Development of an electrochemical sensor based on nanostructured hausmannite-type manganese oxide for detection of sodium ions

The preparation and electrochemical characterization of hausmannite-type manganese oxide to use as a sensing material for sodium ion is described. This paper reports a new via synthetic to obtain of the hausmannite-type manganese oxide and its application in the construction of modified electrode as a voltammetric sensor. The electrochemical activity of hausmannite-type manganese oxide is controlled by intercalation/deintercalation of the sodium ions within the oxide lattice. The detection is based on the measurement of anodic current generated by oxidation of MnIII-MnIV at electrode surface. The best electrochemical response was obtained for a sensor composition of 20% (w/w) hausmannite oxide in the paste, a TRIS buffer solution of pH 6.0-7.0 and a scan rate of 50 mV s-1. A sensitive linear voltammetric response for sodium ions was obtained in the concentration range of 2.01 × 10 -5-2.09 × 10-4 mol L-1 with a slope of 355 μA L mmol-1 and a detection limit of 7.50 × 10 -6 mol L-1 using cyclic voltammetry. The use of hausmannite has significantly improved the selectivity of the sensor compared to the birnessite-type manganese oxide modified electrode. Under the working conditions, the proposed method was successfully applied to determination of sodium ions in urine samples. © 2013 Elsevier B.V.

On the electrochemical behavior of Cu-16%Zn-6.5%Al alloy containing the β'-phase (martensite) in borate buffer

In this work, the electrochemical behavior of Cu-16(wt.%)Zn-6.5(wt.%)Al alloy containing the β'-phase (martensite) was studied in borate buffer solution (pH 8.4) by means of open-circuit potential (EOC), electrochemical impedance spectroscopy (EIS) and cyclic voltammetry (CV). The alloy EOC was -0.29 V vs. Hg/HgO/OH-, similar to that of pure copper in this medium, indicating that the processes which occur on the alloy surface are mainly governed by copper. EIS response was related to the dielectric and transmission properties of the complex oxide layer. The CVs showed peaks concerning the redox reactions for copper and zinc. These peaks were assigned to the formation and reduction of copper and zinc species. Furthermore, they showed that the copper oxidation was suppressed by the presence of zinc and aluminum in the alloy composition. The copper and zinc oxidation to form complex oxide layers and the reduction of the different metallic oxides generated in the anodic potential scan suggest that a solid state reaction could determine the metallic oxide formation. © 2013 Elsevier Ltd. All rights reserved.

Growth of calcium phosphate coating on Ti-7.5Mo alloy after anodic oxidation

Titanium and its alloys are widely used as biomaterials due to their mechanical, chemical and biological properties. To enhance the biocompatibility of titanium alloys, various surface treatments have been proposed. In particular, the formation of titanium oxide nanotubes layers has been extensively examined. Among the various materials for implants, calcium phosphates and hydroxyapatite are widely used clinically. In this work, titanium nanotubes were fabricated on the surface of Ti-7.5Mo alloy by anodization. The samples were anodized for 20 V in an electrolyte containing glycerol in combination with ammonium fluoride (NH4F, 0.25%), and the anodization time was 24 h. After being anodized, specimens were heat treated at 450 °C and 600°C for 1 h to crystallize the amorphous TiO2 nanotubes and then treated with NaOH solution to make them bioactive, to induce growth of calcium phosphate in a simulated body fluid. Surface morphology and coating chemistry were obtained respectively using, field-emission scanning electron microscopy (FEG-SEM), AFM and X-ray diffraction (XRD). It was shown that the presence of titanium nanotubes induces the growth of a sodium titanate nanolayer. During the subsequent invitro immersion in a simulated body fluid, the sodium titanate nanolayer induced the nucleation and growth of nano-dimensioned calcium phosphate. It was possible to observe the formation of TiO2 nanotubes on the surface of Ti-7.5Mo. Calcium phosphate coating was greater in the samples with larger nanotube diameter. These findings represent a simple surface treatment for Ti-7.5Mo alloy that has high potential for biomedical applications. © (2013) Trans Tech Publications, Switzerland.

