Field Instrumentation, Testing, and Long-Term Monitoring of High-Mast Lighting Tower No. 1 at the I-35/US 18 Interchange Near Clear Lake in the State of Iowa Phase 3, TR-562, 2009

The current study was initiated to quantify the stresses induced in critical details on the reinforcing jacket and the tower itself through the use of field instrumentation, load testing, and long-term monitoring. Strain gages were installed on the both the tower and the reinforcing jacket. Additional strain gages were installed on two anchor rods. Tests were conducted with and without the reinforcing jacket installed. Data were collected from all strain gages during static load testing and were used to study the stress distribution of the tower caused by known loads, both with and without the reinforcing jacket. The tower was tested dynamically by first applying a static load, and then quickly releasing the load causing the tower to vibrate freely. Furthermore, the tower was monitored over a period of over 1 year to obtain stress range histograms at the critical details to be used for a fatigue evaluation. Also during the long-term monitoring, triggered time-history data were recorded to study the wind loading phenomena that excite the tower.

East 1 St Street Interchange and I-35 Widening, From MP 94.3 to Oralabor Road, Polk County, Iowa, Project # IM-035-4(140)92--13-77, Environmental Assessment and Section 4(f) De Minimis Impact Finding, 2015

From Proposed Action: "The proposed action consists of reconstructing the East 1st Street/I-35 interchange with a Diverging Diamond interchange, widening I-35 from four (4) lanes to six (6) lanes, and widening East 1st Street from four (4) lanes to five (5) lanes from Delaware Avenue to Frisk Drive. The project also proposes to reconstruct the intersections of East 1st Street/Creekview Drive and East 1st Street/Frisk Drive."

Delayed delivery of second twin: a multicentre study of 35 cases.

OBJECTIVE: The aim of this study was to conduct a statistical analysis to determine the outcome of conservative treatment after delivery of a first fetus in multiple pregnancy and thus define new prognostic factors. STUDY DESIGN: Multicentre retrospective study involving 12 centers over a 10-year period. RESULTS: Twenty-eight twin pregnancies and seven triplet pregnancies which were managed conservatively. In twin pregnancies, 79% of the delayed-delivery fetuses survived; only 7% of the first delivered fetuses survived. The mean interval between deliveries was 47 days. No statistical difference was found concerning cerclage, antibiotic therapy, tocolysis and hospitalization. Earlier delivery of the first twin and premature rupture of membranes for the second twin were significantly related to a longer interval between deliveries. CONCLUSION: Delayed delivery in multifetal pregnancies can be successful if there are no contraindications and these pregnancies are managed in a tertiary perinatal center. Publications limited to successful cases have undoubtedly introduced some bias in assessment.

Nd:YAG Laser Welding of 5083 Aluminium Alloy using Filler Wire

High reflectivity and high thermal conductivity, high vapour pressure of alloyingelements as well as low liquid surface tension and low ionisation potential, make laser welding of aluminium and its alloys a demanding task.Problems that occur during welding are mainly process instabilities of the keyhole and the melt pool, increased plasma formation above the melt pool and loss of alloying elements. These problems lead to unwanted metallurgical defects like hot cracks and porosity in the weld bead andother problems concerning the shape and appearance of the weld bead. In order to minimise the defects and improve the weld quality, the process and beam parameters need to be carefully adjusted along with a consideration concerning the use of filler wire for the welding process. In this work the welding of 3,0 mm thick grade 5083 aluminium alloy plates using a 3,0 kW Nd:YAG laser with grade 5183 filler wire addition is investigated. The plates were welded as butt joints with air gap sizes 0,5 mm, 0,7mm and 1,0 mm. The analysis of the weld beads obtained from the weldedsamples showed that the least imperfections were produced with 0,7 mm air gaps at moderate welding speeds. The analysis also covered the calculation of the melting efficiency and the study of the shape of the weld bead. The melting efficiency was on average around 20 % for the melting process of the welded plates. The weld beads showed the characteristic V-shape of a laser weld and retained this shape during the whole series of experiments.

Tandem-GMA Welding of Low Alloy Structural Steel

The Tandem-GMAW method is the latest development as the consequences of improvements in the welding methods. The twin-wire and then the Tandem-method with the separate power sources has got a remarkable place in the welding of many types of materials with different joint types. The biggest advantage of Tandem welding method is the flexibility of choosing both the electrodes of different types from each other according to the type of the parent material. This is possible because of the feasibility of setting the separate welding parameters for both the wires. In this thesis work the effect of the variation in three parameters on the weld bead in Tandem-GMA welding method is studied. Theses three parameters are the wire feed rate in the slave wire, the wire feed rate in the master wire and the voltage difference in both the wires. The results are then compared to study the behaviour of the weld bead with the change in these parameters.

In vivo electrochemical corrosion study of a CoCrMo biomedical alloy in human synovial fluids.

The present study was initiated with the aim to assess the in vivo electrochemical corrosion behaviour of CoCrMo biomedical alloys in human synovial fluids in an attempt to identify possible patient or pathology specific effects. For this, electrochemical measurements (open circuit potential OCP, polarization resistance Rp, potentiodynamic polarization curves, electrochemical impedance spectroscopy EIS) were carried out on fluids extracted from patients with different articular pathologies and prosthesis revisions. Those electrochemical measurements could be carried out with outstanding precision and signal stability. The results show that the corrosion behaviour of CoCrMo alloy in synovial fluids not only depends on material reactivity but also on the specific reactions of synovial fluid components, most likely involving reactive oxygen species. In some patients the latter were found to determine the whole cathodic and anodic electrochemical response. Depending on patients, corrosion rates varied significantly between 50 and 750mgdm(-2)year(-1).