Flexural strength of acrylic resins polymerized by different cycles

Despite the large number of studies addressing the effect of microwave polymerization on the properties of acrylic resin, this method has received limited clinical acceptance. This study evaluated the influence of microwave polymerization on the flexural strength of a denture base resin. A conventional heat-polymerized (Classico), a microwave-polymerized (Onda-Cryl) and a autopolymerizing acrylic (Jet) resins were used. Five groups were established, according to polymerization cycles: A, B and C (Onda-Cryl, short cycle - 500W/3 min, long - 90W/13 min + 500W/90 see, and manufacturing microwave cycle - 320W/3 min + OW/3 min + 720W/3 min); T(Classico, water bath cycle - 74 degrees C/9h) and Q (Jet, press chamber cycle - 50 degrees C/15 min at 2 bar). Ten specimens (65 x 10 x 3.3 mm) were prepared for each cycle. The flexural strength of the five groups was measured using a three-point bending test at a cross-head speed of 5 mm/min. Flexural strength values were analyzed by one-way ANOVA and the Tukey's test was performed to identify the groups that were significantly different at 5% level. The microwave-polymerized groups showed the highest means (p<0.05) for flexural strength (MPa) (A = 106.97 +/- 5.31; B = 107.57 +/- 3.99; C = 109.63 +/- 5.19), and there were no significant differences among them. The heat-polymerized group (T) showed the lowest flexural strength means (84.40 +/- 1.68), and differ significantly from all groups. The specimens of a microwavable denture base resin could be polymerized by different microwave cycles without risk of decreasing the flexural strength.

Effect of methyl methacrylate monomer on bond strength of denture base resin to acrylic teeth

Bond failures at the acrylic teeth and denture base resin interface are still a common clinical problem in prosthodontics. The effect of methyl methacrylate (MMA) monomer on the bond strength of three types of denture base resins (Acron MC, Lucitone 550 and QC-20) to two types of acrylic teeth (Biotone and Trilux) was evaluated. Twenty specimens were produced for each denture base resin/acrylic tooth combination and were randomly divided into control (acrylic teeth received no surface treatment) and experimental groups (MMA was applied to the surface of the acrylic teeth for 180 s) and were submitted to shear tests (1 mm/mm). Data (MPa) were analyzed using three-way ANOVA/Student's test (alpha = 0.05). MMA increased the bond strength of Lucitone denture base resins and decreased the bond strength of QC-20. No difference was detected for the bond strength of Acron MC base resin after treatment with MMA. (C) 2008 Elsevier Ltd. All rights reserved.

Evaluation of the Bond Strength of Denture Base Resins to Acrylic Resin Teeth: Effect of Thermocycling

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of disinfection and storage on the flexural strength of ocular prosthetic acrylic resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

THE EFFECT of E-GLASS FIBERS and ACRYLIC RESIN THICKNESS on FRACTURE LOAD IN A SIMULATED IMPLANT-SUPPORTED OVERDENTURE PROSTHESIS

Statement of problem. Implant overdenture prostheses are prone to acrylic resin fracture because of space limitations around the implant overdenture components.Purpose. The purpose of this study was to evaluate the influence of E-glass fibers and acrylic resin thickness in resisting acrylic resin fracture around a simulated overdenture abutment.Material and methods. A model was developed to simulate the clinical situation of an implant overdenture abutment with varying acrylic resin thickness (1.5 or 3.0 mm) with or without E-glass fiber reinforcement. Forty-eight specimens with an underlying simulated abutment were divided into 4 groups (n=12): 1.5 mm acrylic resin without E-glass fibers identified as thin with no E-glass fiber mesh (TN-N); 1.5 mm acrylic resin with E-glass fibers identified as thin with E-glass fiber mesh (TN-F); 3.0 mm acrylic resin without E-glass fibers identified as thick without E-glass fiber mesh (TK-N); and 3.0 mm acrylic resin with E-glass fibers identified as thick with E-glass fiber mesh (TK-F). All specimens were submitted to a 3-point bending test and fracture loads (N) were analyzed with a 2-way ANOVA and Tukey's post hoc test (alpha=.05).Results. The results revealed significant differences in fracture load among the 4 groups, with significant effects from both thickness (P<.001) and inclusion of the mesh (P<.001). Results demonstrated no interaction between mesh and thickness (P=.690). The TN-N: 39 +/- 5 N; TN-F: 50 +/- 6.9 N; TK-N: 162 +/- 13 N; and TK-F: 193 +/- 21 N groups were all statistically different (P<.001).Conclusions. The fracture load of a processed, acrylic resin implant-supported overdenture can be significantly increased by the addition of E-glass fibers even when using thin acrylic resin sections. on a relative basis, the increase in fracture load was similar when adding E-glass fibers or increasing acrylic resin thickness. (J Prosthet Dent 2011;106:373-377)

