Influência do teor de calcário no comportamento físico, mecânico e microestrutural de cerâmicas estruturais

There are ores of clay in Piauí State that are used for red structural ceramics, which are naturally contaminated with calcareous vein. This is one thing that impedes its exploration in an adequate way, especially for tile production. The present work aims at verifying the influence of the calcareous contents in the technological structural ceramics area, seeking to determine a maximum permissible calcareous proportion/contents in the ceramic mass using the patterns of the local industry production. For the consecution of this paper, it was characterized the clay and calcareous material by FRX, DRX, TGA and DTA. It was also configurated by extrusion and burnt in the temperatures of 850°C, 900°C, 950°C and 1000°C pieces of the corpus with 0, 5, 10, 15 e 20% of calcareous proportion. After that, it was carried out technological samples of linear retraction, water absortion, apparent porosity, specific apparent mass and mechanic resistance. The results showed the possibility of using calcareous in the ceramic mass and in some cases the technological properties got better

Influência da gipsita no surgimento de eflorescência em telhas cerâmicas

The red ceramic industry is recognized as of major importance in Piauí State. The State capital, Teresina, is the greatest producer of this material ( production about 18 million peaces), which is used mainly for masonry sealing blocks. One of the most frequent problems in this kind of products is the efflorescence. This work has the main objective of studying the influence of gypsum addition on non-glazed tiles, by using the local industry production standards. The raw materials were characterized by FRX, DRX, TGA, DTA and AD. Extruded test specimens were made with the addition of 1, 3 and 5% of gypsum in the ceramic paste, burned at 850oC, 950oC and 1050oC and submitted to further technological tests and microestrutural analysis by the scanning electron microscope. In order to accelerate the aging of bodies of evidence, they were immersed in successive water baths and posterior drying. The reference ceramic paste showed tendency to efflorescence formation after drying and consolidated efflorescence after burning, but no affecting the technological results

Avaliação espectrofotométrica do manchamento de resinas odontológicas contendo nanopartículas

Composite resins have been subjected to structural modifications aiming at improved optical and mechanical properties. The present study consisted in an in vitro evaluation of the staining behavior of two nanohybrid resins (NH1 and NH2), a nanoparticulated resin (NP) and a microhybrid resin (MH). Samples of these materials were prepared and immersed in commonly ingested drinks, i.e., coffee, red wine and acai berry for periods of time varying from 1 to 60 days. Cylindrical samples of each resin were shaped using a metallic die and polymerized during 30 s both on the bottom and top of its disk. All samples were polished and immersed in the staining solutions. After 24 hours, three samples of each resin immersed in each solution were removed and placed in a spectrofotome ter for analysis. To that end, the samples were previously diluted in HCl at 50%. Tukey tests were carried out in the statistical analysis of the results. The results revealed that there was a clear difference in the staining behavior of each material. The nanoparticulated resin did not show better color stability compared to the microhybrid resin. Moreover, all resins stained with time. The degree of staining decreased in the sequence nanoparticulated, microhybrid, nanohybrid MH2 and MH1. Wine was the most aggressive drink followed by coffee and acai berry. SEM and image analysis revealed significant porosity on the surface of MH resin and relatively large pores on a NP sample. The NH2 resin was characterized by homogeneous dispersion of particles and limited porosity. Finally, the NH1 resin depicted the lowest porosity level. The results revealed that staining is likely related to the concentration of inorganic pa rticles and surface porosity

Diseños de investigación utilizados en revistas odontológicas de la red SciELO: una visión bibliométrica

Introducción: El objetivo de esta investigación fue identificar las características que diferencian aquellos diseños de investigación en odontología para su clasificación. Se realizó una revisión bibliométrica descriptiva, donde se identificaron las revistas odontológicas SciELO de la literatura en el área odontológica comprendidas entre el primer semestre del año 2013 y primer semestre del año 2014. Material y método: Estudio bibliométrico descriptivo, donde se identificaron las revistas odontológicas SciELO de la literatura en el área odontológica para determinar los diferentes tipos de diseño de investigación de los artículos originales identificados en revistas de odontología indexadas de base SciELO el primer semestre del año 2013 y el primer semestre del año 2014, mediante un muestreo estratificado con afijación proporcional, el cual, de un total de 4.262 artículos originales que se han publicado, nos arrojó una muestra de 309 artículos. Resultados: De los artículos originales, podemos destacar que la mayor frecuencia la obtienen los diseños de Corte Transversal (121), Casos-Controles (68), In vitro (34), Serie de Casos (25), Ensayo Clínico (13), Revisión de Casos (12), Revisión de un Caso (7). De manera aislada, se observaron publicaciones de artículos tipo: In vivo, Revisión Sistemática, Correlacional, Cohorte, otros (Revisión Website, Estudio Preliminar, Análisis Bibliométrico, etc). Conclusiones: El diseño más utilizado fue el de Corte Transversal; en segundo lugar, el diseño con mayor frecuencia de aplicación fue el de Casos y Controles y, en tercer lugar, se encuentran los estudios In vitro. Se deben mejorar los diseños clínicos en la investigación odontológica para obtener mejor evidencia.

