Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC

Steel is an alloy EUROFER promising for use in nuclear reactors, or in applications where the material is subjected to temperatures up to 550 ° C due to their lower creep resistance under. One way to increase this property, so that the steel work at higher temperatures it is necessary to prevent sliding of its grain boundaries. Factors that influence this slip contours are the morphology of the grains, the angle and speed of the grain boundaries. This speed can be decreased in the presence of a dispersed phase in the material, provided it is fine and homogeneously distributed. In this context, this paper presents the development of a new material metal matrix composite (MMC) which has as starting materials as stainless steel EUROFER 97, and two different kinds of tantalum carbide - TaC, one with average crystallite sizes 13.78 nm synthesized in UFRN and another with 40.66 nm supplied by Aldrich. In order to improve the mechanical properties of metal matrix was added by powder metallurgy, nano-sized particles of the two types of TaC. This paper discusses the effect of dispersion of carbides in the microstructure of sintered parts. Pure steel powders with the addition of 3% TaC UFRN and 3% TaC commercial respectively, were ground in grinding times following: a) 5 hours in the planetary mill for all post b) 8 hours of grinding in the mill Planetary only for steel TaC powders of commercial and c) 24 hours in the conventional ball mill mixing the pure steel milled for 5 hours in the planetary mill with 3% TaC commercial. Each of the resulting particulate samples were cold compacted under a uniaxial pressure of 600MPa, on a cylindrical matrix of 5 mm diameter. Subsequently, the compressed were sintered in a vacuum furnace at temperatures of 1150 to 1250 ° C with an increment of 20 ° C and 10 ° C per minute and maintained at these isotherms for 30, 60 and 120 minutes and cooled to room temperature. The distribution, size and dispersion of steel and composite particles were determined by x-ray diffraction, scanning electron microscopy followed by chemical analysis (EDS). The structures of the sintered bodies were observed by optical microscopy and scanning electron accompanied by EDS beyond the x-ray diffraction. Initial studies sintering the obtained steel EUROFER 97 a positive reply in relation to improvement of the mechanical properties independent of the processing, because it is obtained with sintered microhardness values close to and even greater than 100% of the value obtained for the HV 333.2 pure steel as received in the form of a bar

Sistema de instrumentação mecanizada Hyflex EDM

A Endodontia é uma área em constante evolução. Consideráveis desenvolvimentos nos materiais e técnicas têm sido essenciais para o melhoramento dos resultados nos tratamentos realizados. É exemplo disso mesmo a constituição dos instrumentos Endodônticos primordiais, construídos em cordas de piano, com evolução para aço de carbono, material este que sofria corrosão provocado pelo cloro presente no hipoclorito de sódio. O aço de carbono evoluiu para aço inoxidável e deste as limas endodônticas passaram a ser feitas em níquel-titânio, conferindo-lhes melhor flexibilidade e efeito de memória de forma. Mesmo com todas estas melhorias significativas, fraturas de instrumentos e erros durante a instrumentação continuam a acontecer e com eles veio a necessidade da pesquisa de possíveis melhorias da constituição das limas em NiTi. Como resultado surgiram ligas como o M-wire, fase-R e CM-wire, criadas a partir de tratamentos térmicos, que trouxeram às limas Endodônticas maior flexibilidade e resistência à fratura que os instrumentos feitos em NiTi convencional. A mais recente evolução das limas Ni-Ti, desenvolvida pela Coltene Whaldent (Allstätten, Suiça), são as limas Hyflex EDM, limas para canais radiculares de 5ª geração. O seu processo de fabrico por eletroerosão cria uma superfície única fazendo com que estas limas sejam mais duras e resistam mais à quebra, aliado à sua alta flexibilidade. É possível assim reduzir o número de limas para a limpeza e modelagem dos canais durante os tratamentos endodônticos sem comprometer a preservação da anatomia dos canais. As limas Hyflex EDM possuem, tal como as limas Hyflex CM, o efeito de controle de memória (CM), o que confere propriedades muito similares entre os dois sistemas.