Análise da curva de resfriamento e refino de grão da liga de alumínio AA 356

The macrostructure of an alloy solidification in the raw state is of utmost importance due to its influence on mechanical properties. A structure showing columnar grains is generally undesirable in most applications of cast products and grain refining aims to suppress the formation of these grains and get a fine-grained equiaxed structure that improves the supply of liquid metal and the mechanical properties, as yield strength and tensile strength limit, as well as the tendency of formation of hot cracks. The type and size of grains formed are determined by chemical composition, cooling rate and the use of inoculum for grain refining. Titanium and boron are the major refiners in the aluminum industry and can be added to the molten metal in the form of alloys such as Al-Ti, Al-Ti-B or Al-B. In this paper we will discuss the information obtained from cooling curves and first derivative of the cooling curve to obtain the thermal parameters that influence the process of grain refining alloy AA 356.0

Estudo do efeito do modificador Al-Sr no tratamento de modificação do eutético da liga AA356

The AA356 alloy is an alloy widely used in the automotive industry and aerospace due to its excellent mechanical properties. Refining the structure of eutectic silicon aluminum alloys is a fairly common practice in the foundry through treatment known as modification. This can be achieved by modifying agent adding chemicals such as contained in groups I and IIa of the periodic table and rare earths (europium, céreioi, praseodymium, neodymium, etc.). Has the ability to modify the structure of the eutectic, but only sodium and strontium produce an action modifier strong when used in low concentrations. The modifying effect of the shafts turn silicon into a fibrous form and branched surrounded by metallic matrix in the form of a composite structure that has the highest limit of tensile strength, ductility and machinability. In this work will be obtained ingots with and without the modifier type Al-10% Sr, made in sand molds and are generated and analyzed cooling curves and also the study of the macrostructure and microstructure of the solidified material. It was found that by adding the Al-Sr made shorten the solidification time and lower the grain size

Modificação da superfície do titânio e de sua liga Ti-6Al-4V por recobrimento com TiO2 e hidroxiapatita

In this work, the influence of modifications of the cp-Ti and Ti 6Al 4V alloy, by treating the surface with NaOH and depositing titanium oxide and hydroxyapatite by sol-gel method, on their biocompatibility was studied. The coatings were characterized by scanning electron microscopy and X-ray diffraction which showed that the coatings on Ti 6Al 4V are better than on cp-Ti. Adhesion tests showed that adhesion strength of the coatings on cp-Ti substrate is less than on Ti 6Al 4V as well as cytotoxicity for L929 fibroblast cells is higher

Efeito do Estrôncio (Sr) no tratamento de modificação do eutético da liga Al-1%Si

This study aimed to analyze the cooling curves, micro and macrograph alloy Al-1 %Si without the addition of strontium modifier and with the addition of the same. One of the ways of improving mechanical properties of alloy Al -Si is through the modification process. For the experiments two billets of the alloy Al-1%Si cast iron mold in a billet with addition of 0.02% strontium by weight, and the other billet without the addition of modifier were fused. In the solidification process of billet temperature was monitored and recorded every second for later plotting in Origin 8 program and analyzes the cooling curves obtained. The billets were cut and passed by grinding and polishing to perform the macrograph and micrographs. The results concerning the macrograph indicated that billet without the addition of Strontium particle size obtained was more refined than the billet where the strontium modifier was added. Regarding the micrograph, photos stemmed from the optical microscope didn´t show the expected modification effect by the addition of Strontium. This suggests that the low amount of silicon (1 %) present in the alloy used in this study interfered in the change process, because according to the literature review, Strontium 0.022 % by weight is sufficient to fully modify an alloy with 7% Silicon. The results from the cooling curve showed that both the eutectic temperature and the solidification time remained unchanged with the addition of strontium

Revitalização urbana da avenida nações unidas no município de Bauru

Localizada no centro-oeste do Estado de São Paulo, Bauru é considerada uma cidade de médio porte. Possui aproximadamente 360 mil habitantes (estimativa da população em 2009, segundo o IBGE), e com isso, apresenta diversos problemas relacionados à mobilidade urbana e ao planejamento urbano, tais como: trânsito intenso em determinadas vias, calçadas em mau estado de conservação, falta de incentivo aos meios de transporte mais sustentáveis – modos não motorizados (a pé e bicicletas) e transportes coletivos. Este Trabalho Final de Graduação propõe a requalificação urbana em uma das principais avenidas que da cidade de Bauru, a Nações Unidas. Este projeto tem maior destaque nos usuário de transportes não motorizados, incentivando assim, a maior utilização desses modos no cotidiano dos cidadãos

Estudo da influência da aplicação do fluido de corte no torneamento da liga de alumínio AA7075

