Raman spectra of polymethyl methacrylate optical fibres excited by a 532 nm diode pumped solid state laser

Polymethyl methacrylate (PMMA) optical fibres are fabricated by a preform drawing process. The Raman spectra of PMMA fibres are recorded using a diode pumped solid state laser emitting at 532 nm and a CCD-spectrograph in the 400–3800 cm−1 range. The variation of the Raman intensity with the length of the optical fibre is studied. Investigations are carried out on the variation of FWHM of the Raman peak at 2957 cm−1 with the length of the optical fibre and pump power. The differential scattering cross section and gain coefficient of the Raman peak at 2957 cm−1 in PMMA are calculated in relation to that of toluene.

Raman spectra of polymethyl methacrylate optical fibres excited by a 532 nm diode pumped solid state laser

Polymethyl methacrylate (PMMA) optical fibres are fabricated by a preform drawing process. The Raman spectra of PMMA fibres are recorded using a diode pumped solid state laser emitting at 532 nm and a CCD-spectrograph in the 400–3800 cm−1 range. The variation of the Raman intensity with the length of the optical fibre is studied. Investigations are carried out on the variation of FWHM of the Raman peak at 2957 cm−1 with the length of the optical fibre and pump power. The differential scattering cross section and gain coefficient of the Raman peak at 2957 cm−1 in PMMA are calculated in relation to that of toluene

Studies on short Nylon-6 fiber - elastomer composites with epoxy resin as bonding agent

The thesis describes the development and evaluation of epoxy resin as interfacial bonding agent for short Nylon-6 fiber elastomer composites. Epoxy resin is well known for its adhesive property. The potential use of it as interfacial bonding agent in short fiber composite is not explored yet. Three rubbers viz., acrylonitrile butadiene rubber (NBR), Neoprene rubber (CR) and styrene butadiene rubber (SBR) were selected and different fiber loading were tried. The resin concentration was optimized for each fiber loading with respect to cure characteristics and mechanical properties. Rheological characteristics and thermal degradation of the composites containing different fiber loading and different resin concentrations were studied in detail to find the effect of epoxy resin bonding system. The mechanical properties were studied in detail. The short Nylon -6 fiber improved most of the mechanical properties of all the three rubbers. Tensile strength showed a dip at 10 phr fiber loading in the case of CR while it was continuously increased with fiber loading in the case of NBR and SBR. All the composites showed anisotropy in mechanical properties. The epoxy resin is an effective bonding agent for short Nylon -6 fiber reinforced NBR and CR composites. Epoxy resin improved tensile strength, abrasion resistance and modulus of these composites. SEM studies confirmed the improved bonding of fiber and matrix in the presence of epoxy bonding agent. Epoxy resin was not effective as bonding agent in the case of short Nylon fiber- SBR composite. From the rheological studies of the composites with and without bonding agent it was observed that all the composite exhibited pseudoplasticity, which decreased with temperature. At higher shear rates all the mixes showed plug flow. SEM pictures showed that maximum orientation of fibers occured at a shear rate, just before the onset of plug flow. The presence of fiber reduced the temperature sensitivity of the flow at a given shear rate. Die swell was reduced in the presence of fiber. Shear viscosity of the composite was increased in the presence of resin. Die swell was increased in the presence of epoxy resin for composites at all shear rates. The thermal degradation of NBR and SBR composites with and without bonding agent followed single step degradation pattern. Thermal stability of the composites was improved in the presence of bonding agent. The degradation of virgin elastomer and the composites followed first order kinetics.

Photoacoustic study on the photostability of polymethyl methacrylate films doped with Rhodamine 6G–Rhodamine B dye mixture system

The photosensitivity of dye mixture-doped polymethyl methacrylate (PMMA) films are investigated as a function of laser power, concentration of the dyes, modulation frequency and the irradiation wavelength. Energy transfer from a donor molecule to an acceptor molecule affects the emission output of the dye mixture system. Photosensitivity is found to change with changes in donor–acceptor concentrations. PMMA samples doped with the dye mixture are found to be more photosensitive when the dyes are mixed in the same proportion.

Electron Density Determination of Laser Induced Plasma from Polymethyl Methacrylate Using Phaseshift Detection Technique

Irradiation of a Polymethyl methacrylate target using a pulsed Nd-YAG laser causes plasma formation in the vicinity of the target. The refractive index gradient due to the presence of the plasma is probed using phase-shift detection technique. The phase-shift technique is a simple but sensitive technique for the determination of laser ablation threshold of solids. The number density of laser generated plasma above the ablation threshold from Polymethyl methacrylate is calculated as a function of laser fluence. The number density varies from 2×1016 cm-3 to 2×1017 cm-3 in the fluence interval 2.8-13 J · cm-2.

