Preparation and luminescence properties of the mesoporous MCM-41s intercalated with rare earth complex

Rare earth complex Eu(DBM)(3)phen (DBM: dibenzoylmethane, phen: 1.10-phenanthroline) hits been incorporated into unmodified MCM-41 and modified MCM-41s by aminopropyltriethoxysilane (APTES) or N-[(3-triethoxysilyl)propyl]ethylenediamine(TEPED). Thus, the assemblies of unmodified or modified MCM-41s with rare earth (RE) complex have been obtained. XRD spectra. NMR spectra. diffuse reflectance spectra. and the luminescence spectra were used to characterize the pure RE complex and the corresponding assemblies. The assemblies have better luminescence properties under UV irradiation. and their fluorescence lifetimes on the excited state are longer than that of the corresponding pure complex. The possible mechanisms are also discussed in the context.

Nanocluster-containing mesoporous magnetoceramics from hyperbranched organometallic polymer precursors

Pyrolysis of hyperbranched poly[1,1'-ferrocenylene(methyl)silyne] (5) yields mesoporous, conductive, and magnetic ceramics (6). Sintering at high temperatures (1000-1200 degrees C) under nitrogen and argon converts 5 to 6N and 6A, respectively, in similar to 48-62% yields. The ceramization yields of 5 are higher than that (similar to 36%) of its linear counterpart poly[1,1'-ferrocenylene(dimethyl)silylene] (1), revealing that the hyperbranched polymer is superior to the linear one as a ceramic precursor. The ceramic products 6 are characterized by SEM, XPS, EDX, XRD, and SQUID. It is found that the ceramics are electrically conductive and possess a mesoporous architecture constructed of tortuously interconnected nanoclusters. The iron contents of 6 estimated by EDX are 36-43%, much higher than that (11%) of the ceramic 2 prepared from the linear precursor 1. The nanocrystals in 6N are mainly alpha-Fe2O3 whereas those in 6A are mainly Fe3Si. When magnetized by an external field at room temperature, 6A exhibits a high-saturation magnetization (M-s similar to 49 emu/g) and near-zero remanence and coercivity; that is, 6A is an excellent soft ferromagnetic material with an extremely low hysteresis loss.

Encapsulation of Eu(TTA)(3) into MCM-41 mesoporous molecular sieve by sol-gel method

The rare earth complex Eu(TTA)(3) was successfully encapsulated into MCM-41 mesoporous molecular sieve by the addition of the complex into the sol-gel mixture for the synthesis of MCM-41 mesoporous material under microwave radiation. The as-synthesized MCM-41-hosted Eu(TTA)(3) mesophase was confirmed to possess hexagonally ordered mesostructure and a uniform crystal. size of about 30 nm with XRD and HRTEM techniques. Moreover, the IR spectrum, photoluminescence effect and fluorescence lifetime of the Eu(TTA)(3)/MCM-41 hybrid were also studied. An increase in Stokes' shift and no change in luminescence lifetime were observed to the resultant mesophase in comparison with Eu(TTA)(3) in ethanol solution.

An encapsulation of the rare earth complex in modified mesoporous molecular sieve MCM-41

The encapsulation of a rare earth (RE) complex Eu(DBM)(3)phen in modified S1-MCM-41 with 3-aminopropyltriethoxysilane is reported for the first time. The luminescence intensity of the RE complex in the modified Si-MCM-41 is about 9 times as strong as in unmodified Si-MCM-41 and the luminescence of the RE complex in the modified SI-MCM-41 has good color purity.