含纳米晶颗粒的Yb^3＋/Er^3＋共掺透明碲酸盐玻璃陶瓷的光谱性质研究

在组成为15Li2O-15Nb2O5-70TeO2-0.1Er2O3-0.4Yb2O3（%, 摩尔分数）的碲酸盐玻璃基础上, 采用两步热处理法制备了透明的含纳米晶颗粒碲酸盐玻璃陶瓷. 通过X射线衍射（XRD）测试表明, 玻璃陶瓷中的晶体颗粒组成为Yb6Te5O19.2或Er6Te5O19.2, 晶粒尺寸约为55 nm. 根据Judd-Ofelt理论计算了Er^3＋离子在基质玻璃和玻璃陶瓷中的光谱参数Ωt（t＝2, 4, 6）以及Er^3＋：4I15/2→4I13/2跃迁自发辐射几率, 根据McCumber

卤化铅调整Tm^3＋／Yb^3＋共掺碲酸盐玻璃上转换发光研究

研究了卤化铅调整Tm^3+／Yb^3+共掺碲酸盐玻璃的热稳定性能、Raman光谱和上转换发光光谱，分析了Tm^3+／Yb^3+共掺氧卤碲酸盐玻璃的上转换发光机理．结果发现：混合卤化铅调整Tm^3+／Yb^3+共掺碲酸盐玻璃具有好的热稳定性能、低的声子能量、强的上转换蓝光．这表明混合卤化铅调整Tm^3+／Yb^3+共掺碲酸盐玻璃是一种上转换蓝光激光器的潜在基质材料．

Yb^3＋掺杂锌锗碲酸盐玻璃的热分析、光谱和激光性质

设计了组成为0．70TeO2-(0．20-x)ZnO-xGeO2—0．05La2O3-0．025K2O-0．025Na2O-0．01Yb2O3(摩尔分数x=0,0．05，0．10，0．15和0．20)的碲酸盐激光玻璃，测试了热学性质、吸收光谱、荧光光谱和荧光寿命。计算了Yb^3+离子的吸收截面、受激发射截面、荧光有效线宽等参数。结果表明，组成为0．70TeO2-0．20GeO2-0．05La2O3-0．025K2O-0．025Na2O的玻璃具有优于著名的碲锌钠(TZN)玻璃的热稳定性，高的受激发射截面(1

Yb：铅锌镧碲酸盐玻璃的热学、光谱和激光性质

研究了摩尔组分为70TeO2-(20-x)ZnO-xPbO-5La2O3-2.5K2O-2．5Na2O(x=0，5，10，15，20)的新型多元铅锌镧碲酸盐激光玻璃，外掺Yb2O3为玻璃摩尔组分的1％，测试了试样的物理性质及吸收光谱、荧光光谱和荧光寿命，计算了Yb^3+的吸收截面、受激发射截面、荧光有效线宽等光谱参数，结果表明：该系列玻璃都具有良好的热学稳定性((Tx-Tg)>195℃，高于TZN玻璃(118℃))；当X=15时，样品具有较好的光谱性质：高的受激发射截面(1．25pm^2)、长的荧光寿命(

Yb^3＋敏化Tm^3＋掺杂氧卤碲酸盐玻璃的上转换发光研究

研究了Yb2O3浓度对Tm^3＋／Yb^3＋共掺氧卤碲酸盐玻璃的上转换发光的影响，分析了上转换发光机理。结果发现，通过980nm的激光二极管激发，在室温下同时观察到强烈的蓝光（475nm）和微弱的红光（649nm），分别是由于Tm^3＋离子^1G4→^3H6和^1G4→^3F4跃迁产生的；上转换机理分析表明，上转换蓝光和红光都是由于双光子吸收过程。随Yb2O3浓度增加，Yb^3＋离子寿命降低，Yb^3＋到Tm^3＋的能量转移效率增加，上转换蓝光和红光强度先增加，在Yb2O3摩尔比为3时达到最大，然后降低。

