Thermal Expansivities and Temperature Coefficients of Refractive Indices for Molten Salts

An empirical relation for temperature–independent molar polarization is suggested. When this relation was used, the thermal expansivity was estimated correctly from refractive index data.

Combustion and Thermal Decomposition of a Binary Oxidiser System: Ammonium Perchlorate-Potassium Perchlorate

Combustion behaviour of ammonium perchlorate-potassium perchlorate pellets is studied using Crawford strand burners. At low concentrations of potassium perchlorate (up to 30 percent potassium perchlorate) the burning rate of ammonium perchlorate-potassium perchlorate condensed mixtures increases with potassium perchlorate content. Above 40 percent potassium perchlorate content, combustion sustenance becomes difficult. Decomposition products of ammonium perchlorate sensitize the melting and subsequent decomposition of potassium perchlorate. The results are explained in terms of the melt layer thickness, flame temperature and the resultant surface temperature, and heat wave penetration into the solid. The study suggests the importance of melt layer on the burning surface in the deflagration behaviour of ammonium perchlorate-potassium perchlorate condensed mixtures

Ultrasonic velocities and thermal expansion coefficients of amorphous Se80Te20 and Se90Te10 alloys near glass transitions

Precise measurements of the ultrasonic velocities and thermal expansivities of amorphous Se80Te20 and Se90Te10 alloys are reported near the glass transition. The samples are produced by liquid quenching. The longitudinal and transverse velocities are measured at 10 MHz frequency using the McSkimin pulse superposition technique. The thermal expansivities,agr, are measured using a three-terminal capacitance bridge. Theagr-values show a sharp maximum near the glass transition temperature,T g. The ultrasonic velocities also show a large temperature derivative, dV/dT nearT g. The data are discussed in terms of existing theories of the glass transition. The continuous change inagr shows that the glass transition is not a first-order transition, as suggested by some theories. The samples are found to be deformed by small loads nearT g. The ultrasonic velocities and dV/dT have contributions arising from this deformation.

Thermal reactivity of metal oxalate hydrazinates

Metl oxalate hydrazinates MC2O4·2 N2H4 where M=Mg, Mn, Fe, Co, Ni, Cu, Zn and Cd have been prepared and characterised by chemical analysis and infrared spectra. Thermal reactivity and decomposition of these oxalato complexes have been studied using thermogravimetry and differential thermal analysis. Hydrazinates of Mn, Fe, Co, Ni and Cu oxalates exhibit autocatalytic decomposition behaviour whereas the others do not. This phenomenon can be attributed to the presence of a bridged hydrazine as well as the thermal stability of the anhydrous metal oxalates.

Comparative effects of thermal and high pressure processing on phenolic phytochemicals in different strawberry cultivars

Abstract It is widely considered that high pressure processing (HPP) results in better retention of micronutrients and phytochemicals compared to thermal pasteurization (TP), although some studies indicate that this may not be true in all cases. The aims of this study were (1) to objectively compare the effects of HPP under commercial processing conditions with thermal pasteurization (TP) on the stability of phenolic antioxidants in strawberries following processing and during storage and (2) to evaluate the influence of varietal differences and hence differences in biochemical composition of strawberries on the stability of phenolic antioxidants. Strawberry puree samples from cultivars Camarosa, Rubygem, and Festival were subjected to HPP (600 MPa/20 °C/5 min) and TP (88 °C/2 min). The activities of oxidative enzymes were evaluated before and after processing. Furthermore, the antioxidant capacity (total phenolic content (TPC), oxygen radical absorbance capacity (ORAC), and ferric reducing antioxidant power (FRAP)) and individual anthocyanins (by HPLC) were determined prior to and following processing and after three months of refrigerated storage (4 °C). Depending on the cultivar, HPP caused 15–38% and 20–33% inactivation of polyphenol oxidase and peroxidase, respectively, compared to almost complete inactivation of these enzymes by TP. Significant decreases (p < 0.05) in ORAC, FRAP, TPC and anthocyanin contents were observed during processing and storage of both HPP and TP samples. Anthocyanins were the most affected with only 19–25% retention after three months of refrigerated storage (4 °C). Slightly higher (p < 0.05) loss of TPC and antioxidant capacity were observed during storage of HPP samples compared to TP. Industrial Relevance: The results of the study demonstrated that both high pressure processing and thermal pasteurization result in high retention of phenolic phytochemicals in strawberry products. Under the conditions investigated, high pressure processing did not result in a better retention of phenolic phytochemicals compared to thermal pasteurization. In fact, a slightly higher loss of total polyphenol content and antioxidant capacity were observed during refrigerated storage of HPP processed samples. Our results showed that, high pressure processing may not always be a better alternative to thermal processing for strawberry puree processing if the main objective is better retention of phenolic antioxidants. However, it should be noted that other quality attributes such as sensory properties, where distinct advantages of HPP are expected, were outside the scope of this study.

