Cobalt catalysts derived from hydrotalcite-type precursors applied to steam reforming of ethanol

Catalysts derived from Co/Mg/Al hydrotalcite-type precursors modified with La and Ce were characterized by XANES and tested in ethanol steam reforming. The reaction data showed that, with a molar ratio of water: ethanol = 3:1 in the feed, addition of Ce and La favored acetaldehyde production. Increasing the water content (water:ethanol = 5:1) decreased the acetaldehyde formation by favoring the adsorption of water molecules on these samples, enhancing the acetaldehyde conversion. (C) 2011 Elsevier B.V. All rights reserved.

Effects of adding La and Ce to hydrotalcite-type Ni/Mg/Al catalyst precursors on ethanol steam reforming reactions

Catalyst precursors composed of Ni/Mg/Al oxides with added La and Ce were tested in ethanol steam reforming (ESR) reactions. La and Ce were added by anion-exchange. The oxides were characterized by X-ray photoelectron spectroscopy (XPS) and X-ray absorption near-edge structure (XANES) analysis. The catalyst precursors consist of a mixture of oxides, with the nickel in the form of NiO strongly interacting with the support Mg/Al. The XPS analysis showed a lanthanum-support interaction, but no interaction of Ce species with the support. The reaction data obtained with the active catalysts showed that the addition of Ce and La resulted in better H(2) production at 550 degrees C. The CeNi catalyst provided the higher ethanol conversion, with lower acetaldehyde production, possibly clue to a favoring of water adsorption on the weakly interacting clusters of CeO(2) on the surface. (C) 2010 Elsevier B.V. All rights reserved.

Organic additive-copper(II) complexes as plating precursors

Cu(II) ions previously coordinated with typical electroplating organic additives were investigated as an alternative source of metal for plating bath. The coordination complexes were isolated from reaction between CuSO(4) and organic additives as ligands (oxalate ion, ethylenediamine or imidazole). Deposits over 1010 steel were successfully obtained from electroplated baths using the complexes without any addition of free additives, at pH = 4.5 (H(2)SO(4)/Na(2)SO(4)). These deposits showed better morphologies than deposits obtained from CuSO(4) solution either in the absence or presence of oxalate ion as additive (40 mmol L(-1)), at pH = 4.5 (H(2)SO(4)/Na(2)SO(4))It is suggestive that the starting metal plating coordinated with additives influences the electrode position processes, providing deposits with corrosion potentials shifted over + 200 mV in 0.5 mol L(-1) NaCl (1 mV s(-1)). The resistance against corrosion is sensitive to the type of additive-complex used as precursor. The complex with ethylenediamine presented the best deposit results with the lowest pitting potential (-0.27 V vs 3.0 mol L(-1) CE). It was concluded that the addition of free additives to the electrodeposition baths is not necessary when working with previously coordinated additives. Thus, the complexes generated in ex-situ are good alternatives as plating precursors for electrodeposition bath. (C) 2009 Elsevier B.V. All rights reserved.

The effect of Eu3+ concentration on the Y2O3 host lattice obtained from citrate precursors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Luminescent and morphological study of Sr2CeO4 blue phosphor prepared from oxalate precursors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Study of Monoethanolamine Nitrate Content Reduction in Explosive Slurries

The reduction of the fuel content of a monoethanolamine nitrate (MEAN) fueled explosive slurry was investigated. The work was performed in three phases. The first one involved the MEAN content reduction in a reference slurry from its initial value of 36 down to 24% by weight, the balance being filled with ammonium nitrate, the least expensive item in the slurry composition. This proved to be successful, leading to an overall cost reduction of 17%, while keeping the overall performance quite satisfactory. The second phase consisted in trying to bring the MEAN content down from 24 to 17%. Although this led to further cost reduction, the formulations, obtained by substituting part of the MEAN content by ammonium nitrate/fuel oil (ANFO), produced unsatisfactory results regarding ignition and densities. In the third phase, the Design of Experiments Technique was used to find formulations displaying not only lower cost, but also acceptable overall performance. This led to a raw material cost reduction ranging from 23 to 26% relative to the initial reference slurry formulation.

Activity of Mo(II) allylic complexes supported in MCM-41 as oxidation catalysts precursors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Can dissipation prevent explosive decomposition in high-energy heavy ion collisions?

We discuss the role of dissipation in the explosive spinodal decomposition scenario of hadron production during the chiral transition after a high-energy heavy ion collision. We use a Langevin description inspired by microscopic nonequilibrium field theory results to perform real-time lattice simulations of the behavior of the chiral fields. We show that the effect of dissipation can be dramatic. Analytic results for the short-time dynamics are also presented. (c) 2005 Elsevier B.V. All rights reserved.

Effect of magnesium on structure and properties of LiNbO3 prepared from polymeric precursors

The effect of magnesium addition on the phase formation and electric properties of LiNbO3 powder prepared from polymeric precursor was analyzed. It was shown that the unit-cell volume of the rhombohedral phase decreased with increasing magnesium concentration. Small amounts of secondary phases were observed in LiNbO3 powder doped with 5 and 10 mol% Mg+2. These results indicated that the Mg+2 ion was substituted for niobium ion in the rhombohedral phase. The addition of Mg+2 promotes densification of LiNbO3 ceramics. It was noticed that the increase in additive concentration leads to a decrease of electric properties, K-p and d(33). This is due to formation of LiNb3O8 and MgNb2O6 phases at the grain boundaries. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Synthesis and characterization of antimony tartrate for ceramic precursors

Synthesis and characterization of antimony tartrate used as a precursor of ceramic powders obtained by Pechini's method were carried out. Antimony tartrate was chosen as a substitute for the antimony citrate commonly used in this chemical processing, because of difficulties in preparing the citrate. FTIR and TGA/DTA analysis showed that antimony tartrate, H-2[Sb-2(C4H2O6)(2)]. forms a polymeric structure. The procedure described indicates that the antimony chelate obtained is adequate for Pechini's method.

