Determine Initial Cause for Current Premature Portland Cement Concrete Pavement Deterioration Final Report, 2000

A detailed investigation has been conducted on core samples taken from 17 portland cement concrete pavements located in Iowa. The goal of the investigation was to help to clarify the root cause of the premature deterioration problem that has become evident since the early 1990s. Laboratory experiments were also conducted to evaluate how cement composition, mixing time, and admixtures could have influenced the occurrence of premature deterioration. The cements used in this study were selected in an attempt to cover the main compositional parameters pertinent to the construction industry in Iowa. The hardened air content determinations conducted during this study indicated that the pavements that exhibited premature deterioration often contained poor to marginal entrained-air void systems. In addition, petrographic studies indicated that sometimes the entrained-air void system had been marginal after mixing and placement of the pavement slab, while in other instances a marginal to adequate entrained-air void system had been filled with ettringite. The filling was most probably accelerated because of shrinkage cracking at the surface of the concrete pavements. The results of this study suggest that the durability—more sciecifically, the frost resistance—of the concrete pavements should be less than anticipated during the design stage of the pavements. Construction practices played a significant role in the premature deterioration problem. The pavements that exhibited premature distress also exhibited features that suggested poor mixing and poor control of aggregate grading. Segregation was very common in the cores extracted from the pavements that exhibited premature distress. This suggests that the vibrators on the paver were used to overcome a workability problem. Entrained-air voids formed in concrete mixtures experiencing these types of problems normally tend to be extremely coarse, and hence they can easily be lost during the paving process. This tends to leave the pavement with a low air content and a poor distribution of air voids. All of these features were consistent with a premature stiffening problem that drastically influenced the ability of the contractor to place the concrete mixture. Laboratory studies conducted during this project indicated that most premature stiffening problems can be directly attributed to the portland cement used on the project. The admixtures (class C fly ash and water reducer) tended to have only a minor influence on the premature stiffening problem when they were used at the dosage rates described in this study.

Steel Diaphragms in Prestressed Concrete Girder Bridges, September 2004

Over the years, bridge engineers have been concerned about the response of prestressed concrete (PC) girder bridges that had been hit by over-height vehicles or vehicle loads. When a bridge is struck by an over-height vehicle or vehicle load, usually the outside and in some instances one of the interior girders are damaged in a bridge. The effect of intermediate diaphragms in providing damage protection to the PC girders of a bridge is not clearly defined. This analytical study focused on the role of intermediate diaphragms in reducing the occurrence of damage in the girders of a PC-girder bridge that has been struck by an over-height vehicle or vehicle load. The study also investigated whether a steel, intermediate diaphragm would essentially provide the same degree of impact protection for PC girders as that provided by a reinforced-concrete diaphragm. This investigation includes the following: a literature search and a survey questionnaire to determine the state-of-the-art in the use and design of intermediate diaphragms in PC-girder bridges. Comparisons were made between the strain and displacement results that were experimentally measured for a large-scale, laboratory, model bridge during previously documented work and those results that were obtained from analyses of the finite-element models that were developed during this research for that bridge. These comparisons were conducted to calibrate the finite element models used in the analyses for this research on intermediate diaphragms. Finite-element models were developed for non-skewed and skewed PC-girder bridges. Each model was analyzed with either a reinforced concrete or two types of steel, intermediate diaphragms that were located at mid-span of an interior span for a PC-girder bridge. The bridge models were analyzed for lateral-impact loads that were applied to the bottom flange of the exterior girders at the diaphragms location and away from the diaphragms location. A comparison was conducted between the strains and displacements induced in the girders for each intermediate-diaphragm type. These results showed that intermediate diaphragms have an effect in reducing impact damage to the PC girders. When the lateral impact-load was applied at the diaphragm location, the reinforced-concrete diaphragms provided more protection for the girders than that provided by the two types of steel diaphragms. The three types of diaphragms provided essentially the same degree of protection to the impacted, PC girder when the lateral-impact load was applied away from the diaphragm location.

Effective Structural Concrete Repair, Volume 1 of 3, Repair of Impact Damaged Prestressed Concrete Beams with CFRP, March 2004

Structural concrete is one of the most commonly used construction materials in the United States. However, due to changes in design specifications, aging, vehicle impact, etc. – there is a need for new procedures for repairing concrete (reinforced or pretressed) superstructures and substructures. Thus, the overall objective of this investigation was to develop innovative cost effective repair methods for various concrete elements. In consultation with the project advisory committee, it was decided to evaluate the following three repair methods: • Carbon fiber reinforced polymers (CFRPs) for use in repairing damaged prestressed concrete bridges • Fiber reinforced polymers (FRPs) for preventing chloride penetration of bridge columns • Various patch materials The initial results of these evaluations are presented in this three volume final report. Each evaluation is briefly described in the following paragraphs. A more detailed abstract of each evaluation accompanies the volume on that particular investigation.