Structural and thermal properties of inorganic–organic montmorillonite: Implications for their potential environmental applications

Inorganic–organic clays (IOCs), clays intercalated with both organic cations such as cationic surfactants and inorganic cations such as metal hydroxy polycations have the properties of both organic and pillared clays, and thereby the ability to remove both inorganic and organic contaminants from water simultaneously. In this study, IOCs were synthesised using three different methods with different surfactant concentrations. Octadecyltrimethylammonium bromide (ODTMA) and hydroxy aluminium ([Al13O4 (OH)24(H2O)12]7+ or Al13) are used as the organic and inorganic modifiers (intercalation agents). According to the results, the interlayer distance, the surfactant loading amount and the Al/Si ratio of IOCs strictly depend on the intercalation method and the intercalation agent ratio. Interlayers of IOCs synthesised by intercalating ODTMA before Al13 and IOCs synthesised by simultaneous intercalation of ODTMA and Al13 were increased with increasing the ODTMA concentration used in the synthesis procedure and comparatively high loading amounts could be observed in them. In contrast, Al/Si decreased with increasing ODTMA concentration in these two types of IOCs. The results suggest that Al-pillars can be fixed within the interlayers by calcination and any increment in the amount of ODTMA used in the synthesis procedure did not affect the interlayer distance of the IOCs. Overall the study provides valuable insights into the structure and properties of the IOCs and their potential environmental applications.

Mechanism of the thermal decomposition of polystyrene peroxide

The thermal degradation of polystyrene peroxide was carried out using differential scanning calorimetry. The activation energy (E) was found to be 136 kJ mole–1 at all extents of decomposition. TheE value was found to correspond to-O-O-dissociation. The order of reaction was found to decrease from 2 to 1 as the decomposition progresse.

Studies on Thermal Polymerization of Acrylamide

Thermal polymerization of acrylamide has been followed by the DSC technique, and the activation energy (E) values at different stages of the fraction polymerized (a) have been determined from the exotherm of the thermograms obtained. The trend of variation of E with agr shows that E remains constant up to agr = 0.5 and decreases with a further increase in agr. A close look at the composite nature of the exotherms, agr-t, and agr-T curves shows that the polymerization of acrylamide involves two processes. The first process is the formation of linear polyacrylamide and the second is the simultaneous cross-linking of the linear chains together with the formation of linear polyacrylamide. Experiments such as NH3 detection by differential thermal analysis techniques and annealing studies have been made to shed further light on the polymerization process.

Kinetics of thermal decomposition of barium zirconyl oxalate

Kinetics of the thermal decomposition of anhydrous barium zirconyl oxalate and a carbonate intermediate have been studied. Decomposition of the anhydrous oxalate, though it could be explained based on a contracting-cube model, is quite complex. Kinetics of decomposition of the intermediate carbonate Ba2Zr2O5CO3 is greatly influenced by thermal effects during its formation. (agr-t) curves are sigmoidal and obey a power law equation followed by first order decay. Presence of carbon in the vacuum-prepared carbonate has a strong deactivating effect. Decomposition of the carbonate is accompanied by growth in particle size of the product barium zirconate.

Thermal decomposition of ethyl and isopropyl amine perchlorates

Thermal decomposition of ethyl and isopropyl amine perchlorates has been studied by methods such as DTA, TG, isothermal weight loss measurements and the decomposition products have been analyzed in a mass spectrometer. Activation energy values for thermal decomposition have been calculated fromagr-t plots. The proton transfer dissociation mechanism proposed for the thermal decomposition of ammonium perchlorate (AP) has been extended to explain the decomposition products of these twosubstituted amine perchlorates.

