Protese total fixa em função imediata confeccionada em resina composta indireta

Immediate functioning of osseointegrated implants has been widely employed in edentulous patients due to its safety and high predictability. However, viability and success of immediate-loaded implants is defined by factors such as number of implants, distribution and splinting, as well as reduction of oblique loads and excessive occlusal contacts. The indirect composite resin-modified glass enable building of a highly aesthetic prosthesis, combining satisfactory resistance and better force dissipation on occlusal loading. This article describes a resin composite, mandibular fixed prosthesis on osseointegrated implants in immediate function.

Efeito de um gel de peróxido de carbamida a 10% sobre a resistência de união de restaurações adesivas à dentina

The present study aimed to analyze the effects of tooth bleaching with 10% carbamide peroxide (CP) gel on the bond strength of resin composite restorations to dentin. Material and Methods: Twenty cavities were prepared on the buccal surface of bovine teeth. After acid etching and application of bonding agent on dentin and enamel, the cavities were restored with composite resin. The specimens were divided into groups according to treatment on the surface of enamel / restoration: G1 - control (no treatment) and G2 (10% PC gel application for 8h/day during 14 days). After this period, the teeth were cut to produce beams with 0.81 mm2 cross-sectional area, which were subjected to microtensile test. The fractures were examined with a stereomicroscope and classified as cohesive in resin or dentin, adhesive, or mixed. Results: The statistical analysis (ANOVA / χ2) revealed that the factor treatment interfered with the bond strength, which was significantly higher for specimens of G2 (p <0.05). Adhesive fractures occurred in most of specimens of both groups with values ranging from 48.3% to 75%. Mixed fractures were the second more frequent in G1 and cohesive resin failure in G2. Conclusion: It was concluded that tooth bleaching with 10% of PC increased the bond strength of adhesive restorations to dentin.

Efeito das dimensões dos corpos de prova na resistência à flexão de compósitos restauradores

The aim of this study was to evaluate the influence of specimen size, in comparison with the ISO Standard, on the three point flexural strength of resin composite restorative materials Filtek Supreme and Filtek Z-250. Forty specimens were fabricated for each material with the following length, width and thickness measurements (n = 10): 1) 20 × 2 × 2 mm (ISO 4049); 2) 10 × 2 × 1 mm; 3) 10 × 1 × 1 mm; 4) 8 × 0.8 × 0.8 mm. The composites were inserted in a single increment into two-piece metal device and light-polymerized. The specimens were dry stored at 37 ± 1 °C and protected from light for 7 days. After this period, flexural strength was measured by three-point flexure test using MTS 810 equipment, with a load cell of 10 kN at a speed of 0.5 mm/min. For the evaluated sizes, the results showed significant variability (p = 0.00) with values when compared with the ISO Standard (116.700 MPa), being statistically higher for the test specimens measuring 10 × 1 × 1 mm (142.530 MPa), similar for those of 10  ×  2  ×  1  mm (115.815 MPa) and lower for those of 8 × 0.8 × 0.8 mm (86.650 MPa). There was statistical equality (p = 0.08) for the studied composites (Filtek Supreme, 125.270 MPa; Filtek Z-250, 108.130 MPa). Specimens measuring 10 × 2 × 1 mm provided flexural strength values equivalent to those obtained in the sizes recommended by the ISO 4049 standard, with lower consumption of material, energy and time.

Effect of Er:YAG laser and diamond drill on hybrid layer morphology obtained with self-etch adhesive: analysis by SEM and confocal laser scanning microscopy (CLSM)

This study aimed to evaluate the effect of Er:YAG (L) and diamond drills (DD) on: 1) the microshear bond strength (MPa); 2) the adhesive interface of two-step (TS) – Adper Scotchbond Multipurpose and one-step (OS) adhesives – Adper EasyOne, both from 3M ESPE. Material and methods: According to the preparation condition and adhesives, the samples were divided into four groups: DD_TS (control); DD_OS; L_TS and L_OS. 60 bovine incisors were randomly divided into experimental and groups: 40 for microshear bond strength (n = 10) and 20 for the adhesive interface morphology [6 to measure the thickness of the hybrid layer (HL) and length of tags (t) by CLSM (n = 3); 12 to the adhesive interface morphology by SEM (n = 3) and 2 to illustrate the effect of the instruments on dentine by SEM (n = 1)]. To conduct the microshear bond strength test, four cylinders (0.7 mm in diameter and 1 mm in height with area of adhesion of 0.38 mm) were constructed with resin composite (Filtek Z350 XT – 3M ESPE) on each dentin surface treated by either L or DD and after adhesives application. Microshear bond strength was performed in universal testing machine (EMIC 2000) with load cell of 500 kgf and a crosshead speed of 0.5 mm / min. Adhesive interface was characterized by thickness of hybrid layer (HL) and length of tags (t) in nm, with the aid of UTHSCSA ImageTool software. Results: Microshear bond strength values were: L_TS 34.10 ± 19.07, DD_TS 24.26 ± 9.35, L_OS 33.18 ± 12.46, DD_OS 21.24 ± 13.96. Two-way ANOVA resulted in statistically significant differences only for instruments (p = 0.047). Mann-Whitney identified the instruments which determined significant differences for HL thickness and tag length (t). Concerning to the adhesive types, these differences were only observed for (t). Conclusion: It can be concluded that 1) laser Er:YAG results in higher microshear bond strength values regardless of the adhesive system (TS and OS); 2) the tags did not significant affect the microshear bond strength; 3) the adhesive interface was affected by both the instruments for cavity preparation and the type of adhesive system used.

