Damage tolerance of cold drawn ferritic-austenitic stainless steels wires for prestressed concrete

Damage tolerance of high strength cold-drawn ferritic–austenitic stainless steel wires is assessed by means of tensile fracture tests of cracked wires. The fatigue crack is transversally propagated from the wire surface. The damage tolerance curve of the wires results from the empirical failure load when given as a function of crack depth. As a consequence of cold drawing, the wire microstructure is orientated along its longitudinal axis and anisotropic fracture behaviour is found at macrostructural level at the tensile failure of the cracked specimens. An in situ optical technique known as video image correlation VIC-2D is used to get an insight into this failure mechanism by tensile testing transversally fatigue cracked plane specimens extracted from the cold-drawn wires. Finally, the experimentally obtained damage tolerance curve of the cold-drawn ferritic–austenitic stainless steel wires is compared with that of an elementary plastic collapse model and existing data of two types of high strength eutectoid steel currently used as prestressing steel for concrete.

Residual stress distribution in ferritic-austenitic steel joints made by laser welding

The present investigation addresse the influence of laser welding process-ing parameters used for joining dis-similar metals (ferritic to austenitic steel), on the induced residual stress field. Welding was performed on a Nd:YAG laser DY033 (3300 W) in a continuous wave (CW), keyhole mode. The base metals (BM) employed in this study are AISI 1010 carbon steel (CS) and AISI 304L austenitic stainless steel (SS). Pairs of dissimilar plates of 200 mm x 45 mm x 3 mm were butt joined by laser welding. Different sets of parameters were used to engineer the base metals apportionment at joint formation, namely distinct dilution rates. Residual strain scanning, carried out by neutron diffraction was used to assess the joints. Through-thickness residual stress maps were determined for the laser welded samples of dis-similar steels using high spatial reso-lution. As a result, an appropriate set of processing parameters, able to mi-nimize the local tensile residual stress associated to the welding process, was found.

Residual stress distribution in ferritic to austenitic steel joints made by laser welding,

In this study, autogenous laser welding was used to join thin plates of low carbon ferritic and austenitic stainless steel. Due to the differences in the thermo-physical properties of base metals, this kind of weld exhibits a complex microstructure, which frequently leads to an overall loss of joint quality. Four welded samples were prepared by using different sets of processing parameters, with the aim of minimizing the induced residual stress field. The dissimilar austenitic-ferritic joints obtained under all welding conditions were uniform and free of defects. Variations in beam position did not influence the weld geometiy, which is a typical keyhole welding. Microstructural characterization and residual strain scanning (by neutron diffraction) were used to assess the features of the joints. By varying laser beam power density and by displacing the laser beam towards the carbon steel side, an optimum combination of processing parameters was found.

Overall vs. local mechanical behaviour of ferritic austenitic steel joints made by laser welding

The present investigation addresses the overall and local mechanical performance of dissimilar joints of low carbon steel (CS) and stainless Steel (SS) thin sheets achieved by laser welding in case of heat source displacement from the weld gap centreline towards CS. Welding was performed on a Nd:YAG laser DY033 (3300 W) in a continuos wave (CW), keyhole mode. The tensile behavior of the joint different zones assessed by using a video-image based system (VIC-2D) reveals that the residual stress field, together with the positive difference in yield between the weld metal and the base materials protects the joint from being plastically deformed. The tensile loadings of flat transverse specimens generate the strain localization and failure in CS, far away from the weld.