Microbial quality of hemp (Cannabis sativa L.) and flax (Linum usitatissimum L.) from plants to thermal insulation

Flax and hemp have traditionally been used mainly for textiles, but recently interest has also been focused on non-textile applications. Microbial quality throughout the whole processing chain of bast fibres has not previously been studied. This study concentrates on the microbial quality and possible microbial risks in the production chain of hemp and flax fibres and fibrous thermal insulations. In order to be able to utilize hemp and flax fibres, the bast fibres must be separated from the rest of the plant. Non-cellulosic components can be removed with various pretreatment processes, which are associated with a certain risk of microbial contamination. In this study enzymatic retting and steam explosion (STEX) were examined as pretreatment processes. On the basis of the results obtained in this study, the microbial contents on stalks of both plants studied increased at the end of the growing season and during the winter. However, by processing and mechanical separation it is possible to produce fibres containing less moulds and bacteria than the whole stem. Enzymatic treatment encouraged the growth of moulds in fibres. Steam explosion reduced the amount of moulds in fibres. Dry thermal treatment used in this study did not markedly reduce the amount of microbes. In this project an emission measurement chamber was developed which was suitable for measurements of emissions from both mat type and loose fill type insulations, and capable of interdisciplinary sampling. In this study, the highest amounts of fungal emissions were in the range of 10^3 10^5 cfu/m^3 from the flax and hemp insulations at 90% RH of air. The fungal emissions from stone wool, glass wool and recycled paper insulations were below 10^2 cfu/m^3 even at 90% RH. Equally low values were obtained from bast fibrous materials in lower humidities (at 30% and 80% RH of air). After drying of moulded insulations at 30% RH, the amounts of emitted moulds were in all cases higher compared to the emissions at 90% RH before drying. The most common fungi in bast fibres were Penicillium and Rhizopus. The widest variety of different fungi was in the untreated hemp and linseed fibres and in the commercial loose-fill flax insulation. Penicillium, Rhizopus and Paecilomyces were the most tolerant to steam explosion. According to the literature, the most common fungi in building materials and indoor air are Penicillium, Aspergillus and Cladosporium, which were all found in some of the bast fibre materials in this study. As organic materials, hemp and flax fibres contain high levels of nutrients for microbial growth. The amount of microbes can be controlled and somewhat decreased by the processing methods presented.

Thermal decomposition of doped calcium hydroxide for chemical energy storage

Thermal decomposition of Ca(OH)2 with and without additives has been experimentally investigated for its application as a thermochemical energy storage system. The homogeneous reaction model gives a satisfactory fit for the kinetic data on pure and Ni(OH)2---, Zn(OH)2--- and Al(OH)3---doped Ca(OH)2 and the order of reaction is 0.76 in all cases except for the Al(OH)3-doped sample for which the decomposition is zero order. These additives are shown not only to enhance the reaction rate but also to reduce the decomposition temperature significantly. Some models for solid decomposition reactions, and possible mechanisms in the decomposition of solids containing additives, are also discussed.

Thermal analysis of metal sulfate hydrazinates and hydrazinium metal sulfates

Thermal analysis of metal sulfate hydrazinates, MSO4·xN2H4 (I) (M=Mn, Co, Ni, Zn, Cd; x = 2–3), hydrazinium metal sulfates, (N2H5)2M(SO4)2 (II) (M=Mn, Cu, Zn, Cd), and N2H5LiSO4 have been studied using simultaneous TG-DTGDTA. Both types of complexes, I and II, decompose to the respective metal sulfates or a mixture of metal sulfide and sulfate.

Silica from rice husk through thermal decomposition

The thermal decomposition characteristics of rice husk have been investigated by dynamic thermoanalytical techniques: DTA, TG, DTG and isothermal heating. The observed thermal behaviour is explained on the basis of a superposition of the decomposition of cellulose and lignin, which are the major organic constituents of rice husk. Morphological features of silica in husk as well as the ash are examined by scanning electron microscopy. Silica in the residual ash has been characterised by X-ray diffraction and infrared spectroscopy. Controlled thermal decomposition of rice husk has been shown to be a convenient method for the liberation of silica.

Curing And Thermal Cycling Processes In Pvc Graphite Thick-Films

Abstract is not available.