Bonding Efficacy of New Self-etching, Self-adhesive Dual-curing Resin Cements to Dental Enamel

Purpose: This study evaluated the efficacy of the union between two new self-etching self-adhesive resin cements and enamel using the microtensile bond strength test.Materials and Methods: Buccal enamel of 80 bovine teeth was submitted to finishing and polishing with metallographic paper to a refinement of #600, in order to obtain a 5-mm(2) flat area. Blocks (2 x 4 x 4 mm) of laboratory composite resin were cemented to enamel according to different protocols: (1) untreated enamel + RelyX Unicem cement (RX group); (2) untreated enamel + Bifix SE cement (BF group); (3) enamel acid etching and application of resin adhesive Single Bond + RelyX Unicem (RXA group); (4) enamel acid etching and application of resin adhesive Solobond M + Bifix SE (BFA group). After 7 days of storage in distillated water at 37 degrees C, the blocks were sectioned for obtaining microbar specimens with an adhesive area of 1 mm(2) (n = 120). Specimens were submitted to the microtensile bond strength test at a crosshead speed of 0.5 mm/min. The results (in MPa) were analyzed statistically by ANOVA and Tu key's test.Results: Enamel pre-treatment with phosphoric acid and resin adhesive (27.9 and 30.3 for RXA and BFA groups) significantly improved (p <= 0.05) the adhesion of both cements to enamel compared to the union achieved with as-polished enamel (9.9 and 6.0 for RX and BF).Conclusion: Enamel pre-treatment with acid etching and the application of resin adhesive significantly improved the bond efficacy of both luting agents compared to the union achieved with as-polished enamel.

Structural characterization of phase transition of Al2O3 nanopowders obtained by polymeric precursor method

Nanocrystalline Al(2)O(3)powders have been synthesized by the polymeric precursor method. A study of the evolution of crystalline phases of obtained powders was accomplished through X-ray diffraction, micro-Raman spectroscopy and refinement of the structures through the Rietveld method. The results obtained allow the identification of three steps on the gamma-Al2O3 to alpha-Al2O3 phase transition. The single-phase alpha-Al2O3 Powder was obtained after heat-treatment at 1050 degrees C for 2 h. A study of the morphology of the particles was accomplished through measures of crystallite size, specific surface area and transmission electronic microscopy. The particle size is closely related to gamma-Al2O3 to alpha-Al2O3 phase transition. (c) 2007 Elsevier B.V. All rights reserved.

Theoretical analysis of the structural deformation in Mn-doped BaTiO3

An alternative theoretical method to simulate the structural deformation induced by Mn-doping in BaTiO3 is proposed. The periodic quantum-mechanical method is based on density functional theory at B3LYP level. The structural models were obtained from Rietveld refinement of the undoped and Mn doped BaTiO3 X-ray diffraction data. This modelization gives access to the dopant General effect on the electronic structure. In fact, the influence of the doing element itself on the electronic configuration is barely local: therefore, it is not included in the simulation. The simplicity of the model makes it available for working within a wide range of materials.(C) 2004 Published bv Elsevier B.V.

Thermal decomposition of crystalline Ni-II-Cr-III layered double hydroxide: A structural study of the segregation process

A structural study of the thermal evolution of Ni0.69Cr0.31(OH)(2)(CO3)(0.155)(.)nH(2)O into NiO and tetragonal NiCr2O4 is reported. The characteristic structural parameters of the two coexisting crystalline phases, as well as their relative abundance, were determined by Rietveld refinement of powder x-ray diffraction (PXRD) patterns. The results of the simulations allowed us to elucidate the mechanism of the demixing process of the oxides. It is demonstrated that nucleation of a metastable nickel chromite within the common oxygen framework of the parent Cr-III-doped bunsenite is the initial step of the cationic redistribution. The role that trivalent cations play in the segregation of crystalline spinels is also discussed.

Rapid spot test analysis for the detection of urotropine in pharmaceutical preparations

The widespread falsification and/or adulteration of commercially available pharmaceutical preparations call for reliable methods of drug identification, preferably through selective and rapid sorting color tests that could be undertaken with minimum equipment remote from laboratory facilities. The present work deals with a convenient adaptation and refinement of a spot test devised by Feigl (1966) for urotropine, based on the hydrolytic cleavage of that substance in the presence of sulfuric acid, splitting out formaldehyde which is identified by its color reaction with chromotropic acid. A simple emergency kit was developed for the quick, efficient, inexpensive and easy performance of urotropine tests by semiskilled personnel even in the drugstore laboratory (or office) as well as in a mobile screening operation. It is shown that when the reagents are added according to the recommended sequence a self-heating system is generated, increasing substantially the reactions' rates and the test sensitivity as well. The identification limit found was 25 mug of urotropine, for both solid and liquid samples. The possible interference of 84 substances/materials was investigated. Interference was noted only for methylene blue, acriflavine, Ponceau Red, Bordeaux Red (these dyes are often included in urotropine dosage forms), pyramidone, dipyrone, quinine and tetracycline. A simple procedure for removing most of the interferences is described. Data for 8 commercial dosage forms and results obtained from their analysis are presented.