Development of a Method to Determine Pavement Damage Due to Detours, Project 02-105, Apirl 2005

The research presented in this report provides the basis for the development of a new procedure to be used by the Iowa DOT and cities and counties in the state to deal with detours. Even though the project initially focused on investigating new tools to determine condition and compensation, the focus was shifted to traffic and the gas tax method to set the basis for the new procedure. It was concluded that the condition-based approach, even though accurate and consistent condition evaluations can be achieved, is not feasible or cost effective because of the current practices of data collection (two-year cycle) and also the logistics of the procedure (before and after determination). The gas tax method provides for a simple, easy to implement, and consistent approach to dealing with compensation for use of detours. It removes the subjectivity out of the current procedures and provides for a more realistic (traffic based) approach to the compensation determination.

Effective Structural Concrete Repair, Volume 2 of 3, Use of FRP to Prevent Chloride Penetration in Bridge Columns, March 2004

Structural concrete is one of the most commonly used construction materials in the United States. However, due to changes in design specifications, aging, vehicle impact, etc. – there is a need for new procedures for repairing concrete (reinforced or pretressed) superstructures and substructures. Thus, the overall objective of this investigation was to develop innovative cost effective repair methods for various concrete elements. In consultation with the project advisory committee, it was decided to evaluate the following three repair methods: • Carbon fiber reinforced polymers (CFRPs) for use in repairing damaged prestressed concrete bridges • Fiber reinforced polymers (FRPs) for preventing chloride penetration of bridge columns • Various patch materials The initial results of these evaluations are presented in this three volume final report. Each evaluation is briefly described in the following paragraphs. A more detailed abstract of each evaluation accompanies the volume on that particular investigation.

Effective Structural Concrete Repair, Volume 3 of 3, Evaluation of Repair Materials for Use in Patching Damaged Concrete, March 2004

Structural concrete is one of the most commonly used construction materials in the United States. However, due to changes in design specifications, aging, vehicle impact, etc. – there is a need for new procedures for repairing concrete (reinforced or pretressed) superstructures and substructures. Thus, the overall objective of this investigation was to develop innovative cost effective repair methods for various concrete elements. In consultation with the project advisory committee, it was decided to evaluate the following three repair methods: • Carbon fiber reinforced polymers (CFRPs) for use in repairing damaged prestressed concrete bridges • Fiber reinforced polymers (FRPs) for preventing chloride penetration of bridge columns • Various patch materials The initial results of these evaluations are presented in this three volume final report. Each evaluation is briefly described in the following paragraphs. A more detailed abstract of each evaluation accompanies the volume on that particular investigation.

Sustainable Development and Concrete Technology, May 2004

For a variety of reasons, the concrete construction industry is not sustainable. First, it consumes huge quantities of virgin materials. Second, the principal binder in concrete is portland cement, the production of which is a major contributor to greenhouse gas emissions that are implicated in global warming and climate change. Third, many concrete structures suffer from lack of durability which has an adverse effect on the resource productivity of the industry. Because the high-volume fly ash concrete system addresses all three sustainability issues, its adoption will enable the concrete construction industry to become more sustainable. In this paper, a brief review is presented of the theory and construction practice with concrete mixtures containing more than 50% fly ash by mass of the cementitious material. Mechanisms are discussed by which the incorporation of high volume of fly ash in concrete reduces the water demand, improves the workability, minimizes cracking due to thermal and drying shrinkage, and enhances durability to reinforcement corrosion, sulfate attack, and alkali-silica expansion. For countries like China and India, this technology can play an important role in meeting the huge demand for infrastructure in a sustainable manner.

Two-Lift Portland Cement Concrete Pavements to Meet Public Needs, September 2004

The report reviews the past work in the United States and internationally in the development of two-lift pavements. It points out the strengths and limitations in the construction of such portland cement concrete pavements. Certain cost, mix design, and construction problems are inhibiting the growth of this product. Changes in the availability of aggregates, knowledge of materials and new construction equipment, and the desire for specific surfaces to meet noise, durability, and safety are prompting the need to reconsider this type of construction.

Blended Cements Improving Concrete Properties Using Environmentally Responsible Mixtures, December 2003

Recent research evaluated the behavior of concrete made with supplementary cementitious materials (SCMs) such as fly ash and ground granulated blast-furnace slag under a variety of conditions. Correlations were found among the source and proportion of the SCMs, curing conditions, concrete set time, maturity, strength development, and cracking potential.

