THIN-LAYER ELECTROCHEMICAL DETECTOR COATED WITH NAFION FILM

Electrochemical detection of the flow system has attracted considerable interest in recent years due to its high sensitivity and selectivity towards electroactive compounds. However, the improvement of sensitivity and selectivity is still a desire for practical application. In this note, a thin-layer electrochemical detector of the

Fabrication of Bismuth/Multi-walled Carbon Nanotube Composite Modified Glassy Carbon Electrode for Determination of Cobalt

A bismuth/multi-walled carbon nanotube (Bi/MWNT) composite modified electrode for determination of cobalt by differential pulse adsorptive cathodic stripping voltammetry is described. The electrode is fabricated by potentiostatic pre-plating bismuth film on an MWNT modified glassy carbon (GC) electrode. The Bi/MWNT composite modified electrode exhibits enhanced sensitivity for cobalt detection as compared with the bare GC, MWNT modified and bismuth film electrodes. Numerous key experimental parameters have been examined for optimum analytical performance of the proposed electrode. With an adsorptive accumulation of the Co(II)-dimethylglyoxime complex at -0.8 V for 200 s, the reduction peak current is proportional to the concentration of cobalt in the range of 4.0x10(-11)-1.0x10(-7) mol/L with a lower detection limit of 8.1x10(-11) mol/L. The proposed method has been applied Successfully to cobalt determination in seawater and lake water samples.

Ionophore Based Bismuth Film Electrode for Lead

A Nafion/ionophore, 4-tert-butylcalix[4]arene-tetrakis(N,N-dimethylthioacetamide) composite coated and bismuth film modified glassy carbon electrode. (GC/NA-IONO/BiFE) was described to determine trace lead sensitively and selectively. The characteristics of such modified GC/NA-IONO/BiFE were studied by scanning electron microscopy and cyclic voltammetry. The influence of various experimental parameters upon the stripping lead signal at the GC/NA-IONO/BiFE was explored. Under the optimized conditions, the differential pulse voltammetric stripping response is highly linear over the 0.1-8.0 nM lead range examined (180s preconcentration at -1.2V), with a detection limit of 0.044nM and good precision (RSD=5.4% at 0.5nM). Also applicability to seawater samples was demonstrated at such modified electrode. The high selectivity of ionophore coupled with the excellent electrochemical characteristics of bismuth endow the GC/NA-IONO/BiFE a promising and robust tool for monitoring of trace lead rapidly and precisely.

Observation of C60 film formation on a highly oriented pyrolitic graphite substrate via scanning tunnelling microscopy

We have investigated the early stages in the adsorption process of C60 molecules on a highly oriented pyrolitic graphite (HOPG) substrate. C60 powder was thermally evaporated in UHV of 10−8 Pa conditions onto a freshly cleaved HOPG surface. We did not observe individual fullerenes on the substrate for the case of short deposition times and low evaporation rates. However, small islands of C60 molecules with an fcc structure could be observed when the deposition rate was about 0.2 nm/min and the total thickness was above 1 nm. The islands did not grow in the vicinity of the HOPG steps. The typical lateral dimensions of these islands were of the order of a few hundred square nanometers, having thickness of up to five monolayers. We modified the shapes and positions of these islands by the STM tip, using a small (less than 1 V) bias voltage.

Plasma chloriding of thin-film silver - A novel process in silver-silver chloride reference electrode fabrication

Silver thin films were modified using a novel plasma modification process for the development of thin-film silver-silver chloride reference electrodes. The surface, physical, and electrochemical properties of these electrodes were investigated by atomic force microscopy, thickness and resistivity measurement techniques, as well as impedance spectroscopy and potentiometry. After plasma treatment, thin-film growth was observed and the electrodes, in general, exhibited low interface impedance and a roughened surface. Evidence of a complex surface reorganization was found. Correlating plasma conditions with film properties suggested that increasing pressure and exposure duration increased species availability, therefore governing the reaction rates, while input power appeared to influence the type of surface chemical reactions. Results also indicated that Ar/Cl-2 mixtures should be employed rather than pure chlorine plasmas. (C) 2002 The Electrochemical Society.

