narrowing of the dye fluorescence and a laser threshold of similar to 0.1 mJ/pulse. Local-field effects and light scattering due to structural defects are the main mechanisms contributing to generation of the laser-action observed. (c) 2005 Elsevier B.V. All rights reserved.