Avaliação da potencialidade dos resíduos de gesso de revestimento incorporados em formulações de massas cerâmicas

In building, during the implementation process of major or even minor works, there is a considerable waste of plaster in the steps of coating, making it is a negative factor because of the loss of these processes constructive remains incorporated into buildings, as component, whose final dimensions are higher than those projected. Another negative factor is the disposal of waste gypsum in inappropriate places, thus contributing to the degradation of environmental quality, due to the leaching of this waste and may trigger the formation of sulfuric acid. Therefore, based on this picture, processing and reuse of waste coating, combined with the ceramics industry, which is a strong potential in the reuse of certain types of waste, promote mutual benefits. Thus the overall objective of this work is to conduct a search with scientific and technological aspects, to determine the effect of the incorporation of the residue of plaster for coating, from the building, the formulation of bodies for red ceramic. The residue of plaster coating was collected and characterized. They were also selected raw materials of two ceramic poles of the state of Rio Grande do Norte and formulations have been made with the intention of obtaining those with the best physical and mechanical properties, the residue was added the percentage of 5%, 10%, 15%, 20%, 25% and 30%, in the best formulation of ceramic industry 1 and, according the properties analyses, 5%, 10% and 15% as the best results of ceramic industry 2. The samples were sintered at temperatures of 850 ºC, 950 °C and 1050 °C, the heating rate of 5 ºC / min with isotherm of two hours. They were submitted to testing technology, such as lineal shrinkage, water absorption, apparent porosity, apparent density and bending resistence. The residue incorporation best results in the formulations of mass in red ceramic, were observed between the temperatures of 850 ºC and 950 ºC, in those formulations that have illite clays and medium plastic in their composition, in the range of 0% to 15% residue incorporated

Síntese e caracterização de cerâmicas nanométricas para produção de gás de síntese

In this work, ceramic powders belonging to the system Nd2-xSrxNiO4 (x = 0, 0.4, 0.8, 1.2 and 1.6) were synthesized for their use as catalysts to syngas production partial. It was used a synthesis route, relatively new, which makes use of gelatin as organic precursor. The powders were analyzed at several temperatures in order to obtain the perovskite phase and characterized by several techniques such as thermal analysis, X-rays diffraction, Rietveld refinement method, specific surface area, scanning electron microscopy, energy dispersive spectroscopy of X-rays and temperature programmed reduction. The results obtained using these techniques confirmed the feasibility of the synthesis method employed to obtain nanosized particles. The powders were tested in differential catalytic conditions for dry reforming of methane (DRM) and partial oxidation of methane (POM), then, some systems were chosen for catalytic integrals test for (POM) indicating that the system Nd2-xSrxNiO4 for x = 0, 0.4 and 1.2 calcined at 900 °C exhibit catalytic activity on the investigated experimental conditions in this work without showing signs of deactivation

Estudo do efeito da adição da escória de aciaria no processamento e propriedades finais de telhas cerâmicas

This research presents an overview of the addition steelwork dust of ceramic shingles in order to contribute to the utilization use of such residue. The ceramic industry perspective in the Brazilian State of Piauí is quite promising. Unlike other productive sectors, the ceramic industry uses basically natural raw materials. Its final products are, in short, the result of transforming clay compounds. These raw materials are composed primarily of aluminum oxide, silicon, iron, sodium, magnesium, end calcium, among others. It was verified that steelwork dust is composed primarily of these same oxides, so that its incorporation in to structural ceramics is a very reasonable idea. Both clay and steelwork powder were characterized by AG, XRF, XRD, TGA and DTA. In addition, steelwork dust samples containing (0%, 5%, 10%, 15%, 20% and 25%) were extruded and burned at 800°C, 850°C, 900°C and 950°C. Then t echnological tests of linear shrinkage, water uptake, apparent porosity, apparent density and flexural strengthwere carried at. The results showed the possibility of using steelwork powder in ceramic shingles until 15% significant improvement in physical and mechanical properties. This behavior shows the possibility of burning at temperatures lower than 850ºC, thus promoting a product final cost reduction

