Perovskite-type B-site Bi-doped ceramic membranes for oxygen separation

Novel mixed conducting oxides, B-site Bi-doped perovskites were exploited and synthesized. Cubic perovskite structures were formed for BaBi0.2COyFe0.8-yO3-delta (y less than or equal to 0.4) and BaBixCo0.2Fe0.8-xP3-delta (x=0.1-0.5) The materials exhibited considerable high oxygen permeability at high temperature. The oxygen permeation flux of BaBi0.2Co0.35Fe0.45O3-delta membrane reached about 0.77 x 10(-6) mol/cm(2) s under an air/helium oxygen partial pressure gradient at 900 degrees C, which was much higher than that of other bismuth-contained mixed conducting membranes. The permeation fluxes of the materials increased with the increase of cobalt content, but no apparent simple relationship was found with the bismuth content. The materials also demonstrated excellent reversibility of oxygen adsorption and desorption. Stable time-related oxygen permeation fluxes were found for BaBi0.2CO0.35Fe0.45O3-delta and BaBi0.3Co0.2Fe0.5O3-delta a membranes at 875 degrees C.

Low temperature synthesis of perovskite oxide using the adsorption properties of cellulose

La-0.8Sr(0).2CoO(3) (LSCO) oxide powder was prepared using the adsorption properties of cellulose. The preparation process was studied by XRD, FTIR, TG-DTA and CO2-TPD techniques. The results of XRD, IR and TG-DTA testified that cellulose could successfully reserve the homogeneity of the solution system to the solid precursor. During the early stage of pyrolysis, cellulose was partially oxidized, and some COO- groups appeared in its texture, which were then complexed with the adsorbed metal ions, and effectively suppressed the aggregation of metal ions. Formation of a pure perovskite and the properties of the powder resulted were found to be significantly influenced by the cellulose to metal nitrate ratio. Also the properties of the resulting powder were greatly influenced by the calcination conditions. If the produced carbon dioxide could not be eluted in time, carbonate would be formed in the bulk. Hence, a high calcination temperature (> 800 degreesC) was needed to acquire a pure phase LSCO. At optimized conditions, nano-crystal LSCO could be obtained at as low as 500 degreesC.

Investigation of ideal zirconium-doped perovskite-type ceramic membrane materials for oxygen separation

Zirconium-doped perovskite-type membrane materials of BaCo0.4Fe0.6-xZrxO3-delta (x = 0-0.4) with mixed oxygen ion and electron conductivity were synthesized through a method of combining citric and EDTA acid complexes. The results of X-ray diffraction (XRD), oxygen temperature-programmed desorption (O-2-TPD) and hydrogen temperature-programmed reduction (H-2-TPR) showed that the incorporation of proper amount of zirconium into BaCo0.4Fe0.6O3-delta could stabilize the ideal and cubic structure of perovskite. Studies on the oxygen permeability of the as-synthesized membrane disks under air/He gradient indicated that the content of zirconium in these materials had great effects on oxygen permeation flux, activation energy for oxygen permeation and operation stability. The high oxygen permeation flux of 0.90 ml cm(-2) min(-1) at 950degreesC, the single activation energy for oxygen permeation in the range of 600-950 degreesC and the long-term operation stability at a relatively lower operational temperature of 800 degreesC under air/He gradient were achieved for the BaCo0.4Fe0.4Zr0.2O3-delta material. Meanwhile, the effect of carbon dioxide on structural stability and oxygen permeability of this material was also studied in detail, which revealed that the reversible stability could be attained for it. (C) 2002 Elsevier Science B.V. All rights reserved.

Titanium-based perovskite-type mixed conducting ceramic membranes for oxygen permeation

A titanium-based perovskite-type oxide was synthesized by an improved method of combining EDTA acid and citric acid complexes. High structural stability, good sintering ability, and relatively high oxygen permeation flux were obtained simultaneously for disks synthesized from this ceramic oxide. (C) 2002 Elsevier Science B.V All rights reserved.

Synthesis and characterization of gallium-based perovskite-type dense membrane with oxygen semipermeability

La0.15Sr0.85Ga0.3Fe0.7O3-delta (LSGFO) and La0.15Sr0.85Co0.3Fe0.7O3-delta (LSCFO) mixed oxygen-ion and electron conducting oxides were synthesized by using a combined EDTA and citrate complexing method, and the corresponding dense membranes were fabricated. The properties of the oxide powders and membranes were characterized with combined SEM, XRD, H-2-TPR, O-2-TPD techniques, mechanical strength and oxygen permeation measurement. The results showed that LSGFO had much higher thermochemical stability than LSCFO due to the higher valence stability of Ga3+. After the temperature-programmed reduction by 5% H-2 in Ar from 20 degreesC to 1020 degreesC, the basic perovskite structure of LSGFO was successfully preserved. LSGFO also favors the oxygen vacancy formation better than LSCFO. Oxygen permeation measurement demonstrated that LSGFO had higher oxygen permeation flux than LSCFO, but they had similar activation energy for oxygen transportation, with a value of 110 and 117 kJ . mol(-1), respectively The difference in oxygen permeation fluxes was correlated with the difference in oxygen vacancy concentrations for the two materials.

A novel zirconium-based perovskite-type membrane material for oxygen permeation

A novel zirconium-based membrane material of BaCo0.4Fe0.4Zr0.2O3-6 with cubic perovskite structure was synthesized for the first time through a method of citric and EDTA acid combined complexes. The structural stability was characterized by XRD, O-2-TPD and H-2-TPR techniques respectively. The high oxygen permeation flux of 0.873 mL/cm(2) min at 950 degreesC was obtained under He/Air gradient. Meanwhile, the single activation energy for oxygen permeation and the long-term steady operation of 200 h at 800 degreesC were achieved.