Texture analysis of cold rolled and annealed aluminum alloy produced by twin-roll casting

A 7.4 mm thick strip of 3003 aluminum alloy produced by the industrial twin-roll casting (TRC) process was homogenized at 500 °C for 12 hours, after which it was cold rolled in two conditions: 1) to reduce the strip's thickness by 67%, and 2) to reduce it by 91%. The alloy was annealed at 400 °C for 1 hour in both conditions. The results revealed that a rotated cube texture, the {001}<110> component, predominated in the as-cast condition and was transformed into brass, copper and S type textures during the cold rolling process. There was practically no difference between the deformation textures at the two thickness reductions.

Ortsaufgelöster Nachweis von Elementspuren mittels Laserablation und Resonanzionisations-Massenspektrometrie und Untersuchungen zur Laserablations-Dynamik

Im Rahmen dieser Arbeit wurde eine neue Methode für einen empfindlichen und isotopenselektiven Elementnachweis entwickelt. Unter Einsatz von Laserablation geschieht der Probenaufschluß direkt und mit einer Ortsauflösung von unter 30 m. Hierzu wurde ein hochauflösendes MALDI-TOF-Massenspektrometer, welches üblicherweise für biochemische Fragestellungen eingesetzt wird, mit einem spektroskopischen Aufbau zur resonanten Ionisation von Elementgehalten modifiziert. Die Methode ist somit insbesondere für die Untersuchung von Elementspuren in Festkörperproben mit mikroskopischer Struktur konzipiert. Methodische Entwicklungsarbeiten wurden anhand des Elements Gadolinium durchgeführt. Durch die Verwendung gepulster Farbstofflaser stehen ausreichend hohe Laserfelder zur Verfügung, um unabhängig von Hyperfeinstruktur und Isotopieverschiebung Übergänge aller Isotope im Rahmen des Resonanzionisations-Verfahrens zu sättigen. Darauf konnte eine Isotopenverhältnisanalyse mit einer Genauigkeit im Prozentbereich verwirklicht werden. Verschiedene Anregungsleitern wurden untersucht, und mit elementspezifischen Resonanzüberhöhungen bis zu zwei Größenordnungen über dem nicht-resonant gebildeten Untergrund konnte eine Nachweiseffizienz von über 10-4 (entsprechend sub-fg/g-Niveau) erzielt werden. Dazu wurden Simulationsrechnungen zum atomaren Sättigungsverhalten in starken resonanten Laserfeldern durchgeführt. Erste Anwendungen des Laserablationsverfahrens waren Proben kosmologischer Herkunft. Der physikalische Prozeß der Laserablation bei Metallen wurde unter Hochvakuum-Bedingung systematisch in Abhängigkeit der Laserfluenz untersucht. In der ablatierten Plasmaphase erwies sich der Neutralanteil als besonders geeignet für geschwindigkeitsselektive Laserionisations-Messungen. Eine bimodale Struktur wurde beobachtet, bestehend aus einer thermischen und einer schockwellen-induzierten Komponente. Der ionische Anteil der ablatierten Dampfphase konnte über variable elektrische Feldpulse untersucht werden. Laserablation unter Atmosphärenbedingung wurde an einem beschichteten Messingtarget untersucht. Dabei wurde die Entstehung von permanenten Oberflächenstrukturen beobachtet, welche sich durch Nichtgleichgewichts-Prozesse in der Dampfphase erklären lassen.

Simultaneous stable isotope analysis of methane and nitrous oxide on ice core samples

Methane and nitrous oxide are important greenhouse gases which show a strong increase in atmospheric mixing ratios since pre-industrial time as well as large variations during past climate changes. The understanding of their biogeochemical cycles can be improved using stable isotope analysis. However, high-precision isotope measurements on air trapped in ice cores are challenging because of the high susceptibility to contamination and fractionation. Here, we present a dry extraction system for combined CH4 and N2O stable isotope analysis from ice core air, using an ice grating device. The system allows simultaneous analysis of δD(CH4) or δ13C(CH4), together with δ15N(N2O), δ18O(N2O) and δ15N(NO+ fragment) on a single ice core sample, using two isotope mass spectrometry systems. The optimum quantity of ice for analysis is about 600 g with typical "Holocene" mixing ratios for CH4 and N2O. In this case, the reproducibility (1σ ) is 2.1‰ for δD(CH4), 0.18‰ for δ13C(CH4), 0.51‰ for δ15N(N2O), 0.69‰ for δ18O(N2O) and 1.12‰ for δ15N(NO+ fragment). For smaller amounts of ice the standard deviation increases, particularly for N2O isotopologues. For both gases, small-scale intercalibrations using air and/or ice samples have been carried out in collaboration with other institutes that are currently involved in isotope measurements of ice core air. Significant differences are shown between the calibration scales, but those offsets are consistent and can therefore be corrected for.

Displaced premolars in panoramic radiography: fact or fallacy?

