The Influence of Chemical Activation on Tooth Bleaching Using 10% Carbamide Peroxide

The aim of this study was to assess the influence of manganese gluconate, a chemical activator of bleaching agents, at a concentration of 0.01% on the efficiency of a 10% carbamide peroxide-based bleaching agent. Forty bovine incisors were immersed in a 25% instant coffee solution for seven days and randomly divided into two groups. Group 1 was the control group and consisted of 10% carbamide peroxide-based bleaching gel only. Group 2 consisted of 10% carbamide peroxide-based bleaching gel and 0.01% manganese gluconate. Three readings of color were taken using the Vita Easy-shade spectrophotometer: the initial reading, a reading at seven days, and a reading at 14 days. Total color variation was calculated by Delta E*Lab. Data were submitted to the statistical t-test (5%), which showed that after seven days group 2 had a significant increase in the degree of tooth bleaching compared with group 1. The mean values (+/-SD) were 16.33 (+/-3.95) for group 1 and 19.29 (+/-4.97) for group 2. However, the results for group 1 and group 2 were similar after 14 days. Adding 0.01% manganese gluconate to 10% carbamide peroxide bleaching gel increased the degree of tooth bleaching after a seven-day treatment and did not influence the resulting shade after 14 days.

In Vitro Assessment of Chemical Activation Efficiency During In-office Dental Bleaching

Purpose: This study compared five types of chemical catalyzing agents added to 35% hydrogen peroxide gel, with regard to their capacity of intensifying in-office dental bleaching results.Methods: One-hundred and twenty bovine incisors were used, of which the crowns and roots were cut in the incisor-apical direction, to acquire the dimensions of a human central incisor. The specimens were sectioned in the mesiodistal direction by means of two longitudinal cuts, the lingual halves being discarded. The vestibular halves received prophylaxis with a bicarbonate jet, ultrasound cleaning and acid etching on the dentinal portion. Next, the specimens were stored in receptacles containing a 25% instant coffee solution for two weeks. After the darkening period, initial measurement of the shade obtained was taken with the Easy Shade appliance, which allowed it to be quantified by the CIELab* method. The samples were divided into six groups, corresponding to the chemical activator used: a) none (CON); b) ferric chloride (CF); c) ferrous sulphate (SF); d) manganese gluconate (GM); e) manganese chloride (CM); f) mulberry root extract (RA). Each group received three 10-minute applications of the gels containing the respective activating agents. Next, a new shade measurement was made.Results: The Analysis of Variance and Tukey tests (alpha=5%) showed statistically significant differences for the shade perception values (p=0.002). Groups GM, CM and RA showed significantly higher means than the control group.Conclusion: The presence of some chemical activators is capable of resulting in a significant increase in tooth shade variation.

Preparation and evaluation of an experimental luting glass ionomer cement to be used in dentistry

The aim of this paper is to compare the fluoride-releasing and mechanical properties of an experimental luting glass ionomer cement, which has a modified composition and a commercial luting cement. The experimental powder was obtained by sol-gel process and then, it was used to prepare the experimental cements. The properties of cement pastes, such as setting time and working time, microhardness and diametral tensile strength were determined. Fluoride release from GICs was evaluated at time intervals of 1, 7, 14, 21 and 28 days in deionized water. Atomic force microscopy (AFM) analyses showed that the surface of the experimental cements is more homogeneous than commercial GICs. The mechanical properties and the measure of liberation of fluoride of the two cements were influenced by ratio powder:liquid and chemical composition of the precursor powders. Experimental cements released less fluoride than commercial cements. However, this liberation was more constant during the analyzed period. Thus, the results obtained in this study indicated that the composition of the experimental powder modified by the niobium can lead the formation of the polysalt matrix with good mechanical properties. In other words, we can say that experimental powder offered considerable promise for exploitation in dental field.

The influence of internal surface treatments on tensile bond strength for two ceramic systems

Statement of the Problem: the ceramic composition and surface microstructure of all-ceramic restorations are important components of an effective bonding substrate. Hydrofluoric acid and sandblasting are well-known procedures for surface treatment; however, surface treatment for high alumina-containing and lithium disilicate ceramics have not been fully investigated.Purpose: This in vitro study evaluated the tensile bond strength of resin cement to two types of ceramic systems with different surface treatments.Methods and Materials: Thirty specimens of each ceramic system were made according to the manufacturer's instructions and embedded in polyester resin. Specimens of In-Ceram Alumina [1] and IPS Empress 2 [E] were distributed to three groups with differing surface treatments (n=10): sandblasting with 50 jam aluminum oxide (APA); sandblasting with 110 pm aluminum oxide modified with silica particles (ROCATEC System-RS); a combination of sandblasting with APA and 10% hydrofluoric acid etching (HA) for two minutes on In-Ceram and for 20 seconds for IPS Empress 2. After the respective surface treatments, all the specimens were silanated, and Rely-X resin cement was injected onto the ceramic surface and light polymerized. The specimens were stored in distilled water at 37 degrees C for 24 hours and thermally cycled 1,100 times (5 degrees C/55 degrees C). The tensile bond strength test was performed in a universal testing machine at a 0.5 mm/minute crosshead speed.Results: the mean bond strength values (AWa) for IPS Empress 2 were 12.01 +/- 5.93 (EAPA), 10.34 +/- 1.77 (ERS) and 14.49 +/- 3.04 (EHA). The mean bond strength values for In-Ceram Alumina were 9.87 +/- 2.40 JAPA) and 20.40 +/- 6.27 (IRS). All In-Ceram specimens treated with 10% hydrofluoric acid failed during thermal cycling.Conclusion: the Rocatec system was the most effective surface treatment for In-Ceram Alumina ceramics; whereas, the combination of aluminum oxide sandblasting and hydrofluoric acid etching for 20 seconds worked more effectively for Empress 2 ceramics.

Effect of mechanical cycling on the push-out bond strength of fiber posts adhesively bonded to human root dentin

This study evaluated the effect of mechanical cycling on the bond strength of fiber posts bonded to root dentin. The hypotheses examined were that bond strength is not changed after fatigue testing and bond strength does not present vast variations according to the type of fiber post. Sixty crownless, single-rooted human teeth were endodontically treated, with the space prepared at 12 mm. Thirty specimens received a quartz fiber post (Q-FRC (DT Light-Post), and the remaining 30 specimens received a glass fiber post (G-FRC) (FRC Postec Plus). All the posts were resin luted (All Bond+Duolink), and each specimen was embedded in a cylinder with epoxy resin. The specimens were divided into six groups: G1-Q-FRC+no cycling, G2- Q-FRC+20,000 cycles (load: 50N, angle of 45 degrees; frequency: 8Hz); G3- Q-FRC+2,000,000 cycles; G4- G-FRC+no cycling; G5- G-FRC+20,000 cycles; G6- GFRC+2,000,000 cycles. The specimens were cut perpendicular to their long axis, forming 2-mm thick disc-samples, which were submitted to the push-out test. ANOVA (alpha=.05) revealed that: (a) QFRC (7.1 +/- 2.2MPa) and G-FRC (6.9 +/- 2.1MPa) were statistically similar (p=0.665); (b) the no cycling groups (7.0 +/- 2.4MPa), 20,000 cycles groups (7.0 +/- 2.1MPa) and 2,000,000 cycles groups (7.0 +/- 2.0MPa) were statistically similar (p=0.996). It concluded that mechanical cycling did not affect the bond strength of two fiber posts bonded to dentin.