Effect of tartrate content on aging and deposition condition of copper-tin electrodeposits from a non-cyanide acid bath

The effect of the presence of tartrate additive on the chemical stability of a Cu-Sn acid bath was evaluated. It was observed that this additive hinders decomposition of the Cu/Sn deposition bath with storage time, since the decrease in electrochemical efficiency was attenuated. In addition, it was observed that optimal galvanostatic deposition with or without tartrate occurs at approximately 11 mA cm(-2). However, in the presence of tartrate the deposition charge was lower, leading to lower energy consumption. SEM analysis showed that the tartrate added to the plating bath caused a marked change in the morphology of the Cu/Sn films obtained gal vanostatic ally. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal- and mechanical-loading

Objectives. This study evaluated the effect of thermal- and mechanical-cycling on the shear bond strength of three low-fusing glassy matrix dental ceramics to commercial pure titanium (cpTi) when compared to conventional feldspathic ceramic fused to gold alloy.Methods. Metallic frameworks (diameter: 5 min, thickness: 4 mm) (N = 96, n = 12 per group) were cast in cpTi and gold alloy, airborne particle abraded with 150 mu m aluminum oxide. Low-fusing glassy matrix ceramics and a conventional feldspathic ceramic were fired onto the alloys (thickness: 4mm). Four experimental groups were formed; Gr1 (control group): Vita Omega 900-Au-Pd alloy; Gr2: Ticeram-cpTi; Gr3: Super Porcelain Ti-22-cpTi and G4: Vita Titankeramik-cpTi. While half of the specimens from each ceramic-metal combination were randomly tested without aging (water storage at 37 C for 24h only), the other half were first thermocycled (6000 cycles, between 5 and 55 C, dwell time: 13 s) and then mechanically loaded (20,000 cycles under SON load, immersion in distilled water at 37 C). The ceramic-alloy interfaces were loaded under shear in a universal test machine (cross-head speed: 0.5 mm/min) until failure occur-red. Failure types were noted and the interfaces of the representative fractured specimens from each group were examined with stereo microscope and scanning electron microscope (SEM). in an additional study (N = 16, n = 2 per group), energy dispersive X-ray spectroscopy (EDS) analysis was performed from ceramic-alloy interfaces. Data were analyzed using ANOVA and Tukey's test.Results. Both ceramic-metal combinations (p < 0.001) and aging conditions (p < 0,001) significantly affected the mean bond strength values. Thermal- and mechanical-cycling decreased the bond strength (MPa) results significantly for Gr3 (33.4 +/- 4.2) and Gr4 (32.1 +/- 4.8) when compared to the non-aged groups (42.9 +/- 8.9, 42.4 +/- 5.2, respectively). Gr1 was not affected significantly from aging conditions (61.3 +/- 8.4 for control, 60.7 +/- 13.7 after aging) (p > 0.05). Stereomicroscope images showed exclusively adhesive failure types at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface but with a visible dark titanium oxide layer in Groups 2-4 except Gr1 where remnants of bonder ceramic was visible. EDS analysis from the interfacial zone for cpTi-ceramic groups showed predominantly 34.5-85.1% O(2) followed by 1.1-36.7% Aland 0-36.3% Si except for Super Porcelain Ti-22 where a small quantity of Ba (1.4-8.3%), S (0.7%) and Sn (35.3%) was found. In the Au-Pd alloy-ceramic interface, 56.4-69.9% O(2) followed by 15.6-26.2% Si, 3.9-10.9% K, 2.8-6% Na, 4.4-9.6% Al and 0-0.04% Mg was observed.Significance. After thermal-cycling for 6000 times and mechanical-cycling for 20,000 times, Triceram-cpTi combination presented the least decrease among other ceramic-alloy combinations when compared to the mean bond strength results with Au-Pd alloy-Vita Omega 900 combination. (c) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Ag precipitation and dissolution reactions in the Cu-3 wt.% Al-4 wt.% Ag alloy

The Ag precipitation and dissolution reactions in the Cu-3 wt.% Al-4 wt.% Ag alloy were studied using isothermal and non-isothermal analyses. The activation energy values, obtained for the Ag precipitation reaction indicated that, when the Kissinger, Ozawa and Johnson-MehI-Avrami methods are compared, the Kissinger method is the most appropriate. Although the Johnson-Mehl-Avrami equation often does not fit precipitation data, the energy values obtained for Ag precipitation kinetics are in agreement with what was experimentally observed. For the dissolution reaction of Ag precipitates the activation energy values obtained from the Kissinger and Ozawa methods are higher than that found in the literature for the Ag dissolution in Cu. This discrepancy seems to be related to the fact that the activation energy is influenced by the heating rate. (c) 2006 Elsevier B.V. All rights reserved.

