Ba0.5Sr0.5Co0.8Fe0.2O3-delta ceramic hollow-fiber membranes for oxygen permeation

Setf-supported asymmetric hollow-fiber membranes of mixed oxygen-ionic and electronic conducting perovskite Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCF) were prepared by a combined phase-inversion and sintering technique. The starting inorganic powder was synthesized by combined EDTA-citrate complexing process followed by thermal treatment at 600 degrees C. The powder was dispersed in a polymer solution and then extruded into hollow-fiber precursors through a spinneret. ne fiber precursors were sintered at elevated temperatures to form gastight membranes, which were characterized by SEM and gas permeation tests. Performance of the hollow fibers in air separation was both experimentally and theoretically studied at various conditions. The results reveal that the oxygen permeation process was controlled by the slow oxygen surface exchange kinetics under the investigated conditions. The porous inner surface of the prepared perovskite hollow-fiber membranes considerably favored the oxygen permeation. The maximum oxygen flux measured was 0.031 mol-m(-2).s(-1) at 950 degrees C with the sweep gas flow rate of 0.522 mol(.)m(-2).s(-1). To improve the oxygen flux of BSCF perovskite membranes, future work should be focused on surface modification rather than reduction of the membrane thickness. (c) 2006 American Institute of Chemical Engineers.

A general route to synthesize supported isolated oxide and mixed-oxide nanoclusters at sizes below 5 nm

A simple and efficient route to prepare supported nanocrystalline oxides is presented. The synthesis procedure, i.e. in situ autocombustion of a glycine complex, allows the production of nanocrystals in a porous matrix presenting larger pore size. An example of successful formation of 2-5 nm nanocrystals is given for a single oxide (Fe2O3), a mixed-oxide structure (LaCoO3 perovskite-type) and a nickel-doped oxide. © 2011 The Royal Society of Chemistry.

Study of the physical properties of metals and oxides at extreme pressure and temperature conditions

The high-pressure and temperature investigations on transition metals, metal doped-oxide system, nanocrystalline materials are presented in this dissertation. The metal-doped oxide systems are technologically important because of their applications, e.g. LSC, opto electronic applications, luminescence from lasers, etc., and from the earth sciences point of view, e.g. the study of trace elements in the MgO-SiO2 system, which accounts for 50% of the Earth's chondritic model. We have carried out thorough investigations on Cr2O3 and on chromium bearing oxides at high PT-conditions using in situ X-ray diffractometry and florescence spectroscopy techniques. Having obtained exciting results, an attempt to focus on the mechanism of the coordination of transition metals in oxides has been made. Additionally, the florescence from the metals in host oxides was found to be helpful to obtain information on structural variations like changes in the coordination of the doped element, formation of new phases, the diffusion processes. The possible reactions taking place at extreme conditions in the MgO-SiO2 system has been observed using florescence as markers. A new heating assemblage has been designed and fabricated for a precise determination of temperature at high pressures. An equation combining pressure shifts of ruby wavelength and temperature has been proposed. We observed that the compressibility of nanocrystalline material (MgO and Ni) is independent of crystallite size. A reduction in the transition pressure of nanocrystalline ceria at high-pressure has been observed as compare to the corresponding bulk material. ^

Evaluation of strontium-site-deficient Sr2Fe1.4Co0.1Mo0.5O6-δ-based perovskite oxides as intermediate temperature solid oxide fuel cell cathodes

In this paper strontium-site-deficient Sr₂Fe_1.4Co_0.1Mo_0.5O_6-δ-based perovskite oxides (S_xFCM) were prepared and evaluated as the cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFCs). All samples exhibited a cubic phase structure and the lattice shrinked with increasing the Sr-deficiency as shown in XRD patterns. XPS results determined that the transition elements (Co/Fe/Mo) in S_xFCM oxides were in a mixed valence state, demonstrating the small polaron hopping conductivity mechanism existed. Among the samples, S_1.950FCM presented the lowest coefficient of thermal expansion of 15.62 × 10^-6 K^-1, the highest conductivity value of 28 S cm^-1 at 500 °C, and the lowest interfacial polarization resistance of 0.093 Ω cm² at 800 °C, respectively. Furthermore, an anode-supported single cell with a S_1.950FCM cathode was prepared, demonstrating a maximum power density of 1.16 W cm^-2 at 800 °C by using wet H₂ (3% H₂O) as the fuel and ambient air as the oxidant. These results indicate that the introduction of Sr-deficiency can dramatically improve the electrochemical performance of Sr₂Fe_1.4Co_0.1Mo_0.5O_6-δ, showing great promise as a novel cathode candidate material for IT-SOFCs.

Stoichiometry dependence of the evolution of the irradiated-induced defect clusters in lanthanum-doped ceria

To study the stoichiometry dependence of irradiation e ects in fluorite-type mixed oxide nuclear fuel (UPuO2), ion implantation in La doped ceria was used. Cerium dioxide single crystals with 0 mol%, 5 mol% and 25 mol% La concentration were irradiated with 1 MeV Kr ions at 800 C. In-situ transmission electron microscope (TEM) was utilized to observe the the damage process and defects created by the ion beam irradiation. Dislocation loops were observed after irradiation and were determined to be on {111} planes, but not on {220} or {200} planes. Ab substantial difference in the average size of dislocation loops for 0 %, 5% and 25% cases was observed at several doses.The growth rate of dislocation loops and the oxygen vacancy di usivity were found to be inversely correlated.