Yielding of engineering polymers at strain rates of up to 500 s-1

A method is described for measuring the mechanical properties of polymers in compression at strain rates in the range approximately 300-500 s-1. A gravity-driven pendulum is used to load a specimen on the end of an instrumented Hopkinson output bar and the results are processed by a microcomputer. Stress-strain curves up to high strains are presented for polycarbonate, polyethersulphone and high density polyethylene over a range of temperatures. The value of yield stress, for all three polymers, was found to vary linearly with log (strain rate) at strain rates up to 500 s-1. © 1985.

Fabrication of an organic field effect transistor using nano imprinting of Ag inks and semiconducting polymers

A simple and cheap procedure for flexible electronics fabrication was demonstrated by imprinting metallic nanoparticles (NPs) on flexible substrates. Silver NPs with an average diameter of 10 nm were prepared via an improved chemical approach and Ag Np ink was produced in α-terpineol with a concentration up to 15%. Silver micro/nanostructures with a dimension varying from nanometres to microns were produced on a flexible substrate (polyimide) by imprinting the as-prepared silver ink. The fine fluidic properties of an Ag NP/α-terpineol solution and low melting temperatures of silver nanoparticles render a low pressure and low temperature procedure, which is well suited for flexible electronics fabrication. The effects of sintering and mechanical bending on the conductivity of imprinted silver contacts were also investigated. Large area organic field effect transistors (OFET) on flexible substrates were fabricated using an imprinted silver electrode and semiconducting polymer. The OFET with silver electrodes imprinted from our prepared oleic acid stabilized Ag nanoparticle ink show an ideal ohmic contact; therefore, the OFET exhibit high performance (Ion/Ioff ratio: 1 × 103; mobility: 0.071 cm2 V-1 s-1). © 2010 IOP Publishing Ltd.

The dominant role of the solvent-water interface in water droplet templating of polymers

We investigate the formation of microstructured polymer networks known as Breath Figure templated structures created by the presence of water vapour over evaporating polymer solutions. We use a highly controlled experimental approach to examine this dynamic and non-equilibrium process to uniquely compare pure solvent systems with polymer solutions and demonstrate using a combination of optical microscopy, focused ion-beam milling and SEM analysis that the porous polymer microstructure is completely controlled by the interfacial forces that exist between the water droplet and the solvent until a final drying dilation of the imprints. Water droplet contact angles are the same in the presence or absence of polymer and are independent of size for droplets above 5 μm. The polymer acts a spectator that serves to trap water droplets present at the air interface, and to transfer their shape into the polymer film. For the smallest pores, however, there are unexpected variations in the contact angle with pore size that are consistent with a possible contribution from line tension at these smaller dimensions. © The Royal Society of Chemistry.