Analyse titanium surface irradiated with laser, with and without deposited of durapatite

OBJETIVO: Estudar a superfície de implantes osseointegráveis utilizando discos de titânio irradiados com feixe de laser. MÉTODOS: A amostra foi irradiada com feixes de laser de alta intensidade (Nd-YAG), posteriormente depositado hidróxiapatita e submetido a tratamento térmico. Foi analisada sob MEV (Microscópio Eletrônico de Varredura) e realizada análise morfológica qualitativa com microfotografias em vários aumentos. RESULTADOS: A superfície irradiada com laser apresentou deformidade superficial e característica isomórfica; a aplicação de hidroxiapatita pelo método de biomimético aumentou quantitativamente a área da superfície de titânio. CONCLUSÃO: A deposição de hidroxiapatita apresentou melhor característica isomórfica e aumento quantitativo da área superficial estudada, a amostra demonstrou características não encontradas nos implantes disposto no mercado.

Surface and Biomechanical Study of Titanium Implants Modified by Laser With and Without Hydroxyapatite Coating, in Rabbits

Surface and biomechanical analysis of titanium implant surfaces modified by laser beam with and without hydroxyapatite. Titanium implants with 3 different surfaces were inserted into the tibias of 30 rabbits: group I (GI) machined surface (control group), group II irradiated with laser (GII), and group III irradiated with laser and hydroxyapatite coating applied-biomimetic method (GIII). Topographical analysis with scanning electron microscopy was made before surgery in the tibia. These rabbits were distributed into 2 periods of observation: 4 and 8 weeks postsurgery, after which biomechanical analysis (removal torque) was conducted. Statistical analysis used the Student-Newman-Keuls method. Surface showed roughness in GII and GIII. Biomechanical analysis demonstrated values with significant differences in GII and GIII. Titanium implants modified by laser irradiation can increase osseointegration during the initial phase.

Increased Viability of Odontoblast-Like Cells Subjected to Low-Level Laser Irradiation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Er : YAG and diode laser irradiation on the root surface: Morphological and thermal analysis

Background: the aim of the present study was to compare the effects of Er:YAG and diode laser treatments of the root surface on intrapulpal temperature after scaling and root planing with hand instruments.Methods: Fifteen extracted single-rooted teeth were scaled and root planed with hand instruments. The teeth were divided into 3 groups of 5 each and irradiated on their buccal and lingual surfaces: group A: Er:YAG laser, 2.94 mum/100 mJ/10 Hz/ 30 seconds; group B: diode laser, 810 nm/1.0 W/0.05 ms/30 seconds; group C: diode laser, 810 nm/1.4 W/0.05 ms/30 seconds. The temperature was monitored by means of a type T thermocouple (copper-constantan) positioned in the pulp chamber to assess pulpal temperature during and before irradiation. Afterwards, the specimens were longitudinally sectioned, and the buccal and lingual surfaces of each root were analyzed by scanning electron microscopy.Results: In the Er:YAG laser group, the thermal analysis revealed an average temperature of -2.2 +/- 1.5degreesC, while in the diode laser groups, temperatures were 1.6 +/- 0.8degreesC at 1.0 W and 3.3 +/- 1.0degreesC at 1.4 W. Electronic micrographs revealed that there were no significant morphological changes, such as charring, melting, or fusion, in any group, although the specimens were found to be more irregular in the Er:YAG laser group.Conclusions: the application of Er:YAG and diode lasers at the utilized parameters did not induce high pulpal temperatures. Root surface irregularities were more pronounced after irradiation with an Er:YAG laser than with a diode laser.

Effect of Er,Cr:YSGG and Er:YAG laser irradiation on the adhesion of blood components on the root surface and on root morphology

The aim of this study was to conduct an in vitro evaluation, by scanning electron microscopy (SEM), of the adhesion of blood components on root surfaces irradiated with Er,Cr:YSGG (2.78 mu m) or Er:YAG (2.94 mu m) laser, and of the irradiation effects on root surface morphology. Sixty samples of human teeth were previously scaled with manual instruments and divided into three groups of 20 samples each: G1 (control group) - no treatment; G2 - Er,Cr:YSGG laser irradiation; G3 - Er:YAG laser irradiation. After performing these treatments, blood tissue was applied to 10 samples of each group, whereas 10 samples received no blood tissue application. After performing the laboratory treatments, the samples were observed under SEM, and the resulting photomicrographs were classified according to a blood component adhesion scoring system and root morphology. The results were analyzed statistically (Kruskall-Wallis and Mann Whitney tests, alpha = 5%). The root surfaces irradiated with Er:YAG and Er,Cr:YSGG lasers presented greater roughness than those in the control group. Regarding blood component adhesion, the results showed a lower degree of adhesion in G2 than in G1 and G3 (G1 x G2: p = 0.002; G3 x G2: p = 0.017). The Er:YAG and Er,Cr:YSGG laser treatments caused more extensive root surface changes. The Er:YAG laser treatment promoted a greater degree of blood component adhesion to root surfaces, compared to the Er,Cr:YSGG treatment.

