Solution heat treatment of plasma nitrided 15-5PH stainless steel - Part I: Improvement of the corrosion resistance

The results of the investigation on Solution Heat Treatment of Plasma Nitrided (SHTPN) precipitation-hardened steel 15-5PH are presented. The layers have been obtained by the plasma nitriding process followed by solution heat treatment at different temperatures. The influence of the solution heat treatment after nitriding on the dissolution process of the nitrided layer has been considered. The nitrided layers were studied by scanning electron microscopy, X-ray microanalysis (EDX), and X-Ray diffraction. Micro-hardness tests of the nitrided layers and solubilized nitrided layers have been carried out and interpreted by considering the processing conditions. It was found that high nitrogen austenitic cases could be obtained after SHTPN of martensitic precipitation-hardened steel (15-5PH). When Solution Heat Treatment (SHT) was performed at 1100 °C, some precipitates were observed. The amount of precipitates significantly reduced when the temperature increased. The EDX microanalysis indicated that the precipitate may be chromium niobium nitride. When the precipitation on the austenite phase occurred in small amount, the corrosion resistance increased in SHTPN specimens and the pit nucleation potential also increased. The best corrosion result occurred for SHT at 1200 °C.

Enhancement of Corrosion Resistance AISI 304 Steel by Plasma Polymerized Thin Films

The purpose of this work is the deposition of films in order to increase the corrosion resistance of AISI 304 steel, which is a material used to construct the reactors for bioethanol production. This deposition inhibits the permeation of corrosive species to the film-metal interface. Thin films were prepared by radio-frequency plasma enhanced chemical vapor deposition (RF-PECVD) method using plasmas of hexamethyldisiloxane/argon/oxygen mixtures excited by signals of different powers. The plasma was generated by the application of RF power of 13.56 MHz to the sample holder while keeping grounded the topmost electrode and the chamber walls. The effect of the RF power on the properties of the samples was investigated by perfilometry, X-ray photoelectron spectroscopy (XPS), contact angle, and electrochemical impedance spectroscopy (EIS). The results of the corrosion resistance tests of the AISI 304 steel were interpreted in terms of the energy delivered to the growing layer by plasma excitation power.

Application of Mossbauer spectroscopy to the study of corrosion resistance in NaCl solution of plasma nitrided AISI 316L stainless steel

Corrosion research in steels is one of the areas in which Mossbauer spectroscopy has become a required analytical technique, since it is a powerful tool for both identifying and quantifying distinctive phases (which contain Fe) with accuracy. In this manuscript, this technique was used to the study of corrosion resistance of plasma nitrided AISI 316L samples in the presence of chloride anions. Plasma nitriding has been carried out using dc glow-discharge, nitriding treatments, in medium of 80 vol.% H-2 and 20 vol.% N-2, at 673 K, and at different time intervals: 2, 4, and 7 h. Treated samples were characterized by means of phase composition and morphological analysis, and electrochemical tests in NaCl aerated solution in order to investigate the influence of treatment time on the microstructure and the corrosion resistance, proved by conversion electron Mossbauer spectroscopy (CEMS), glancing angle X-ray diffraction (GAXRD), scanning electron microscopy (SEM) and potentiodynamic polarization. A modified layer of about 8 gin was observed for all the nitrided samples, independently of the nitriding time. A metastable phase, S phase or gamma(N), was produced. It seems to be correlated with gamma`-Fe-4 N phase. If the gamma(N) fraction decreases, the gamma` fraction increases. The gamma(N) magnetic nature was analyzed. When the nitriding time increases, the results indicate that there is a significant reduction in the relative fraction of the magnetic gamma(N) (in) phase. In contrast, the paramagnetic gamma(N) (p) phase increases. The GAXRD analysis confirms the Mossbauer results, and it also indicates CrN traces for the sample nitrided for 7 h. Corrosion results demonstrate that time in the plasma nitriding treatment plays an important role for the corrosion resistance. The sample treated for 4 h showed the best result of corrosion resistance. It seems that the epsilon/gamma` fraction ratio plays an important role in thin corrosion resistance since this sample shows the maximum value for this ratio. (c) 2008 Published by Elsevier B.V.