Assessment of maturity degree of composts from domestic solid wastes by fluorescence and fourier transform infrared spectroscopies

Methods of assessment of compost maturity are needed so the application of composted materials to lands will provide optimal benefits. The aim of the present paper is to assess the maturity reached by composts from domestic solid wastes (DSW) prepared under periodic and permanent aeration systems and sampled at different composting time, by means of excitation-emission matrix (EEM) fluorescence spectroscopy and Fourier transform infrared spectroscopy (FT-IR). EEM spectra indicated the presence of two different fluorophores centered, respectively, at Ex/Em wavelength pairs of 330/425 and 280/330 nm. The fluorescence intensities of these peaks were also analyzed, showing trends related to the maturity of composts. The contour density of EEM maps appeared to be strongly reduced with composting days. After 30 and 45 days of composting, FT-IR spectra exhibited a decrease of intensity of peaks assigned to polysaccharides and in the aliphatic region. EEM and FT-IR techniques seem to produce spectra that correlate with the degree of maturity of the compost. Further refinement of these techniques should provide a relatively rapid method of assessing the suitability of the compost to land application.

Photoluminescence of crystalline and disordered BTO : Mn powder: Experimental and theoretical modeling

Disordered and crystalline Mn-doped BaTiO3 (BTO:Mn) powders were synthesized by the polymeric precursor method. After heat treatment, the nature of visible photoluminescence (PL) at room temperature in amorphous BTO:Mn was discussed, considering results of experimental and theoretical studies. X-ray diffraction (XRD), PL, and UV-vis were used to characterize this material. Rietveld refinement of the BTO:Mn from XRD data was used to built two models, which represent the crystalline BTO:Mn (BTO:Mn,) and disordered BTO:Mn (BTO:Mn-d) structures. Theses models were analyzed by the periodic ab initio quantum mechanical calculations using the CRYSTAL98 package within the framework of density functional theory at the B3LYP level. The experimental and theoretical results indicated that PL is related with the degree of disorder in the BTO:Mn powders and also suggests the presence of localized states in the disordered structure. (c) 2006 Elsevier B.V. All rights reserved.

Effect of PbO excess on the formation of lead magnesium niobate perovskite by the columbite method

The effect of lead excess on the pyrochlore-type formation in Pb(Mg1/3Nb2/3)O-3 (PMN) powders has been investigated. The polymeric precursor method was used in the synthesis of the columbite in association to the partial oxalate method to synthesize the PMN powder samples. Structure refinement of the columbite precursor and PMN powders was carried out using the Rietveld method. The quantitative phase analysis showed that the amount of perovskite phase is not affected by PbO excess, but a great excess drives the pyrochlore-type formation so that 3 wt.% of PbO causes the predominance of Mg-containing pyrochlore phase. Using the refined data obtained from the Rietveld refinement, the compositional fluctuation in the perovskite phase was calculated from Nb/Mg ratio values and Pb occupation factor. Mg inclusion occurs concomitant with Ph one into PMN perovskite phase and this effect is directed by PbO excess during powder synthesis. (C) 2003 Elsevier B.V. All rights reserved.

Thermal analysis applied in the crystallization study of SrSnO3

SrSnO3 was synthesized by the polymeric precursor method with elimination of carbon in oxygen atmosphere at 250 A degrees C for 24 h. The powder precursors were characterized by TG/DTA and high temperature X-ray diffraction (HTXRD). After calcination at 500, 600 and 700 A degrees C for 2 h, samples were evaluated by X-ray diffraction (XRD), infrared spectroscopy (IR) and Rietveld refinement of the XRD patterns for samples calcined at 900, 1,000 and 1,100 A degrees C. During thermal treatment of the powder precursor ester combustion was followed by carbonate decomposition and perovskite crystallization. No phase transition was observed as usually presented in literature for SrSnO3 that had only a rearrangement of SnO6 polyhedra.