Kinetics of martensite decomposition in the Cu-9Al-6Ag alloy

The non-occurrence of the beta' -> (alpha+ gamma(1)) decomposition reaction in the Cu-9 wt.% Al-6 wt.% Ag alloy, on ageing between 200 and 450 degrees C, is discussed considering the influence of Ag on point defects redistribution and energy difference between martensite and the ordered parent phase. (c) 2005 Elsevier B.V All rights reserved.

Coating residual stress effects on fatigue performance of 7050-T7451 aluminum alloy

The tendency of the aircraft industry is to enhance customer value by improving performance and reducing environmental impact. In view of availability, aluminum alloys have a historically tendency to faster insertion due to their lower manufacturing and operated production infrastructure. In landing gear components, wear and corrosion control of many components is accomplished by surface treatments of chrome electroplating on steel or anodizing of aluminum. One of the most interesting environmentally safer and cleaner alternatives for the replacement of hard chrome plating or anodizing is tungsten carbide thermal spray coating, applied by the high velocity oxy fuel (HVOF) process. However, it was observed that residual stresses originating from these coatings reduce the fatigue strength of a component.An effective process as shot peening treatment, considered to improve the fatigue strength, pushes the crack sources beneath the surface in most of medium and high cycle cases, due to the compressive residual stress field induced. The objective of this research is to evaluate a tungsten carbide cobalt (WC-Co) coating applied by the high velocity oxy fuel (HVOF) process, used to replace anodizing. Anodic films were grown on 7050-T7451 aluminum alloy by sulfuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on axial fatigue strength of anodic films grown on the aluminum alloy surface is to degrade the stress-life performance of the base material. Three groups of specimens were prepared and tested in axial fatigue to obtain S-N curves: base material, base material coated by HVOF and base material shot peened and coated.Experimental results revealed increase in the fatigue strength of Al 7050-T7451 alloy associated with the WC 17% Co coating. on the other hand, a reduction in fatigue life occurred in the shot peened and coated condition. Scanning electron microscopy technique and optical microscopy were used to observe crack origin sites, thickness and coating/substrate adhesion. (c) 2007 Elsevier B.V. All rights reserved.

Laser weld: microstructure and corrosion study of Ag-Pd-Au-Cu alloy of the dental application

The laser Welding process was introduced into dentistry by the end of the 1980s, resulting on a great impulse to that area with the development of cheaper and smaller equipment, using simpler technique. This allowed greater use of that process on the confection of prostheses compared to the brazing process since the heat source for that process is a concentrated light beam of high power, which minimizes distortion problems on the prosthetic pieces. Ag-Pd-Au-Cu alloy used on the confection of dental implant prostheses was observed before and after subjection to the laser welding process. The microstructure was analyzed with the. use of optic microscopy and the corrosion resistance was studied by the traditional electrochemical techniques and by electrochemical impedance, under environmental conditions simulating the aggressiveness found in the mouth cavity. A structural change was detected on the weld area, which presented a refined microstructure deriving from the high-speed cooling. The base metal out of the weld area presented a fusion coarse microstructure. The electrochemical essays showed differences on the potentiodynamic polarization behavior in both weld and metal base areas, indicating superior corrosion resistance in the weld area. The impedance spectra were characterized by capacitive distorted components, presenting linear impedance in the low frequencies area. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Microstructure and corrosion resistance of inorganic-organic (ZrO2-PMMA) hybrid coating on stainless steel

Zirconia-polymethylmetacrylate hybrids prepared by a sol-gel method were deposited by dip-coating on stainless steel to improve the resistance against wet corrosion. The effect of the concentration of polymethylmetacrylate and the number of coating applications on the microstructure and corrosion performance of coated samples was investigated. The microstructural properties of samples was analyzed by scanning electron and atomic force microscopy, adhesion tests and profilemeter measurements. The electrochemical corrosion was evaluated through potentiodynamic polarization curves at room temperature. Results show that the sample prepared with 17 vol.% of polymethylmethacrylate has a maximum corrosion resistance, smaller roughness, are hermetic and adherent to the substrate. This film increases the life time of the stainless steel by a factor 30. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Effect of a non-peptide angiotensin receptor antagonist on water intake caused by centrally administered carbachol in the rat

Angiotensin II (ANG II) administered centrally produces drinking by acting on subtype 1 ANG II (AT1) receptors, Carbachol, a cholinergic receptor agonist, also induces drinking behavior by a central action. In the present study we determined whether the response to carbachol also involves AT1 receptors. Male Holtzman rats (250-300 g) with stainless steel cannula implanted into the lateral ventricle (LV) were used. Water intake after injection of 0.15 M NaCl (1.0 mu l) into the LV was 0.2 +/- 0.01 ml/h (N = 8). The AT1 receptor antagonist DUP-753 (50 nmol/mu l) injected into the LV reduced water intake induced by ANG II (10 nmol/mu l) from 9.2 +/- 1.4 to 0.4 +/- 0.1 ml/h (N = 8), and water intake induced by carbachol (2 nmol/mu l) from 9.8 +/- 1.4 ml/h to 3.7 +/- 0.8 ml/h (N = 8), These results suggest that AT1 receptors play a role in the drinking behavior observed after central cholinergic stimulation in rats.