Formulação de massas cerâmicas para porcelanas elétricas utilizando resíduos oriundos de corpos de fusíveis

The power industry generates as waste ceramic bodies of electrical fuses that are discarded after use. The formulation of ceramic bodies for porcelain electrical insulators using waste from the bodies fuse allocation promotes environmentally appropriate, through the reuse of the material. This work evaluated the technical feasibility of using waste for use in electrical porcelains with formulations containing the residue, feldspar and kaolinite. The raw materials were processed through grinding and sieving to 200 mesh. The ceramic material obtained from the proposed formulations with 25%, 30%, 34% and 40% of the residue went through a vibratory mill for grinding and homogenization, and then were sieved at 325 mesh. The samples were shaped in a uniaxial press, with the application of 25 MPa and sintered at 1100° C, 1150°C, 1200°C, 1225°C and 1250°C, at levels of 20 and 45 minutes. Were also developed bodies of evidence with reference formulations obtained without residue, to establish a comparison on physical, mechanical and electrical. The tests were conducted and technology: linear shrinkage, porosity, water absorption, resistance to bending to three points, measuring insulation resistance electrical resistivity of the material, X-ray diffraction and X-ray fluorescence Waste characterizations pointed to the existence of two phases: mullite and quartz phases are of great importance in the microstructure of the ceramic and this fact reveals a possibility for reuse in electrical porcelains. The mullite is an important constituent because it is a phase that makes it possible to increase the mechanical strength in addition to the body allows the use at high temperatures. The use of ceramic bodies residue fuses, proved feasible for application in electrical porcelain and the most significant results were obtained by the formulations with 25% waste and sintering at 1200°C

Aplicação da metodologia de planejamento de experimentos para formulação de massas cerâmicas para telhas

Rio Grande do Norte State stands out as one great producer of structural clay of the brazilian northeastern. The Valley Assu ceramic tiles production stands out obtained from ilitics ball clays that abound in the region under study. Ceramics formulation and the design of experiments with mixture approach, has been applied for researchers, come as an important aid to decrease the number of experiments necessary to the optimization. In this context, the objective of this work is to evaluate the effects of the formulation, temperature and heating rate in the physical-mechanical properties of the red ceramic body used for roofing tile fabrication of the Valley Assu, using design of mixture experiments. Four clays samples used in two ceramics industry of the region were use as raw material and characterized by X-ray diffraction, chemical composition, differential thermal analysis (DTA), thermogravimetric analysis (TGA), particle size distribution analysis and plasticity techniques. Afterwards, they were defined initial molded bodies and made specimens were then prepared by uniaxial pressing at 25 MPa before firing at 850, 950 and 1050 ºC in a laboratory furnace, with heating rate in the proportions of 5, 10 e 15 ºC/min. The following tecnologicals properties were evaluated: linear firing shrinkage, water absorption and flexural strength. Results show that the temperature 1050 ºC and heating rate of 5 ºC/min was the best condition, therefore presented significance in all physical-mechanical properties. The model was accepted as valid based of the production of three new formulations with fractions mass diferents of the initial molded bodies and heated with temperature at 1050 ºC and heating rate of 5 ºC/min. Considering the formulation, temperature and heating rate as variables of the equations, another model was suggested, where from the aplication of design of experiments with mixtures was possible to get a best formulation, whose experimental error is the minor in relation to the too much formulations

Sinterização de matrizes cerâmicas à base de alumina reforçadas por carbetos a partir de precursores poliméricos

Ceramic composites produced with polymerics precursors have been studied for many years, due to the facility of obtaining a complex shape, at low temperature and reduces cost. The main objective of this work is to study the process of sintering of composites of ceramic base consisting of Al2O3 and silicates, reinforced for NbC, through the technique of processing AFCOP, as well as the influence of the addition of LZSA, ICZ and Al as materials infiltration in the physical and mechanical properties of the ceramic composite. Were produced ceramic matrix composites based SiCxOy e Al2O3 reinforced with NbC, by hidrosilylation reaction between D4Vi and D1107 mixtured with Al2O3 as inert filler, Nb and Al as reactive filler. The specimens produced were pyrolised at 1200, 1250 and 1400°C and infiltred with Al, ICZ and LZSA, respectively. Density, porosity, flexural mechanical strength and fracture surface by scanning electron microscopy were evaluated. The microstructure of the composites was investigated by X-ray diffraction to identify the presence of crystalline phases. The composites presented apparent porosity varying of 31 up to 49% and mechanical flexural strength of 14 up to 34 MPa. The infiltration process improviment of the densification and reduction of the porosity, as well as increased the values of mechanical flexural strength. The obtained phases had been identified as being Al3Nb, NbSi2, Nb5S3, Nb3Si and NbC. The samples that were submitted the infiltration process presented a layer next surface with reduced pores number in relation to the total volume

Tratamento ortodôntico de Classe III não cirúrgico e reabilitação com facetas cerâmicas

Poster apresentado no XXIV Congresso Anual da Ordem dos Médicos Dentistas, Lisboa, 12-14 Novembro 2015.

