The Effect of Splint Material Rigidity in Implant Impression Techniques

Purpose This in vitro study compared the dimensional accuracy of two impression techniques Duralay splinted impression copings (D) and metal splinted impression copings (M) for implant supported pros theses Materials and Methods A master cast with four parallel implant abutment analogs and a passive framework were fabricated Vinyl polysiloxane impression material was used for all impressions with a metal stock tray Two groups (D and M) were tested (n = 5) The measurement method employed was just one titanium screw tightened to the framework Each group s measurements were analyzed using software that received the images of a video camera coupled to a stereomicroscope at X100 magnification The results were analyzed statistically (t test) Results The mean values of abutment/framework interface gaps were master cast = 32 mu m (SD 2), group D = 165 mu m (SD 60), and group M = 69 mu m (SD 36) There was a statistically significant difference between the D and M groups (P <= 001) Conclusion Under the limitations of this study, it could be suggested that a more accurate working cast can be fabricated using metal splinted impression copings INT J ORAL MAXILLOFAC IMPLANTS 2010 25 1153-1158

THE SERVICE LIFE of IMPLANT-RETAINED OVERDENTURE ATTACHMENT SYSTEMS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Cytotoxicity of monomers, plasticizer and degradation by-products released from dental hard chairside reline resins

Objectives. The aim of this study was to evaluate the cytotoxic effect of the monomers isobutyl methacrylate (IBMA) and 1,6-hexanediol dimethacrylate (1,6-HDMA), the plasticizer di-n-butyl phthalate (DBP), and the degradation by-products methacrylic acid (MA) and benzoic acid (BA) on L929 cells. Based on previous investigations on the release of these compounds from hard chairside reline resins, a range of concentrations (mu mol/L) were selected for the cytotoxicity tests (IBMA, 5.491406.57; 1,6-HDMA, 1.2239.32; DBP, 1.12143.8; MA, 9.07581; BA, 3.19409).Methods. Cytotoxic effects were assessed using MTT and 3H-thymidine assays after the cells had been exposed to the test compounds at the given concentrations for 24h. Cytotoxicity was rated based on cell viability relative to controls (cells exposed to medium without test substances).Results. DNA synthesis activity was inhibited by all compounds. Mitochondrial dehydrogenase activity decreased in cells treated with monomers, plasticizer and MA by-product, whereas no cytotoxic effect was observed on contact with BA at the majority of concentrations tested. The ranges of suppression for 3H-thymidine assay were: IBMA, 2595%; 1,6-HDMA, 9598%; DBP, 4098%; MA, 9799%; BA, 5471%. For MTT assay, the ranges of suppression were: IBMA, 096%; 1,6-HDMA, 2689%; DBP, 1780%; MA, 5266%; BA, 027%. The 3H-thymidine assay was more sensitive than the MTT assay.Significance. This study evaluated the cytotoxicity of a wide range of concentrations of monomers (IBMA and 1,6-HDMA), plasticizer (DBP) and degradation by-products (MA and BA), including those expected to be released from hard chairside reline resins. The differences observed in the cytotoxicity of these compounds, along with other properties, may assist the dental practitioners in the selection of reline materials with improved service life performance and low risk of adverse reactions in patients who wear relined dentures.

Radiographic effect of different radiopacifiers on a potential retrograde filling material

Objective. The objective of this study was to evaluate the radiopacity of white Portland cement (PC) associated with bismuth oxide (Bi(2)O(3)), barium sulfate (BaSO(4)), iodoform (CHI(3)), and zirconium oxide (ZrO(2)). White mineral trioxide aggregate (WMTA) and PC without radiopacifier were used as positive and negative controls, respectively.Study design. Following International Organization for Standardization (ISO) 6876/2001, 5 circular specimens (10 x 1 mm) were made from each material. After the materials set, radiographs were taken using occlusal film and a graduated aluminum step-wedge varying in thickness from 2 to 16 mm. The dental X-ray unit (GE1000) was set at 50 Kvp, 10 mA, 18 pulses/s, and distance of 33.5 cm. The radiographs were digitized, and radiopacity was compared with the aluminum step-wedge, using Wixwin-2000 software (Gendex). Data (mm Al) were analyzed using analysis of variance and Tukey tests.Results. The PC + Bi(2)O(3) and WMTA samples presented greater radiopacity (5.88 and 5.72 mm Al, respectively), followed by PC + ZrO(2) (3.87 mm Al) and PC + CHI(3) (3.50 mm Al). The PC + BaSO(4) and PC samples presented the lowest radiopacity values (2.35 and 1.69 mm Al, respectively), which were below the minimum value recommended by the ISO.Conclusion. Analysis of the present results led to the conclusion that all of the materials tested presented acceptable radiopacity, except PC + BaSO(4) and pure PC. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: 628-632)

Effect of light-curing units on microleakage under dental composite resins

The aim of this study was to determine the effect of two light-curing units (QTH and LED) on microleakage of Class II composite resin restorations with dentin cavosurface margins. Twenty extracted mandibular first premolars, free of caries and fractures were prepared two vertical slot cavities in the occluso-mesial and -destal surfaces (2 mm buccal-lingually, 2 mm proximal-axially and cervical limit in enamel) and divided into 4 equal groups (n = 8): GI and GII: packable posterior composite light-activated with LED and QTH, respectively; GIII and GIV: micro-hybrid composite resin light-activated with LED and QTH, respectively. The composite resins were applied following the manufacturer's instructions. After 24 h of water storage specimens were subjected to thermocycling for a total of 500 cycles at 5 and 55A degrees C and the teeth were then sealed with impermeable material. Teeth were immersed in 0.5% Basic fuchsin during 24 h at room temperature, and zero to three levels of penetration score were attributed. The Mann-Whitney and Kruskal-Wallis tests showed significant statistically similar (P > 0.05) from GI to GII and GIII to GIV, which the GII (2.750) had the highest mean scores and the GIII and GIV (0.875) had lowest mean scores. The use of different light-curing units has no influence on marginal integrity of Class II composite resin restorations and the proprieties of composite resins are important to reduce the microleakage.