Resonance Raman and surface-enhanced resonance Raman studies of polymer-modified electrodes which mimic heme enzymes

Iron-5,10,15,20-tetraphenylporphyrin (FeTPP) has been incorporated into films of a coordinating hydrogel polymer support medium, poly(gamma-ethyl-L-glutamate) (PEG) functionalised with imidazole pendant arms (PEG-Im), and studied in situ on silver electrodes using a combination of both resonance Raman (RR) and surface-enhanced resonance Raman (SERR) spectroscopy. The SERR spectra give information on the portion of the film close to the electrode surface while RR spectra probe the

Nanocrystalline SnO2-based, UVB-activated, colourimetric oxygen indicator

Nanocrystalline SnO2, ncSnO(2), is used as a photosensitiser in a colourimetric O-2 indicator that comprises a sacrificial electron donor, glycerol, a redox dye, methylene blue (MB), and an encapsulating polymer, hydroxyethyl cellulose (HEC). Upon exposure to a burst of UVB light the indicator is activated (photo-bleached) as the MB is photoreduced by the ncSnO(2) particles. In the absence of oxygen, the film stays bleached, but recovers its original colour upon exposure to oxygen. Unlike its TiO2-based predecessor, the HEC/glycerol/MB/ncSnO(2) O-2 indicator is not activated by UVA light from white fluorescent lamps, but is by UVB light. This feature provides much greater control in the activation of the indicator. Other work shows the rate of activation depends upon I-0.75, where I is the UVB irradiance, indicating a partial dependence upon the electron-hole recombination process. The half-life of the recovery of the original colour of a UV-activated film, t(50), is directly proportional to the ambient level of oxygen. The advantages of using this indicator in modified atmosphere packaging as a possible quality assurance indicator are discussed briefly. (c) 2008 Elsevier B.V. All rights reserved.

Demonstration of a novel, flexible, photocatalytic oxygen-scavenging polymer film

The preparation of a novel, flexible, photocatalytic, oxygen-scavenging polymer film is described. The film incorporates nanocrystalline titania particles in an ethyl cellulose polymer film, with or without an added sacrificial electron donor of triethanolamine. When coated on the inside of a glass vessel its UV-driven light-scavenging action is demonstrated by platinum octaethyl porphyrin coated glass beads sealed inside, since their luminescence increases with increasing UV-irradiation time. When used as a flexible film, work with an oxygen electrode shows that the film is able to scavenge oxygen at an average rate of 0.017 cm(3) O-2 h(-1) cm(-2) over a 24 h period, which compares favourably to other, well-established oxygen-scavenger systems. The potential of using such as system for oxygen scavenging in packaging is discussed briefly. (c) 2005 Elsevier B.V. All rights reserved.

Development of a novel UV indicator and dosimeter film

A novel UV indicator is described, comprising nanocrystalline particles of titania dispersed in a film of a polymer, hydroxyl ethyl cellulose (HEC), containing: a mild reducing agent, triethanolamine (TEOA) and a redox indicator, methylene blue (MB). The UV indicator film is blue-coloured in the absence of UV light and loses colour upon exposure to UV light, attaining within a few min a steady-state degree of bleaching that can provide a measure of the irradiance of the incident light. The original blue colour of the film returns once the source of UV light is removed. The spectral characteristics of a typical UV indicator film, and its components, are discussed and the UV-absorbing action of the titania particles highlighted. From the measured %bleaching undergone by a typical UV indicator as a function of light irradiance the indicator appears fully bleached, within 7 min, by a UV irradiance of 3 mW cm (-) or greater. The mechanism by which the UV indicator works is described. The reversible nature of the UV indicator is removed by covering a typical UV indicator with a thin, largely oxygen impermeable, polymer film, such as the regenerated cellulose found in Sellotape(TM). The product is a UV dosimeter, the response of which is related to the intensity and duration of the incident UV light, as well as the amount of titania in the film. A typical UV dosimeter film is fully bleached by 250 mJ cm(-2) of UV light. The possible use of these novel indicators to measure UV exposure levels, irradiance and dose, is discussed.

