Achieving perpendicular alignment of rigid polythiophene backbones to the substrate by using solvent-vapor treatment

The rigid backbone of the poly(3-butylthiophene) molecule adopts a perpendicular orientation with respect to the substrate by using a solvent-vapor treatment (see figure). Small and closely contacting spherulites instead of conventional whisker-like crystals are achieved. This could be utilized to improve charge-carrier mobility particularly in the direction normal to the film plane by designing and constructing thick crystalline domains in the functional layer.

Study of controllable aggregation morphology of ABA amphiphilic triblock copolymer in dilute solution by changing the solvent property

We have studied, both experimentally and theoretically, the aggregation morphology of the ABA amphiphilic triblock copolymer in dilute solution by changing the solvent property. Experimental results showed that the micellar morphology changed from spheres to rods and then to vesicles by changing the common solvent from N-N-dimethylformamide (DMF) to dioxane and then to tetrahydrofuran (THF). These controllable aggregates were also obtained by Monte Carlo simulation. The simulative results showed that the solvent property is a key factor that determines the copolymer aggregation morphology. The morphology changed from spheres to rods and then to vesicles by increasing the solvent solubility, corresponding to the change of stretched of the copolymer chains in the micellar cores. This result is in good agreement with the experimental one. Moreover, the simulative results revealed that the end-to-end distant of the ABA triblock copolymer in the vesicle was larger than that in the spheres and rods, indicating that the copolymer chains were more stretched in vesicles than in the spheres and rods. Furthermore, we gave the distribution of the fraction of the chain number with the end-to-end distance. The results indicated that the amount of folded chains is almost the same as that of stretched chains in the vesicle. Although most chains were folded, stretched chains could be found in the rod and sphere micelles.

A reversibly tunable colloidal photonic crystal via the infiltrated solvent liquid-solid phase transition

A reversibly tunable colloidal photonic crystal between two stop bands was realized by a liquid-solid phase transition of liquid infiltrated into the air voids of silica opals. The difference of the peak wavelengths of the two stop bands was dependent on the diameter of the silica opals and the difference of the refractive index of the filled solvent between the solid and liquid state. The reversibly tunable photonic crystals have good stability and reproducibility.

Development of nanodomain and fractal morphologies in solvent annealed block copolymer thin films

We have systematically studied the thin film morphologies of asymmetric polystyrene-block-poly(ethylene oxide) (PS-b-PEO) diblock copolymer subjected to solvent vapors of varying selectivity for the constituent blocks. Upon a short treatment in neutral or PS-selective vapor, the film exhibited a highly ordered array of hexagonally packed, cylindrical microdomains. In the case of PEO selective vapor annealing, such ordered cylindrical microdomains were not obtained. instead, fractal patterns on the microscale were observed and their growth processes investigated. Furthermore, hierarchical structures could be obtained if the fractal pattern was exposed to neutral or PS selective vapor.

Dewetting of polymethyl methacrylate on the patterned elastomer substrate by solvent vapor treatment

The dewetting evolution process of polymethyl methacrylate (PMMA) film on the flat and prepatterned polydimethylsiloxane (PDMS) substrates (with square microwells) by the saturated solvent of methyl ethyl ketone (MEK) treatment has been investigated at room temperature by the optical microscope (OM) and atomic force microscope (AFM). The final dewetting on the flat PDMS substrate led to polygonal liquid droplets, similar to that by temperature annealing. However, on the patterned PDMS substrate, depending on the microwells' structure of PDMS substrate and defect positions that initiated the rupture and dewetting of PMMA, two different kinds of dewetting phenomena, one initiated around the edge of the microwells and another initiated outside the microwells, were observed. The forming mechanism of these two different dewetting phenomena has been discussed. The microwells were filled with liquid droplets of PMMA after dewetting due to the formation of fingers caused by the pinning of the three-phase-line at the edge of the microwells and their rupture.

Solvent extraction of lanthanides and yttrium from nitrate medium with CYANEX 925 in heptane

The extraction behavior of lanthanides and yttrium usinsg CYANEX 925 (mixture of branched chain alkylated phosphine oxides) in n-heptane from nitrate medium has been studied. The effects of aqueous phase ionic strength, CYANEX 925 concentration in the organic phase, and temperature on Sm3+, Nd3+ and Y3+ extraction have been investigated. The extractability of the lanthanides and yttrium increases with increasing nitrate concentration, as well as with increasing CYANEX 925 concentration. An extraction mechanism is proposed based on slope analysis. Furthermore, the infra-red spectra of CYANEX 925 saturated with lanthanides are employed to provide evidence of the composition of the complex. The relationship between the logarithm of the distribution ratio and lanthanide atomic number is also discussed which indicates that yttrium can be separated from fight lanthanides. In addition separation of the light and heavy lanthanide groups is also possible using CYANEX 925. From the temperature dependence data, the thermodynamic parameters values (Delta H, Delta S and Delta G) are calculated.

