Damage removal and strain relaxation in As+-implanted Si0.57Ge0.43 epilayers grown by gas source molecular beam epitaxy

The damage removal and strain relaxation in the As+-implanted Si0.57Ge0.43 epilayers were studied by double-crystal x-ray diffractometry and transmission electron microscopy. The results presented in this paper indicate that rapid thermal annealing at temperatures higher than 950 degrees C results in complete removal of irradiation damage accompained by the formation of GeAs precipitates which enhance the removal process of dislocations.

NiO removal of Ni/Au Ohmic contact to p-GaN after annealing

The Ni/Au contact was treated with oxalic acid after annealing in O_2 ambient, and its I-V characteristic showed the property of contact has been obviously improved. An Auger electron spectroscopy (AES) depth pro-file of the contact as-annealed showed that the top layer was highly resistive NiO, while an X-ray photo-electron spectroscopy (XPS) of oxalic acid treated samples indicated that the NiO has been removed effectively. A scanning electron microscope (SEM) was used to observe the surface morphology of the contacts, and it was found that the lacunaris surface right after annealing became quite smooth with lots of small Au exposed areas after oxalic acid treatment. When the test probe or the subsequently deposited Ti/Au was directly in contact with these small Au areas, they worked as low resistive current paths and thus decrease the specific contact resistance.