One of the ways to minimize the effects of unproductive time caused by tool wear can be achieved by introducing an efficient system of lubrication and cooling in the process. However, in the last decade the research had the goal to restrict the maximum use of refrigerants and / or lubricants in metal-mechanical production. The important factors that justify this procedure include the operational costs of production, ecological issues, and the legal requirements of environmental conservation and preservation of human health. The purpose of the proposed work is the study of machining by turning with the focus on the influence caused by the application of cutting fluid in several ways of application (abundant and MQF) and also by comparing the results obtained by machining without the presence of fluid . For this purpose, the turning tests are conducted using an aluminum alloy (AA 7075). The response variables to be analyzed were obtained from the roughness (Ra and Ry), the stresses presented (VB) and their progression in relation to the cutting length achieved, the type of chip formed, in addition to changes in the degree of finish (roughness) presented by the turned parts. The results of this study should provide more detailed information about the actual influence of cutting fluids in turning this alloy, which are characterized by high rates of deformation when the formation of damaging your chip machining and also the quality of surface generated. Therefore, it is expected to provide subsidies to promote the optimization of machining this alloy making the most of the role of cutting fluid

Análise macro e micrográfica da liga AA-356 conforme a taxa de resfriamento

The present work aims to study the characteristics of the alloy Al - 7 % Si - 0 , 3Mg ( AA356 ) , more specifically characterize the macrostructure and microstructure and mechanical properties of the alloy ingots AA356 obtained in metal molds and sand molds for power studying the structures through the difference of cooling rates . This alloy is explained by the fact of referring league has excellent combination of properties such as low solidification shrinkage and good fluidity, good weldability , high wear resistance , high strength to weight ratio, has wide application in general engineering , and particularly in the automotive and aerospace engineering . In this work we will verify this difference in properties through two different cooling rates . We monitor the solid solidification temperatures by thermocouples building with them the cooling curve as a tool that will aid us to evaluate the effectiveness of the grain refining because it achieved with some important properties of the alloy as the latent heat of solidification fraction the liquid and solid temperatures, the total solidification time, and identify the presence of inoculants for grain refinement. Thermal analysis will be supported by the study of graphic software “Origin “will be achieved where the cooling curve and its first derivative that is the cooling rate. Made thermal analysis, analysis will be made in macrographs ingots obtained for observation of macrostructures obtained in both types of ingots and also analysis of micrographs where sampling will occur in strategic positions ingots to correlate with the microstructure. Finally will be collecting data from Brinell hardness of ingots and so then correlating the properties of their respective ingots with cooling rate. We found that obtained with cast metal ingots showed superior properties to the ingots obtained with sand mold

Usinagem da liga de níquel inconel 718 com pastilhas de cerâmica

The machining of super alloys resistant to high temperatures such as nickel alloys, inconel 718 specifically, is a very difficult job to obtain improvements in the process, due to the difficulty of machining at high cutting speeds, the use of these alloys in industries showed great developments in recent years, its application in aeronautical industry spread being used in vane turbo, compressor parts, props and set elements. The automotive, chemical, medical and others also took advantage of the great features of inconel 718 and has used the material. The high temperature resistant alloys have high machining difficulty, a fact that is associated with high cutting forces generated during machining which result in high temperatures. High levels of temperatures can cause deterioration of the cutting edge, with subsequent deformation or breakage, wear most common obtained in machining such materials are flank wear the formation of built-up edge for cutting and notch wear. The experimental part of the work consists in machining of nickel-based alloy Inconel 718 heat treated for hardness, using a tool based ceramic silicon nitride Sandvik (Si3N4) in order to compare the best results obtained in the master's thesis of SANTOS (2010) who used a tool ceramics also the basis of silicon nitride which was developed in the doctoral thesis of SOUZA (2005). Assays were performed on a CNC lathe and was noted for each cutting edge results obtained. Tests were made starting from an initial condition of the tool with cutting speed of 200 m/min, feed 0.5 mm and 0.5 mm depth of cut was reduced cutting speed for the subsequent tests with the same conditions of feed and depth of cut. The tool presented wear instant under two 200 m/min and 100 m/min, premature rupture of 50 m/min and finally cut provided with difficulty... (Complete abstract click electronic access below)

Crescimeno de apatita na superfície da liga Ti-7, 5Mo empregando tratamento higrotérmico

The objective of the present work was to evaluate surface of experimental alloy Ti-7.5Mo after hydrothermal treatment. Ingots were obtained in arc melting furnace under an argon atmosphere and then homogenized under vacuum at 1100ºC for 86.4 ks to eliminate chemical segregation and after cold worked discs were cutting and grinding. For surface treatment, samples were immersed in a container with NaOH aqueous solution 5M, autoclaved, washed with distilled water. Followed, samples were heat treated and they were soaking in 5xSBF to form an apatite layer on the surface. Surfaces were investigated by, scanning electron microscopy, X-Rays powder diffraction, atomic force microscopy and contact angle, in order to evaluate the wettability of the alloy surface. The results were compared with our previous studies using the group of chemical surface treatments and results shows better condition is 120 minutes in the autoclave

Caracterização da liga do sistema binário Ti-15Mo para aplicações biomedicas

As they have excellent mechanical properties, corrosion resistance and biocompatibility, much research has been conducted with respect to biomedical applications of titanium alloys. This work aims to study the experimental system binary alloy Ti-15Mo, in the raw state of fusion and heat treatment after homogenization, solubilization and calcination (simulating conditions employed for nanotube growth) targeting biomedical applications. Samples were obtained by casting the components in an electric arc furnace with inert atmosphere of argon. After obtaining the alloy, it was heat treated at three different heat treatments, namely homogenizing, calcining and simulation solubilization. The phases present were analyzed by X-ray diffraction, optical microscopy and microhardness testing

