An experimental study on cracking evolution in concrete and cement mortar by the b-value analysis of acoustic emission technique

Notched three point bend (TPB) specimens made with plain concrete and cement mortar were tested under crack mouth opening displacement (CMOD) control at a rate of 0.0004 mm/s and simultaneously acoustic emissions (AE) released were recorded during the experiments. Amplitude distribution analysis of AE released during concrete was carried out to study the development of fracture process in concrete and mortar specimens. The slope of the log-linear frequency-amplitude distribution of AE is known as the AE based b-value. The AE based b-value was computed in terms of physical process of time varying applied load using cumulative frequency distribution (Gutenberg-Richter relationship) and discrete frequency distribution (Aki's method) of AE released during concrete fracture. AE characteristics of plain concrete and cement mortar were studied and discussed and it was observed that the AE based b-value analysis serves as a tool to identify the damage in concrete structural members. (C) 2012 Elsevier Ltd. All rights reserved.

Verification of Masonry Building Code to Flexural Behavior of Cement-Stabilized Soil Block

Most studies involving cement-stabilized soil blocks (CSSB) concern material properties, such as the characteristics of erosion and strength and how the composition of the block affects these properties. Moreover, research has been conducted on the performance of various mortars, investigating their material properties and the tensile bond strength between CSSB units and mortar. In contrast, very little is currently known about CSSB masonry structural behavior. Because structural design codes of traditional masonry buildings were well developed over the past century, many of the same principles may be applicable to CSSB masonry buildings. This paper details the topic of flexural behavior of CSSB masonry walls and whether the Masonry Standards Joint Committee (MSJC) code can be applied to this material for improved safety of such buildings. DOI: 10.1061/(ASCE)MT.1943-5533.0000566. (C) 2013 American Society of Civil Engineers.

SASW evaluation of asphaltic and cement concrete pavements using different heights of fall for a spherical mass

A number of spectral analysis of surface wave tests were performed on asphaltic and cement concrete pavements by dropping freely a 6.5kg spherical mass, having a radius of 5.82cm, from a height (h) of 0.51.5m. The maximum wavelength ((max)), up to which the shear wave velocity profile can be detected with the usage of surface wave measurements, increases continuously with an increase in h. As compared to the asphaltic pavement, the values of (max) and (min) become greater for the chosen cement concrete pavement, where (min) refers to the minimum wavelength. With h=0.5m, a good assessment of the top layers of both the present chosen asphaltic and the cement concrete pavements, including soil subgrade, can be made. For a given h, as compared to the selected asphaltic pavement, the first receiver in case of the chosen cement concrete pavement needs to be placed at a greater distance from the source. Inverse analysis has also been performed to characterise the shear wave velocity profile of different layers of the pavements.

Microcracking and fracture process in cement mortar and concrete: a comparative study using acoustic emission technique

This article reports the acoustic emission (AE) study of precursory micro-cracking activity and fracture behaviour of quasi-brittle materials such as concrete and cement mortar. In the present study, notched three-point bend specimens (TPB) were tested under crack mouth opening displacement (CMOD) control at a rate of 0.0004 mm/sec and the accompanying AE were recorded using a 8 channel AE monitoring system. The various AE statistical parameters including AE event rate , AE energy release rate , amplitude distribution for computing the AE based b-value, cumulative energy (I E) pound and ring down count (RDC) were used for the analysis. The results show that the micro-cracks initiated and grew at an early stage in mortar in the pre peak regime. While in the case of concrete, the micro-crack growth occurred during the peak load regime. However, both concrete and mortar showed three distinct stages of micro-cracking activity, namely initiation, stable growth and nucleation prior to the final failure. The AE statistical behavior of each individual stage is dependent on the number and size distribution of micro-cracks. The results obtained in the laboratory are useful to understand the various stages of micro-cracking activity during the fracture process in quasi-brittle materials such as concrete & mortar and extend them for field applications.