Attainment of lead titanate - Through the thermal decomposition of coprecipitated 8-hydroxyquinolinate precursors

Crystalline PbTiO3 was obtained through the thermal decomposition of 8-hydroxyquinolinate of lead(II) and that of titanium(IV), which was monitored by TG/DTG/DTA under different atmospheric conditions and with varying heating rates. The compound was prepared from adding 8-hydroxyquinoline solution in the solution of metallic ions Pb(II):Ti(IV) (1:1) Linder constant stirring at 3degreesC, having the pH adjusted to 10. The results of these investigations show that different thermal behavior related to the precursor occurred and also the consequent formation of residues which have different crystallinities. No carbonate residues from the thermal decomposition could be determined by XRD and IR. Only PbTiO3 was observed and confirmed by DSC at 470degreesC, temperature lower than the tetragonal-cubic transition.

Electrosynthesis of binuclear ruthenium complexes from [RuCl3(dppb)(L)] precursors [L = pyridine, 4-methylpyridine or dimethyl sulfoxide; dppb=1,4-bis(diphenylphosphino)butane]

Electrolysis has been examined as a method of synthesis for [(L)(dppb)Ru(mu-Cl)(3)RuCl(dppb)] complexes, where dppb = 1,4-bis(diphenylphosphino)butane and L = pyridine (py), 4-methylpyridine (4-pic) or dimethyl sulfoxide (DMSO), by using [RuCl3(dppb)(L)] as precursors. The products of the electrolysis were characterized by P-31-{H-1} NMR, cyclic voltammetry and near infrared spectroscopy. The presence of the [Ru2Cl5(dppb)(2)] complex in the electrochemical cell suggests a mechanism by which the starting original species from the bulk solution reacts with the reduced form [RuCl2(dppb)(L)] generated at the surface of the electrode. The crystal structure of the precursor mer-[RuCl3(dppb)(4-pic)] was determined by X-ray diffraction.

Local Er(III) environment in luminescent titanosilicates prepared from microporous precursors

The local environment of Er3+ ions in microporous titanosilicate ETS-10 and in synthetic narsarsukite and glassy materials obtained by calcination of ETS-10 has been investigated by EXAFS, Raman and photoluminescence spectroscopies. Er L-III-edge EXAFS studies of Er3+-doped ETS-10 support the view that the exchanged Er3+ ions reside close to the (negatively charged) TiO6 octahedra. In ETS-10, Er3+ is partially bonded to framework oxygen atoms and hydration water molecules. The Er...Ti distance (3.3 Angstrom) is similar to the Na...Ti distances (3.15-3.20 Angstrom) reported previously for Na-ETS-10. Although the exact location of the ErO6 units within the host structure of Er3+-doped synthetic narsarsukite is still an open question, it is most likely that Er3+ substitutes Ti4+ rather than Na+ ions. EXAFS spectroscopy indicates that no significant clustering of erbium atoms occurs in the titanosilicate samples studied. Evidence for the insertion of Er3+ ions in the framework of narsarsukite has been obtained by Raman spectroscopy. This is indicated by the increasing full-width at half-maximum (FWHM) of the 775 cm(-1) peak and the increasing intensity of the anatase peaks as the erbium content increases. In addition, as the narsarsukite Er3+ content increases a band at ca. 515 cm(-1) firstly broadens and subsequently a new peak appears at ca. 507 cm(-1).Er3+-doped narsarsukite exhibits a characteristic local vibrational frequency, (h) over bar omega ca. 330 cm(-1), with an electron-phonon coupling, g ca. 0.2, which constitutes additional evidence for framework Er3+ insertion. The number of lines in the infrared emission spectrum of synthetic narsarsukite indicates the presence of two optically-active erbium centres with very similar local environments and an average I-4(13/2) lifetime of 7.8 +/- 0.2 ms.

BaTiO3 obtained through metallic stearate precursors

Metallic stearates were used as precursors to obtain BaTiO3. Barium and titanium stearate mixtures were homogenized in ball mill containing some amount of ammonium stearate. The mixture of the precursors was evaluated by simultaneous TG/ DTA and TMA, and residues from thermal decomposition were characterized by XRD and SEM. It could be verified that the residues from the thermal decomposition in both oxidant and inert atmospheres were the BaTiO3 but with characteristic morphological and crystalline aspects depending on the experimental conditions in which the mixtures of precursors were obtained. (C) 2002 Elsevier B.V. B.V. All rights reserved.

The influence of crystallization route on the properties of lanthanum-doped Bi4Ti3O12 thin films prepared from polymeric precursors

Pure and lanthanum-doped Bi4Ti3O12 thin films were deposited on Pt/Ti/SiO2/Si substrate using a polymeric precursor solution. The spin-coated films were specular and crack-free and crystalline after annealing at 700 degreesC for 2 h. Crystallinity and morphological evaluation were examined by X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Multilayered films obtained using the intermediate-crystalline layer route present a dense microstructure with spherical grains. Films obtained using the intermediate-amorphous layer, present elongated grains around 250 nm in size. The dielectric and ferroelectric properties of the lanthanum-doped Bi4Ti3O12 films are strongly affected by the crystallization route. The hysteresis loops are fully saturated with a remnant polarization and drive voltage of the films, heat-treated by the intermediate-crystalline (P-r = 20.2 muC/cm(2) and V = 1.35 V) and for the film heat-treated by amorphous route (P-r = 22.4 muC/cm(2) and V = 2.99 V). (C) 2004 Elsevier B.V. All rights reserved.