Cr^3＋，Yb^3＋，Er^3＋共掺磷酸盐铒玻璃转镜调Q激光性质研究

研究了Cr^3＋，Yb^3＋，Er^3＋共掺磷酸盐铒玻璃转镜调Q激光性质．三种Er2O3掺杂浓度的激光实验结果表明，在Er2O3名义掺杂浓度为0．5wt％时，玻璃的综合激光性质最好，重复频率为0．1Hz时，它的激光阈值功率为14．5mJ，最大输出能量为9．6mJ，斜率效率为0．55％．在同种实验条件下，比较了Cr14和Kigre公司生产的QE-7S激光性质参数，实验表明，前者激光阈值功率稍低，而后者的斜率效率和最大输出功率略高．

Experimental study on a nonlinear photonics process of Er(0.5)Yb(3): FOV oxyfluoride nanophase vitroceramics

We study the nonlinear photonics of rare-earth-doped oxyfluoride nanophase vitroceramics (FOV), oxyfluoride glass (FOG), and ZBLAN fluoride glass. We found that an interesting fluorescence intensity inversion phenomenon between red and green fluorescence occurs from Er(0.5)Yb(3):FOV The dynamic range Sigma of the intensity inversion between red and green fluorescence of Er(0.5)Yb(3):FOV is about 5.753 x 10(2), which is 100 to 1000 times larger than those of other materials. One of the applications of this phenomenon is double-wavelength fluorescence falsification-preventing technology, which is proved to possess the novel antifriction loss and antiscribble properties. (c) 2007 Optical Society of America.

Tm^3＋-Yb^3＋共掺氧氟硅酸盐玻璃热学性能和上转换发光特性研究

稀土掺杂氧氟玻璃是一种优良的上转换发光材料，制备了组分为35SiO2—15AlO1.5-（45-x）PbF2-xCdF2—0．1TmF3—1．5YbF3（x=0，10，20，30）的氧氟硅酸盐玻璃，系统研究了CdF2含量对其热学性能和光学性能的影响。研究表明用CdF2部分替代PbF，可以提高玻璃的热稳定性、使紫外吸收截至边向短波方向移动；随着CdF2含量的增加，开始Tm^3＋蓝光和红光上转换发光增强缓慢，而后迅速增强．而近红外上转换发射先显著增强后增强放缓；由于蓝光和近红外发光强度远大于红光发光强度，所以

碱金属氟化物对掺Yb~(3+)氟磷酸盐玻璃析晶稳定性和光谱性质的影响

研究了碱金属氟化物对掺Yb3+氟磷玻璃的光谱性质和析晶稳定性能的影响。运用倒易法计算了Yb3+的发射截面。结果显示,LiF的引入对吸收和发射截面的提高作用较大并出现最佳引入量极值,其次为KF。碱金属氟化物的引入可提高二元体系的析晶稳定性能,使玻璃网络结构得到改善;拉曼光谱显示二元体系中引入YbF3后玻璃网络结构得到增强,而在引入碱金属氟化物的三元体系中掺杂YbF3后破坏了网络完整性,降低系统析晶稳定性能。