Low embodied energy cement stabilised rammed earth building-A case study

Rammed earth is a monolithic construction and the construction process involves compaction of processed soil in progressive layers in a rigid formwork. Durable and thinner load bearing walls can be built using stabilised rammed earth. Use of inorganic additives such as cement for rammed earth walls has been in practice since the last 5-6 decades and cement stabilised rammed earth (CSRE) buildings can be seen across the world. The paper deals with the construction aspects, structural design and embodied energy analysis of a three storey load bearing school building complex. The CSRE school complex consists of 15 classrooms, an open air theatre and a service block. The complex has a built-up area of 1691.3 m(2) and was constructed employing manual construction techniques. This case study shows low embodied energy of 1.15 GJ/m(2) for the CSRE building as against 3-4 GJ/m(2) for conventional burnt clay brick load bearing masonry buildings. (C) 2013 Elsevier B.V. All rights reserved.

Do stable isotopes in carbonate cement of Mio-Pleistocene Himalayan sediments record paleoecological and paleoclimatic changes?

Non-pedogenic carbonates, such as carbonate cement and nodules in the sandstones, are quite common in the terrestrial geological record. Unlike pedogenic carbonates, their stable isotope ratios lack investigations for paleo-climatic reconstructions. The present investigation therefore, explores the possibility of use of stable isotope studies of non-pedogenic carbonates from the Mb-Pleistocene Siwalik Group of sediments exposed in the Ramnagar sub-basin of the NW Himalaya. Petrographic studies reveal the dominance of micrite fabric in carbonate nodules both of pedogenic and non-pedogenic samples irrespective of specific stratigraphic unit However, calcite as cement in the sandstones shows the dominance of micrite fabric in the younger in age sediments. Seventy-two non-pedogenic carbonate samples from the carbonate nodules and cement in the Siwalik sandstones, ranging in age between similar to 1 Ma and 12.2 Ma, were analyzed for delta C-13 and delta O-18 values. The delta C-13 values vary from -24.77 parts per thousand to -1.1 parts per thousand and delta O-18 values vary from -15.34 parts per thousand to -7.81 parts per thousand. Pedogenic and non-pedogenic carbonates ranging in age between similar to 1 Ma and 6 Ma have largely similar delta C-13 values and the range of delta C-13 values indicate the dominance of C-4 type of vegetation. However, unlike pedogenic carbonates which showed the dominance of C-3 type of vegetation pre- 7 Ma on the basis of delta C-13 -depleted isotopic values (Singh et al., 2011), delta C-13 values are largely enriched in the corresponding aged non-pedogenic carbonates revealing no information on specific type of vegetation. Likewise, paleoprecipitational reconstructions from delta O-18 values in pedogenic carbonates showed a progressive increase in aridity from similar to 12 Ma to recent excluding short term increases in rainfall/monsoon intensity at around 10 Ma, 5 Ma, and 1.8 Ma (Singh et al., 2012). On the contrary, such reconstructions are not possible from the delta O-18 values of non-pedogenic carbonates and indeed the delta O-18 values of non-pedogenic carbonates are largely depleted to as much as 6 parts per thousand from the corresponding pedogenic carbonates. Such differences in delta C-13 and delta O-18 values of non-pedogenic carbonates from pedogenic carbonates are primarily due to the dependence of the former on groundwater conditions responsible for precipitating carbonate. Further, a comparison of isotopic values between non-pedogenic and pedogenic carbonates can be interpreted that post-6 Ma and pre-6 Ma non-pedogenic carbonates were largely formed by shallow and deep groundwater conditions respectively. The result of these investigative studies therefore, suggests that the stable delta C-13 and delta O-18 values of non-pedogenic carbonates, unlike the pedogenic carbonates and irrespective of nature of calcite fabric, showed their little importance in paleoclimatic and paleoecological reconstructions. (C) 2014 Elsevier B.V. All rights reserved.

Effect of Input Source Energy on SASW Evaluation of Cement Concrete Pavement

A series of spectral analyses of surface waves (SASW) tests were conducted on a cement concrete pavement by dropping steel balls of four different values of diameter (D) varying between 25.4 and 76.2 mm. These tests were performed (1) by using different combinations of source to nearest receiver distance (S) and receiver spacing (X), and (2) for two different heights (H) of fall, namely, 0.25 and 0.50 m. The values of the maximum wavelength (lambda(max)) and minimum wavelength (lambda(min)) associated with the combined dispersion curve, corresponding to a particular combination of D and H, were noted to increase almost linearly with an increase in the magnitude of the input source energy (E). A continuous increase in strength and duration of the signals was noted to occur with an increase in the magnitude of D. Based on statistical analysis, two regression equations have been proposed to determine lambda(max) and lambda(min) for different values of source energy. It is concluded that the SASW technique is capable of producing nearly a unique dispersion curve irrespective of (1) diameters and heights of fall of the dropping masses used for producing the vibration, and (2) the spacing between different receivers. The results presented in this paper can be used to provide guidelines for deciding about the input source energy based on the required exploration zone of the pavement. (C) 2014 American Society of Civil Engineers.

