Effect of immersion cleansers on the bond strength between a denture base resin and acrylic resin teeth

The aim of the present study was to assess the shear bond strength between a heat-polymerized denture base resin and acrylic resin teeth after immersion in different denture cleansers by simulating a 180-day use. Two acrylic teeth (Biotone, Biotone IPN, Dentsply Ind. e Com., Rio de Janeiro, RJ, Brazil) were chosen for bonding to a heat-polymerized denture base resin (Lucitone 550- Dentsply Ind. e Com., Rio de Janeiro, RJ, Brazil). Eighty specimens were produced and divided into eight groups (n=10) according to their experimental condition (distilled water, 2% chlorhexidine digluconate, 1% sodium hypochlorite and Corega Tabs). Shear bond strength tests (MPa) were performed with a universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed by two-way analysis of variance (ANOVA) and Student-Newman-Keuls' multiple comparisons post hoc analysis (α=.05). The shear bond strength results revealed statistically significant differences between the groups. For the Biotone IPN tooth, significantly lower shear bond strength values were found for the group immersed in sodium-perborate solution (4.48±2.18 MPa) than for the group immersed in distilled water (control group) (10.83±1.84 MPa). For Biotone, significantly higher bond strength values (10.04±3.28 MPa) were found for the group immersed in Corega Tabs than for the control group (5.45±2.93 MPa). The immersion in denture cleanser solutions was more detrimental to the conventional acrylic denture tooth (Biotone) than to the highly cross-linked denture tooth (Biotone IPN). However, this effect was not observed for the groups immersed in Corega Tabs solution, regardless of the type of denture tooth. © 2013 Elsevier Ltd.

Nanoparticle characterization of Er-doped SnO2 pellets obtained with different pH of colloidal suspension

SnO2:2 at. %Er xerogel samples were obtained by sol-gel technique from colloidal suspensions with distinct pHs. The evaluation of critical regions inside the nanocrystallite is fundamental for the interpretation of the influence of pH on the emission data. In this way, the nanocrystal depletion layer thickness was obtained with the help of photoluminescence, Raman, X-ray diffraction, and field-emission gun scanning electron microscopy measurements. It was observed that acid suspensions (pH < 7) lead to high surface disorder in which a larger number of cross-linked bonds Sn-O-Sn among nanoparticles are present. For these samples, the nanoparticle depletion layer is larger as compared to samples obtained from other pH. Photoluminescence measurement in the near infrared region indicates that the emission intensity of the transition 4I13/2 → 4I15/2 is also influenced by the pH of the starting colloidal suspension, generating peaks more or less broadened, depending on location of Er3+ ions in the SnO2 lattice (high or low symmetry sites). © 2013 AIP Publishing LLC.

Matrizes poliméricas reticuladas de alta amilose e pectina para liberação controlada de fármacos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Caracterização físico-química de galactomananas de Adenanthera pavonina (Carolina) e Delonix regia (Flamboyant) reticuladas com trimetafosfato de sódio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito da isoflavona da soja e treinamento resistido sobre a composição corporal e densidade mineral óssea em mulheres na pós-menopausa

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência da acidez da suspensão coloidal para a geração de defeitos pontuais e emissão no infra vermelho em SnO2 dopado com Er

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Efeito do treinamento contrarresistência e isoflavona na densidade mineral óssea em mulheres na pós-menopausa

This study aimed to investigate the independent and additive effects of counter-resistance training (RT) and soy isoflavone supplement (ISO) on bone mineral density (BMD) and bone turnover in postmenopausal women. This study used a placebo-controlled, double-blinded (soy), randomized two (ISO vs. placebo) x two (RT vs. no RT) design. Eighty sedentary postmenopausal women, aged 45-70 years, were randomly assigned to one of four groups (71 completed a 9-month intervention): RT+ISO (n=15); no RT+ISO (n=20); RT+placebo (n=18); no RT+placebo (n=18). Participants randomized to ISO received 100mg/ day/oral of soy isoflavone; and those to RT attended supervised counter-resistance training sessions at least twice a week. At baseline and 9-month, BMD was estimated by dual-energy X-ray absorptiometry (DXA). Serum levels of C-terminal cross-linked telopeptide of type I collagen (CTX), osteocalcin, and insulin-like growth factor-1 (IGF-1) were measured as bone turnover. ANOVA with time as the repeated measure and test t were used in the statistical analysis. After 9 months of intervention, neither ISO nor RT alone affected BMD at any site or levels of CTX, osteocalcin, and IGF-1 (p>0.05). ISO and RT had no additive effects on BMD and bone turnover. RT groups showed significantly increased muscle strength (+ 35.2%) (p=0.02). We found no additive effects of resistance training and soy isoflavone on bone mineral density or bone turnover in postmenopausal women after 9-months.