Modification of Phenol Formaldehyde Resin for Improved Mechanical Properties

Phenolic resins suffer from the presence of microvoids on curing. This often leads to less than satisfactory properties in the cured resin. This disadvantage has limited the use of phenolic resins to some extent. This study is an attempt to improve the mechanical properties of the phenolic resol resins by chemical modification aimed at reducing the microvoid population. With this end in view various themoset resins synthesised under predetennined conditions have been employed for modifying phenolic resols. Such resins include unsaturated polyester, epoxy and epoxy novolac prepolymers. The results establish the effectiveness of these resins for improving the mechanical properties of phenolics. Experimental and analytical techniques used include FTIR, DMA, TGA, SEM and mechanical property evaluation. While most of the modifier resins employed give positive results the effect of adding UP is found to be surprising as well as impressive.

Marine bacterial prodigiosin as dye for rubber latex, polymethyl methacrylate sheets and paper

Prodigiosin is known for its immunomodulatory, antibacterial, antimycotic, antimalarial, algicidal and anticancer activities. Here, we reported the evaluation of prodigiosin pigment as a dyeing agent in rubber latex, paper and polymethyl methacrylate (PMMA) so that it can be considered as an alternative to synthetic pigments. Maximum color shade was obtained in rubber sheet prepared with 0.5 parts per hundred gram of rubber (phr) pigment and PMMA sheet incorporated with 0.08 μg pigment. Results indicate scope for utilization of prodigiosin as dye for PMMA and rubber and also prodigiosin dyed paper as a pH indicator. Further, being a natural and water insoluble pigment, it is ecofriendly

Modification of Unsaturated Polyester Resin by Polyurethane Prepolymers

Unsaturated polyester resins (UPRs) are extensively used by the fiber-reinforced plastic (FRPs) industry. These resins have the disadvantages of brittleness and poor resistance to crack propagation. In this study, UPRs were chemically modified by reactive blending with polyurethane prepolymers having terminal isocyanate groups. Hybrid networks were formed by copolymerisation of unsaturated polyesters with styrene and simultaneous reaction between terminal hydroxyl groups of unsaturated polyester and isocyanate groups of polyurethane prepolymer. The prepolymers were based on toluene diisocyanate (TDI) and each of hydroxy-terminated natural rubber (HTNR), hydroxy- terminated polybutadiene (HTPB), polyethylene glycol (PEG), and castor oil. Properties like tensile strength, toughness, impact resistance, and elongation-at-break of the modified UPRs show considerable improvement by this modification. The thermal stability of the copolymer is also marginally better

Epoxidized Phenolic Novolac: A Novel Modifier for Unsaturated Polyester Resin

Unsaturated polyester resins (UPRs) are used widely in the fiber-reinforced plastics (FRPs) industry. These resins have the disadvantages of brittleness and poor resistance to crack propagation. In this study, hybrid polymer networks (HPNs) based on UPR and epoxidized phenolic novolacs (EPNs) were prepared by reactive blending. A HPN is composed of a backbone polymer containing two types of reactive groups that can take part in crosslinking reactions via different mechanisms. EPNs were prepared by glycidylation of novolacs using epichlorohydrin. The novolacs had varying phenol: formaldehyde ratios. Blends of unsaturated polyester with EPN were then prepared. The physical properties of the cured blends were compared with those of the control resin. EPN shows good miscibility and compatibility with the resin and improves the toughness and impact resistance substantially. Considerable enhancement of tensile strength is also noticed at about 5% by weight of epoxidized novolac resin. TGA, DMA, and DSC were used to study the thermal properties of the toughened resin and the fracture behavior was studied using SEM. The blends are also found to have better thermal stability. Blending with EPN can be a useful and cost-effective technique for modification of UPR

Association Behavior of Biotinylated and Non-Biotinylated PolyEthylene Oxide-b-Poly(2-(Diethylamino)Ethyl Methacrylate)

Biotinylated and non-biotinylated copolymers of ethylene oxide (EO) and 2-(diethylamino)ethyl methacrylate (DEAEMA) were synthesized by the atom transfer radical polymerization technique (ATRP). The chemical compositions of the copolymers as determined by NMR are represented by PEO₁₁₃PDEAEMA₇₀ and biotin-PEO₁₀₄PDEAEMA₉₃ respectively. The aggregation behavior of these polymers in aqueous solutions at different pHs and ionic strengths was studied using a combination of potentiometric titration, dynamic light scattering (DLS), static light scattering (SLS), and transmission electron microscopy (TEM). Both PEO-b-PDEAEMA and biotin-PEO-b-PDEAEMA diblock copolymers form micelles at high pH with hydrodynamic radii (Rh) of about 19 and 23 nm, respectively. At low pH, the copolymers are dispersed as unimers in solution with Rh of about 6-7 nm. However, at a physiological salt concentration (cs) of about 0.16M NaCl and a pH of 7-8, the copolymers form large loosely packed Guassian chains, which were not present at the low cs of 0.001M NaCl. The critical micelle concentrations (CMC) and the cytotoxicity of the copolymers were investigated to determine a suitable polymer concentration range for future biological applications. Both PEO-b-PDEAEMA and biotin-PEO-b-PDEAEMA diblock copolymers possess identical CMC values of about 0.0023 mg/g, while the cytotoxicity test indicated that the copolymers are not toxic up to 0.05mg/g (> 83% cell survival at this concentration).