Bond strength between acrylic resin and maxillofacial silicone

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of polymerization and accelerated aging on iris color stability of ocular prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Esthetic Interim Acrylic Resin Prosthesis Reinforced with Metal Casting

Fabrication of an interim prosthesis is an important procedure in oral rehabilitation because it aids in determining the esthetics, phonetics, and occlusal relationship of the definitive restoration. The typical material (acrylic resin) used in interim prostheses commonly fails due to fractures. During extended oral rehabilitation with fixed partial prostheses, high strength interim prostheses are often required to protect hard and soft tissues, avoid dental mobility, and to allow the clinician and patient a chance to evaluate cosmetics and function before the placement of the definitive prosthesis. Furthermore, a satisfactory interim prosthesis can serve as a template for the construction of the definitive prosthesis. The maintenance of this prosthesis is important during treatment for protection of teeth and occlusal stability. Procedures to reinforce interim prostheses help to improve performance and esthetics in long-term treatment. Due to the low durability of acrylic resin in long-term use, the use of reinforcing materials, such as metal castings or spot-welded stainless steel matrix bands, is indicated in cases of extensive restoration and long-term treatment. This paper describes an easy technique for fabricating a fixed interim prosthesis using acrylic resin and a cast metallic reinforcement.

Bond strength of denture teeth to acrylic resin: effect of thermocycling and polymerisation methods

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Chromatic stability of acrylic resins of artificial eyes submitted to accelerated aging and polishing

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of the color stability of two techniques for reproducing artificial irides after microwave polymerization

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of weathering and thickness on the superficial microhardness of acrylic resin and ocular button

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Alteration of blue pigment in artificial iris in ocular prosthesis: Effect of paint, drying method and artificial aging

The artificial iris is the structure responsible for the dissimulation and aesthetics of ocular prosthesis. The objective of the present study was to evaluate the color stability of artificial iris of microwaveable polymerized ocular prosthesis, as a function of paint type, drying method and accelerated aging. A total of 40 discs of microwaveable polymerized acrylic resin were fabricated, and divided according to the blue paint type ( n = 5): hydrosoluble acrylic, nitrocellulose automotive, hydrosoluble gouache and oil paints. Paints where dried either at natural or at infrared light bulb method. Each specimen was constituted of one disc in colorless acrylic resin and another colored with a basic sclera pigment. Painting was performed in one surface of one of the discs. The specimens were submitted to an artificial aging chamber under ultraviolet light, during 1008 h. A reflective spectrophotometer was used to evaluate color changes. Data were evaluated by 3-way repeated-measures ANOVA and the Tukey HSD test (alpha = 0.05). All paints suffered color alteration. The oil paint presented the highest color resistance to artificial aging regardless of drying method. (C) 2010 British Contact Lens Association. Published by Elsevier Ltd. All rights reserved.

Microscopical analysis of Candida albicans biofilms on heat-polymerised acrylic resin after chlorhexidine gluconate and sodium hypochlorite treatments

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Development and application of methods for determination of residual monomer in dental acrylic resins using high performance liquid chromatography

Two high-performance liquid chromatographic methods for determination of residual monomer in dental acrylic resins are described. Monomers were detected by their UV absorbance at 230 nm, on a Nucleosil((R)) C-18 (5 mu m particle size, 100 angstrom pore size, 15 x 0.46 cm i.d.) column. The separation was performed using acetonitrile-water (55:45 v/v) containing 0.01% triethylamine (TEA) for methyl methacrylate and butyl methacrylate, and acetonitrile-water (60:40 v/v) containing 0.01% TEA for isobutyl methacrylate and 1,6-hexanediol dimethacrylate as mobile phases, at a flow rate of 0.8 mL/min. Good linear relationships were obtained in the concentration range 5.0-80.0 mu g/mL for methyl methacrylate, 10.0-160.0 mu g/mL for butyl methacrylate, 50.0-500.0 mu g/mL for isobutyl methacrylate and 2.5-180.0 mu g/mL for 1,6-hexanediol dimethacrylate. Adequate assay for intra- and inter-day precision and accuracy was observed during the validation process. An extraction procedure to remove residual monomer from the acrylic resins was also established. Residual monomer was obtained from broken specimens of acrylic disks using methanol as extraction solvent for 2 h in an ice-bath. The developed methods and the extraction procedure were applied to dental acrylic resins, tested with or without post-polymerization treatments, and proved to be accurate and precise for the determination of residual monomer content of the materials evaluated. Copyright (c) 2005 John Wiley & Sons, Ltd.