Influencia de la atmósfera de sinterización en las propiedades mecánicas de los aceros P/M AISI 430.LInfluence of sintering atmosphere on the mechanical properties of steel P/M AISI 430L

Se ha estudiado el acero inoxidable pulvimetalúrgico AISI 430L, comparando la sinterización en dos atmósferas diferentes; en vacío, y en una atmósfera que contiene nitrógeno. Se ha desarrollado un tratamiento térmico con objeto de incrementar las propiedades mecánicas, mediante la modificación microestructural de los nitruros complejos de hierro y cromo precipitados durante la etapa de sinterización. Se han evaluado las propiedades físicas y a la vez se ha realizado un análisis microestructural con el fin de relacionar la microestructura con el incremento en las propiedades mecánicas. Influence of sintering atmosphere on the mechanical properties of steel P / M AISI 430L. It has studied the stainless steel powder metallurgy AISI 430L. It has compared the sintering in two different atmospheres; in vacuum, and in an atmosphere containing nitrogen. It has developed a heat treatment with the aim of improving the mechanical properties. This has been done through microstructural modification of complex nitrides of iron and chromium precipitates during the phase of sintering. Physical properties have been evaluated and are been performing a microstructural analysis for microstructure related to the increase in mechanical properties.

Colonización bacteriana y oxidación de aceros inoxidables austeníticos, ferríticos y dúplex sinterizados

Las características y capacidades de los aceros inoxidables sinterizados se han investigado en una doble vertiente. Por una parte con vista a sus capacidades de resistencia a la oxidación en caliente y por otra parte se ha investigado su capacidad para retener microorganismos que contribuyan a la descontaminación de un ambiente. Por ello, para cada una de estas funciones se han utilizado los aceros inoxidables sinterizados, que se han considerado más adecuados. Para estudiar sus capacidades de resistencia a la oxidación en caliente se ha utilizado un acero inoxidable austenítico AISI 304L, un acero inoxidable ferrítico AISI 430L y un acero inoxidable Fe-16Cr-3Al. Para estudiar sus capacidades para retener microorganismos se ha utilizado un acero inoxidable austenítico AISI 316L, un acero inoxidable ferrítico AISI 430L y un acero inoxidable dúplex 50%/50% de los anteriores. Para esta última finalidad los aceros se han compactado a tres diferentes presiones 300, 500 y 700 MPa, a las que corresponden diferentes porosidades. En relación con el comportamiento frente a la oxidación en caliente, se han cuantificado los incrementos positivos o negativos de volumen, masa y densidad en los diferentes tipos de sinterización y estados de tratamiento de oxidación. Como tónica general de comportamiento, puede decirse que los aceros sinterizados bajo vacío son más resistentes a la oxidación, que los sinterizados en atmósfera de N2-5H2 y que los aceros inoxidables austeníticos son algo más resistentes, que los Cr-Al y estos, a su vez, más que los aceros inoxidables ferríticos. Respecto a la retención de microorganismos, los tres aceros inoxidables sinterizados se han ensayado en diferentes medios de cultivo, utilizando cuatro especies de bacterias. Los mejores resultados se han obtenido con Staphylococcus aureus, muy favorable para su observación y recuento. Se han cuantificado, una vez sinterizados y colonizados por los microorganismos, para cada material y presión de compactación, las áreas de cada uno de los poros y el número de microorganismos situados en los poros y en la superficie sin poros. Se ha establecido en cada caso la densidad de microorganismos en las zonas de poros y en las zonas sin poros. Como tónica general puede decirse, que los aceros inoxidables austeníticos aparecen más favorables para estos estudios, que los aceros dúplex y estos más que los inoxidables ferríticos. Asimismo, se desprende que las áreas de los poros dependen de forma unívoca de la presión de compactación y que para áreas de poros decrecientes las densidades de microorganismos son crecientes. En consecuencia, podría deducirse, que a igualdad de área de poros en una superficie, aquella que tuviera los poros más pequeños, retendría mayor cantidad de bacterias. ABSTRACT The characteristics and capacities of sintered stainless steels have been researched from two perspectives: firstly, with a view to their resistance to hot oxidation, and secondly their capacity to retain microorganisms able to decontaminate the environment. For both these functions, sintered stainless steels were used, which are considered to be the most fit for purpose. To study their resistance to hot oxidation, we used austenitic stainless steel AISI 304L, ferritic stainless steel AISI 430L and stainless steel Fe-16Cr-3Al. To study their ability to retain microorganisms, we used austenitic stainless steel AISI 316L, ferritic stainless steel AISI 430L, and duplex stainless steel, being a 50/50 blend of the two former ones. For this last purpose, the steels were compacted at three different pressures (300, 500 and 700 MPa) corresponding to different porosities. With regard to the hot oxidation, we quantified the positive or negative increments in volume, mass and density in the different types of sintering and oxidation treatment states. As a general performance trend, we observed that vacuum sintered steels are more resistant to oxidation than those sintered in an atmosphere of N2-5H2, and that austenitic stainless steels are slightly more resistant than the Cr-Al steels which, in turn, are more resistant than the ferritic stainless steels. With regard to the retention of microorganisms, the three sintered stainless steels were tested in different culture media using four types of bacteria. The best results for observation and counting were obtained with Staphylococcus aureus bacteria. Once sintered and colonized by microorganisms, for each material and compacting pressure we quantified the areas of the pores and the number of microorganisms situated in the pores and on the pore-free surface. In each case, the density of microorganisms in the pores and in the pore-free areas was established. As a general rule, we can say that the austenitic stainless steels appear to be more favourable for this type of study than the duplex steels which, in turn, are more favourable than the ferritic stainless steels. It also emerged that the areas with the pores depend unequivocally on the compacting pressure, and that the smaller the area of the pore the higher the density of the microorganisms. Consequently, it can be deduced that comparing an equal area of pores on a surface, the one with the smaller pores would retain a larger number of bacteria.