OBJECTIVE: To test the null hypothesis that there is no difference between premolar position visualized on panoramic radiographs (PRs) and lateral headfilms (LHs). MATERIALS AND METHODS: The prevalence of differences in the direction of crown angulation between PR and LH was assessed. Furthermore, brass wire markers with different sagittal and transverse angulations were placed in a dry skull. With the markers in place, LHs and PRs were taken. RESULTS: A difference in the direction of crown angulation of unerupted second premolars between PR and LH occurred in 19.5% of patients. The reason for the angulation differences is a buccolingual orientation of the tooth, which appears as a mesiodistal angulation on the PR. CONCLUSION: The null hypothesis was rejected since in one-fifth of the patients premolar projection differs between the panoramic radiograph and the lateral headfilm.

Experimental investigation of regular fluids and nanofluids during flow boiling in a single microchannel at different heat fluxes and mass fluxes

The dissipation of high heat flux from integrated circuit chips and the maintenance of acceptable junction temperatures in high powered electronics require advanced cooling technologies. One such technology is two-phase cooling in microchannels under confined flow boiling conditions. In macroscale flow boiling bubbles will nucleate on the channel walls, grow, and depart from the surface. In microscale flow boiling bubbles can fill the channel diameter before the liquid drag force has a chance to sweep them off the channel wall. As a confined bubble elongates in a microchannel, it traps thin liquid films between the heated wall and the vapor core that are subject to large temperature gradients. The thin films evaporate rapidly, sometimes faster than the incoming mass flux can replenish bulk fluid in the microchannel. When the local vapor pressure spike exceeds the inlet pressure, it forces the upstream interface to travel back into the inlet plenum and create flow boiling instabilities. Flow boiling instabilities reduce the temperature at which critical heat flux occurs and create channel dryout. Dryout causes high surface temperatures that can destroy the electronic circuits that use two-phase micro heat exchangers for cooling. Flow boiling instability is characterized by periodic oscillation of flow regimes which induce oscillations in fluid temperature, wall temperatures, pressure drop, and mass flux. When nanofluids are used in flow boiling, the nanoparticles become deposited on the heated surface and change its thermal conductivity, roughness, capillarity, wettability, and nucleation site density. It also affects heat transfer by changing bubble departure diameter, bubble departure frequency, and the evaporation of the micro and macrolayer beneath the growing bubbles. Flow boiling was investigated in this study using degassed, deionized water, and 0.001 vol% aluminum oxide nanofluids in a single rectangular brass microchannel with a hydraulic diameter of 229 µm for one inlet fluid temperature of 63°C and two constant flow rates of 0.41 ml/min and 0.82 ml/min. The power input was adjusted for two average surface temperatures of 103°C and 119°C at each flow rate. High speed images were taken periodically for water and nanofluid flow boiling after durations of 25, 75, and 125 minutes from the start of flow. The change in regime timing revealed the effect of nanoparticle suspension and deposition on the Onset of Nucelate Boiling (ONB) and the Onset of Bubble Elongation (OBE). Cycle duration and bubble frequencies are reported for different nanofluid flow boiling durations. The addition of nanoparticles was found to stabilize bubble nucleation and growth and limit the recession rate of the upstream and downstream interfaces, mitigating the spreading of dry spots and elongating the thin film regions to increase thin film evaporation.

Effect of Impurities upon Current Efficiency in the Electrolysis of Zinc Sulphate Solution

There are many elements which are detrimental to the current efficiency in the electrolysis of zinc sulphate solution. Fortunately the majority of these elements are easily removed in the purification process and cause no further trouble. The elements that are likely to cause trouble in ordinary plant operations are antimony, arsenic, cobalt, nickel, manganese and germanium. The following tests were made to determine the mutual effect on the current efficiency when several of the impurities were present in the electrolyte.

Electrolytic Recovery of Copper and Zinc from Brasses

Reclaimed metals, or secondary metals, are becoming of great im­portance in the metal industries of the world. Secondary metals are an important factor in production. The increase in the secondary production of copper is due to many factors. One of these may be its permenance, that is, the metal does not corrode very readily. Another reason for increase in production is the high price paid for it.

The Theory of Alloy Deposition and The Effect of a Rotating Cathode Upon Such Deposition, with Special Attention to the Possibility of Depositing Sterling Silver

In the past few years a great deal of atten­tion has been given to the electrodeposition of alloys. For the main part, this investigation has been of scien­tific interest only; but in a few instances, such work has attained commercial importance.

Lunch

Music by Highland Symphony Brass

Is differentiation of frequently encountered foreign bodies in corpses possible by Hounsfield density measurement?

The radiological determination of foreign objects in corpses can be difficult if they are fragmented or deformed. With multislice computed tomography, radiodensities--referred to as Hounsfield units (HU)--can be measured. We examined the possibility of differentiating 21 frequently occurring foreign bodies, such as metals, rocks, and different manmade materials by virtue of their HU values. Gold, steel, and brass showed mean HU values of 30671-30710 (upper measurable limit), mean HU values for steel, silver, copper, and limestone were 20346, 16949, 14033, and 2765, respectively. The group consisting of objects, such as aluminum, tarmac, car front-window glass, and other rocks, displayed mean HU values of 2329-2131 HU. The mean HU value of bottle glass and car side-window glass was 2088, whereas windowpane glass was 493. HU value determination may therefore help in preautopsy differentiation between case-relevant and irrelevant foreign bodies and thus be useful for autopsy planning and extraction of the objects in question.