Concrete Paving Notes Construction No.1, 2005

This booklet will help developers, consultants, and engineers planning concrete pavement construction projects, superintendents and supervisors who want a basic training aid and reference, and crew members new to the concrete paving industry. It provides a general description of current concrete pavement construction practices, from establishing preconstruction control mechanisms to sealing joints. It also provides a quick troubleshooting reference.

Improving Concrete Pavement Curing, March 2003

· Evaluate the effect of different curing materials and techniques on concrete pavement properties. · Better understand the relationships between various concrete test measurements and concrete properties affected by curing.

Developing Smooth, Quiet, Safe Portland Cement Concrete Pavements, March 2004

The concrete paving industry has spent large amounts of time working to provide safe, quiet, and smooth pavements for the traveling public as their needs and driving habits have changed since the advent of the automobile. During that time, the efforts of research, design, and construction were directed at one of the problems at a time. Current public surveys indicate that the traveling public wishes to have safe, quiet, and smooth pavements. This report identifies the problems remaining in the areas of developing smooth, quiet, and safe portland cement concrete pavement in each pavement we build. It develops the research framework that can be used to bring the existing information together with additional research in each area. The resulting answers can be used in each pavement design for a quiet, safe, and smooth pavement that is also long lasting.

Two Lift Portland Cement Concrete Pavements to Meet Public Needs, September 2004

The report reviews the past work in the United States and internationally in the development of two-lift pavements. It points out the strengths and limitations in the construction of such portland cement concrete pavements. Certain cost, mix design, and construction problems are inhibiting the growth of this product. Changes in the availability of aggregates, knowledge of materials and new construction equipment, and the desire for specific surfaces to meet noise, durability, and safety are prompting the need to reconsider this type of construction.

Ultra-Thin PCC Overlays, January 2005

· Evaluate conventional methods of slab removal and asphalt surface preparation for subsequent overlays of portland cement concrete (PCC) in the “remove and replace” areas. · Evaluate existing asphaltic concrete surface under the “remove and patch” areas of rehabilitation areas and evaluate joint formation in the areas of patching. · Evaluate polypropylene fiber enhanced concrete at the three-inch depth to determine the cost/benefit of its inclusion. · Evaluate the performance of the rehabilitated ultra-thin whitetopping sections and the extended performance of the existing ultra-thin sections with and without patching. · Validate existing ultra-thin whitetopping design procedures of the Portland Cement Association (PCA) and American Concrete Pavement Association (ACPA) for application in Iowa.

Desafios da gestão e liderança feminina em Cabo Verde: como exercer a liderança em espaços de identidade masculina

O objectivo do presente estudo é identificar, caracterizar e entender os factores que contribuem para a eficácia da gestão e liderança da mulher cabo-verdiana num cenário de chefia de topo, em espaços caracterizados pela predominância masculina, transformando-se assim num desafio constante para as mulheres a nível mundial e em particular, para as mulheres cabo-verdianas. Foi realizada uma pesquisa bibliográfica sobre liderança e sobre género, mais especificamente, sobre o papel da mulher no contexto do trabalho. Trata-se de uma pesquisa de natureza exploratória, utilizando uma abordagem qualitativa e quantitativa. Neste sentido, foi analisado o processo da liderança feminina no contexto mundial e nacional, a evolução da sua participação nas chefias de topo, os factores que contribuem para o seu desempenho, e o que fazer para vencer os desafios e atingir a eficácia. O método de pesquisa utilizado foi a pesquisa quantitativa e qualitativa, através de aplicação de um questionário a trinta gestores de primeira linha, com o objectivo de avaliar a forma como o líder se auto percepciona, bem assim como ele é percepcionado pelo seu superior hierárquico, pelos colegas e pelos subordinados directos. As conclusões do estudo apontam para a existência de divergências entre as percepções dos líderes e dos outros membros da organização em relação à liderança exercida. Por outro lado, a questão do género parece ter pouca influência na eficácia da liderança. The aim of this paper is to identify, characterize and understand the factors that contribute to effective management and leadership of the Cape Verdean women in male dominated areas characterized by a background of top management. This scenario is characterized by a high male predominance, which represents a constant challenge for women worldwide and in particular for the Cape Verdean women. A literature search on the topics of leadership and on gender, specifically on the role of women in the work context was carried out. It is an exploratory research, using a qualitative and quantitative approach. In this sense the process of women's leadership in global and national context, the evolution of their participation in top leadership, the factors that contribute to their performance as well as how to overcome challenges and achieve efficiency were considered. The research method used was a qualitative and quantitative research through application of a questionnaire to 30 first line managers, in order to assess how the leader perceives itself, as well as, how he is perceived by his superior, colleagues and direct reports. The conclusions indicate that there are important differences between the perception of the leaders and other members of the organization in relation to the leadership exercise. On the other hand, gender seems to have little influence on leadership effectiveness.