Tribocorrosion behaviour of anodic treated titanium surfaces intended for dental implants

Tribocorrosion plays an important role in the lifetime of metallic implants. Once implanted, biomaterials are subjected to micro-movements in aggressive biological fluids. Titanium is widely used as an implant material because it spontaneously forms a compact and protective nanometric thick oxide layer, mainly TiO2, in ambient air. That layer provides good corrosion resistance, and very low toxicity, but its low wear resistance is a concern. In this work, an anodizing treatment was performed on commercial pure titanium to form a homogeneous thick oxide surface layer in order to provide bioactivity and improve the biological, chemical and mechanical properties. Anodizing was performed in an electrolyte containing β-glycerophosphate and calcium acetate. The influence of the calcium acetate content on the tribocorrosion behaviour of the anodized material was studied. The concentration of calcium acetate in the electrolyte was found to largely affect the crystallographic structure of the resulting oxide layer. Better tribocorrosion behaviour was noticed on increasing the calcium acetate concentration. © 2013 IOP Publishing Ltd.

Chemical characterization and bioactivity of epoxy resin and Portland cement-based sealers with niobium and zirconium oxide radiopacifiers

The purpose of this study was to characterize and to evaluate the bioactivity potential of experimental root canal sealers (ES) based on Portland cement, epoxy resin with nano- and micro-particles of niobium or zirconium oxide used as radiopacifiers in comparison to AH Plus and MTA Fillapex. Methods Specimens of the sealers (10 mm in diameter × 1 mm thick) were prepared and the radiopacity was evaluated according to ISO 6876 (2012) specifications. Characterization of the sealers was performed under the scanning electron microscope (SEM) immediately after setting and after immersion for 28 days in Hank's balanced salt solution (HBSS). In addition X-ray energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and Fourier transform infrared (FT-IR) spectroscopy were also performed. The pH and calcium ion release were measured after 1, 7, 14, 21 and 28 days after completion of seating using a digital pH meter and an atomic absorption spectrophotometer, respectively. Results The experimental sealers exhibited an average radiopacity of 2.5 mm thickness of aluminum, which was similar to MTA Fillapex (P > 0.05) and inferior to AH Plus (P < 0.05). AH Plus did not show bioactivity. Although the experimental sealers did not exhibit the formation of hydration product, they encouraged the deposition of crystalline spherical structures of calcium deficient phosphate. The highest pH and calcium release values were observed with the experimental sealers (P < 0.01). ES-Nb-micro was the only sealer to present hexagonal shaped crystal deposition. Significance Novel root canal sealers based on a mixture of Portland cement, epoxy resin and radiopacifier exhibited a degree of bioactivity although no evidence of cement hydration was demonstrated on material characterization. The radiopacifier particle size had limited effect on the sealer microstructure and chemical properties.

Radiopacity and cytotoxicity of Portland cement associated with niobium oxide micro and nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Understanding growth mechanisms and tribocorrosion behaviour of porous TiO2 anodic films containing calcium, phosphorous and magnesium

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Anodization mechanism on SiC nanoparticle reinforced al matrix composites produced by power metallurgy

Specimens of aluminum-based composites reinforced by silicon carbide nanoparticles (Al/SiCnp) produced by powder metallurgy (PM) were anodized under voltage control in tartaric-sulfuric acid (TSA). In this work, the influence of the amount of SiCnp on the film growth during anodizing was investigated. The current density versus time response and the morphology of the porous alumina film formed at the composite surface are compared to those concerning a commercial aluminum alloy (AA1050) anodized under the same conditions. The processing method of the aluminum alloys influences the efficiency of the anodizing process, leading to a lower thicknesses for the unreinforced Al-PM alloy regarding the AA1050. The current density versus time response is strongly dependent on the amount of SiCnp. The current peaks and the steady-state current density recorded at each voltage step increases with the SiCnp volume fraction due to the oxidation of the SiCnp. The formation mechanism of the anodic film on Al/SiCnp composites is different from that occurring in AA1050, partly due the heterogeneous distribution of the reinforcement particles in the metallic matrix, but also to the entrapment of SiCnp in the anodic film.

