REGROWTH RATES OF AMORPHOUS LAYERS IN SILICON-ON-SAPPHIRE FILMS.

The rate and direction of regrowth of amorphous layers, created by self-implantation, in silicon-on-sapphire (SOS) have been studied using time resolved reflectivity (TRR) experiments performed simultaneously at two wavelengths. Regrowth of an amorphous layer towards the surface was observed in specimens implanted with 3 multiplied by (times) 10**1**5Si** plus /cm**2 at 50keV and regrowth of a buried amorphous layer, from a surface seed towards the sapphire, was observed in specimens implanted with 1 multiplied by (times) 10**1**5Si** plus /cm**2 at 175keV. Rapid isothermal heating to regrow the layers was performed in an electron beam annealing system. The combination of 514. 5nm and 632. 8nm wavelengths was found to be particularly useful for TRR studies since the high absorption in amorphous silicon, at the shorter wavelength, means that the TRR trace is not complicated by reflection from the silicon-sapphire interface until regrowth is nearly complete.

PHOTOENHANCED DEPOSITION OF HYDROGENATED AMORPHOUS SILICON THIN FILMS.

This paper will review the different U. V. lamp photo-CVD (Chemical Vapor Deposition) techniques which have been utilized for the production of highly photoconductive hydrogenated amorphous silicon (a-Si:H) thin films. Most of these require the transmission of U. V. light through a window into the reaction vessel; leading to unwanted U. V. light absorption by the window and the a-Si:H film which tends to form on its inner surface. A deposition system developed in our laboratory will also be described, which circumvents these problems by incorporating a windowless discharge lamp into the reaction vessel.