Morphological and luminescent studies on nanosized Er, Yb-Yttrium oxide up-converter prepared from different precursors

In this paper, we report luminescent and morphological studies with yttrium oxide samples doped with ytterbium and erbium. The samples were prepared by the combustion method and also from different precursors: oxalate, basic carbonate and polymeric resin. All powders were identified Lis being an yttrium oxide with a C-form structure, independent of the employed precursor. From mean crystallite size measurements, it was verified that oxides prepared through the polymeric precursor and combustion methods lead to the smallest crystallite size. Particle shape and size were investigated by SEM and TEM, and showed that both the oxalate precursor and the combustion methods do not provide oxide materials of suitable shape or size, on the other hand. The basic carbonate and polymeric precursors resulted in spherically shaped particles with an average diameter of 90 and 15 run. respectively, Upon 980 run diode laser excitation, green and red emission lines were detected for all samples and were assigned to the H-2(11/2) S-4(3/2) -> I-4(15/2) and (4)Fg(9/2) -> 4I(15/12) transitions, respectively. Such transitions are characteristic for Er3+ and result from energy transfer from Yb3+ energy levels, F-2(7/2) -> F-2(5/2). A relationship between the decrease in the mean crystallite size and the enhancement in red emission was also established as well as the influence of the presence of a high percentage of Yb-3 Both factors promote ET from Yb3+ (F-2(5/2)) to Er3+ (I-4(11/2)). (c) 2004 Elsevier B.V. All rights reserved.

SiO2-PbF2-CdF2 glasses and glass ceramics

Lead-Cadmium fluorosilicate stable glasses were prepared and the vitreous domain region determined in the composition diagram. Characteristic temperatures were obtained from thermal analysis and the structural studies performed illustrate clearly the role played by lead atoms in the glasses crystallization behavior and the glass-forming ability of cadmium atoms. The occurrence of either a cubic lead fluoride or a lead-cadmium fluoride solid solution in crystallizing samples was found to be dependent on Er3+ doping. The optically active ions were found to concentrate in the crystalline phase and in fact play the role of nucleating agent as suggested from X-ray diffraction and EXAFS measurements. (C) 2002 Elsevier B.V. Ltd. All rights reserved.

Spectroscopic properties of Er3+ in oxysulfide glasses

Er3+ -containing gallium-lanthanum oxysulfide glasses have been prepared from Ga2O3 and La2S3 in a sulfur/argon reactive atmosphere. The samples have been characterized by absorption and emission spectroscopy and IR emission kinetics. Er3+ electronic transition intensities have been analyzed in the light of the Judd-Ofelt formalism, and quantum efficiencies evaluated for the Er3+ emission at 1.5 and 2.7 mum. The results so obtained suggest that these glasses display favorable properties concerning IR optical applications. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Electron trapping of laser-induced carriers in Er-doped SnO2 thin films

In order to investigate optically excited electronic transport in Er-doped SnO2, thin films are excited with the fourth harmonic of an Nd:YAG laser (266nm) at low temperature, yielding conductivity decay when the illumination is removed. Inspection of these electrical characteristics aims knowledge for electroluminescent devices operation. Based on a proposed model where trapping defects present thermally activated cross section, the capture barrier is evaluated as 140, 108, 100 and 148 meV for doped SnO2, thin films with 0.0, 0.05, 0. 10 and 4.0 at% of Er, respectively. The undoped film has vacancy levels as dominating, whereas for doped films. there are two distinct trapping centers: Er3+ substitutional at Sn lattice sites and Er3+ located at grain boundary. (C) 2007 Elsevier Ltd. All rights reserved.

New glasses in the system InF3-BaF2-ErPO4

New glasses have been obtained in the system InF3-BaF2-ErPO4. Glass compositions with up to 30% mol Er3+ were shown to exist and characterized by thermal analysis, x-ray: diffraction, IR absorption and electronic spectroscopy. The systems with high Er3+ content were studied recording IR and visible emission spectral characteristics. A specially elaborated technique allowed the preparation of a high purity phosphate precursor ErPO4. X-ray identification of the crystalline phases appearing during thermal treatment have been carried out and parameters of a mixed fluoride Ba4In3-nErnF17 calculated.