Effect of cold-working process on corrosion behavior of copper

The microstructure, microhardness, texture and corrosion resistance of cold-swaged and cold-wiredrawn copper rods were evaluated. Elongated grains along the deformation direction were observed for both materials and the width of these grains decreased with the increase of reduction in area. Wiredrawn copper rods have higher microhardness than the swaged rods for the same reduction in area. The copper grains in both cold-worked rods presented a preferential orientation in the [1 1 0] crystallographic direction but this trend was more pronounced for swaged rods. The corrosion resistance of wiredrawn copper rods investigated in H(2)SO(4) solutions was lower than that of swaged rods, and for both deformed materials the corrosion resistance decreased with the deformation degree. (C) 2011 Elsevier Ltd. All rights reserved.

Flexural strengthening of reinforced concrete beams with carbon fibers reinforced polymer (CFRP) sheet bonded to a transition layer of high performance cement-based composite

Resistance to corrosion, high tensile strength, low weight, easiness and rapidity of application, are characteristics that have contributed to the spread of the strengthening technique characterized by bonding of carbon fibers reinforced polymer (CFRP). This research aimed to develop an innovate strengthening method for RC beams, based on a high performance cement-based composite of steel fibers (macro + microfibers) to be applied as a transition layer. The purpose of this transition layer is better control the cracking of concrete and detain or even avoid premature debonding of strengthening. A preliminary study in short beams molded with steel fibers and strengthened with CFRP sheet, was carried out where was verified that the conception of the transition layer is valid. Tests were developed to get a cement-based composite with adequate characteristics to constitute the layer transition. Results showed the possibility to develop a high performance material with a pseudo strain-hardening behavior, high strength and fracture toughness. The application of the strengthening on the transition layer surface had significantly to improve the performance levels of the strengthened beam. It summary, it was proven the efficiency of the new strengthening technique, and much information can be used as criteria of projects for repaired and strengthened structures.

Hot-Dip Aluminizing of Low-Carbon Steels

In a relatively short period of sixty-five years, aluminum has grown to the rank of fifth in total weight of met­als produced in the world. Throughout its short life, aluminum has been found to have excellent corrosion-resistant properties; yet only in recent years has aluminum been under consideration as a corrosion-resistant coating for iron and steel.

Corrosion behaviour of new duplex stainless steel reinforcements embedded in chloride contaminated concrete

The use of reinforcing stainless steels (SS) in concrete have proved to be one of the most effective methods to guarantee the passivity of reinforced concrete structures exposed to chloride contaminated environment. The present research studies the corrosion behaviour of a new duplex SS reinforcements with low nickel content (LND) (more economicaly compatible) is compared with the conventional austenitic AISI 304 SS and duplex AISI 2304 SS. Corrosion behaviour of ribbed SS reinforcements was studied in mortars with chloride content (0, 0.4, 2 and 4% Cl ⎯ ) using linear polarization resistance and potentiostatic pulses technique, Ecorr and Rp values were monitored over the exposure time. The obtained icorr data for the new duplex stainless steel LND no afforded passivity breakdown after one year exposure

Pitting Corrosion in Austenitic Stainless Steel Water Tanks of Hotel Trains

The water storage tanks of hotel trains suffered pitting corrosion. To identify the cause, the tanks were subjected to a detailed metallographic study and the chemical composition of the austenitic stainless steels used in their construction was determined. Both the tank water and the corrosion products were further examined by physicochemical and microbiological testing. Corrosion was shown to be related to an incompatibility between the chloride content of the water and the base and filler metals of the tanks. These findings formed the basis of recommendations aimed at the prevention and control of corrosion in such tanks. Se han detectado problemas de corrosión por picaduras en los depósitos de agua de trenes hotel. Para identificar las causas se llevó a cabo un detallado estudio metalográfico así como de la composición química de los aceros inoxidables austeníticos utilizados en su construcción. También se realizaron estudios fisicoquímicos y microbiológicos de los productos de corrosión. Se ha encontrado que los problemas de corrosión están relacionados con la incompatibilidad entre el contenido en cloruros del agua y los metales base y de aporte de la soldadura de los tanques. En base a estos hallazgos se proponen una serie de recomendaciones encaminadas a la prevención y control de la corrosión de dichos depósitos.

