Interactions between iron, manganese, and the Al-Si eutectic in hypoeutectic Al-Si alloys

Sand-cast plates were used to determine the effect of iron and manganese concentrations on porosity levels in Al-9 pet Si-0.5 pet Mg alloys. Iron increased porosity levels. Manganese additions increased porosity levels in alloys with 0.1 pet Fe, but reduced porosity in alloys with 0.6 and I pet Fe. Thermal analysis and quenching were undertaken to determine the effect of iron and manganese on the solidification of the Al-Si eutectic. At high iron levels, the presence of large beta-Al5FeSi was found to reduce the number of eutectic nucleation events and increase the eutectic grain size. The preferential formation of alpha-Al15Mn3Si2 upon addition of manganese reversed these effects. It is proposed that this interaction is due to beta-Al5FeSi and the Al-Si eutectic having common nuclei. Porosity levels are proposed to be controlled by the eutectic grain size and the size of the iron-bearing intermetallic particles rather than the specific intermetallic phase that forms.

Edge-to-edge matching - The fundamentals

The basis of the present authors' edge-to-edge matching model for understanding the crystallography of partially coherent precipitates is the minimization of the energy of the interface between the two phases. For relatively simple crystal structures, this energy minimization occurs when close-packed, or relatively close-packed, rows of atoms match across the interface. Hence, the fundamental principle behind edge-to-edge matching is that the directions in each phase that correspond to the edges of the planes that meet in the interface should be close-packed, or relatively close-packed, rows of atoms. A few of the recently reported examples of what is termed edge-to-edge matching appear to ignore this fundamental principle. By comparing theoretical predictions with available experimental data, this article will explore the validity of this critical atom-row coincidence condition, in situations where the two phases have simple crystal Structures and in those where the precipitate has a more complex structure.

The corrosion performance of anodised magnesium alloys

The corrosion performance of anodised magnesium and its alloys, such as commercial purity magnesium (CP-Mg) and high-purity magnesium (HP-Mg) ingots, magnesium alloy ingots of MEZ, ZE41, AM60 and AZ91D and diecast AM60 (AM60-DC) and AZ91D (AZ91D-DC) plates, was evaluated by salt spray and salt immersion testing. The corrosion resistance was in the sequential order: AZ91D approximate to AM60 approximate to MEZ >= AZ91D-DC >= AM60-DC > HP-Mg > ZE41 > CP-Mg. It was concluded the corrosion resistance of an anodised magnesium alloy was determined by the corrosion performance of the substrate alloy due to the porous coating formed on the substrate alloy acting as a simple corrosion barrier. (c) 2006 Elsevier Ltd. All rights reserved.

Atmospheric corrosion of copper and the colour, structure and composition of natural patinas on copper

This paper describes the results of atmospheric corrosion testing and of an examination of patina samples from Brisbane, Denmark, Sweden, France, USA and Austria. The aim was threefold: (1) to determine the structure of natural patinas and to relate their structure to their appearance in service and to the atmospheric corrosion of copper; (2) to understand why a brown rust coloured layer forms on the surface of some copper patinas; (3) to understand why some patinas are still black in colour despite being of significant age. During the atmospheric corrosion of copper, a two-layer patina forms on the copper surface. Cuprite is the initial corrosion product and cuprite is always the patina layer in contact with the copper. The growth laws describing patina formation indicate that the decreasing corrosion rate with increasing exposure time is due to the protective nature of the cuprite layer. The green patinas were typically characterised by an outer layer of brochantite, which forms as individual crystals on the surface of the cuprite layer, probably by a precipitation reaction from an aqueous surface layer on the cuprite layer. Natural patinas come in a variety of colours. The colour is controlled by the amount of the patina and its chemical composition. Thin patinas containing predominantly cuprite were black. If the patina was sufficiently thick, and the [Fe]/[Cu] ratio was low, then the patina was green, whereas if the [Fe]/[Cu] ratio was approximately 10 at%, then the patina is rust brown in colour. The iron was in solid solution in the brochantite, which might be designated as a (copper/iron) hydroxysulphate. In the brown patinas examined, the iron was distributed predominately in the outermost part of the patina. (c) 2005 Elsevier Ltd. All rights reserved.

Effect of over-doped yttrium on the microstructure, mechanical properties and thermal properties of a Zr-based metallic glass

The effects of over-doped yttrium on the microstructure, mechanical properties and thermal behaviour of an oxygen-contaminated Zr51Cu20.7Ni12Al16.3 bulk metallic glass are studied systematically. It has been found that, when yttrium doping is beyond the optimum doping, the glass-forming ability enhancement effect induced by yttrium addition decreases and the mechanical properties are adversely affected. In this study, a new phase with an orthorhombic structure (a = 0.69 nm, b = 0.75 nm and c = 0.74 nm) is identified in the yttrium over-doped alloys. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Microstructures and electrolytic properties of yttrium-doped ceria electrolytes: Dopant concentration and grain size dependences

The microstructures and electrolytic properties of YxCe1-xO2-x/2 (x = 0.10-0.25) electrolytes with average grain size in the range 90 nm-1.7 mu m were systematically investigated. Through detailed transmission electron microscopy characterization, nanosized domains were observed. The relationship of the domains, the doping level and grain sizes were determined, and their impacts on the electrolytic properties were systematically studied. It was found that the formation of domains has a negative impact on the electrolytic properties, so that electrolytic properties can be adjusted through careful control of domain formation, doping level and grain size. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Determination of strontium segregation in modified hypoeutectic Al-Si alloy by micro X-ray fluorescence analysis

Analysis of intra- and inter-phase distribution of modifying elements in aluminium-silicon alloys is difficult due to the low concentrations used. This research utilises a mu-XRF (X-ray fluorescence) technique at the SPring-8 synchrotron radiation facility X-ray source and reveals that the modifying element strontium segregates exclusively to the eutectic silicon phase and the distribution of strontium within this phase is relatively homogeneous. This has important implications for the fundamental mechanisms of eutectic modification in hypoeutectic aluminium-silicon alloys. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.