Planar waveguides based on nanocrystalline and Er3+ doped SnO2

Luminescent SnO2: x%mol Er3+ (x=0.1-2.0) thin films have been spin coated on borosilicate and silica substrates from water colloidal suspensions that could be prepared containing up to 40% in weight SnO2 nanocrystalline powders. High Resolution Transmission Electron Microscopy results show the well known SnO2 cassiterite structure and nanocrystallites around 10 nm in diameter, corroborating results from X-ray diffraction. Mono and multi layers have been prepared from the stable colloidal suspensions and films thickness was observed to increase linearly, up to 200 nm, with the colloidal suspensions nanoparticles amount. Excitation and emission spectra have been measured and Er3+ ions were found to be essentially incorporated into the cassiterite structure, substituting for Sn4+, for doping concentration lower than 0.05 mol%. Er3+ ions also appear segregated at the grains surface for higher doping concentration. The optical parameters (refractive index, thickness and propagating modes) of a waveguide sample were measured at 632.8 and 543.4 nm by the prism coupling technique. A monomodal waveguide was obtained with attenuation loss of 3.5 dB/cm along a 2.5 cm optical path.

Er-doped silica-based waveguides prepared by different techniques: RF-sputtering, sol-gel and ion-exchange

Erbium-activated silica-based planar waveguides were prepared by three different technological routes: RF-sputtering, sol-gel and ion exchange. Various parameters of preparation were varied in order to optimize the waveguides for operation in the NIR region. Particular attention was devoted to the minimization of the losses and the increase of the luminescence efficiency of the metastable I-4(13/2) state of the Er3+ ion. Waveguide properties were determined by m-line spectroscopy and loss measurements. Waveguide Raman and luminescence spectroscopy were used to obtain information about the structure of the prepared films and about the dynamical processes related to the luminescence of the Er3+ ions.

Blue cooperative luminescence properties in Yb3+ doped GeO2-PbO-Bi2O3 vitreous system for the production of thin films

Germanate glasses are of interest for optoelectronic applications because they combine high mechanical strength, high chemical durability and temperature stability with a large transmission window (400 to 4500 nm) and high refractive index (2.0). GeO2-PbO-Bi2O3 glasses doped with Y-b(3+) were fabricated by melting powders in a crucible and then pouring them in a brass mold. Energy Dispersive Spectroscopy showed that the glass composition has a high spatial uniformity and that the Yb concentration in the solid sample is proportional to the Yb concentration in the melt, what was confirmed by absorption measurements. Intense blue emission at 507 nm was observed, corresponding to half of the wavelength of the near infrared region (NIR) emission; besides, a decay lifetime of 0.25 ms was measured and this corresponds to half of the decay lifetime in the infrared region; these are very strong indications of the presence of blue cooperative luminescence. Larger targets have been produced to be sputtered, resulting in thin films for three dimensional (3D) display and waveguide applications. (c) 2006 Elsevier B.V. All rights reserved.

Erbium- and ytterbium-doped sol-gel SiO2-HfO2 crack-free thick films onto silica on silicon substrate

Aware of the difficulties in applying sol-gel technology on the preparation of thin films suitable for optical devices, the present paper reports on the preparation of crack-free erbium- and ytterbium-doped silica: hafnia thick films onto silica on silicon. The film was obtained using a dispersion of silica-hafnia nanoparticles into a binder solution, spin-coating, regular thermal process and rapid thermal process. The used methodology has allowed a significant increase of the film thickness. Based on the presented results good optical-quality films with the required thickness for a fiber matching single mode waveguide were obtained using the erbium- and ytterbium-activated sol-gel silica:hafnia system. The prepared film supports two transversal electric modes at 1550 nm and the difference between the transversal electric mode and the transversal magnetic mode is very small, indicating low birefringence. Photoluminescence of the I-4(13/2) -> I-4(15/2) transition of erbium ions shows a broad band centered at 1.53 mu m with full width at a half maximum of 28 nm. Up-conversion emission was carried out under different pump laser powers, and just one transition at red region was observed. (c) 2006 Elsevier B.V. All rights reserved.

Er3+-doped germanate glasses for active waveguides prepared by Ag+/K+ <-> Na+ ion-exchange

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Rare Earth Doped SnO(2) Nanoscaled Powders and Coatings: Enhanced Photoluminescence in Water and Waveguiding Properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efficient Distributed Feedback Dye Laser in Silk Fibroin Films

We observed longitudinal single-mode operation in a distributed feedback dye laser consisting of silk fibroin films doped with Rhodamine 6G dye and infiltrated with silica or silver nanoparticles.