Fine-tuning of a nanostructure, swelling, and drug delivery profile by blending ureasil-PEO and ureasil-PPO hybrids

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Ureasil-polyether hybrid blend with tuneable hydrophilic/hydrophobic features based on U-PEO1900 and U-PPO400 mixtures

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterização do compósito obtido a partir de borracha natural com negro e resíduos de couro aplicado como pisos e revestimentos

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Modificação superficial de nanopartículas de óxido de ferro por poli(ácido aspártico) reticulado

Pós-graduação em Química - IQ

Immobilization of papain on chitin and chitosan and recycling of soluble enzyme for deflocculation of saccharomyces cerevisiae from bioethanol distilleries

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Obtenção de amido resistente por intercruzamento e por tratamento hidrotérmico, e sua incorporação em bolos

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Impact of Solvent Quality on the Density Profiles of Looped Triblock Copolymer Brushes by Neutron Reflectivity Measurements

Preferential adsorption of poly(2-vinylpyridine)-deuterated polystyrene-poly(2-vinylpyridine) (PVP-dPS-PVP) triblock copolymers from toluene onto silicon leads to the formation of dPS loops tethered by the PVP end blocks. Using neutron reflectometry, we have determined the segment density profiles of these looped polymer brushes in toluene, a good solvent for the dPS block, and in cyclohexane at 20 °C (poor solvent), 32 °C, (near-Θ solvent), and 50 °C (marginal solvent). While the swelling behavior qualitatively agrees with that observed for singly grafted brushes, there are interesting differences in the local structural details: In a good solvent, the segment density profiles are composed of an inner parabolic region and a long, extended tail. In cyclohexane, the profiles are described by exponential decays. We ascribe these features to a novel polydispersity effect that arises due to tethering the PS loops by both ends. The results also show that the less dense layers undergo more significant changes in swollen height as solvent quality is changed and that the looped brushes of different molecular weight, asymmetry, and tethering density adhere to scaling relationships derived for lightly cross-linked polymer gels.

Investigation of the relationship between the structure and function of Ts2, a neurotoxin from Tityus serrulatus venom

Scorpion toxins targeting voltage-gated sodium (NaV) channels are peptides that comprise 6076 amino acid residues cross-linked by four disulfide bridges. These toxins can be divided in two groups (a and beta toxins), according to their binding properties and mode of action. The scorpion a-toxin Ts2, previously described as a beta-toxin, was purified from the venom of Tityus serrulatus, the most dangerous Brazilian scorpion. In this study, seven mammalian NaV channel isoforms (rNaV1.2, rNaV1.3, rNaV1.4, hNaV1.5, mNaV1.6, rNaV1.7 and rNaV1.8) and one insect NaV channel isoform (DmNaV1) were used to investigate the subtype specificity and selectivity of Ts2. The electrophysiology assays showed that Ts2 inhibits rapid inactivation of NaV1.2, NaV1.3, NaV1.5, NaV1.6 and NaV1.7, but does not affect NaV1.4, NaV1.8 or DmNaV1. Interestingly, Ts2 significantly shifts the voltage dependence of activation of NaV1.3 channels. The 3D structure of this toxin was modeled based on the high sequence identity (72%) shared with Ts1, another T. serrulatus toxin. The overall fold of the Ts2 model consists of three beta-strands and one a-helix, and is arranged in a triangular shape forming a cysteine-stabilized a-helix/beta-sheet (CSa beta) motif.