(Ba3MTiMO9)-Ti-III-O-V (M-III = Fe, Ga, Y, Lu, M-V = Nb, Ta, Sb) perovskite oxides Synthesis, structure and dielectric properties

We describe the synthesis structures and dielectric properties of new perovskite oxides of the formula (Ba3MTiMO9)-Ti-III-O-V for M-III = Fe Ga Y Lu and M-V = Nb Ta Sb While M-V = Nb and Ta oxides adopt disordered/partially ordered 3C perovskite structures where M-III/Ti/M-V metal-oxygen octahedra are corner connected the M-V = Sb oxides show a distinct preference for the 6H structure where Sb-V/Ti-IV metal-oxygen octahedra share a common face forming (Sb Ti)O-9 dimers that are corner-connected to the (MO6)-O-III octahedra The preference of antimony oxides (Sb-V 4d(10)) for the 6H structure which arises from a special Sb-V-O chemical bonding that tends to avoid linear Sb-O-Sb linkages unlike Nb-V/Ta-V d(0) atoms which prefer similar to 180 degrees Nb/Ta-O-Nb/Ta linkages - is consistent with the crystal chemistry of M-V-O oxides in general The dielectric properties reveal a significant difference among Mill members All the oxides with the 3C structure excepting those with Mill = Fe show a normal low loss dielectric behaviour with epsilon = 20-60 in the temperature range 50-400 degrees C the M-III = Fe members with this structure (M-V = Nb Ta) display a relaxor-like ferroelectric behaviour with large E values at frequencies <= 1 MHz (50-500 degrees C) (C) 2010 Elsevier Masson SAS All rights reserved

Crystal structure and electrical properties of CaNaBi2Nb3O12 ceramics

Monophasic CaNaBi2Nb3O12 powders were synthesized via the conventional solid-state reaction route. Rietveld refinement of the X-ray powder diffraction (XRD) data and selected area electron diffraction (SAED) studies confirmed the phase to be a three-layer Aurivillius oxide associated with an orthorhombic B2cb space group. The dielectric properties of the ceramics have been studied in the 300-800 K temperature range at various frequencies (1 kHz to 1 MHz). A dielectric anomaly was observed at 676 K for all the frequencies corresponding to the ferroelectric to paraelectric phase transition as it was also corroborated by the high temperature X-ray diffraction studies. The incidence of the polarization-electric field (P vs. E) hysteresis loop demonstrated CaNaBi2Nb3O12 to be ferroelectric.

Characterization of coprecipitated ferroelectric Bi2 VO5·5

Fine powders of orthorhombic bismuth vandate (Bi2VO5.5) have been synthesized by coprecipitation method. Powder X-ray diffraction and electron microscopic techniques have been used to characterize these samples. The formation of the monophasic Bi2VO5.5 was confirmed. The compacted powders sintered at 1070 K have been characterized for their dielectric properties as a function of both temperature (300-900 K) and frequency (100 Hz-10 MHz) and found to be superior to those obtained by the conventional solid-state reaction route.

Structural and Dielectric-Properties Of A Novel BI2O3-(1-X)WO3-XCUO Solid-Solution

A novel solid solution in the system Bi-W-Cu-O has been synthesized and its structural and dielectric properties studied. The solid solution Bi2O3-(1-x)WO3-xCuO exists up to x = 0.7; the solid solutions up to x = 0.65 are orthorhombic but stabilize in tetragonal structure in a narrow range around x = 0.7. The solid solutions are non-centrosymmetric and exhibit ferroelectric behaviour similar to their parent phase Bi2WO6. The Curie point of the solid solution is found to decrease with increase in x.