Influence of soil grading on the characteristics of cement stabilised soil compacts

The paper deals with experimental investigations aiming at specifying optimum soil grading limits for the production of cement stabilised soil bricks (CSSB). Wide range of soil grading curves encompassing both fine and coarse grained soils were considered. Strength, durability and absorption characteristics of CSSB were examined considering 14 different types of soil grading curves and three cement contents. The investigations show that there is optimum clay content for the soil mix which yields maximum compressive strength for CSSB and the optimum clay content is about 10 and 14 % for fine grained and coarse grained soils respectively. Void ratio of the compacted specimens is the lowest at the optimum clay content and therefore possesses maximum strength at that point. CSSB using fine grained soils shows higher strength and better durability characteristics when compared to the bricks using coarse grained soils.

Observation of phase transformations in cement during hydration

We report the phase transformations in Portland cement before and after hydration. The hydration mechanism was studied in detail by using a full Rietveld refinement of the X-ray diffraction (XRD) patterns, Fourier Transformed Infra-Red (FTIR) spectroscopy, Thermogravimetric Analysis (TGA) and Mossbauer spectroscopy at room temperature. From the Rietveld refinement of XRD data, alite, belite, celite, brown-millerite and low quartz phases were detected and quantified as major phases in dry cement powder. After hydration, calcium carbonate, portlandite and ettringite phases were found to form. A large reduction in the amounts of alite and belite phases were observed suggesting the formation of amorphous C-S-H phase and emphasizing the role of alite phase in flash setting of cement, as justified by the XRD and FTIR spectroscopy. Mossbauer spectra of all the unset samples showed quadrupole split doublets corresponding to the brownmillerite phase which remains unchanged even after about one week of hydration, suggesting that brownmillerite did not transform to other phases during initial stage of hydration process. (C) 2015 Elsevier Ltd. All rights reserved.

Molecular Dynamics Simulation of Barnacle Cement

Barnacle cement is an underwater adhesive that is used for permanent settlement. Its main components are insoluble protein complexes that have not been fully studied. In present article, we chose two proteins of barnacle cement for study, 36-KD protein and Mrcp-100K protein. In order to investigate the characteristic of above two proteins, we introduced the method of molecular modeling. And the simulation package GROMACS was used to simulate the behavior of these proteins. In this article, before the simulations, we introduce some theories to predict the time scale for polymer relaxation. During the simulation, we mainly focus on two properties of these two proteins: structural stability and adhesive force to substrate. First, we simulate the structural stability of two proteins in water, and then the stability of 36-KD protein in seawater environment is investigated.We find that the stability varies in the different environments. Next, to study adhesive ability of two proteins, we simulate the process of peeling the two proteins from the substrate (graphite). Then, we analyze the main reasons of these results. We find that hydrogen bonds in proteins play an important role in the protein stability. In the process of the peeling, we use Lennard–Jones 12-6 potential to calculate the van der Waals interactions between proteins and substrate.

Equivalent Model Of Expansion Of Cement Mortar Under Sulphate Erosion

The expansion property of cement mortar under the attack of sulfate ions is studied by experimental and theoretical methods. First, cement mortars are fabricated with the ratio of water to cement of 0.4, 0.6, and 0.8. Secondly, the expansion of specimen immerged in sulphate solution is measured at different times. Thirdly, a theoretical model of expansion of cement mortar under sulphate erosion is suggested by virtue of represent volume element method. In this model, the damage evolution due to the interaction between delayed ettringite and cement mortar is taken into account. Finally, the numerical calculation is performed. The numerical and experimental results indicate that the model perfectly describes the expansion of the cement mortar.