Fabrication of U. S. S. stainless and heat resisting steels.

"Seventh printing, 1957."

Transpassivation of Fe-Cr-Ni stainless steels

A transpassivation model was proposed for Fe–Cr–Ni stainless steels. In this model, the important steps and processes involved in transpassivation were illustrated. With some reasonable assumptions, transpassivation behaviours were predicted, such as the changes in film composition, film thickness, anodic current density and AC impedance spectrum in transpassive and secondary passive regions. It was demonstrated that these theoretical predictions were in good agreement with experimentally observed transpassivity of Fe–Cr–Ni stainless steels.

Defects in steel investment castings

A general investigation was performed, in an industrial environment, of the major types of defect specific to investment castings in steel. As a result of this work three types of metallurgical defect were selected for further study. In the first of these, defects in austenitic stainless steel castings were found to result from deoxidation by-products. As a result of metallographic investigation and the statistical analysis of experimental data, evidence was found to support the hypothesis that the other two classes of defects - in martensite stainless and low alloy steels -both resulted from internal or grain boundary oxidation of the chromium alloy constituent This was often found to be followed by reaction between the metal oxides and the ceramic mould material. On the basis of this study, proposals are made for a more fundamental investigation of the mechanisms involved and interim suggestions are given for methods of ameliorating the effect in an industrial situation.

Microstructural and environmental effects on fatigue crack propagation in duplex stainless steels

Fatigue crack initiation and propagation in duplex stainless steels are strongly affected by microstructure in both inert and aggressive environments. Fatigue crack growth rates in wrought Zeron 100 duplex stainless steel in air were found to vary with orientation depending on the frequency of crack tip retardation at ferrite/austenite grain boundaries. Fatigue crack propagation rates in 3.5% NaCl solution and high purity water are increased by hydrogen assisted transgranular cyclic cleavage of the ferrite. The corrosion fatigue results are interpreted using a model for the cyclic cleavage mechanism.

Process Monitoring and Defect Detection of Additive Manufacturing Using Inline Coherent Imaging

