Si-based thin film coating on Y-TZP: Influence of deposition parameters on adhesion of resin cement

This study evaluated the influence of deposition parameters for Si-based thin films using magnetron sputtering for coating zirconia and subsequent adhesion of resin cement. Zirconia ceramic blocks were randomly divided into 8 groups and specimens were either ground finished and polished or conditioned using air-abrasion with alumina particles coated with silica. In the remaining groups, the polished specimens were coated with Si-based film coating with argon/oxygen magnetron discharge at 8:1 or 20:1 flux. In one group, Si-based film coating was performed on air-abraded surfaces. After application of bonding agent, resin cement was bonded. Profilometry, goniometry, Energy Dispersive X-ray Spectroscopy and Rutherford Backscattering Spectroscopy analysis were performed on the conditioned zirconia surfaces. Adhesion of resin cement to zirconia was tested using shear bond test and debonded surfaces were examined using Scanning Electron Microscopy. Si-based film coating applied on air-abraded rough zirconia surfaces increased the adhesion of the resin cement (22.78 ± 5.2 MPa) compared to those of other methods (0-14.62 MPa) (p = 0.05). Mixed type of failures were more frequent in Si film coated groups on either polished or air-abraded groups. Si-based thin films increased wettability compared to the control group but did not change the roughness, considering the parameters evaluated. Deposition parameters of Si-based thin film and after application of air-abrasion influenced the initial adhesion of resin cement to zirconia. © 2013 Elsevier B.V. All rights reserved.

Estudo eletroquímico da corrosão em chapas de aço galvanizado e fosfatizado por coil-coating

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Anthocyanins, pigment stability and antioxidant activity in jabuticaba [myrciaria cauliflora (Mart) O Berg]

Different solvents were evaluated for the extraction of jabuticaba anthocyanin pigments, identifying, quantifying and verifying the stability of the anthocyanins, as well as the conduction of three antioxidant activity assays and determination of the vitamin C levels. The maceration with ethanol acidified with HCl 1.5 mol L-1 (85:15) provides better pigment extraction and stability. The skin is anthocyanin rich, presenting 1.59 and 2.06 g 100 g-1 of dry matter in the Paulista and Sabará varieties, respectively. Cyanidin 3-glucoside is the majority pigment of the skins, followed by delphinidin 3-glucoside. The highest level of vitamin C was found in the skins and seeds of both varieties. It was verified that the skins, presented more antioxidant activity, in free radical capture, as well as in retarding the lipid oxidation process.

Estudo da influência do tratamento térmico em filmes supercondutores, do sistema BSCCO obtido pela técnica de spin-coating

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of a Polymeric Protective Coating on Optical and Electrical Properties of Poly(p-phenylene vinylene) Derivatives

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Nondecalcified Histologic Study of Bone Response to Titanium Implants Topographically Modified by Laser With and Without Hydroxyapatite Coating

The purpose of this study was nondecalcified histologic analysis of titanium implants modified by laser with and without hydroxyapatite. Implants with three modified surfaces were inserted into rabbit tibias: group 1, machined surface; group 2, irradiated (laser); and group 3, irradiated and hydroxyapatite coated (biomimetic method). The mean surface roughness (Ra) scores of groups 2 and 3 were higher than that of group 1. Bone-implant contact measurements at 30 and 60 days for groups 2 and 3 were higher than for group 1. Bone area at 30 and 60 days for group 2 was higher than for groups 1 and 3. Titanium implants modified by laser with and without hydroxyapatite exhibit increased early osseointegration.