Access technique and its problems in parenteral nutrition - Guidelines on Parenteral Nutrition, Chapter 9

Catheter type, access technique, and the catheter position should be selected considering to the anticipated duration of PN aiming at the lowest complication risks (infectious and non-infectious). Long-term (>7-10 days) parenteral nutrition (PN) requires central venous access whereas for PN <3 weeks percutaneously inserted catheters and for PN >3 weeks subcutaneous tunnelled catheters or port systems are appropriate. CVC (central venous catheter) should be flushed with isotonic NaCl solution before and after PN application and during CVC occlusions. Strict indications are required for central venous access placement and the catheter should be removed as soon as possible if not required any more. Blood samples should not to be taken from the CVC. If catheter infection is suspected, peripheral blood-culture samples and culture samples from each catheter lumen should be taken simultaneously. Removal of the CVC should be carried out immediately if there are pronounced signs of local infection at the insertion site and/or clinical suspicion of catheter-induced sepsis. In case PN is indicated for a short period (max. 7-10 days), a peripheral venous access can be used if no hyperosmolar solutions (>800 mosm/L) or solutions with a high titration acidity or alkalinity are used. A peripheral venous catheter (PVC) can remain in situ for as long as it is clinically required unless there are signs of inflammation at the insertion site.

Removal of fractured endodontic instruments using an Nd:YAG laser.

OBJECTIVE Fractured endodontic instruments inhibit optimal cleaning and filling of dental root canals, which may result in a less favorable prognosis for the tooth. Several techniques are available to remove fractured instruments; however, healthy tooth substance often must be destroyed in the process. This study was intended to evaluate Nd:YAG laser treatment as a method to remove fractured stainless steel instruments without destroying healthy tooth substance. METHOD AND MATERIALS Stainless steel endodontic instruments were fractured in 33 unprocessed root canals of mandibular central and lateral incisors and premolars in vitro. A brass tube charged with solder was placed at the coronal end of the fractured instrument and laser energy was used to melt the solder, connecting the fractured instrument with the brass tube. The success rates of connecting and removal of fractured instruments from the root channel were recorded for each case. RESULTS Connecting was achieved in every case in which more than 1.5 mm of the fractured instrument was tangible (22 out of 22). In cases where less than 1.5 mm was tangible, the rate for successful connection decreased to 4 out of 11 (36.4%). Fractured endodontic instruments were removed successfully in 17 out of 22 cases (77.3%) in which more than 1.5 mm was tangible. If less than 1.5 mm was tangible, the removal success rate decreased to 3 out of 11 cases (27.3%). CONCLUSION Our data support Nd:YAG laser-mediated connecting of a brass tube to a fractured endodontic instrument as a feasible and tissue conserving removal approach when more than 1.5 mm of the instrument is tangible.

Stable oxygen isotope record and benthic foraminiferal abundances in Cretaceous sediments of Demerara Rise

During the mid-Cretaceous period, the global subsurface oceans were relatively warm, but the origins of the high temperatures are debated. One hypothesis suggests that high sea levels and the continental configuration allowed high-salinity waters in low-latitude epicontinental shelf seas to sink and form deep-water masses (Brass et al., 1982, doi:10.1038/296620a0; Arthur and Natland, 1979; Chamberlin, 1906). In another scenario, surface waters in high-latitude regions, the modern area of deep-water formation, were warmed through greenhouse forcing (Bice and Marotzke, 2001, doi:10.1029/2000JC000561), which then propagated through deep-water circulation. Here, we use oxygen isotopes and Mg/Ca ratios from benthic foraminifera to reconstruct intermediate-water conditions in the tropical proto-Atlantic Ocean from 97 to 92 Myr ago. According to our reconstruction, intermediate-water temperatures ranged between 20 and 25 °C, the warmest ever documented for depths of 500-1,000 m. Our record also reveals intervals of high-salinity conditions, which we suggest reflect an influx of saline water derived from epicontinental seas around the tropical proto-North Atlantic Ocean. Although derived from only one site, our data indicate the existence of warm, saline intermediate waters in this silled basin. This combination of warm saline intermediate waters and restricted palaeogeography probably acted as preconditioning factors for the prolonged period of anoxia and black-shale formation in the equatorial proto-North Atlantic Ocean during the Cretaceous period.

Clay mineralogy of sediments from the Bengal Fan

We have measured the relative abundances of smectite, illite, chlorite, and kaolinite in a composite section of the distal Bengal Fan. Two sources of sediment appear to dominate, a smectite-poor, illite-rich source associated with rapid denudation of the Himalayas and a smectite-rich, illite-poor source probably on the continental margin of the Indian sub-continent. Changes in source appear to be related to uplift in the Himalayas and Tibetan Plateau both directly and through the climatic and oceanographic consequences of uplift.