Microstructural and dielectric properties of KCl-added bismuth vanadate ceramics

The effect of KCI addition on the microstructural, structural and dielectric properties of bismuth vanadate, Bi2VO5.5 (BiV) has been examined. The average grain size of BN ceramics increases with increase in KCl content (from an average grain size of TO to 80 mu m) as a result of the increased liquid-phase formation of KCI, at the grain boundaries. Differential scanning calorimetry (DSC) carried out on the KCl-added samples indicates an upward shift in the transition temperature (T-c), from 723 K (for BN) to 734 K (for 5 mol% KCl-added BiV). On further increase in the KCI content, T-c shifts down to about 722 K for 10 mol%. This trend is consistent with that of the lattice strain data. The relative permittivity as well as the dielectric loss decrease by more than half of the original values upon the addition of KCI. The relative permittivities of the KCl-added ceramics are comparable with the values predicted by the logarithmic mixture rule. Impedance analyses suggest that the grain boundary resistance of the KCl-added BiV ceramics is higher by two orders of magnitude than that of BN ceramics. The KCl-added BN ceramics exhibit ferroelectric domains and the domain density decreases as the grain boundary region is approached.

Lithium borate-strontium bismuth tantalate glass nanocomposite: a novel material for nonlinear optic and ferroelectric applications

Glass nanocomposites in the system (100 - x)Li2B4O7-xSrBi(2)Ta(2)O(9) (0 less than or equal to x less than or equal to 22.5, in molar ratio) were fabricated via a melt quenching technique followed by controlled heat-treatment. The as-quenched samples were confirmed to be glassy and amorphous by differential thermal analysis (DTA) and X-ray powder diffraction (XRD) techniques, respectively. The phase formation and crystallite size of the heat-treated samples (glass nanocomposites) were monitored by XRD and transmission electron microscopy (TEM). The relative permittivities (epsilon(tau)') of the glass nanocomposites for different compositions were found to lie in between that of the parent host glass (Li2B4O7) and strontium bismuth tantalate (SBT) ceramic in the frequency range 100 Hz-40 MHz at 300 K, whereas the dielectric loss (D) of the glass nanocomposite was less than that of both the parent phases. Among the various dielectric models employed to predict the effective relative permittivity of the glass nanocomposite, the one obtained using the Maxwell's model was in good agreement with the experimentally observed value. Impedance analysis was employed to rationalize the electrical behavior of the glasses and glass nanocomposites. The pyroelectric response of the glasses and glass nanocomposites was monitored as a function of temperature and the pyroelectric coefficient for glass and glass nanocomposite (x = 20) at 300 K were 27 muC m(-2) K-1 and 53 muC m(-2) K-1, respectively. The ferroelectric behavior of these glass nanocomposites was established by P vs. E hysteresis loop studies. The remnant polarization (P-r) of the glass nanocomposite increases with increase in SBT content. The coercive field (E-c) and P-r for the glass nanocomposite (x = 20) were 727 V cm(-1) and 0.527 muC cm(-2), respectively. The optical transmission properties of these glass nanocomposites were found to be composition dependent. The refractive index (n = 1.722), optical polarizability (am = 1.266 6 10 23 cm 3) and third-order nonlinear optical susceptibility (x(3) = 3.046 6 10(-21) cm(3)) of the glass nanocomposite (x = 15) were larger than those of the as-quenched glass. Second harmonic generation (SHG) was observed in transparent glass nanocomposites and the d(eff) for the glass nanocomposite (x = 20) was found to be 0.373 pm V-1.

Effect of neodymium (Nd) doping on the dielectric and ferroelectric characteristics of sol-gel derived lead zirconate titanate (53/47) thin films

The results of the studies on the effect of rare earth Nd doping on the phase formation behavior and electrical properties of sol-gel derived Pb-1.05(Zr0.53Ti0.47)O-3 (PZT) thin films are presented. The perovskite phase is obtained up to 5 at. % doping and beyond that pyrochlore phase was found to coexist with the perovskite phase in all the films. The transition temperature of undoped lead zirconate titanate (PZT) film was found to be reduced with Nd doping. The Nd doped films also exhibited typical relaxor-type behavior and a diffuse phase transition, similar to that observed in relaxor materials. The introduction of Nd into the PZT lattice probably introduces disorder in the B site of ABO(3) lattice, which causes the observed dielectric relaxation. Efforts were made to isolate the irreversible component contributions in low field dielectric and high field polarization switching behavior. (C) 2001 American Institute of Physics.