Controlling the response characteristics of luminescent porphyrin plastic film sensors for oxygen

Two porphyrins, platinum(II) octaethylporphyrin (Pt-OEP) and palladium(II) octaethylporphyrin (Pd-OEP), are incorporated into a wide variety of different encapsulating matricies and tested as oxygen sensors, The excited state lifetimes of the two porphyrins are quite different, 0.091 ms for Pt-OEP and 0.99 ms for Pd-OEP, and Pt-OEP-based oxygen sensors are found to be much less sensitive than Pd-OEP-based ones to quenching by oxygen, Two major response characteristics of an oxygen sensor are (i) its sensitivity toward oxygen and (ii) its response and recovery times when exposed to an alternating atmosphere of nitrogen and air. The response characteristics of a rang of Pt-OEP, and Pd-OEP-based oxygen sensors were determined using cellulose acetate butyrate (CAB), poly(methyl methacrylate) (PMMA), and PMMA/CAB polymer blends as the encapsulating media. Pt-OEP and Pd-OEP oxygen sensors have better response characteristics (i.e., more sensitive and lower response and recovery times) when CAB is used as the encapsulating medium rather than PMMA. For both Pt-OEP- and Pd-OEP-based oxygen sensors, in either polymer, increasing the level of tributyl phosphate plasticizer improves the response characteristics of the final oxygen-sensitive film. Pt-OEP in different unplasticized PMMA/CAB blended films produced a range of oxygen sensors in which the response characteristics improved with increasing level of CAB present.

Use of luminescent gold compounds in the design of thin-film oxygen sensors

The use of two gold compounds incorporated into thin plastic films as luminescence quenching oxygen sensors is described. The films are sensitive both to gaseous oxygen and to oxygen dissolved in nonaqueous media such as ethanol. The luminescence quenching of these sensors by oxygen obeys the Stern-Volmer equation and Stern-Volmer constants of 5.35 x 10(-3) and 0.9 x 10(-3) Torr(-1) are found, respectively, for the two dyes in a polystyrene polymer matrix. The sensitivity of the films is strongly influenced by the nature of the polymer matrix, and greatest sensitivity was found in systems based an the polymers polystyrene or cellulose acetate butyrate. Sensitivity was not found to be temperature dependent though raising the temperature hom 15 to 50 degrees C did result in a slight decrease in emission intensity and a hypsochromic shift in the emission wavelength. The rate of response and recovery of the sensors can be increased either by decreasing film thickness or by increasing the operating temperature. The operational and storage stability of these films is generally good though exposure to light should be avoided as one of the dyes tends to undergo photobleaching probably due to a photoinduced ligand substitution reaction.

Textural, viscoelastic and mucoadhesive properties of pharmaceutical gels composed of cellulose polymers

