The ω Phase Formation during Laser Cladding and Remelting of Quasicrystal Forming AlCuFe on Pure Aluminum

We report the formation ω phase in the remelted layers during laser cladding and remelting of quasicrystal forming Al65Cu23.3Fe11.7 alloy on pure aluminum. The ω phase is absent in the clad layers. In the remelted layer, the phase nucleates at the periphery of the primary icosahedral phase particles. A large number of ω phase particles forms enveloping the icosahedral phase growing into aluminum rich melt, which solidify as α-Al solid solution. On the other side it develops an interface with aluminum. A detailed transmission electron microscopic analysis shows that ω phase exhibits orientation relationship with icosahedral phase. The composition analysis performed using energy dispersive x-ray analyzer suggests that this phase has composition higher aluminum than the icosahedral phase. The analysis of the available phase diagram information indicates that the present results represent large departure from equilibrium conditions. A possible scenario of the evolution of the ω phase has been suggested.

Determination of solid fraction evolution during solidification of aluminum alloy in presence of linear electromagnetic stirring

In many industrial casting processes, knowledge of the solid fraction evolution during the solidification process is a key factor in determining the process parameters such as cooling rate, stirring intensity and in estimating the total solidification time. In the present work, a new method of estimating solid fraction is presented, which is based on calorimetric principles. In this method, the cooling curve data at each point in the melt, along with the thermal boundary conditions, are used to perform energy balance in the mould, from which solid fraction generation during any time interval can be estimated. This method is applied to the case of a rheocasting process, in which Al-Si alloy (A356 alloy) is solidified by stirring in a cylindrical mould placed in the annulus of a linear electromagnetic stirrer. The metal in the mould is simultaneously cooled and stirred to produce a cylindrical billet with non-dendritic globular microstructure. Temperature is measured at key locations in the mould to assess the various heat exchange processes prevalent in the mould and to monitor the solidification rate. The results obtained by energy balance method are compared with those by the conventional procedure of calculating solid fraction using the Schiel equation.

The effect of host glass on optical absorption and fluorescence of Nd3+ in xNa(2)O-(30-x)K2O-70B(2)O(3) glasses

The effect of host glass composition on the optical absorption and fluorescence spectra of Nd3+ has been studied in mixed alkali borate glasses of the type xNa(2)O-(30-x)K2O-69.5B(2)O(3)-0.5Nd(2)O(3) (X = 5,10,15,20 and 25). Various spectroscopic parameters such as Racah (E-1, E-2 and E-3), spin-orbit (xi(4f)) and configuration interaction (alpha, beta) parameters have been calculated. The Judd-Ofelt intensity parameters (Omega(lambda)) have been calculated and the radiative transition probabilities (A(rad)), radiative lifetimes (tau(r)), branching ratios (beta) and integrated absorption cross sections (Sigma) have been obtained for certain excited states of the Nd3+, ion and are discussed with respect to x. From the fluorescence spectra, the effective fluorescence line widths (Deltalambda(eff)) and stimulated emission cross sections (sigma(p)) have been obtained for the three transitions F-4(3/2) --> I-4(9/2), F-4(3/2) --> I-4(11/2) and F-4(3/2) --> I-4(13/2) of Nd3+. The stimulated emission cross section (sigma(p)) values are found to be in the range (2.0-4.8) x 10(-2)0 cm(2) and they are large enough to indicate that the mixed alkali borate glasses could be potential laser host materials.

Direct Infrared Absorption Spectroscopy of Benzene Dimer

The direct infrared (IR) absorption spectrum of benzene dimer formed in a free-jet expansion was recorded in the 3.3 mu m region for the first time. This has led to the observation of the C H stretching fundamental mode nu(13) (B(1u)), which is both IR and Raman forbidden in the monomer. Moreover, the IR forbidden and Raman allowed nu(7) (E(2g)) mode has been observed as well. These two modes were found to be red-shifted along with the IR allowed nu(20) (E(1u)) mode, as previously reported by Erlekam et al. [Erlekam; Frankowski; Meijer; Gert von Helden J. Chem. Phys. 2006, 124, 171101], using ion-dip spectroscopy, contrary to the blue-shift predicted earlier by theoretical studies. The observation of the nu(13) band indicates that the symmetry is reduced in the dimer, confirming the T-shaped structure observed by Erlekam et al. Our experimental results have not provided any direct evidence for the presence of the parallel displaced geometry, the main objective of the present work, as predicted by theoretical calculations.