Growth and characterization of ferroelectric glycine phosphite single crystals

Single crystals of a recent ferroelectric material, glycine phosphite were grown from aqueous solution employing the techniques of slow cooling and controlled evaporation. Powder X-ray diffraction studies as well as thermal analysis were carried out on the grown crystals. The morphology of the crystal has been determined using contact and optical goniometry. The mechanical hardness of the crystal was evaluated by Vickers indentation method. Thickness dependence of the dielectric properties has been investigated and the results can be interpreted in terms of a surface layer of lower dielectric constant.

Field Induced Dielectric Properties of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 Thin Films

DC electric field induced dielectric properties of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (PMN-PT) thin films were studied as a function of frequency at different temperatures. It was observed that the dielectric constant (ε) and dissipation factor (tanδ) were decreased in presence of bias field. The temperature of dielectric maxima was found to increase with increasing bias level. The low temperature (ferroelectric behavior. Since the absence of long range interaction among the nanopolar clusters in PMN and its family is believed to be the origin of relaxor behavior, disappearance of relaxor nature in PMN-PT (70/30) films could be attributed to manifestation of long-range order at higher bias voltage. This was observed in the temperature dependence of dielectric constant i.e. the films neither exhibited any frequency dispersion in the temperature of dielectric maximum (Tm) nor showed any diffused phase transition. The relaxor property of PMN-PT thin films was studied in terms of diffused phase transition together with frequency dispersion of the temperature of dielectric maximum (Tm). Vogel-Fulcher relation was used to analyze the frequency dependence of temperature of dielectric maximum.

Dielectric Properties of Pulsed Excimer Laser Ablated BaBi2Nb2O9 Thin Films

The dielectric response of BaBi2Nb2O9 (BBN) thin films has been studied as a function of frequency over a wide range of temperatures. Both dielectric constant and loss tangent of BBN thin films showed a ‘power law’ dependence with frequency, which was analyzed using the Jonscher's universal dielectric response model. Theoretical fits were utilized to compare the experimental results and also to estimate the value of temperature dependence parameters such as n(T) and a(T) used in the Jonscher's model. The room temperature dielectric constant (ε') of the BBN thin films was 214 with a loss tangent (tanδ) of 0.04 at a frequency of 100 kHz. The films exhibited the second order dielectric phase transition from ferroelectric to paraelectric state at a temperature of 220 °C. The nature of phase transition was confirmed from the temperature dependence of dielectric constant and sponteneous polarization,respectively. The calculated Currie constant for BBN thin films was 4 × 105°C.

Impact of Template Layers on Dielectric and Electrical Properties of Pulsed-Laser Ablated Pb(Mg1/3 Nb2/3)O3 - PbTiO3 Thin Films

A study was done on pulsed laser deposited relaxor ferroelectric thin films of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (PMN-PT) deposited on platinized silicon substrates with template layers to observe the influence of the template layers on physical and electrical properties. Initial results, showed that perovskite phase (80% by volume) was obtained through proper selection of the processing conditions on Pt/Ti/SiO2/Si substrates. The films were grown at 300°C and then annealed in a rapid thermal annealing furnace in the temperature range of 750-850°C to induce crystallization. Comparison of the films annealed at different temperatures revealed a change in crystallinity, perovskite phase formation and grain size. These results were further used to improve the quality of the perovskite PMN-PT phase by inserting thin layers of TiO2 on the Pt substrate. These resulted in an increase in perovskite phase in the films even at lower annealing temperatures. Dielectric studies on the PMN-PT films show very high values of dielectric constant (1300) at room temperature, which further improved with the insertion of the template seed layer. The relaxor properties of the PMN-PT were correlated with Vogel-Fulcher theory to determine the actual nature of the relaxation process.