Effect of different dental composite resins on the polymerization process

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Changes in the morphology and ultrastructure of the Dufour's gland during the life cycle of the bumble bee queen, Bombus terrestris L-(Hymenoptera : Bombini)

The Dufour's gland is found closely associated with the sting apparatus of all female hymenopterans, playing multiple roles among bees. In some species of Bombus the gland may be involved in production of nestmate recognition pheromones, but in B. terrestris its function is not certain yet. The morphology of the :Dufour's gland of B. terrestris queens and the ultrastructural features of its cells were studied in different ages and behavioural stages using routine transmission electron microscopy. Measurements of the length and the diameter of the gland in the same conditions were also made. The Dufour's gland of the queen increases significantly in size (both in length and in diameter) with age and reproductive activity the ultrastructural features of the gland show electrondense material that comes from the haemolymph. This material is also present in the intercellular spaces, and is conducted to the subcuticular space, to be released directly into the glandular lumen. Hence at least part of the secretion is probably taken up directly from the haemolymph. The ultrastructural features indicate a more active phase of the gland corresponding to the period of egg-laying of the queen, and a decrease in activity when the queen is in hibernation as well as after the competition point. In conclusion, the gland is probably involved in reproduction, more specifically, in the marking off eggs.

Y-TZP ceramic processing from coprecipitated powders: A comparative study with three commercial dental ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Assessment of the effectiveness of light-emitting diode and diode laser hybrid light sources to intensify dental bleaching treatment

Objective. To evaluate the effectiveness of the color change of hybrid light-emitting diode (LED) and low-intensity infrared diode laser devices for activating dental bleaching and to verify the occurrence of a color regression with time. Material and methods. A total of 180 specimens obtained from human premolars were immersed in a coffee solution for 15 days for darkening and then divided into eight experimental groups (n = 20 in each) as follows: G1, bleaching without light; G2, bleaching with halogen light; G3, bleaching with a blue LED (1000 mW/470 nm) and a laser device (120 mW/795 nm) simultaneously; G4, bleaching with an LED emitting blue light (1000 mW/470 nm); G5, bleaching with a blue LED (800 mW/470 nm) and a laser device (500 mW/830 nm) simultaneously; G6, bleaching with a blue LED device (800 mW); G7, bleaching with a green LED (600 mW/530 nm) and a laser device (120 mW/795 nm) simultaneously; and G8, bleaching with a green LED (600 mW). Three measurements were performed (at baseline and 14 days and 12 months after bleaching) using a Vita Easyshade spectrophotometer. The data were submitted to two-way ANOVA and a Tukey test. Results. All groups showed significantly higher Delta E values than Group G1, with the exception of Group G8. Variations in the Delta E values at 14 days were significant when compared with those obtained at baseline and after 12 months. Conclusions. Light activation of the bleaching gel provided faster and more intense bleaching than use of the bleaching gel without light activation. Combinations of low-intensity diode lasers are ineffective as a bleaching gel activator. Color regression was observed after 12 months of storage.

A study of the microstructural characteristics of dental amalgams

Metallographic studies by scanning electron microscopy and energy dispersive spectroscopy carried out for two types of dental amalgam showing a porous multiphase material. Surface analysis shows that the structure of the Dispersalloy amalgam consists of gamma-Ag3Sn, gamma(1)-Ag2Hg3, eta'-Cu6Sn5, epsilon-Cu3Sn and eutectic Ag-Cu phases. while Velvalloy amalgam consists mainly of gamma, gamma(1) and gamma(2)-Sn7-8Hg phases. The latter phase presents an uniform distribution often associated with voids.

Histomorphological response of dogs' dental pulp capped with white mineral trioxide aggregate

Foi objetivo deste trabalho estudar a reação do tecido pulpar ao capeamento com agregado de trióxido mineral (MTA) branco. Para isto, foram utilizados 15 dentes de cães, onde após o preparo de cavidades na região cervical da face vestibular e exposição pulpar, estas foram capeadas com MTA branco. Os animais foram sacrificados após 60 dias do término dos procedimentos clínicos e os dentes processados em laboratório para obtenção de cortes histológicos. Foi observada formação de ponte de tecido duro em todas as polpas. em alguns casos, não havia dentina tubular mas somente uma estrutura de aspecto morfológico peculiar, selando a cavidade de exposição pulpar. Apenas dois casos apresentaram inflamação pulpar. Conclui-se que o MTA branco possui as características necessárias de um material para capeamento pulpar.

Characterization of ceramic powders used in the inCeram systems to fixed dental Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)