A comparison between the chemical behaviour of lead-gold and lead-bismuth eutectics towards 316L stainless steel

Lead-gold eutectic (LGE) has been recently proposed as an alternative target material for high power spallation sources. In order to compare the corrosive properties of LGE to the better-studied eutectic of lead-bismuth (LBE), an isothermal twin-loop made of SS 316L was built and operated at the Institute of Physics of the University of Latvia. We have measured the concentration of steel alloying elements dissolved in both alloys at the end of two test campaigns via ICP-OES. In case of LGE, a pronounced concentration increase of Fe, Ni, Mn and Cr is found in the liquid metal, which is significantly higher compared to LBE. Similar results were obtained during complementary investigations on material samples exposed to both alloys in this twin-loop at 400 ◦C and 450 ◦C. These findings indicate that in contact with LGE, SS 316L steel suffers from substantial chemical attack. Detailed investigations using structure materials other than SS 316L have to be undertaken before qualifying LGE as a serious alternative to LBE.

Ductilidad del acero inoxidable bajo en níquel para estructuras de hormigón armado / Ductility in a new low nickel stainless steel for reinforced concrete

En este trabajo se presentan los diagramas tensióndeformación de un nuevo acero inoxidable con bajo contenido en níquel, un inoxidable convencional AISI 304 y un acero al carbono de uso común en estructuras de hormigón armado. Dicha ductilidad se ha estudiado determinando la tensión máxima (fmax), la tensión en el límite elástico (fy) y la deformación bajo carga máxima (εmax). Los tres materiales se han evaluado utilizando criterios aceptados internacionalmente, como son el índice p (capacidad de rotación plástica), el índice A* (área plástica de endurecimiento) y el índice de tenacidad Id (energía total absorbida en el punto de alargamiento bajo carga máxima), los resultados obtenidos se han comparado con los aceros convencionales de armaduras 500SD, 500N y 500H (EC-2).

Fracture micromechanisms and residual stresses of a highly resistant duplex stainless steel

The paper presents some preliminary results of an ongoing research intended to qualify a highly resistant duplex stainless steel wire as prestressing steel and, gets on insight on (he wires' fracture micromechanism and residual stresses field. SEM fractographic analysis of the stainless steel wires indicates an anisotropic fracture behavior in tension, in presence of surface flaws, attributed to the residual stresses generated through the fabrication process. The residual stresses magnitude influences the damage tolerance, its knowledge being a key issue in designating/qualifying the wires as prestressing steels.

Effect of Thermal Relaxation on LSP Induced Residual Stresses and Fatigue Life Enhancement of AISI 316L stainless steel

Effect of Thermal Relaxation on LSP Induced Residual Stresses and Fatigue Life Enhancement of AISI 316L stainless steel

Fracture micromechanisms and residual stresses of a highly resistant duplex stainless steel

The paper presents some preliminary results of an ongoing research intended to qualify a highly resistant duplex stainless steel wire as prestressing steel and, gets on insight on (he wires' fracture micromechanism and residual stresses field. SEM fractographic analysis of the stainless steel wires indicates an anisotropic fracture behavior in tension, in presence of surface flaws, attributed to the residual stresses generated through the fabrication process. The residual stresses magnitude influences the damage tolerance, its knowledge being a key issue in designating/qualifying the wires as prestressing steels.

Effects of hydrogen assisted stress corrosion on damage tolerance of a high-strength duplex stainless steel wire for prestressing concrete

The study brings new insights on the hydrogen assisted stress corrosion on damage tolerance of a high-strength duplex stainless steel wire which concerns its potential use as active reinforcement for concrete prestressing. The adopted procedure was to experimentally state the effect of hydrogen on the damage tolerance of cylindrical smooth and precracked wire specimens exposed to stress corrosion cracking using the aggressive medium of the standard test developed by FIP (International Prestressing Federation). Stress corrosion testing, mechanical fracture tests and scanning electron microscopy analysis allowed the damage assessment, and explain the synergy between mechanical loading and environment action on the failure sequence of the wire. In presence of previous damage, hydrogen affects the wire behavior in a qualitative sense, consistently to the fracture anisotropy attributable to cold drawing, but it does not produce quantitative changes since the steel fully preserves its damage tolerance.

Stainless steel : construction and engineering memorandum, no. 24 /

"TID-5327; Engineering."

Corrosion studies on 304 stainless steel containing one percent boron-10 /

"U.S. Atomic Energy Commission Contract AT(29-1)-1106."

Stainless steel information manual for the Savannah River Plant /

"Metals, Ceramics, and Materials (TID-4500, 20th Ed.)."

Stainless steel handbook.

Mode of access: Internet.