Effects of Er,Cr:YSGG Laser Irradiation on Root Surfaces for Adhesion of Blood Components and Morphology

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Adhesion strength characterization of PVDF/HA coating on cp Ti surface modified by laser beam irradiation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effects of laser-weld joint opening size on fatigue strength of Ti-6Al-4V structures with several diameters

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of Ultrasonic and ErCr:YSGG Laser Retrograde Cavity Preparation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS).Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM).Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM.Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.

Influence of prior 810-nm-diode intracanal laser irradiation on hydrophilic resin-based sealer obturation

Dentin wall structural changes caused by 810-nm-diode laser irradiation can influence the sealing ability of endodontic sealers. The objective of this study was to evaluate the apical leakage of AH Plus and RealSeal resin-based sealers with and without prior diode laser irradiation. Fifty-two single-rooted mandibular premolars were prepared and divided into 4 groups, according to the endodontic sealer used and the use or non-use of laser irradiation. The protocol for laser irradiation was 2.5W, continuous wave in scanning mode, with 4 exposures per tooth. After sample preparation, apical leakage of 50% ammoniacal silver nitrate impregnation was analyzed. When the teeth were not exposed to irradiation, the Real Seal sealer achieved the highest scores, showing the least leakage, with significant differences at the 5% level (Kruskal-Wallis test, p = 0.0004), compared with AH Plus. When the teeth were exposed to the 810-nm-diode laser irradiation, the sealing ability of AH Plus sealer was improved (p = 0282). In the Real Seal groups, the intracanal laser irradiation did not interfere with the leakage index, showing similar results in the GRS and GRSd groups (p = 0.1009).

Confocal Laser Microscopic Analysis of Biofilm on Newer Feldspar Ceramic

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Dentin bond strength: Influence of laser irradiation, acid etching, and hypermineralization

Objective: the purpose of the present study was to investigate the effects of ND:YLF laser irradiation (1.31 J/cm(2); 250 mJ per pulse), acid etching, and hypermineralization on the shear bond strength (SBS) of the Scotchbond Multi-Purpose Plus (3M Dental Products) bonding system. Summary Background Data: Previous studies had shown that the pretreatment of the dentin substrate with laser irradiation can influence the SBS, Methods: Sixty bovine incisors were selected and stored at -18 degrees C, Dentinal buccal surface was exposed and radiographs were taken to control dentin thickness, the specimens were separated into 2 groups: (1) the control, which was kept in distilled water at 4 degrees C; (2) the hypermineralized, which was kept in hypermineralizing solution at 4 degrees C for 14 days, Each group was divided into 3 subgroups according to the type of dentin pretreatment used: M (acid etching + primer + bond); AL (acid etching + primer + bond + laser); and LA (laser + acid etching + primer + bond). A standard composite resin cylinder (Z100-3M) was bonded to the dentinal surface and the SBS performed on an Instron machine (500 Kg load cell at 0.5 mm/min), followed by scanning electron microscopy (SEM) and x-ray diffraction analysis. Results: Analysis of variance (ANOVA) determined that the pretreatments influenced the SBS values (p < 0.05): AL (9.96 MPa), M (7.28 MPa), and LA (4.87 MPa), the interaction between the group and pretreatment factors also influenced the SBS (p < 0.05). The highest values were obtained for the interaction control/AL (11.64 MPa), Conclusion: the results suggested that dentin treatment with laser after the application of the adhesive system is efficient in achieving higher bond strength and is promising as a possible new adhesive substrate.

Hydroxyapatite deposition study through polymeric process on commercially pure Ti surfaces modified by laser beam irradiation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Investigação da Interface Metal-Porcelana da Liga Ni-Cr-Mo Soldada a LASER

The interface formed between the metal and the porcelain of a LASER welded Ni-Cr-Mo alloy was studied. The characterization was carried out through optical microscopy, scanning electron microscopy, X-ray dispersive spectroscopy-EDS and mechanical testing by three-point flexion test-TPE in the region LASER welded with and without the porcelain. The porcelain adhesion with the alloy alone is possible after the oxidation of the metallic surface and subsequent application of an adhesive called opaco. The applied porcelain, on the base metal and fusion zone presented some distinct behaviors. After the TPF test the base metal presented fractures while that in the fusion zone was completely gone. One noticed that the region submitted to the LASER welding showed less porcelain adhesion than the region of the base metal due to the microestructural refinement of the fusion zone. These results can be evidenced by the EDS of the studied regions. The TPF had demonstrated that the Ni-Cr-Mo alloy submitted to the LASER welding, undergone significant alterations in its mechanical properties after the application of the porcelain.