Effects of a postweld heat treatment on a submerged arc welded ASTM A537 pressure vessel steel

Postweld heat treatment (PWHT) is frequently applied to steel pressure vessels, following the requirements of the ASME code (section VIII), which establishes the parameters of the PWHT based on the thickness and chemical composition of the welded section. This work shows the results of an analysis undertaken on a sample of ASTM A537 C1 steel subjected to qualifying welding procedure tests including PWHT (650 degreesC/5 h), the results obtained showed that this PWHT practice promoted a reduction in the mechanical properties of the base metal and the heat-affected zone (HAZ).

Design, manufacturing, and testing of a Nb3Sn coil employing Ti alloy as structural material

We describe the design, manufacturing, and testing results of a Nb3Sn superconducting coil in which TiAIV alloys were used instead of stainless steel to reduce the magnetization contribution caused by the heat treatment for the A-15 Nb-3 Sn phase formation that affects the magnetic field homogeneity. Prior to the coil manufacturing several structural materials were studied and evaluated in terms of their mechanical and magnetic properties in as-worked, welded, and heat-treated conditions. The manufacturing process employed the wind-and-react technique followed by vacuum-pressure impregnation(VPI) at 1 MPa atm. The critical steps of the manufacturing process, besides the heat treatment and impregnation, are the wire splicing and joint manufacturing in which copper posts supported by Si3N4 ceramic were used. The coil was tested with and without a background NbTi coil and the results have shown performance exceeding the design quench current confirming the successful coil construction.

A Non-Destructive Testing Based on Electromagnetic Measurements and Neural Networks for the Inspection of Concrete Structures

This paper presents a new non-destructive testing (NDT) for reinforced concrete structures, in order to identify the components of their reinforcement. A time varying electromagnetic field is generated close to the structure by electromagnetic devices specially designed for this purpose. The presence of ferromagnetic materials (the steel bars of the reinforcement) immersed in the concrete disturbs the magnetic field at the surface of the structure. These field alterations are detected by sensors coils placed on the concrete surface. Variations in position and cross section (the size) of steel bars immersed in concrete originate slightly different values for the induced voltages at the coils.. The values for the induced voltages were obtained in laboratory tests, and multi-layer perceptron artificial neural networks with Levemberg-Marquardt training algorithm were used to identify the location and size of the bar. Preliminary results can be considered very good.

SAE 1045 steel/WC-Co/Ni-Cu-Ni/SAE 1045 steel joints prepared by dynamic diffusion bonding: Microelectrochemical studies in 0.6 M NaCl solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Ag addition on the thermal behavior of the Cu-11 mass% Al alloy

In this work the influence of Ag additions on the thermal behavior of the Cu-11 mass% Al alloy was studied using differential scanning calorimetry, in situ X-ray diffractometry and scanning electron microscopy. The results indicated that changes in the heating rate shift the peak attributed to alpha phase formation to higher temperatures, evidencing the diffusive character of this reaction. The activation energy value for the alpha phase formation reaction, obtained from a non-isotherm kinetic model, is close to that corresponding to Cu atoms self diffusion, thus confirming that this reaction is dominated by Cu atoms diffusion through the martensite matrix.

(alpha + gamma(1)) Complex phase formation in the Cu-10 mass% Al-6mass% Ag alloy

In this work the (alpha + gamma(1)) complex phase formation reaction in the Cu-10mass% Al-6mass% Ag alloy was studied using Differential Scanning Calorimetry (DSC), Differential Thermodilatometry (DTD), X-ray diffractometry (XRD), Optical (OM) and Scanning Electron Microscopies (SEM). The results indicated the presence of two different processes, related to a change in the Ag diffusion route from the alpha matrix to the (alpha + gamma(1)) complex phase.

Metallurgical evaluation of a copper-based alloy for dental castings.

The present study was designed to evaluate the metallurgical properties of an experimental, low-cost copper-zinc-aluminum-nickel alloy for dental castings. Some specimens were subjected to heat treatment after induction casting. The extent of corrosion was determined by measuring weight loss of specimens stored in a sodium sulfite solution. In the as-cast specimens, tests demonstrated the presence of three phases: the first consisted of copper-zinc-aluminum, the second was similar but lower in copper and aluminum, and the third consisted of an intermetallic compound of manganese-nickel-phosphorus. After heat treatment, the first phase remained relatively constant, the second was converted to Cu3Al, and the third increased in volume. The weight loss from the as-cast specimens was eight times that of the heat-treated specimens. It was concluded that the heat treatment substantially changed the microstructure and improved the corrosion resistance of the experimental alloy.