This study examined the mechanical/textural, viscoeiastic and mucoadhesive properties of a range of aqueous gels composed of either hydroxyethylcellulose (HEC) or sodium carboxymethylcellulose (Na CMC). The mechanical/textural properties of each formulation were determined using texture profile analysis. The viscoelastic properties of each formulation were examined over a defined frequency range (0.01-1.0 Hz) using oscillatory rheometry in conjunction with stainless steel parallel plate geometry. The mucoadhesive properties of the gels were evaluated by measuring the tensile force required to overcome the gel/mucin adhesive interaction. Both gel hardness and compressibility, properties that affect the ease of product removal from a container and spreadability, increased as a function of increasing polymer concentrations. This is attributed to the effects of HEC and Na CMC on gel viscosity. Gel adhesiveness, a property related to bioadhesion, also increased as a function of polymer concentration and is attributed to the reported adhesive nature of these polymers. Increasing frequency of oscillation increased the storage and loss moduli yet decreased bath the dynamic viscosity of each gel type and also the loss tangent of HEC (but not Na CMC) gels. Therefore, following exposure to the range of oscillatory stresses that may be expected in vivo, HEC gels will be more susceptible than Na CMC gels to alterations in these rheological properties. Consequently, it would be expected that the clinical performance of HEC gels will be modified to a greater extent than Na CMC gels. In general, HEC gels exhibited a greater elastic nature than Na CMC gels over the frequency range employed for oscillation The storage and loss moduli and dynamic viscosity of both gel types increased, yet the loss tangent of both gel types decreased as a function of increasing polymer concentration. Gel mucoadhesive strength was dependent on both the time of contact of the formulation with mucin and also on polymer concentration. In conclusion, this study has characterised a number of gels containing either HEC or Na CMC in terms of their mechanical/textural, viscoelastic and mucoadhesive properties. Due to its relevance to the clinical performance, it is suggested that the information derived from these methods may be usefully combined to provide a more rational basis for the selection of polymers and their formulation as topical drug delivery systems. (C) 1997 Elsevier Science B.V.

Cyclic nanoindentation and nano-impact fatigue characterisation of functionally graded TiN/TiNi shape memory film

This paper investigates the mechanism of nanoscale fatigue of functionally graded TiN/TiNi films using nano-impact and multiple-loading-cycle nanoindentation tests. The functionally graded films were deposited on silicon substrate, in which TiNi films maintain shape memory and pseudo elastic behavior, while a modified TiN surface layer provides tribological and anti-corrosion properties. Nanomechanical tests were performed to comprehend the localized film performance and failure modes of the functionally graded film using NanoTestTM equipped with Berkovich and conical indenter between 100 μN to 500 mN loads. The loading mechanism and load history are critical to define film failure modes (i.e. backward depth deviation) including the shape memory effect of the functionally graded layer. The results are sensitive to the applied load, loading type (e.g. semi-static, dynamic) and probe geometry. Based on indentation force-depth profiles, depth-time data and post-test surface observations of films, it is concluded that the shape of the nanoindenter is critical in inducing the localized indentation stress and film failure, including shape recovery at the lower load range. Elastic-plastic finite element (FE) simulation during nanoindentation loading indicated that the location of subsurface maximum stress near the interface influences the backward depth deviation type of film failure. A standalone, molecular dynamics simulation was performed with the help of a long range potential energy function to simulate the tensile test of TiN nanowire with two different aspect ratios to investigate the theory of its failure mechanism.

Action Spectra of P25 TiO2 and a visible light absorbing, carbon-modified titania in the photocatalytic degradation of stearic acid

The photonic efficiencies of films of Evonik (formerly Degussa) P25 TiO2 and carbon-modified TiO2 Kronos VLP 7000 samples are reported as a function of excitation wavelength (300–430 nm; FWHM ∼ 7.5 nm), i.e. the action spectra, for the degradation of stearic acid, a model organic for the photocatalytic destruction of solid surface organic pollutants. For each of these semiconductor photocatalysts, at 365 nm (FWHM = 18 nm), the dependence of the rate of degradation of stearic acid, upon the irradiance, I, is determined and the rate is found to be proportional to I0.65 and I0.82 for P25 and Kronos titania, respectively. Assuming this relationship holds at all wavelengths, the action spectra for two different semiconductor photocatalysts is modified by plotting, (RSA (rate of stearic acid destruction, units: molecules cm−2 s−1)/Iθ) vs. wavelength of excitation (λexcit), and both differ noticeably from those of the original (unmodified) action spectra, which are plots of (RSA/I = photonic efficiency, ξ) vs. λexcit. The shape of the modified action spectrum for P25 TiO2 is consistent with that reported by others for other organic mineralisation reactions and correlates well with diffuse reflectance data for P25 TiO2 (Kubelka–Munk plot), although there is some evidence that the active phase, in the photodegradation of stearic acid, is the anatase form present in P25. The unmodified and modified action spectra of the beige Kronos VLP 7000 TiO2 compound exhibits little or no activity in the visible i.e. (λexcit > 400 nm) and a peak at 350 nm. The Kronos powder contains a yellow/brown conjugated, extractable, organic sensitiser which has been identified by others as the species responsible for its reported photocatalytic visible light activity. But, irradiation of the Kronos powder film, with and without a stearic acid coating, in air, using UVA or visible light, bleaches rapidly (<60 min) most, if not all, of the little colour exhibited by the original Kronos powder. The photobleached form of the Kronos has a similar action spectrum to that of the unbleached form, which, in turn, appears very similar to that of P25 titania, at wavelengths >350 nm. It is proposed that the difference between the Kronos and P25 powder films at wavelengths <350 nm is due to a photodegradation-resistant, previously unidentified (but extractable using MeCN) UV-absorbing organic species in the former which screens the titania particles at these lower wavelengths. The implications of these observations are discussed briefly.