Caracterização estrutural da Liga Al-1% Si

The aim of this study is to characterize the macrostructure and microstructure of Al - 1%Si alloy obtained in sand and metallic molds. Aluminium has good mechanical properties, but adding silicon, even in small quantities, can change the microstructure and improves mechanical behavior. Workpieces were castings in metallic and sand molds and one can see a difference in their cooling curve, macroscopic and microscopic structures. The sand mold casting has lower cooling rate and so its grains are larger. Due to the lower concentration of grain boundary, the hardness is lower compared to that found in metallic molds, which has smaller grains and a higher hardness. Therefore, it can be concluded that the cooling rate and alloying elements affect the final microstructure of the workpiece

Análise da curva de resfriamento da liga de alumínio AA 356

It is very important to study the macrostructure of a material in the crude state of solidification due to influence the mechanical properties, as well as the study of their cooling curve. In the present work was to study the alloy AA 356, its macrostructure and its cooling curve. The material was cast in two different molds, a sand and other metallic. In this paper we study the differences in its macrostructure and its cooling curves. In macrostructure can observe the absence of the three zones of solidification and the presence of large pores because of moisture in the sand. In the sample taken from the metal mold can observe the three zones of solidification: a coquilhada, columnar and equiaxed

Crescimento de apatita na superfície da liga Ti-25Ta empregando dois tipos de tratamento de superfície: biomimético e deposição de polímero por eletrofiação

Titanium and its alloys has been widely used as materials for metallic biomaterials implants are usually employed to restore the hard tissue function, being used for artificial joints and bones, synthetic plates, crowns, dental implants and screws . Objective of this work was the surface modification of Ti-alloy 25Ta from biomimetic surface treatment of employment and deposition of polymer by electrospinning. The league was obtained from the fusion of the pure elements in the arc furnace with controlled atmosphere. The ingots were subjected to heat treatment, cold forged and sectioned discs with 13 mm diameter and 3 mm thick. Two surface treatments was evaluated, biomimetic and electrospinning with PCL fiber. The biomimetic treatment was performed involving alkaline treatment for three molarities 1.5M, 3M and 5M with immersion in SBF. The electrospinning was performed using PCL polymer alloy surface after the alkali treatment Ti25Ta 1M. For this group the polymer coated surfaces were immersed in calcium phosphate containing solution for immobilization of apatite. The results were compared with previous studies using surface treatment group to verify hydroxyapatite formation on the sample surface and it is concluded that the best condition is biomimetic treatment with 5M alkali treatment and heat treatment at 80 ° C for 72 hours

Comparação dos efeitos de compressão isostática e compressão uniaxial na obtenção da liga NiTi por metalurgia do pó

Several alloys present the shape memory effect and among them, the equiatomic NiTi alloy, nitinol, is the most important one. It is usually used in several engineering applications and also in biomedical devices, in the fabrication of orthodontic wire, stents and Judet staples. Although a considerable amount of these biomedical devices is utilized in Brazil and a fraction of it is already made here, all nitinol used is bought abroad. Thus, it is important to develop the necessary know-how to fabricate NiTi wire and sheet. It would mean less importation with job creation and wealth generation for the country. In this work nitinol was obtained powder metallurgy from elemental powders of Ti and Ni using uniaxial compression and uniaxial compression followed by isostatic compression. The final densities achieved were determined by the Archimedes method. The precipitation of intermetallic secondary phases was studied and the samples were characterized by metallographic analysis, optical microscopy and X-ray diffraction. Results indicated that 50 hours sintering route showed a low amount of intermetallics, and no trace of unreacted powder. XRD and metallography at room temperature indicated B19’ as the predominant phase, which corresponds to martensite. Although density results showed little dispersion, the most dense sample was compacted under uniaxial compression and presented 4.8 g/cm3, corresponding to 20.84% porosity. Density variation was considered normal to the measurement process and independent of the compaction mode

Estudo de tempos e temperaturas de sinterização na obtenção da liga NiTi por metalurgia do pó

The nickel-titanium alloys are very attractive and so it is widely used in industry, engineering applications in general and also in biomedical and dental applications. Besides showing the shape of memory effect, biocompatibility and superelastic, the alloy commercially known as Nitinol, has excellent mechanical properties. Most devices used in Brazil have been produced nationally, but using imported material is also necessary, which shows the need of produce the alloy nationally. In this study we have investigated the influence of sintering temperatures and times to obtain nickel-titanium alloys by powder metallurgy alloys and the characterization of the precipitated intermetallic phases by using the post-mix of elemental nickel and titanium in proportion of 49.5% Ti - 50.5% Ni. The samples were sintered at 930ºC for periods of 30, 40 and 50 hours and were characterized by optical microscopy using metallography and x-ray diffraction. The results of the study show that the 50 hours sintering time was the most suitable time for obtaining the alloy, observing a low volume of precipitated intermetallic phases and absence of Ni and Ti residuals