With applications ranging from aerospace to biomedicine, additive manufacturing (AM) has been revolutionizing the manufacturing industry. The ability of additive techniques, such as selective laser melting (SLM), to create fully functional, geometrically complex, and unique parts out of high strength materials is of great interest. Unfortunately, despite numerous advantages afforded by this technology, its widespread adoption is hindered by a lack of on-line, real time feedback control and quality assurance techniques. In this thesis, inline coherent imaging (ICI), a broadband, spatially coherent imaging technique, is used to observe the SLM process in 15 - 45 $\mu m$ 316L stainless steel. Imaging of both single and multilayer builds is performed at a rate of 200 $kHz$, with a resolution of tens of microns, and a high dynamic range rendering it impervious to blinding from the process beam. This allows imaging before, during, and after laser processing to observe changes in the morphology and stability of the melt. Galvanometer-based scanning of the imaging beam relative to the process beam during the creation of single tracks is used to gain a unique perspective of the SLM process that has been so far unobservable by other monitoring techniques. Single track processing is also used to investigate the possibility of a preliminary feedback control parameter based on the process beam power, through imaging with both coaxial and 100 $\mu m$ offset alignment with respect to the process beam. The 100 $\mu m$ offset improved imaging by increasing the number of bright A-lines (i.e. with signal greater than the 10 $dB$ noise floor) by 300\%. The overlap between adjacent tracks in a single layer is imaged to detect characteristic fault signatures. Full multilayer builds are carried out and the resultant ICI images are used to detect defects in the finished part and improve upon the initial design of the build system. Damage to the recoater blade is assessed using powder layer scans acquired during a 3D build. The ability of ICI to monitor SLM processes at such high rates with high resolution offers extraordinary potential for future advances in on-line feedback control of additive manufacturing.

Influence of grinding operations on surface integrity and chloride induced stress corrosion cracking of stainless steels

Stainless steels were developed in the early 20th century and are used where both the mechanical properties of steels and corrosion resistance are required. There is continuous research to allow stainless steel components to be produced in a more economical way and be used in more harsh environments. A necessary component in this effort is to correlate the service performance with the production processes. The central theme of this thesis is the mechanical grinding process.  This is commonly used for producing stainless steel components, and results in varied surface properties that will strongly affect their service life. The influence of grinding parameters including abrasive grit size, machine power and grinding lubricant were studied for 304L austenitic stainless steel (Paper II) and 2304 duplex stainless steel (Paper I). Surface integrity was proved to vary significantly with different grinding parameters. Abrasive grit size was found to have the largest influence. Surface defects (deep grooves, smearing, adhesive/cold welding chips and indentations), a highly deformed surface layer up to a few microns in thickness and the generation of high level tensile residual stresses in the surface layer along the grinding direction were observed as the main types of damage when grinding stainless steels. A large degree of residual stress anisotropy is interpreted as being due to mechanical effects dominating over thermal effects. The effect of grinding on stress corrosion cracking behaviour of 304L austenitic stainless steel in a chloride environment was also investigated (Paper III). Depending on the surface conditions, the actual loading by four-point bend was found to deviate from the calculated value using the formula according to ASTM G39 by different amounts. Grinding-induced surface tensile residual stress was suggested as the main factor to cause micro-cracks initiation on the ground surfaces. Grinding along the loading direction was proved to increase the susceptibility to chloride-induced SCC, while grinding perpendicular to the loading direction improved SCC resistance. The knowledge obtained from this work can provide a reference for choosing appropriate grinding parameters when fabricating stainless steel components; and can also be used to help understanding the failure mechanism of ground stainless steel components during service.

Sinterização de aço inoxidável reforçado com partículas nanométricas dispersas de carbeto de nióbio - NbC

Metal powder sintering appears to be promising option to achieve new physical and mechanical properties combining raw material with new processing improvements. It interest over many years and continue to gain wide industrial application. Stainless steel is a widely accepted material because high corrosion resistance. However stainless steels have poor sinterability and poor wear resistance due to their low hardness. Metal matrix composite (MMC) combining soft metallic matrix reinforced with carbides or oxides has attracted considerable attention for researchers to improve density and hardness in the bulk material. This thesis focuses on processing 316L stainless steel by addition of 3% wt niobium carbide to control grain growth and improve densification and hardness. The starting powder were water atomized stainless steel manufactured for Höganäs (D 50 = 95.0 μm) and NbC produced in the UFRN and supplied by Aesar Alpha Johnson Matthey Company with medium crystallite size 16.39 nm and 80.35 nm respectively. Samples with addition up to 3% of each NbC were mixed and mechanically milled by 3 routes. The route1 (R1) milled in planetary by 2 hours. The routes 2 (R2) and 3 (R3) milled in a conventional mill by 24 and 48 hours. Each milled samples and pure sample were cold compacted uniaxially in a cylindrical steel die (Ø 5 .0 mm) at 700 MPa, carried out in a vacuum furnace, heated at 1290°C, heating rate 20°C stand by 30 and 60 minutes. The samples containing NbC present higher densities and hardness than those without reinforcement. The results show that nanosized NbC particles precipitate on grain boundary. Thus, promote densification eliminating pores, control grain growth and increase the hardness values