Temperature dependence of the energy gap and free carrier absorption in bulk InAs0.05Sb0.95 single crystals

Temperature dependence of the energy gap and free carrier absorption in a high-quality InAs0.05Sb0.95 single crystal was studied between 90 K and 430 K through the absorption spectra. At this alloy concentration, the room-temperature energy gap was measured to be 0.15 eV. Varshni- and the Bose–Einstein-type fit parameters were obtained from the measured temperature dependence of the energy gap, and the latter gave the zero-temperature gap to be 0.214 eV. It was found that although Weider’s empirical formula for the dependence of the energy gap on temperature and the alloy concentration agrees with the value of the gap at room temperature, it is inaccurate in describing its temperature dependence. From the free carrier absorption measurements, the phonon limited cross section of 7.35×10−16 cm2 at 15 μm was deduced at room temperature.

Alloying induced degradation of the absorption edge of InAsxSb1-x

InAsxSb1−x alloys show a strong bowing in the energy gap, the energy gap of the alloy can be less than the gap of the two parent compounds. The authors demonstrate that a consequence of this alloying is a systematic degradation in the sharpness of the absorption edge. The alloy disorder induced band-tail (Urbach tail) characteristics are quantitatively studied for InAs0.05Sb0.95.

Multiphoton absorption in CsLiB6O10 with femtosecond infrared laser pulses

Nonlinear absorption and refraction characteristics of cesium lithium borate (CsLiB6O10) crystal have been studied using Z-scan technique. Ti:sapphire laser with 110 fs pulse width operating at 800 nm wavelength and pulse repetition rate of 1 kHz is used as the source of photons. Intensity of the laser pulse is varied from 0.541 to 1.283 T W/cm2 to estimate the intensity dependence of multiphoton absorption coefficients. Using the theory of multiphoton absorption proposed by Sutherland [ Handbook of Nonlinear Optics, in 2nd ed., edited by D. G. McLean and S. Kirkpatrick, Dekker, New York (2003) ], found that open aperture Z-scan data fit well for the five-photon absorption (5PA) process. 5PA coefficients are obtained by fitting the expressions into the open aperture experimental data for various peak intensities (I00). The nonlinear refractive index n2 estimated from closed aperture Z-scan experiment is 1.075×10−4 cm2/T W at an input peak intensity of 0.723 T W/cm2. The above experiment when repeated with a 532 nm, 6 ns pulsed laser led to an irreversible damage of the sample resulting in an asymmetric open aperture Z-scan profile. This indicates that it is not possible to observe multiphoton absorption in this regime of pulse width using 532 nm laser.

Influence of two photon absorption induced free carriers on coherent polariton and phonon generation in ZnTe crystals

Combination of femtosecond Kerr, two photon absorption, and impulsive stimulated Raman scattering (ISRS) experiments have been carried out to investigate the effect of pulse energy and crystal temperature on the generation of coherent polaritons and phonons in 〈110〉 cut ZnTe single crystals of three different resistivities. We demonstrate that the effect of two photon induced free carriers on the creation of both the polaritons and phonons is largest at 4 K where the free carrier lifetime is enhanced. The temperature dependant ISRS on high and low purity ZnTe crystals allows us to unambiguously assign the phonon mode at 3.5 THz to the longitudinal acoustic mode at X-point in the Brillouin zone, LA(X).

State of bismuth in BaBiO3 and BaBi1-xPbxO3: Bi 4f photoemission and Bi L3 absorption spectroscopic studies

The 2p 6d feature in the Bi L3 spectra has different energies in the semiconducting (0.0≤x<0.7) and the superconducting (x=0.75) compositions of BaBi1−xPbxO3. The Bi 4f core level spectrum shows distinct features ascribable to Bi III and Bi V in BaBiO3 and in the semiconducting compositions; the width of the 4f peaks is also considerably larger in these compositions compared to that in BaBi0.25Pb0.75O3, which shows a single sharp Bi 4f feature.