Role of La0.5Sr0.5COO3 template layers on dielectric and electrical properties of pulsed-laser ablated Pb(Nb2/3Mg1/3)O-3-PbTiO3 thin films

Relaxor ferroelectric thin films of 0.7Pb(Mg1/3Nb2/3)O-3-0.3PbTiO(3) (PMN-PT) deposited on platinized silicon substrates with and without template layers were studied. Perovskite phase (80% by volume) was obtained through proper selection of the processing conditions on bare Pt/Ti/SiO2/Si substrates. The films were initially grown at 300 degreesC using pulsed-laser ablation and subsequently annealed in a rapid thermal annealing furnace in the temperature range of 750-850 degreesC to induce crystallization. Comparison of microstructure of the films annealed at different temperatures showed change in perovskite phase formation and grain size etc. Results from compositional analysis of the films revealed that the films initially possessed high content of lead percentage, which subsequently decreased after annealing at temperature 750-850 degreesC. Films with highest perovskite content were found to form at 820-840 degreesC on Pt substrates where the Pb content was near stoichiometric. Further improvement in the formation of perovskite PMN-PT phase was obtained by using buffer layers of La0.5Sr0.5CoO3 (LSCO) on the Pt substrate. This resulted 100% perovskite phase formation in the films deposited at 650 degreesC. Dielectric studies on the PMN-PT films with LSCO template layers showed high values of relative dielectric constant (3800) with a loss factor (tan delta) of 0.035 at a frequency of 1 kHz at room temperature. (C) 2002 Elsevier Science B.V. All rights reserved.

Tuning of dielectric properties and magnetism of SrTiO(3) by site-specific doping of Mn

Combining experiments with first-principles calculations, we show that site-specific doping of Mn into SrTiO(3) has a decisive influence on the dielectric properties of these doped systems. We find that phonon contributions to the dielectric constant invariably decrease sharply on doping at any site. However, a sizable, random dipolar contribution only for Mn at the Sr site arises from a strong off-centric displacement of Mn in spite of Mn being in a non-d(0) state; this leads to a large dielectric constant at higher temperatures and gives rise to a relaxor ferroelectric behavior at lower temperatures. We also investigate magnetic properties in detail and critically reevaluate the possibility of a true multiglass state in such systems.

Investigations on multimagnetron sputtered Zn1-xMgxO thin films through metal-ferroelectric-semiconductor configuration

The effect of Mg doping in ZnO is investigated through structural, electrical, and optical properties. Zn1−xMgxO (0<×<0.3) thin films were deposited on Si (100) and corning glass substrates using multimagnetron sputtering. Investigations on the structural properties of the films revealed that the increase in Mg concentration resulted in phase evolution from hexagonal to cubic phase. The temperature dependent study of dielectric constant at different frequencies exhibited a dielectric anomaly at 110 °C. The Zn0.7Mg0.3O thin films exhibited a well-defined polarization hysteresis loop with a remnant polarization of 0.2 μC/cm2 and coercive field of 8 kV/cm at room temperature. An increase in the band gap with an increase in Mg content was observed in the range of 3.3–3.8 eV for x = 0–0.3. The average transmittance of the films was higher than 90% in the wavelength region λ = 400–900 nm.

Nonlinear dielectric behavior in three-component ferroelectric superlattices

Three-component ferroelectric superlattices consisting of alternating layers of SrTiO3, BaTiO3, and CaTiO3 (SBC) with variable interlayer thickness were fabricated on Pt(111)/TiO2/SiO2/Si (100) substrates by pulsed laser deposition. The presence of satellite reflections in x-ray-diffraction analysis and a periodic concentration of Sr, Ba, and Ca throughout the film in depth profile of secondary ion mass spectrometry analysis confirm the fabrication of superlattice structures. The Pr (remnant polarization) and Ps (saturation polarization) of SBC superlattice with 16.4-nm individual layer thickness (SBC16.4) were found to be around 4.96 and 34 μC/cm2, respectively. The dependence of polarization on individual layer thickness and lattice strain were studied in order to investigate the size dependence of the dielectric properties. The dielectric constant of these superlattices was found to be much higher than the individual component layers present in the superlattice configuration. The relatively higher tunability ( ∼ 55%) obtained around 300 K indicates that the superlattice is a potential electrically tunable material for microwave applications at room temperature. The enhanced dielectric properties were thus discussed in terms of the interfacial strain driven polar region due to high lattice mismatch and electrostatic coupling due to polarization mismatch between individual layers.