Temperature rise in cavities prepared by high and low torque handpieces and Er : YAG laser

Objective The aim of this study was to compare intrapulpal temperature increases produced by a high-speed high-torque (speed-increasing) handpiece, a high-speed low-torque handpiece (air-turbine) and an Er: YAG (Erbium: Yttrium-Aluminum-Garnet) laser. Subject and methods Thirty bovine incisors were reduced to a dentine thickness of 2.0 mm. Class V preparations were prepared to a depth of 1.5 mm, measured with a caliper or by a mark on the burs. A thermocouple was placed inside the pulp chamber to determine temperature increases (C). Analysis was performed on the following groups (n = 10) treated with: G1, low-torque handpiece; G2, high-torque handpiece; and G3, Er: YAG laser (2.94 mu m at 250 mJ/4 Hz), all with water cooling. The temperature increases were recorded with a computer linked to the thermocouples. Results The data were submitted to ANOVA and Tukey statistical test. The average temperature rises were: 1.92 +/- 0.80 degrees C for G1, 1.34 +/- 0.86 degrees C for G2, and 0.75 +/- 0.39 degrees C for G3. There were significant statistical differences among the groups (p = 0.095). All the groups tested did not have a change of temperature that exceeds the threshold of 5.5 degrees C. Conclusion Temperature response to the low and high torque handpieces seemed to be similar, however the Er: YAG laser generated a lower temperature rise.

Er3+-doped germanate glasses for active waveguides prepared by Ag+/K+ <-> Na+ ion-exchange

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Rare Earth Doped SnO(2) Nanoscaled Powders and Coatings: Enhanced Photoluminescence in Water and Waveguiding Properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Er(3+)-Based Diureasil Organic-Inorganic Hybrids

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Investigation on the structural properties in Er-doped PbTiO3 compounds: A correlation between experimental and theoretical results

The aim of this work is to investigate the structural properties of the (Pb1-xErx)TiO3 (PET) powders, with x varying from 0.01 to 0.08, prepared by the polymeric precursor method. Combined X-ray diffraction, Raman spectroscopy and ab initio calculation reveal a diffuse phase-transition of a tetragonal to a cubic phase. The crystalline models built allowed to calculate electronic properties and to analyze the behavior of the doping element in the structure of the material, which are consistent with the experimental results that indicate the beginning of phase-transition from tetragonal to cubic. (C) 2007 Elsevier B.V. All rights reserved.

Growth of silver nano-particle embedded in tellurite glass: Interaction between localized surface plasmon resonance and Er3+ ions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Localized surface plasmon resonance interaction with Er3+-doped tellurite glass

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Optical emission and electron capture of rare-earth trivalent ions located at distinct sites in SnO(2) thin films

We present photoluminescence and decay of photo excited conductivity data for sol-gel SnO(2) thin films doped with rare earth ions Eu(3+) and Er(3+), a material with nanoscopic crystallites. Photoluminescence spectra are obtained under excitation with several monochromatic light sources, such as Kr(+) and Ar(+) lasers, Xe lamp plus a selective monochromator with UV grating, and the fourth harmonic of a Nd: YAG laser (4.65eV), which assures band-to-band transition and energy transfer to the ion located at matrix sites, substitutional to Sn(4+). The luminescence structure is rather different depending on the location of the rare-earth doping, at lattice symmetric sites or segregated at grain boundary layer, where it is placed in asymmetric sites. The decay of photo-excited conductivity also shows different trapping rate depending on the rare-earth concentration. For Er-doped films, above the saturation limit, the evaluated capture energy is higher than for films with concentration below the limit, in good agreement with the different behaviour obtained from luminescence data. For Eu-doped films, the difference between capture energy and grain boundary barrier is not so evident, even though the luminescence spectra are rather distinct.

Optical transition probabilities and compositional dependence of Judd-Ofelt parameters of Er3+ ions in fluoroindate glass

Fluoroindate glasses containing 1, 2, 3, and 4 mol% ErF3 were prepared in a dry box under an argon atmosphere. Absorption spectra of these glasses at room temperature were obtained. The Judd-Ofelt parameters Ωλ (λ = 2, 4, 6) for f-f transitions of Er3+ ions as well as transition probabilities, branching ratios, radiative lifetimes, and peak cross-sections for stimulated emission of each band were determined. The concentration effect on the intensities is analyzed. The optical properties of the fluoroindate glasses doped with Er3+ ions are compared with those of other glasses described in the literature. © 1995.

Optical spectroscopy of Er3+ and Yb3+ co-doped fluoroindate glasses

Optical absorption, Stokes, and anti-Stokes photoluminescence were performed on Er3+-Yb3+ co-doped fluoroindate glasses. For compounds prepared with a fixed 2 mol % ErF3 concentration and YbF3 contents ranging from 0 to 8 mol %, important upconversion processes were observed as a function of temperature and photon excitation energy. Based on the experimental data, two mechanisms for the upconversion (or anti-Stokes photoluminescence) processes were identified and analyzed in detail. At high Yb contents, the upconversion mechanisms are mostly determined by the population of the 2F5/2 levels of Yb3+ ions (or 4I11/2 levels of Er3+ ions, by energy transfer) regardless of the photon excitation energy and temperature of measurement. Moreover, green and red light emission have similar intensities when a large Yb3+ content is present. © 1998 American Institute of Physics.