Development of corrosion of steel bars embedded in mortar made with slag from secondary metallurgy

The aim of this work is to study the evolution of the corrosion rate of reinforcements embedded in mortar specimens that have been partly or fully replaced by the sand ladle furnace white slag. Prisms are manufactured mortar 6cm x 8cm x 2cm in which are embedded reinforcing steel bars of 6mm diameter B500SD. At the time of mixing were added varying amounts of chloride ion content by weight of cement (0%, 0.4%, 0.8%, 1.2%, 2%). The specimens were made totally or partially replacing the white slag, getting four different mixes depending on the degree of substitution. After curing the specimens for 28 days in moist chambers proceeded to dry up naturally. Here are gradually dampened by its conservation in a moist chamber, periodically measuring the corrosion rate of the bars using the technique of polarization curve. The results, in terms of corrosion current and corrosion potential, were compared with those obtained on standard samples, without replacement by slag aggregate. The analysis of results allows us to know, depending on the type of mortar used, the chloride threshold with the depassivation produced steel and the corrosion rates achieved in steels in the active state in terms of mortar moisture, obtained from qualitatively using gravimetric techniques. The results achieved to date support the conclusion that no significant differences in the behavior against corrosion induced by chloride ions, between the steel bars embedded in standard samples and the steel bars embedded in samples including with aggregates from slag. Both the chloride threshold resulting in the depassivation steel as the corrosion rate reached through the bars in an active state are very similar in both types of mortars when they have the same moisture content.

An experimental and numerical study of the pattern of cracking of concrete due to steel reinforcement corrosion

In this work, cracking of concrete due to steel reinforcement corrosion is experimentally and numerically studied. The tests combined accelerated corrosion—to generate the cracks—with impregnation under vacuum with resin containing fluorescein—to enhance their visibility under ultraviolet light. In parallel, a model—called expansive joint element—was developed to simulate the expansion of the oxide and finite elements with an embedded adaptable cohesive crack were used to describe concrete cracking. The results show that a good agreement exists between the experimental and numerical crack patterns, which constitutes promising progress towards a comprehensive understanding of corrosion-induced cracking in reinforced concrete.

Effects of hydrogen assisted stress corrosion on damage tolerance of a high-strength duplex stainless steel wire for prestressing concrete

The study brings new insights on the hydrogen assisted stress corrosion on damage tolerance of a high-strength duplex stainless steel wire which concerns its potential use as active reinforcement for concrete prestressing. The adopted procedure was to experimentally state the effect of hydrogen on the damage tolerance of cylindrical smooth and precracked wire specimens exposed to stress corrosion cracking using the aggressive medium of the standard test developed by FIP (International Prestressing Federation). Stress corrosion testing, mechanical fracture tests and scanning electron microscopy analysis allowed the damage assessment, and explain the synergy between mechanical loading and environment action on the failure sequence of the wire. In presence of previous damage, hydrogen affects the wire behavior in a qualitative sense, consistently to the fracture anisotropy attributable to cold drawing, but it does not produce quantitative changes since the steel fully preserves its damage tolerance.

Galvanic Corrosion of High-Temperature Low-Sag (HTLS) High Voltage Conductors: New Materials - New Challenges

High-Temperature Low-Sag (HTLS) high voltage overhead conductors offer higher operating temperatures, reduced resistance and less sag than conventional designs. With up to twice the current capacity for the same diameter conductor, they may help ease the power shortage in the constantly increasing electricity demand, but there might be some concerns about their corrosion resistance. These new conductors use materials relatively new to the power industry, such as advanced carbon fiber polymer matrix composites and unique metal matrix composites/nano-composites predominantly used in aerospace industries. This study has made an initial assessment of potential galvanic corrosion problems in three very different HTLS designs: ACCC (Aluminum Conductor Composite Core), ACCR (Aluminum Conductor Composite Reinforced) and ACSS (Aluminum Conductor Steel Supported). In particular the ACCC design was evaluated for its resistance to corrosion and compared to the other designs. The study concludes that all three designs can develop galvanic corrosion under certain circumstances. While the results are not sufficient to make service life predictions of any of the tested conductors, they point out the necessity of thorough corrosion testing of all new conductor designs.