Low-frequency high-temperature internal friction in Ti-13Nb-13Zr alloy

Recent studies have been done to achieve biomedical alloys containing non-toxic elements and presenting low elastic moduli. It has been reported that Ti-Nb-Zr alloys rich in beta phase, especially Ti-13Nb-13Zr, have potential characteristics for substituting conventional materials such as Ti-6Al-4V, stainless steel and Co alloys. The aim of this work is to study the internal friction (IF) of Ti-13Nb-13Zr (TNZ) alloy due to the importance of the absorption impacts in orthopedic applications. The internal friction of this alloy produced by arc melting was measured using an inverted torsion pendulum with the free decay method. The measurements were performed from 77 to 700 K with heating rate of 1 K/min, in a vacuum better than 10-5 mBar. The results show a relaxation structure at high temperature strongly dependent on microstructure of the material. Qualitative discussions are presented for the experimental results, and the possibility of using the TNZ as a high damping material is briefly mentioned.

Crystallographic structure of Ti-6Al-4V, Ti-HP and Ti-CP under high-pressure

The phase stability of a commercial purity (Ti-CP), high purity (Ti-HP) and Ti-6Al-4V alloy were investigated in a diamond anvil cell up to 32 GPa and 298 K using a polychromatic X-ray beam. The Ti-CP and Ti-HP shown the same HCP (c/a∼0.632) to Hexagonal (c/a∼1.63) non reversible martensitic transition at about 9 GPa. The as received Ti-6Al-4V shows a very low relative volume fraction β-Ti / α-Ti. No phase changes were observed in the Ti-6Al-4V alloy in the pressure range of this study. The α phase of the Ti-6Al-4V shows monotonic volume cell pressure dependence. This volume change is reversible and non-hysteretic. The cell of the a phase recovered its original volume when the pressure was released. © 2010 IOP Publishing Ltd.

Cutting performance of diamond coated Si3N4 tool during turning

Silicon nitride cutting tools have been used successfully for machining hard materials, like: cast irons, nickel based alloys, etc. However these cutting tools with diamond coating present little information on dry turning operations of gray cast iron. In the present work, Si3N4 square inserts was developed, characterized and subsequently coated with diamond for dry machining operations on gray cast iron. All experiments were conducted with replica. It was used a 1500, 3000, 4500 m cutting length, feed rate of 0.33 mm/rev and keeping the depth of cut constant and equal to 1 mm. The results show that wear in the tool tips of the Si3N4 inserts, in all cutting conditions, was caused by both mechanical and chemical processes. To understand the tool wear mechanisms, a morphological analysis of the inserts, after experiments, has been performed by SEM and optical microscopy. Diamond coated PVD inserts showed to be capable to reach large cutting lengths when machining gray cast iron. © (2010) Trans Tech Publications.

In vitro analysis with human bone marrow stem cells on Ti-15Mo alloy for dental and orthopedic implants application

Aim: Nowadays, research on orthopedic and dental implants is focused on titanium alloys for their mechanical properties and corrosion resistance in the human body environment. Another important aspect to be investigated is their surface topography, which is very important to osseointegration. With laser beam irradiation for roughening the implants surface an easier control of the microtopography is achieved, and surface contamination is avoided. The aim of this study was to assess human bone marrow stem cells response to a newly developed titanium alloy, Ti-15Mo, with surface topography modified by laser beam irradiation. Materials and methods: A total of 10 Ti machined disks (control), 10 Ti-15Mo machined disks and 10 Ti-15Mo disks treated by laser beam-irradiation were prepared. To study how Ti-15Mo surface topografy can induce osteoblast differentiation in mesenchymal stem cells, the expression levels of bone related genes and mesenchymal stem cells marker were analyzed, using real time Reverse Transcription-Polymerase Chain Reaction. Results: In Test 1 (comparison between Ti-15Mo machined disks and Ti-machined disks) quantitative real-time RT-PCR showed a significant induction of ALPL, FOSL1 and SPP1, which increase 20% or more. In Test 2 (comparison between Ti-15Mo laser treated disks and Ti-machined disks) all investigated genes were up-regulated. By comparing Test 1 and Test 2 it was detected that COL1A1, COL3A1, FOSL1 and ENG sensibly increased their expression whereas RUNX2, ALPL and SPP1 expression remained substantially unchanged. Conclusion: The present study demonstrated that laser treated Ti-15Mo alloys are promising materials for implants application.