Frequency upconversion in a Pr(3+) doped chalcogenide glass containing silver nanoparticles

We report on orange-to-blue frequency upconversion (UC) in Pr(3+) doped chalcogenide glass (Ga(10)Ge(25)S(65)) doped with Ag(2)S and heat treated under different conditions to nucleate silver nanoparticles (NPs). The experiments were performed using 7 ns pulses from a dye laser that operates at similar to 590 nm, in resonance with the (3)H(4)->(1)D(2) transition of Pr(3+) ions. The enhancement observed in the UC emission at similar to 494 nm, ascribed as (3)P(0)->(3)H(4) transition of the Pr(3+) ion, is attributed to the large local field acting on the emitting ions due to the presence of the metallic NPs. (C) 2008 American Institute of Physics.

Novel fabrication process of planar waveguides in rare-earth doped fluoroindate glasses

We report the successful fabrication of planar waveguides in rare-earth doped fluoroindate glass substrates. A new procedure for waveguide fabrication using a thermally evaporated AgF nonmetallic film was developed. The refractive index changes of more than 0.03, associated to low propagation losses achieved, open new perspectives and show the potentiality of using this glass family toward further developments in fabrication and design of integrated optical devices for optical communication wavelengths.© 1995 American Institute of Physics.

Frequency upconversion in Nd3+-doped fluoroindate glass

We report the observation of frequency upconversion in fluoroindate glasses with the following compositions: (mol%) (39 - x)InF3-20ZnF2-20SrF2-16BaF 2-2GdF3-2NaF-1GaF3-xNdF3 (x = 0.05, 0.1, 0.5, 1, 2, 3). The excitation source was a dye laser in resonance with the 4I9/2→(2G5/2, 2G7/2) transition of the Nd3+ ions. The upconverted fluorescence spectra show emissions from ∼ 350 to ∼ 450 nm, corresponding to transitions 4D3/2→4I9/2 ;4D3/2→4I11/2; 2P3/2→ 4I9/2; 4D3/2→4I13/2; 2P3/2→4I11/2; 4D3/2→4I15/2; and 2P3/2 → 4I13/2. The dependence of the fluorescence signals on the laser intensity indicates that two laser photons participate in the process. The temporal behavior of the signal indicates that energy transfer among the Nd3+ ions is the main mechanism which contributes to upconversion at 354 and 382 nm.

Giant non-linear absorption in Er3+-doped fluoroindate glass

Non-linear absorption is observed in Er3+-doped fluoroindate glass (in mol% 37InF2:20ZnF2:20SrF2:16BaF2:2GdF2: 2NaF:1GaF3:2ErF3) when the sample is irradiated with a CW laser emitting at 650 nm. An intensity dependence of the optical transmittance is detected. Saturation and sequential absorption of two photons are responsible for the decrease of 50% in the transmittance. The results are explained by simple models which are solved based on rate-equations for the populations of energy levels.

Sol-Gel Erbium-Doped Silica-Hafnia Planar and Channel Waveguides

Erbium activated SiO2 -HfO2 planar waveguides, doped with Er3+ concentrations ranging from 0.01 to 4 mol%, were prepared by sol-gel method. The films were deposited on v-SiO2 and silica-on-silicon substrates using dip-coating technique. The waveguides show high densification degree, effective intermingling of the two film components, and uniform surface morphology. The waveguide deposited on silica-on-silicon substrates shows one single propagation mode at 1.5μm, with a confinement coefficient of 0.81 and an attenuation coefficient of 0.8 dB/cm at 632.8nm. Emission in the C-telecommunication band was observed at room temperature for all the samples upon continuouswave excitation at 980 nm or 514.5 nm. The shape of the emission band corresponding to the 4I13/2 → 4I15/2 transition is found to be almost independent both on erbium content and excitation wavelength, with a FWHM between 44 and 48 nm. The 4I13/2 level decay curves presented a single-exponential profile, with a lifetime ranging between 1.1 - 6.6 ms, depending on the erbium concentration. Infrared to visible upconversion luminescence upon continuous-wave excitation at 980 nm was observed for all the samples. Channel waveguide in rib configuration was obtained by etching the active film in order to have a well confined mode at 1.5 μm.

Waveguide features in self-patternable amine functionalized organic-inorganic hybrids

We report the use of organic-inorganic sol-gel derived poly(oxyehylene)/ siloxane hybrid doped with methacrylic acid modified zirconium (IV) n-propoxide for the fabrication of low cost waveguides trough direct UV laser writing. The organic-inorganic hybrids were processed as monoliths with size and shape control. The effective guiding region was identified and the number of modes was estimated via mode field analyses. A grating was successfully superimposed on the channel and the respective reflection spectrum was measured, enabling the determination of the guiding region dimension, the calculation of the effective refractive index of the guided mode. © 2007 IEEE.

Photodegradation of phenol red on a Ni-doped niobate/carbon composite

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Single precursor route to efficient cobalt sulphide counter electrodes for dye sensitized solar cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)