Initiation and early crack growth in VHCF of stainless steels : Experimental and theoretical analysis

Mechanical fatigue is a failure phenomenon that occurs due to repeated application of mechanical loads. Very High Cycle Fatigue (VHCF) is considered as the domain of fatigue life greater than 10 million load cycles. Increasing numbers of structural components have service life in the VHCF regime, for instance in automotive and high speed train transportation, gas turbine disks, and components of paper production machinery. Safe and reliable operation of these components depends on the knowledge of their VHCF properties. In this thesis both experimental tools and theoretical modelling were utilized to develop better understanding of the VHCF phenomena. In the experimental part, ultrasonic fatigue testing at 20 kHz of cold rolled and hot rolled stainless steel grades was conducted and fatigue strengths in the VHCF regime were obtained. The mechanisms for fatigue crack initiation and short crack growth were investigated using electron microscopes. For the cold rolled stainless steels crack initiation and early growth occurred through the formation of the Fine Granular Area (FGA) observed on the fracture surface and in TEM observations of cross-sections. The crack growth in the FGA seems to control more than 90% of the total fatigue life. For the hot rolled duplex stainless steels fatigue crack initiation occurred due to accumulation of plastic fatigue damage at the external surface, and early crack growth proceeded through a crystallographic growth mechanism. Theoretical modelling of complex cracks involving kinks and branches in an elastic half-plane under static loading was carried out by using the Distributed Dislocation Dipole Technique (DDDT). The technique was implemented for 2D crack problems. Both fully open and partially closed crack cases were analyzed. The main aim of the development of the DDDT was to compute the stress intensity factors. Accuracy of 2% in the computations was attainable compared to the solutions obtained by the Finite Element Method.

Laser cladding and its potential to reduce particulate matter emissions from the automotive and locomotive sector

Laser Cladding (LC) is an emerging technology which is used both for coating applications as well as near-net shape fabrication. Despite its significant advantages, such as low dilution and metallurgical bond with the substrate, it still faces issues such as process control and repeatability, which restricts the extension to its applications. The following thesis evaluates the LC technology and tests its potential to be applied to reduce particulate matter emissions from the automotive and locomotive sector. The evaluation of LC technology was carried out for the deposition of multi-layer and multi-track coatings. 316L stainless steel coatings were deposited to study the minimisation of geometric distortions in thin-walled samples. Laser power, as well as scan strategy, were the main variables to achieve this goal. The use of constant power, reduction at successive layers, a control loop control system, and two different scan strategies were studied. The closed-loop control system was found to be practical only when coupled with the correct scan strategy for the deposition of thin walls. Three overlapped layers of aluminium bronze were deposited onto a structural steel pipe for multitrack coatings. The effect of laser power, scan speed and hatch distance on the final geometry of coating were studied independently, and a combined parameter was established to effectively control each geometrical characteristic (clad width, clad height and percentage of dilution). LC was then applied to coat commercial GCI brake discs with tool steel. The optical micrography showed that even with preheating, the cracks that originated from the substrate towards the coating were still present. The commercial brake discs emitted airborne particles whose concentration and size depended on the test conditions used for simulation in the laboratory. The contact of LC cladded wheel with rail emitted significantly less ultra-fine particles while maintaining the acceptable values of coefficient of friction.