Effect of molybdenum on the formation of Ti6Si2B in mechanically alloyed Ti-Mo-Si-B powders

This paper discusses on effect of molybdenum on the Ti6Si2B formation in mechanically alloyed and hot-pressed Ti-xMo-22Si-11B (x= 2, 5, 7 and 10 at%) alloys. High-energy ball milling and hot pressing were utilized to produce homogeneous and dense materials, which were characterized by scanning electron microscopy, X-ray diffraction, electron dispersive spectrometry, and Vickers hardness. The excessive agglomeration during milling was more pronounced in Moricher powders, which was minimized with the formation of brittle phases. Hot pressing of mechanically alloyed Ti-xMo-22Si-11B powders produced dense samples containing lower pore amounts than 1%. Ti6Si2B was formed in microstructure of the hot-pressed Ti-2Mo-22Si-11B alloy only. In Mo-richer quaternary alloys, the Ti3Si and Ti5Si3 phases were preferentially formed during hot pressing. Oppositely to the ternary phase, the Ti3Si phase dissolved a significant Mo amount. Vickers hardness values were reduced in hot-pressed Ti-xMo-22Si-11B alloys containing larger Mo amounts, which were dissolved preferentially in Ti solid solution. © (2012) Trans Tech Publications, Switzerland.

Physicochemical analysis of Ti-Si-B powder aalloys

Titanium alloys of Ti-Si-B system were manufactured by blended elemental powder method using Ti, Si and B powders as starting materials. It was found that uniaxial and isostatic pressing followed by hot pressing at around 1000°C, for 20 minutes, provided good densification of such alloys. The physicochemical studies were performed by means of scanning electron microscopy, X-ray diffraction, atomic force microscopy and microindentation/wear tests. The investigations revealed a multiphase microstructure formed mainly by α-titanium, Ti6Si2B, Ti5Si3, TiB and Ti3Si phases. The phase transformations after pressureless sintering at 1200°C was also studied by X-ray diffraction for the Ti-18Si-6B composition. As stated in some other researches, these intermetallics in the α-titanium matrix provide high wear resistance and hardness, with the best wear rate of 0.2 mm3/N.m and the highest hardness of around 1300 HV. © (2012) Trans Tech Publications, Switzerland.

High-pressure assisted sintering of Ti-20Si-10B and Ti-10Si-5B powders

This work presents the structural characterization of Ti-10Si-5B and Ti-20Si-10B (at-%) alloys produced by high-pressure assisted sintering. Sintering was performed in air at 1100 and 1200°C for 60 s using pressure levels of 5 GPa. Structural evaluation of sintered samples was conducted by means of scanning electron microscopy and energy dispersive spectrometry. Samples were successfully consolidated after sintering, which presented theoretical density values higher than 99%. The microstructures of the sintered Ti-10Si-5B and Ti-20Si-10B alloys revealed the presence of the TiSS, TiB, TiB2, Ti5Si3, Ti5Si4, TiSi, and TiSi2.phases. A small amount of Ti6Si2B was formed after high-pressure assisted sintering of the Ti-20Si-10B alloy (5GPa, 1100°C for 60 s) indicating that equilibrium structures were not achieved during short sintering times. No oxygen and carbon contamination was detected in structures of Ti-Si-B alloys after high-pressure sintering at 1100 and 1200°C without controlled atmosphere. © (2012) Trans Tech Publications, Switzerland.

Analysis on turning Ti-6Al-4V with different cooling methods

The aim of this paper is to optimize the machining of Ti-6Al-4V alloy, by studying the chip formation, roughness and tool wear for different cooling conditions. The results were compared between cooling methods, minimal quantity of fluid (MQF) and flooding, and also without fluid for the tool H13A. The turning of Ti-6Al-4V has shown good results on roughness (0, 8μm) and tool life, which was 11% lower with MQF than with the flooding method. The tool wear causes variation of the shear angle, which promotes strength hardening of the chip. As a result, the machined surface could be damaged. The use of the cutting fluid helps to save the cutting edge and could reduce the strength hardening. Nevertheless, it could also facilitate the formation of built-up edge. The nucleation of alpha lamellar colonies can occur due to a combination of deformation rates and temperature, mainly when the flooding is used, but it's not conclusive. The lamellar colonies were also found with the MQF in some regions, however, this structure did not show hardness variation compared to equiaxial. For all this reasons, the machining parameters might be carefully chosen.

