Drug release enhancement from silicone intravaginal rings by incorporation of water soluble excipients

120

Design of a silicone intravaginal ring for the delivery of oxybutynin

95

Novel, antibacterial silicone biomaterials for the prevention of microbial adherence and infection in urinary catheters

P122 93

Heavier-than-water silicone oil mixture as a long-term tamponade agent:A pilot study

Purpose: To evaluate the tamponade effect on the retina of a heavier-than-water silicone oil mixture and to compare it with the effect of silicone oil. Methods: Prospective, non-randomised, comparative pilot study. Phakic/pseudophakic patients with retinal detachment undergoing vitrectomy with Densiron 68 or silicone oil were recruited. The 'separation volume', defined as the relative volume of the space between intraocular tamponade agent and retina, was estimated using magnetic resonance imaging in both groups and compared. Results: Nine participants were included; 4 received silicone oil and 5 Densiron 68. The mean separation volume was statistically significantly larger in the silicone oil group (0.477 ± 0.419 cm ) than in the Densiron group (0.042 ± 0.013 cm ; p = 0.014). Conclusions: In this study Densiron achieved an excellent tamponade effect in the retina. © 2011 S. Karger AG, Basel.

Pseudo-endothelial dystrophy associated with emulsified silicone oil

Purpose. To describe endothelial changes associated with emulsified silicone oil. Methods. Report of a case. Results. A 77-year-old man had multiple and diffuse clear vesicles on the endothelium of his left eye (LE). The cornea was clear and thin. He had undergone pars plana vitrectomy and intraocular silicone oil injection 5 years before presentation. Specular microscopy revealed numerous small bubbles of emulsified silicone oil and a mild degree of endothelial damage. Conclusion. Emulsified silicone oil can adhere to the endothelium and induce an apparent droplet-like endotheliopathy.

Hard coatings on elastomers for reduced permeability and increased wear resistance

In this study, three different elastomers, namely hydrogenated nitrile butadiene rubber, fluoroelastomer and silicone, have been subjected to two different hard metallised coatings by ion implantation process. The three different elastomers are commonly used in various seal applications, where reduced wear and gas permeability are essential in maintaining seal performance and functionality. Samples of these rubbers have been coated with chromium coating in one set of tests. In the second set of tests, samples of elastomers have been coated with tungsten carbide coating being deposited on all the three different elastomers. Wear, gas permeability and mechanical behaviour of the coated samples were compared with each other and with the control uncoated elastomers. All the coated samples showed good reduction in gas permeability. With the use of metallised coatings, there has been improved resistance to wear in all the coated samples. Adhesion strength and effect of coating on the elastomer have been investigated by mechanical testing. Mechanical tests revealed good adhesion of metal coatings on all the rubber samples, and there was no detrimental effect on the mechanical properties after coating. © 2012 Institute of Materials, Minerals and Mining.