Micellar and surface properties of a poly(methyl methacrylate)-block-poly(N-isopropylacrylamide) copolymer in aqueous solution

Critical micelle concentrations (cmc) of aqueous solutions of poly(methyl methacrylate)-block-poly(N-isopropylacrylamide) were determined at several temperatures by surface tensiometry. Below the lower critical solution temperature (LCST), the low Delta(mic) H-0 determined can be assigned to the PMMA block being tightly coiled in the dispersed molecular state, so that the unfavorable interactions of hydrophobic entities with water are minimized. Above the LCST the cmc value was found to increase; an anomalous behavior that can be directly related to the micelle-globule transition of the hydrophilic block. Interestingly, above the LCST the surface tension of relatively concentrated solutions was found to depend weakly on temperature not following the usual strong decrease with temperature expected for aqueous solutions. (C) 2007 Elsevier Inc. All rights reserved.

Thermo-responsive poly(methyl methacrylate)-block-poly(N-isopropylacrylamide) block copolymers synthesized by RAFT polymerization: micellization and gelation

RAFT polymerization was used to prepare PMMA-b-PNIPAM copolymers. Two different chain transfer agents, tBDB and MCPDB, were used to mediate the sequential polymerizations. Micellar solutions and gels were prepared from the resulting copolymers in aqueous solution. When heated above T-c of PNIPAM (about 31 degrees C), DLS revealed that PNIPAM coronas collapsed, resulting in aggregation of the original micelles. The micellar gels underwent syneresis above T-c as water was expelled from the ordered gel structure, the lattice periodicity of which was determined by SANS. A large decrease in lattice spacing was observed above T-c. The gel became more viscoelastic at high temperature, as revealed by shear rheometry which showed a large increase in G".

Comparison of white metal and resin socket terminations for wire ropes

Previously the authors have presented both theoretical and experimental work discussing the operating mechanism of a wire rope held in a tapered socket by means of a cast resin cone. The work reported here extends the investigation to address the question of whether the same socket fabricated with white metal operates in the same manner. To date, previous investigations have compared the operational efficiency of resin and white metal in terms of both strength and/or fatigue endurance. Some other work has analysed the operation of resin sockets or specific cast metal terminations. This paper seeks to draw the results from this work together, and, in addition to a theoretical analysis, presents experimental data obtained from a direct comparison of the operation mechanism for the same sockets filled with resin or white metal. Results show that white metal terminations have a very different distribution of stresses along the length of the socket basket from resin terminations, and a smaller but still significant amount of socket draw. For both types of termination the socket draw develops high frictional gripping forces which can transfer the load from the rope to the socket. The different stress distributions mean that the consequences of termination fabrication defects may not be the same for resin and white metal terminations.

Using a water-soluble melamine-formaldehyde resin to improve the hardness of Norway spruce wood

Samples of Norway spruce wood were impregnated with a water-soluble melamine formaldehyde resin by using short-term vacuum treatment and long-term immersion, respectively. By means of Fourier transform infrared (FTIR) spectroscopy and UV microspectrophotometry, it was shown that only diffusion during long-term immersion leads to sufficient penetration of melamine resin into the wood structure, the flow of liquids in Norway spruce wood during vacuum treatment being greatly hindered by aspirated pits. After an immersion in aqueous melamine resin solution for 3 days, the resin had penetrated to a depth > 4 mm, which, after polymerization of the resin, resulted in an improvement of hardness comparable to the hardwood beech. A finite element model describing the effect of increasing depth of modification on hardness demonstrated that under the test conditions chosen for this study, a minimum impregnation depth of 2 mm is necessary to achieve an optimum increase in hardness. (C) 2004 Wiley Periodicals, Inc.

Mechanisms of femtosecond laser-induced refractive index modification of poly(methyl methacrylate)

The mechanisms of refractive index change in poly(methyl methacrylate) by frequency doubled femtosecond laser pulses are investigated. It is demonstrated that positive refractive index modificaton can be caused by a combination of depolymerization and crosslinking.