Percepción de la seguridad y salud en el trabajo en una población perteneciente a 11 clínicas odontológicas particulares de Bogotá, D.C, 2016.

Objetivo: Establecer la relación entre la percepción de seguridad con los factores ocupacionales y socio demográficos de los trabajadores pertenecientes a 11 clínicas odontológicos particulares en Bogotá. Materiales y métodos: Estudio de corte transversal en población de trabajadores pertenecientes a clínicas odontológicas particulares de Bogotá (Colombia). La muestra incluyó 105 odontólogos y 107 auxiliares pertenecientes a 11 clínicas odontológicas privadas en Bogotá que cumplieron con los criterios de selección. Se incluyeron variables ocupacionales y socio demográficas y las relacionadas con el sistema de seguridad y salud en el trabajo. Se aplicó el “Cuestionario Nórdico Sobre Seguridad en el Trabajo. Para los factores socio-demográficos de la población estudiada, se utilizó estadística descriptiva, medidas de frecuencia absoluta y porcentual, las variables cuantitativas se describieron con medidas de tendencia central y de dispersión; para la asociación de las variables cualitativas con el tipo de percepción se usó la prueba Ji Cuadrado de Pearson o el test exacto de Fisher para valores esperados menores de 5. Resultados: Las dimensiones con mejor percepción fueron las relacionadas con la confianza en la eficacia de los sistemas de seguridad (D7 3.35±0.43) y la Administración de justicia de seguridad (D3 3.1±0.55). Las dimensiones que evalúan la Gestión de empoderamiento de seguridad (D2 2.74±0.99) y la prioridad de los trabajadores con la seguridad (D5 2.64±0.54) tuvieron la menor percepción. La percepción de seguridad fue buena en general teniendo en cuenta que el promedio de todas las dimensiones fue superior a 2.5; percepción mayor significativamente en los hombres (3.78±0.38), odontólogos (3.89±0.38) y personal que tienen o han tenido pareja (3.83±0.4). Las personas con más trabajos adicionales (4.07±0.17), mayor nivel educativo (3.89±0.31), mayor antigüedad laboral (3.92±0.51) y trabajadores mayores de 30 años (3.89±0.35), mostraron mejor percepción de seguridad. En el análisis multivariado los factores cargo y antigüedad laboral encontraron asociación en las dimensiones 2, 4 y 6 (p<0.001), mientras que para las variables numéricas, las dimensiones 1, 3, 4 y 6 tuvieron asociación significativa las variables género y posición (p<0.001). Conclusiones: La percepción de seguridad en las siete dimensiones se relacionó con el género, edad, estado civil, nivel educativo, cargo, posición y antigüedad laboral. No se encontraron diferencias significativas por turno de trabajo o clínica.

The pottery from A and C-Group tombs at Serra West in the Museum of Natural History, La Plata

Abstract: The Museum of Natural History, La Plata, Argentina, houses a ceramic collection of the A-Group and C-Group cultures from Nubian tombs at Serra West (AA and ACS cemeteries), on the west bank of the Nile in Lower Nubia. It has been originated from the division after the excavations made by the Franco-Argentine Archaeological Expedition in Sudan between 1961 and 1963, as part of the UNESCO campaigns to save the Nubian monuments.

Ramesside, Late Nubian and christian pottery from Serra West in the Museum of Natural History, La Plata

Resumen: El Museo de Ciencias Naturales de La Plata, Argentina, posee una colección de piezas cerámicas provenientes del asentamiento egipcio y de la iglesia de Aksha, y de las tumbas nubias de Serra Oeste, sobre la margen izquierda del Nilo en la Baja Nubia, que pertenecen a las culturas meroítica y del Grupo X. Esta colección es producto del reparto después de las excavaciones realizadas por la Expedición Franco-Argentina en Sudán entre 1961 y 1963, como parte de las campañas de la UNESCO para salvar los monumentos de Nubia.

La cerámica de la Segunda Edad del Hierro en el País Vasco: Estudio tecnológico, funcional y social

670 p. Capítulos de introducción, metodología, discusión y conclusiones en castellano e inglés.