Silica-based Nano-coating on Zirconia Surfaces Using Reactive Magnetron Sputtering: Effect on Chemical Adhesion of Resin Cements

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

INFLUENCE OF HVOF COATING ON THE FATIGUE STRENGTH OF 15-5 PH STAINLESS STEEL

Structural component failures due to cyclic loading are associated to surface damage of materials and its interaction with environment. Fatigue failure occurs with stresses below the yield strength of each material and is a result of crack initiation and propagation. In aeronautical components is an important parameter to be considered in project, as well as the corrosion and wear resistance. Thermally sprayed HVOF coatings have been considered to replace galvanic chromium deposits with comparable performance for wear and corrosion resistance. The aim of present research is to study the influence of WC-13Co-4Cr applied by HVOF, on the axial fatigue strength of 15-5 PH stainless steel. The shot peening treatment was used to restore fatigue performance.

Effect of Silver Nanoparticles in a Hydroxyapatite Coating applied by Atmospheric Plasma Spray

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Edible Coating on the Drying and Quality of Papaya (Carica papaya)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Poly(epsilon-caprolactone) nanocapsules carrying the herbicide atrazine: effect of chitosan-coating agent on physico-chemical stability and herbicide release profile

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Fe-doping on the structural, microstructural, optical, and ferroeletric properties of Pb1/2Sr1/2Ti1-xFexO3 oxide prepared by spin coating technique

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Carbon Film Coating of Abutment Surfaces: Effect on the Abutment Screw Removal Torque

Purpose: To evaluate the effect of diamond-like carbon (DLC) coating of prefabricated implant abutment on screw removal torque (RT) before and after mechanical cycling (MC).Materials and Methods: Fifty-four abutments for external-hex implants were divided among 6 groups (n = 9): S, straight abutment (control); SC, straight coated abutment; SCy, straight abutment and MC; SCCy, straight coated abutment and MC; ACy, angled abutment and MC; and ACCy, angled coated abutment and MC. The abutments were attached to the implants by a titanium screw. RT values were measured and registered. Data (in Newton centimeter) were analyzed with analysis of variance and Dunnet test (alpha = 0.05).Results: RT values were significantly affected by MC (P = 0.001) and the interaction between DLC coating and MC (P = 0.038). SCy and ACy showed the lowest RT values, statistically different from the control. The abutment coated groups had no statistical difference compared with the control. Scanning electron microscopy analysis showed DLC film with a thickness of 3 mm uniformly coating the hexagonal abutment.Conclusion: DLC film deposited on the abutment can be used as an alternative procedure to reduce abutment screw loosening.

Bioavailability of plant pigment phytochemicals in Angelica keiskei in older adults: A pilot absorption kinetic study

BACKGROUND/OBJECTIVES: Angelica keiskei is a green leafy vegetable rich in plant pigment phytochemicals such as flavonoids and carotenoids. This study examined bioavailability of flavonoids and carotenoids in Angelica keiskei and the alteration of the antioxidant performance in vivo.SUBJECTS AND MATERIALS: Absorption kinetics of phytochemicals in Angelica keiskei were determined in healthy older adults (>60 y, n = 5) and subjects with metabolic syndrome (n = 5). Subjects consumed 5 g dry Angelica keiskei powder encapsulated in gelatin capsules with a low flavonoid and carotenoid liquid meal. Plasma samples were collected at baseline, 0.5, 1, 2, 3, 4, 5, 6, 7, and 8 h. Samples were analyzed for flavonoids and carotenoids using HPLC systems with electrochemical and UV detection, respectively, and for total antioxidant performance by fluorometry.RESULTS: After ingestion of Angelica keiskei increases in plasma quercetin concentrations were observed at 1-3 and 6-8 hr in the healthy group and at all time points in the metabolic syndrome group compared to baseline (P < 0.05). Plasma lutein concentrations were significantly elevated in both the healthy and metabolic syndrome groups at 8 hr (P < 0.05). Significant increases in total antioxidant performance were also observed in both the healthy and the metabolic syndrome groups compared to baseline (P < 0.05).CONCLUSIONS: Findings of this study clearly demonstrate the bioavailability of phytonutrients of Angelica keiskei and their ability to increase antioxidant status in humans.