Histological analysis of the osseointegration of Ti-30Ta dental implants after surface treatment

Metallic biomaterials are used to reinforce or to restore the form and function of hard tissues. Implants and prosthesis are used to replace shoulders, knees, hips and teeth. When these materials are inserted in bone several biological reactions happen. This process can be associated to surface properties (topography, roughness and surface energy). In this work, the influence of biomimetic surface treatment in the osseointegration of Ti-30Ta dental implants was evaluated. Ingots were obtained from titanium and tantalum by using an arc-melting furnace. They were submitted to heat treatment at 1,100°C for 1 h, cooled in water and cold worked by swaging. Then, screw-shaped implants (2.0 mm diameter by 2.5 mm length) were manufactured and they were implanted in a rat's femur. Animals were divided into two groups: untreated (control group) and treated (biomimetic surface treatment). They were sacrificed 30 days after implantation. For histological analysis, implants with surrounding tissue were removed and immersed in formaldehyde. Samples were embedded in polymethyl methacrylate and after polymerization, cut with a saw, polished and mounted on glass slides. The results obtained suggest that biomimetic surface treatment was able to promote an increase osseointegration on the surface of dental implants. © Springer-Verlag Berlin Heidelberg 2013.

Analysis of the bioactive surface of Ti-35Nb-7Zr alloy after alkaline treatment and solution body fluid

The purpose of this work was to evaluate the Ti-35Nb-7Zr experimental alloy after surface treatment and soaking in solution body fluid (SBF) to form bonelike apatite. The Ti-35Nb-7Zr alloy was produced from commercially pure materials (Ti, Nb and Zr) by an arc melting furnace. All ingots were submitted to sequences of heat treatment (1100 °C/2 h and water quenching), cold working by swaging procedures and heat treatment (1100 °C/2 h and water quenching). Discs with 13 mm diameter and 3 mm in thickness were cut. The samples were immersed in NaOH aqueous solution with 5 M at 60 °C for 72 h, washed with distilled water and dried at 40 °C for 24 h. After the alkaline treatment, samples were heat treated in both conditions: at 450 and 600 °C for 1 h in an electrical furnace in air. Then, they were soaking in SBF for 24 h to form an apatite layer on the surface. The surfaces were investigated by using scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX), infrared spectroscopy (FTIR) and contact angle measurements. The results indicate that calcium phosphate could form on surface of Ti-35Nb-7Zr experimental alloy. © Springer-Verlag Berlin Heidelberg 2013.

Growth of TiO2 nanotubes by anodization of Ti-7.5Mo in NH 4F solutions

Titanium and its alloys are widely used as biomaterials due to their mechanical, chemical and biological properties. To enhance the biocompatibility of titanium alloys, various surface treatments have been proposed. In particular, the formation of titanium oxide nanotubes layers has been extensively examined. According to the literature, it is possible to induce the growth of TiO2 on the surface of titanium, employing the aqueous anodizing electrolyte. This Ti-7.5Mo alloy was anodized in glycerol electrolytes containg 0.25 wt% of NH4F, with variations in time, voltage and calcinations temperature. After anodization, the sample surfaces were analyzed with a field emission scanning electron microscopy, DRX and contact angle measurements. It was possible to observe the formation of TiO2 on the surface and these findings represent a simple surface treatment for Ti alloys that has high potential for biomedical applications. Copyright © 2013 American Scientific Publishers. All rights reserved.