Formation of nonextinct ring-banded textures and multistacked lamella of tetra-aniline-block-poly(L-lactide) rod-coil diblock oligomer films induced by solvent vapor treatment

The self-assembly processes of the rod-coil diblock oligomer thin film of tetra-aniline (TANI)-block-poly(L-lactide) (PLLA) with different film thicknesses induced in the coil-selective solvent of acetone vapor at room temperature were studied. The morphologies of the oligomer films were determined by the film thickness. For the thicker film (232 nm), the nonextinct concentric ring-banded textures could form. While for the thinner and appropriate film (about 6 nm), multistacked diamond-shaped appearances with the periodic thickness being about 8.5 nm(6-nm-thick extended PLLA chain and 2.5-nm-thick p-pi conjugating TANI bimolecular layer) formed. The possible formation models of those two regular morphologies were presented in detail.

Effects of molecular weight, solvent and substrate on the dewetting morphology of polystyrene films

Surface morphology of polystyrene (PS) films on different substrates by spin-coating before and after annealing was observed using atomic force microscopy (AFM). The effects of polymer molecular weight, substrates, solvents, and annealing conditions on the morphology of the films were investigated. Before annealing, the grain height decreases, and simultaneously the grain diameter increases with molecular weight (M-w) within the measured molecular weight. After annealing. the situation is opposite, i.e., the grain height increases while the grain diameter decreases with M-w. Furthermore, after annealing the smaller surface roughness (Ra) was obtained. It was also found that film surface roughness (Ra) depends on the vapor pressure and dipole moment of different used solvents as well as the substrates. The experimental results show that when the used solvents have similar dipole moment but different vapor pressure, the Ra of PS film decreased with the decreasing vapor pressure of solvents whether on silicon or on mica. And when the used solvents have close vapor pressure but different dipole moment, the Ra decreased with the increasing of solvent dipole moments on both substrates.

Morphology development of ultrathin symmetric diblock copolymer film via solvent vapor treatment

We have followed the time development of the microdomain structure in symmetric diblock copolymer poly(styrene-b-methyl methacrylate), P(S-b-MMA), ultrathin films via PMMA-selective solvent vapor treatment by atomic force microscopy (AFM). After preparation on a substrate preferentially attracting the PMMA block, PS forms a continuous layer at a film's free surface. With subsequent solvent vapor treatment, the film gradually shows a well-ordered hexagonally packed nanocylinders structure. It is shown that only when the film thickness is less than the 1/2L(0) (lamellar repeat spacing), and exposed to PMMA block selective solvent for an appropriate time, can the well-ordered hexagonally packed nanocylinders form. On an extended solvent vapor treatment, a mixed morphology containing nanocylinders and stripes appears, followed by the striped morphologies. When the annealing time is long enough, the film comes back to the flat surface again, however, with PMMA instead of PS dominating the free surface.

Copolymers derived from bismaleimide oligomer with active solvent

An oligomer from 4, 4'-bis(maleimido)diphenyl methane and methylenedianiline were dissolved in active solvent N,N-dimethyl acrylamide in a solid content up to 50-70%; the solution was poured in a sheet-shaped module and irradiated b y Co-60 with the dose from 20 to 350 kGy at room temperature. The polymerized sheet was postcured at 180degreesC to obtain a transparent red-orange sheet with tensile strength above 100 MPa. The glass transition temperature before and after postcuring was around 100degreesC and 150-180degreesC, respectively. Styrene was used along with DMAA to decrease the water absorption for the copolymers.

Morphology and structure of poly(di-n-butylsilane) single crystals prepared by controlling kinetic process of solvent evaporation

The silicon backbone conformation in poly(di-n-butylsilane) (PDBS) has been shown to be a 7/3 helix at ambient conditions, which is in marked contrast to the near-planar conformation of its homologous polymers with side chain lengths of one to three or six to eight carbon atoms. In this work, both the 7/3 helical and near-planar chain conformations are achieved by controlling the solvent evaporation rate around room temperature. The chain conformation and crystal structure obtained in this method have been correlated to the crystal morphology by wide-angle X-ray diffraction, transmission electron microscopy, electron diffraction, optical microscopy, atomic force microscopy, and UV absorption spectrum. The lath-shaped single crystals obtained at 12 degreesC correspond to an orthorhombic form with near-planar chain conformation whereas the lozenge-shaped single crystals obtained at 30 degreesC (in coexistence with the lath-shaped crystals) are orthohexagonal with a 7/3 helix.

Solvent-induced microphase separation in diblock copolymer thin films with reversibly switchable morphology

We have studied the surface morphology of symmetric poly(styrene)-block-poly(methyl methacrylate) diblock copolymer thin films after solvent vapor treatment selective for poly(methyl methacrylate). Highly ordered nanoscale depressions or striped morphologies are obtained by varying the solvent annealing time. The resulting nanostructured films turn out to be sensitive to the surrounding medium, that is, their morphologies and surface properties can be reversibly switchable upon exposure to different block-selective solvents.

Ionic liquid solvent based on cyclic guanidinium cation for nucleophilic displacement reactions

The nucleophilic displacement reaction of n-bromooctane and potassium iodide in ionic liquid based on cyclic guanidinium cation(2) was investigated. The kinetic reasult shows that the rate of the reaction is enhanced in ionic liquid (2). The same reaction in [bmim][PF6](1)(where bmim = 1-butyl-3-methylimidazolium) was also studied. It was found that as a reaction medium ionic liquid (2) is better than (1) for nucelophilic displacement reactions.