Nanosecond nonlinear absorption in Au and Ag nanoparticles precipitated glasses induced by a femtosecond laser

We obtain Au and Ag nanoparticles precipitated in glasses by irradiation of focused femtosecond pulses, and investigate the nonlinear absorptions of the glasses by using Z-scan technique with ns pulses at 532 nm. We observe the saturable absorption behavior for An nanoparticles precipitated glasses and the reverse saturable ones for Ag ones. We also obtain, by fitting to the experimental results in the light of the local field effect near and away from the surface plasmon resonance, chi(m)((3)) = 4.5 x 10(-7) and 5.9 x 10(-8) esu for m the imaginary parts of the third-order susceptibilities for Au and Ag nanoparticles, respectively. The nonlinear response of Au nanoparticles in the glass samples arises mainly from the hot-electron contribution and the saturation of the interband transitions near the surface plasmon resonance, whereas that of Ag nanoparticles in the glass samples from the interband transitions. These show that the obtained glasses can be used as optoelectronic devices suiting for different demands. (c) 2005 Elsevier B.V. All rights reserved.

A chemically inert Rashba split interface electronic structure of C-60, FeOEP and PTCDA on BiAg2/Ag(111) substrates

The fields of organic electronics and spintronics have the potential to revolutionize the electronics industry. Finding the right materials that can retain their electrical and spin properties when combined is a technological and fundamental challenge. We carry out the study of three archetypal organic molecules in intimate contact with the BiAg2 surface alloy. We show that the BiAg2 alloy is an especially suited substrate due to its inertness as support for molecular films, exhibiting an almost complete absence of substrate-molecular interactions. This is inferred from the persistence of a completely unaltered giant spin-orbit split surface state of the BiAg2 substrate, and from the absence of significant metallic screening of charged molecular levels in the organic layer. Spin-orbit split states in BiAg2 turn out to be far more robust to organic overlayers than previously thought.

The study on the interface adhesion comparison of the MgF2, Al2O3, SiO2 and Ag thin films

Adhesion between the interface of pure silver thin film and three kinds of low refractive index coatings MgF2, Al2O3, SiO2 were compared in this article. The results indicated that the adhesion of Al2O3 and Ag was evidently superior to that of MgF2 and Ag, and the adhesion of MgF2 and Ag was evidently superior to that Of SiO2 and Ag. Reasons were analyzed accordingly. On the other hand, we compared the effect on the optical characteristic of Ag film when these three kinds of films were used as protective coatings and enhanced coatings. Considering the difference of the adhesion between Ag and MgF2, Al2O3, SiO2, suited uses are given for each other. © 2004 Elsevier B.V. All rights reserved.

Influence of Cr interlayer on the structure and optical properties of Ag films on glass substrate by magnetron sputtering

Optical properties and microstructure of Ag film on glass substrate with Cr intermediate layer were studied by using spectrophotometer and XRD. The spectra results showed that introducing Cr intermediate layer reduced the surface roughness and promoted the reflectivity of Ag film. The XRD analysis showed that the crystalline grains increased and the stress decreased. The adhesion was also improved by using the tape test method. (c) 2006 Published by Elsevier B.V.

Effect of alumina and chromium interlayers on microstructures and optical properties of thin Ag films on glass substrates

Effects of alumina and chromium interlayers on the microstructure and optical properties of thin Ag films are investigated by using spectrophotometry, x-ray diffraction and AFM. The characteristics of Ag films in Ag/glass, Ag/Al2O3/glass and Ag/Cr/glass stacks are analysed. The results indicate that the insertion of an Al2O3 or Cr layer decreases the grains and influences the reflectance of Ag films. The reflectance of the Ag film can be increased by controlling the thickness of alumina interlayer. The stability of Ag films is improved and the adhesion of Ag films on glass substrates is enhanced by alumina as an interlayer.