Corrosion resistance of 2024 aluminum alloy coated with plasma deposited a-C:H:Si:O films

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Investigation of the reactivity of metal oxide catalysts for the gas-phase phenol methylation

The gas-phase phenol methylation with methanol was investigated both from catalitic and spectroscopic point of view. In particular, the work focus on the behavior of metal oxide catalysts, like iron(III) vanadate and aluminum vanadate. Spectroscopic studies include: X-ray diffraction and Raman analysis for catalyst charactrerization; Diffuse reflectance infrared fourier transform spectroscopy and in-situ Infrared spectroscopy in vacuum for investigation of interactions between reactants and surface of catalysts.

Correlação entre microestrutura e comportamento de corrosão em duas ligas do sistema Al-Fe-Si produzidas pelos processos industriais de lingotamento contínuo e semi-contínuo.

As chapas de ligas de alumínio trabalháveis são produzidas atualmente por dois processos, o método de vazamento contínuo conhecido TRC (Twin Roll Continous Casting) ou pelo método tradicional de vazamento de placas DC (Direct Chill). A fabricação de ligas de alumínio pelos dois processos confere características microestruturais diferentes quando comparadas entre si, o que se reflete em suas propriedades. Além disto, ocorrem variações microestruturais ao longo da espessura, especialmente nas chapas produzidas pelo processo TRC. Neste sentido, é importante estudar a evolução microestrutural que ocorre durante o seu processamento e sua influência com relação à resistência à corrosão. Dessa forma foi realizado neste trabalho um estudo comparativo do comportamento de corrosão, bem como das microestruturas do alumínio de alta pureza AA1199 (99,995% Al) e das ligas de alumínio AA1050 (Fe+Si0,5%) e AA4006 (Fe+Si1,8%) produzidas pelos processos industriais de lingotamento contínuo e semi-contínuo. Os resultados obtidos evidenciaram que as microestruturas das ligas AA4006 DC e AA4006 TRC são distintas, sendo observada maior fração volumétrica dos precipitados na liga fabricada pelo processo TRC comparativamente ao DC. Para caracterizar o comportamento de corrosão foram realizados ensaios de Espectroscopia de Impedância Eletroquímica e Polarização Potenciodinâmica, que mostraram a maior resistência à corrosão localizada para a liga fabricada pelo processo TRC em comparação ao processo DC. Além disso, foi verificada, em ordem decrescente, uma maior resistência à corrosão do alumínio AA1050, seguida pela superfície da liga AA4006 e por fim, pelo centro da chapa desta última. Os resultados obtidos por espectroscopia de impedância eletroquímica para as ligas AA4006 fabricadas pelo processo TRC apresentaram melhor desempenho que o processo DC, principalmente em intervalos de 2 a 12 horas de imersão na solução de sulfato de sódio contaminada com íons cloreto. Para tempos de imersão acima de 4 horas foi observado comportamento indutivo em baixas frequências para os dois tipos de processamento investigados, o que foi associado à adsorção de espécies químicas, principalmente íons sulfato e oxigênio, na interface metal/óxido. As curvas de polarização anódica mostraram maior resistência à corrosão localizada para a liga fabricada pelo processo viii TRC em comparação ao processo DC. Este comportamento foi associado às diferentes características microestruturais, observadas para liga AA4006 obtida pelos dois processos.

Role of reinforcement/matrix interfacial strength in fatigue crack propagation in particulate SiC reinforced aluminum alloy 8090

A study has been made of the influence of the reinforcement/matrix interfacial strength on fatigue crack propagation in a powder metallurgy aluminum alloy 8090-SiC particulate composite. The interfacial region has been altered by two separate routes, the first involving aging of the 8090 matrix, with the subsequent formation of precipitate free zones at the boundaries, and the second consisting of oxidizing the surface of the SiC particles before their incorporation into the composite. In the naturally aged condition, oxidation of the SiC leads to a reduction in fatigue crack growth resistance at higher values of stress intensity range ΔK. This is due to a proportion of the crack growth occurring through voids formed in association with many of the weak SiC interfaces which have retained a layer of thick surface oxide after processing. On overaging no difference in crack growth rate is discernible between the oxidized and unoxidized SiC composites. It is proposed that this is due to similar levels of interfacial weakening having occurred in both composites, indicating that this is an important factor in the reduction of the high ΔK crack growth resistance of the unoxidized SiC composite on aging.