Modified electrodes with Keggin-type polyoxotungstates

O objectivo deste trabalho é a produção de novos eléctrodos modificados com polioxotungstatos (POMs) do tipo Keggin, incluindo POMs lacunares e substituídos por metais de transição. A preparação e caracterização dos polioxotungstatos encontram-se descritas no Capítulo 2. No Capítulo 3 descreve-se a produção de eléctrodos de carbono vítreo funcionalizados com sais híbridos de tetra-n-butilamónio de vários silicotungstatos pelo método de evaporação da gota. As propriedades electroquímicas dos polioxotungstatos imobilizados foram comparadas com as das espécies solúveis correspondentes. A morfologia dos depósitos foi avaliada por microscopia óptica e por microscopia electrónica de varrimento. No capítulo 4 descreve-se a preparação de novos eléctrodos compósitos de carbono e poli(hexilmetacrilato) com fosfotungstatos. Os estudos electroquímicos revelaram que as principais características dos POMs são mantidas e que os processos de redução são controlados por difusão, dependendo da difusão dos protões da solução. O Capítulo 5 descreve a construção de filmes em multicamadas ultrafinos contendo POMs e polietilenimina, preparados pelo método de auto-montagem camada-sobre-camada em eléctrodos de carbono vítreo. Os filmes em multicamada foram caracterizados por voltametria cíclica e por microscopia electrónica de varrimento e foi usada a espectroscopia de absorção de UV-Vis em placas de quartzo para monitorar o crescimento de filme. Os resultados voltamétricos revelaram que os processos de redução dos POM são confinados à superfície. Alguns destes eléctrodos modificados revelaram propriedades electrocatalíticas relativamente à redução dos aniões nitrito, bromato e/ou iodato. A espectroscopia de impedância electroquímica também foi usada na caracterização destes filmes e os resultados revelaram que a resistência à transferência de carga aumenta com o aumento do número de bicamadas para ambas as espécies redox, indicando que a espessura do filme tem um efeito importante sobre a cinética de reacções de transferência de carga. No capítulo 6 descreve-se a síntese de filmes híbridos orgânicos/inorgânicos compostos por poli(3,4-etilenodioxitiofeno) (PEDOT) e por silicotungstatos do tipo Keggin através da polimerização electroquímica, em condições aquosas, na superfície de electrodos de carbono vítreo. A voltametria cíclica revelou que as características principais dos POMs são mantidas nos filmes. Verificou-se que estes filmes são muito estáveis, possivelmente devido a fortes interacções electrostáticas entre os POMs aniónicos e o polímero positivamente carregado. A espectroscopia de impedância electroquímica foi também utilizada e os resultados mostraram que a resistência de transferência de carga aumenta com o aumento do pH e para valores de potenciais mais elevados. O capítulo 7 apresenta as conclusões finais e possíveis trabalhos futuros.