Analysis of diametrical wear of grinding wheel and roundness errors in the machining of steel VC 131

Due to the high industrial competitiveness, the rigorous laws of environmental protection, the necessary reduction of costs, the mechanical industry sees itself forced to worry more and more with the refinement of your processes and products. In this context, can be mentioned the need to eliminate the roundness errors that appear after the grinding process. This work has the objective of verifying if optimized nozzles for the application of cutting fluid in the grinding process can minimize the formation of the roundness errors and the diametrical wear of grinding wheel in the machining of the steel VC 131 with 60 HRc, when compared to the conventional nozzles. These nozzles were analyzed using two types of grinding wheels and two different cutting fluids. Was verified that the nozzle of 3mm of diameter, integral oil and the CBN grinding wheel, were the best options to obtain smaller roundness errors and the lowest diametrical wears of grinding wheels.

Synthesis and crystal phase evaluation of hydroxylapatite using the rietveld-maximum entropy method

Bioceramic systems based on hydroxylapatite (HAP) are an important class of bioactive materials that may promote bone regeneration. The aim of this research was to evaluate how the stoichiometry of HAP influences its microstructural properties when diagnosed using the combined Rietveld method and Maximum entropy method (MEM). The Rietveld Method (RM) is recognizably a powerful tool used to obtain structural and microstructural information of polycrystalline samples analyzed by x-ray diffraction. Latterly have combined the RM with the maximum entropy method (MEM), with the goal of improve structural refinement results. The MEM provides high resolution maps of electron density and their analysis leave the accurate localization of atoms inside of unit cell. Like that, cycles Rietveld-MEM allow an excellent structural refinement In this work, a hydroxylapatite sample obtained by emulsion method had its structure refined using one cycle Rietveld-MEM with x-ray diffraction data. The indices obtained in initial refinement was Rwp = 7.50%, Re = 6.56%, S - 1.14% e RB = 1.03%. After MEM refinement and electron densities maps analysis to correction of atomics positions, the news indicators of Rietveld refinement quality was Rwp = 7.35%, Re = 6.56%, S = 1.12% and RB = 0.75%. The excellent result obtained to RB shows the efficiency of MEM as auxiliary in the refinement of structure of hydroxylapatite by RM.

Investigation of the metal/porcelain interface in LASER-welded Ni-Cr-Mo alloy

The interface formed between the metal and the porcelain of laser-welded Ni-Cr-Mo alloy was studied on a metallurgical basis. The characterization was carried out by using optical microscope, electron scan microscopy and X-ray dispersive spectroscopy techniques and mechanical three-point flexion tests, in the laser-welded region, with and without porcelain. The union of the porcelain with the alloy is possible only after the oxidation of the metallic surface and the subsequent application of a bonding agent known as opaque. The porcelain applied to the base metal and weld bead showed different behaviours - after the flexion test, the base metal showed cracks, while that in the weld bead broke away completely. It was noted that the region subjected to laser welding had lower adherence to the porcelain than the base metal region, due to microstructural refinement of the weld bead. These results can be shown by the X-ray dispersive spectroscopy carried out on the regions studied. The flexion tests demonstrated that the Ni-Cr-Mo alloy subject to laser welding had significant alterations in its mechanical properties after application of the porcelain.

Strontium isotope stratigraphy of the Pelotas Basin

Dados da razão isotópica de estrôncio foram obtidos a partir da análise de conchas de foraminíferos recuperadas dos depósitos terciários da Bacia de Pelotas visando o refinamento do arcabouço cronoestratigráfico dessa seção. Este artigo representa a primeira abordagem à obtenção de idades numéricas para esses estratos. A estratigrafia de isótopos de estrôncio permitiu a identificação de oito hiatos deposicionais na seção Eoceno-Plioceno, aqui classificados como desconformidade, além de uma seção condensada. O reconhecimento de hiatos deposicionais representa um importante avanço, considerando a baixa resolução cronoestratigráfica da seção cenozóica da Bacia de Pelotas. Além disso, foi identificado um substancial aumento na taxa de sedimentação na seção neomiocênica. Tendências gerais de paleotemperatura e produtividade foram identificadas com base em dados das razões isotópicas de oxigênio e carbono da seção Oligoceno-Mioceno. Essas tendências são coerentes com eventos globais, evidenciando as condições ambientais durante a sedimentação.

Phase transitions and interface phenomena in the cryogenic temperature domain of a niobate nanostructured ceramic

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Photodegradation of phenol red on a Ni-doped niobate/carbon composite

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)