980 nm 抽运下Yb-Tm-Ho 三掺氟磷酸盐玻璃的2 μm 荧光性质

The thermal stability, 2 μm fluorescence properties and energy transfer mechanism in Ho³⁺ doped fluorophosphate glass sensitized by Yb³⁺ and Tm³⁺ were investigated. The characteristic temperatures, absorption spectrum and fluorescence spectrum of the glass sample were measured. ΔT calculated from the characteristic temperatures shows that the thermal stability of fluorophosphate glass is better than fluoride glass. According to the absorption spectrum, several spectroscopic parameters of the glass sample, such as Judd-Ofelt parameters and spontaneous transition probability were calculated and compared with other glass hosts. The largest spontaneous transition probability for Ho³⁺:⁵ I7&rarr⁵I8 transition in fluorophosphate glass which is 78.48 s^-1 indicates that fluorophosphate glass is an appropriate base glass to achieve 2 m fluorescence. From the fluorescence spectrum of the glass sample, the extremely strong 2.0 μm fluorescence intensity is observed, which is higher than the intensity of 1.8 μm fluorescence, showing that Ho³⁺ ions sensitized by Yb³⁺ and Tm³⁺ is efficient. Meanwhile, the absorption sections and emission sections of Yb³⁺, Tm³⁺ and Ho³⁺ were calculated and the pumping scheme and energy transfer mechanism among Yb³⁺, Tm³⁺ and Ho³⁺ are discussed. The study indicates that Yb-Tm-Ho tri-doped fluorophosphate glass is a significant sensitization glass system under 980 nm excitation for 2 μm applications.

Ag~+-Li~+离子交换制作Er~(3+)/Yb~(3+)共掺磷酸盐玻璃平面光波导(英文)

制备了化学稳定的Er^3＋／Yb^3＋共掺的磷酸盐玻璃，并在其中制作了用于光放大器和激光器的平面光波导．这种磷酸盐玻璃的失重速率为4．7×10^-5g·cm^-2·hr^-1，小于Kigre公司商业化的磷酸盐玻璃QX／Er的失重速率．采用Ag^＋-Li^＋交换技术制作了平面光波导并用m-线光谱在632．8nm测量了平面光波导的有效折射率．根据反WKB法得到折射率形貌，计算了离子交换参数如：离子交换深度、表面折射率，折射率改变和扩散系数等．

热处理对共沉淀法制备YAG纳米粉体性能的影响

以Al（NO3）3和Y（NO3）3为原料，采用共沉淀法制备出粒度大小为60-100nm，颗粒呈球形的纯相YAG纳米粉。研究了前驱物在不同条件下热处理对YAG纳米粉体性能的影响，并对前驱物在焙烧过程中的物相变化进行了观察。发现延长前驱物在低温下的干燥时间会导致晶粒尺寸增大，而采用在晶化温度前后分别进行保温的方法可在较低的温度获得纯相的YAG粉体。对比了焙烧温度和保温时间对产物粒度的影响，结果表明：在保证粉体晶化完全的前提下，升高焙烧温度比延长保温时间对晶粒尺寸有更显著的影响。

Effects of Yb ion concentration on the spectral properties of lead silica glasses

The spectral properties in different concentration of Yb ions (0.5-5 mol%)-doped silica glasses are explored in this paper. The glasses are prepared by traditional melting method. The absorption spectra and the fluorescent lifetime (tau(f)) are measured at room temperature and low temperature (18 K). The stimulated cross-section (sigma(emi)) and potential laser properties (beta(min), I-sat, I-min) are calculated based on the absorption spectra. The absorption cross-section (sigma(abs)) are in the range 1.08 x 10(-20) - 1.18 x 10(-20) cm(2) in different glasses, the fluorescence lifetime (tau(f)) change from 1.9 to 1.2 ms with the increase of Yb3+ concentration. The potential laser properties indicate that lead silica glass is a good host for highly Yb ion doping glass. (c) 2005 Elsevier B.V. All rights reserved.

Gain and noise figure of a double-pass waveguide amplifier based on Er/Yb-doped phosphate glass

A waveguide amplifier is fabricated by Ag+-Na+ two-step ion exchange on Er/Yb-doped phosphate glass. The spectroscopic performance of glass and the properties of channel waveguide are characterized. A double-pass configuration is adopted to measure the gain and noise figure (NF) of the waveguide amplifier, and the comparison of gain and NF for the single and double-pass configuration of the waveguide amplifier is presented. The results show that the double-pass configuration can make the gain increase from 8.8dB (net gain 2.2dB/cm) of the single-pass one to 14.6 dB (net gain 3.65 dB/cm) for small input power at 1534 nm, and the NF are all lower than 5.5dB for both the configurations.