Growth of calcium phosphate coating on Ti-7.5Mo alloy after anodic oxidation

Titanium and its alloys are widely used as biomaterials due to their mechanical, chemical and biological properties. To enhance the biocompatibility of titanium alloys, various surface treatments have been proposed. In particular, the formation of titanium oxide nanotubes layers has been extensively examined. Among the various materials for implants, calcium phosphates and hydroxyapatite are widely used clinically. In this work, titanium nanotubes were fabricated on the surface of Ti-7.5Mo alloy by anodization. The samples were anodized for 20 V in an electrolyte containing glycerol in combination with ammonium fluoride (NH4F, 0.25%), and the anodization time was 24 h. After being anodized, specimens were heat treated at 450 °C and 600°C for 1 h to crystallize the amorphous TiO2 nanotubes and then treated with NaOH solution to make them bioactive, to induce growth of calcium phosphate in a simulated body fluid. Surface morphology and coating chemistry were obtained respectively using, field-emission scanning electron microscopy (FEG-SEM), AFM and X-ray diffraction (XRD). It was shown that the presence of titanium nanotubes induces the growth of a sodium titanate nanolayer. During the subsequent invitro immersion in a simulated body fluid, the sodium titanate nanolayer induced the nucleation and growth of nano-dimensioned calcium phosphate. It was possible to observe the formation of TiO2 nanotubes on the surface of Ti-7.5Mo. Calcium phosphate coating was greater in the samples with larger nanotube diameter. These findings represent a simple surface treatment for Ti-7.5Mo alloy that has high potential for biomedical applications. © (2013) Trans Tech Publications, Switzerland.

Performance of race instrumentation system in curved root canals: a comprehensive analysis by three study methods

In this study, curved maxillary molar root canals were instrumented with RaCe rotary system to evaluate: 1. the occurrence of canal transportation using a radiographic platform; 2. the action of the instruments on the dentin walls, centering ability and canal enlargement by analysis of digital images; and the percentage of regular dentin surfaces and debris within the canal by histological analysis. Ten mesiobuccal roots of extracted human maxillary molars were embedded in acrylic resin and sectioned at the middle and apical thirds. Root canal shaping was performed using the RaCe rotary system at 250 rpm and 1 Ncm torque. Each instrument set was used five times according to a crowndown technique in the following sequence: 40/0.10, 35/0.08, 25/0.06, 25/0.04, 25/0.02 (working length - WL), 30/0.02 (WL) and 35/0.02 (WL). Each instrument was inserted until resistance was felt and then pulled back, followed by brushing movements towards all canal walls. Each specimen was assessed by three study methods: radiographic platform, digitized image assessment and histological analysis. The radiographic platform showed lack of apical transportation. No statistically significant difference (Wilcoxon test, p>0.05) was found between the middle and apical thirds regarding instrument action on dentin walls, centering ability, area of root canal enlargement, percentage of regular dentin surfaces and debris within the root canal. It may be concluded that RaCe system is a suitable method for the preparation of curved root canals, regarding the maintenance of root canal original path, action on dentin walls, canal enlargement and removal of debris from the root canal lumen.

Improvements of plasma immersion ion implantation (PIII) and deposition (PIII&D) processing for materials surface modification

Plasma immersion ion implantation (PIII) process is a three dimensional surface modification method that is quite mature and well known to the surface engineering community nowadays, especially to those working in the field of plasma-materials interaction, aiming at both industrial and academic applications. More recently, deposition methods have been added to PIII, the PIII&D, opening possibilities of broader range of applications of these techniques. So, PIII&D is becoming a routine method of surface modification, with the advantage of pushing up the retained dose levels limited by the sputtering due to ion implantation. Therefore, well adherent, thick, three-dimensional films without stress are possible to be achieved, at relatively low cost, using PIII&D. In this paper, we will discuss about a few PIII and PIII&D experiments that have been performed recently to achieve surface improvements in different materials: 1 - high temperature nitrogen PIII in Ti6Al4V alloy in which a deep nitrogen rich treated layer resulted in surface improvements as increase of hardness, corrosion resistance and resistance to wear of the Ti alloy; 2 - nanostructures in ZnO films, obtained by PIII&D of vaporized & ionized Zn source; 3 - combined implantation and deposition of calcium for biomaterial activity of Ti alloy (PIII&D), allowing the growth of hydroxyapatite in a body solution; 4 - magnetron sputtering deposition of Cr that was enhanced by the glow discharge Ar plasma to allow implantation and deposition of Cr on SAE 1070 steel (PIII&D) resulting in surfaces with high resistance to corrosion; and 5 - implantation of nitrogen by ordinary PIII into this Cr film, which improved resistance to corrosion, while keeping the tribological properties as good as for the SAE 1070 steel surface. © 2012 Elsevier B.V.

Efeito do oxigênio nas propriedades anelásticas da liga Ti-10Mo para aplicação biomédica

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)