Matriz oclusal para restauração com resina composta de baixa contração: simplificação eficiência

The composite resin is the material of election for direct restorations in posterior teeth currently. The restorative dentistry aims to improve each day the material and facilitate the restorative technique. This paper describes the technique of occlusal matrix made to speed up and preservation the occlusal surface of a first molar tooth affected by caries lesion. A new resin-based composite was used called Silorane, which may be placed in larger increments due the material has low shrinkage and polymerization stress. The use of occlusal matrix associated with a low shrinkage resin composite can simplify the clinical work, and result in a restoration with excellent reproduction of anatomical.

Effect of time interval between bleaching and bonding on tag formation

The objective of this study was to assess penetration of adhesive material in enamel bleached with 35% hydrogen peroxide using optical polarized light microscopy. Extracted human teeth were randomly assigned to 5 groups, each representing a specific time interval between bleaching and the application of an adhesive material. They were designated as: (TC) the control group-restorations in unbleached teeth; (T0) comprising restorations carried out immediately after bleaching; (T7) comprising restorations 7 days after bleaching; (T14) comprising restorations 14 days after bleaching; and (T21) comprising restorations 21 days after bleaching. Length of resin tags was measured with an Axiophot photomicroscope at a x 400 magnification, and the results subjected to an ANOVA for a comparison between groups, with a p value of < 0.05. Differences between the groups were verified using a Tukey test at a confidence level of 5%. The specimens in the control group (TC) and experimental groups T7, T14 and T21 showed better penetration of adhesive material into enamel in comparison with experimental group T0. This suggests that a gap of at least 7 days should be left between bleaching enamel with 35% hydrogen peroxide and placing adhesive bonding agents and undertaking resin composite restoration work.

Abrasion resistance of direct and indirect resins as a function of a sealant veneer

Abrasive wear is one of the most common type of wear that not only affect teeth, as also dental restorations. Thus to investigate one of the etiological factors as tooth brushing procedure is clinical relevant in order to select the best material combination that may prevent damage of resin dental restoration's abrasion. This study evaluated the influence of tooth brushing on mass loss and surface roughness of direct Venus (Vs) and indirect Signum (Sg) resin composites, with and without a surface sealant, Fortify (F). Twenty-four specimens were prepared with each resin composite, using their proprietary curing units, according to manufacturer's instructions. All the specimens were polished and ultrasonically cleaned in distilled water for 5 minutes. Half of the specimens of each resin (n = 12) were covered with F (Vs F and Sg F ), except for the control (C) specimens (Vs C and Sg C ), which were not sealed. Mass loss (ML) as well as surface roughness (Ra ) was measured for all the specimens. Then, the specimens were subjected to toothbrush-dentifrice abrasion, using a testing machine for 67.000 brushing strokes, in an abrasive slurry. After brushing simulation, the specimens were removed from the holder, rinsed thoroughly and blot dried with soft absorbent paper. The abrasion of the material was quantitatively determined with final measurements of ML and surface roughness, using the method described above. ML data were analyzed by two-way analysis of variance (ANOVA) and the analysis indicated that resin composites were not statistically different; however, the specimens sealed with F showed higher ML. Ra mean values of the groups Vs F and Sg F significantly increased. Tooth brushing affects mainly the roughness of the direct and indirect resin composites veneered with a sealant.

Comportamento do esmalte de dentes decíduos após desafio desmineralizante em função de materiais restauradores: estudo ao microscópio de luz polarizada

Pós-graduação em Biopatologia Bucal - ICT

Resistência de união entre um cimento resinoso e uma cerâmica aluminizada submetida a diferentes tratamentos de superfície

Pós-graduação em Odontologia Restauradora - ICT

Contração de polimerização e expansão higroscópica de resinas compostas: análise pela técnica de video-imagem

To evaluate the volumetric changes due to polymerization and thermocycling on different resin-composites. Methods: Thirteen A2 Universal Dentin shade resin-composites (n = 10) from eight manufacturers were evaluated (4Seasons, Grandio, Venus, Amelogen Plus, P90, Z350, Esthet-X, Amaris, Vita-l-escence, Natural-Look, Charisma, Z250 and Opallis). The polymerization shrinkage percentage (PS) was calculated using an image measurement device (ACUVOL - Bisco Dental). Equal volumes of material, standardized by a semisphere polyurethane matrix (d = 3mm) were used and, after 5 minutes of relaxation, the baseline volume measurements were obtained with 18 J of energy dose from the LED light-curing unit. Measurements were obtained after 5 minutes and PS values calculated. Specimens were stored in a drydark environment for 24 hours and re-measured. Specimens were then thermocycled in distilled water between 5oC and 55oC for 20,000 cycles, subjected to another volume measurement at 5,000 cycle intervals. Specimens were gently dried prior to each measurement. Results: Repeated measurements were made using ANOVA (α = 0.05) showed that all resin-composite volumes were influenced by the number of cycles. Volumes at 5 minutes post-polymerization (12.47 ± 0.08) were significantly lower than those at baseline (12.80 ± 0.09). Volumes at 24 hours (12.43 ± 0.19) were insignificantly lower than those at 5 minutes postpolymerization. With regards to the impact of thermocycling, all specimens showed statistically significant increases in volume after 5,000 cycles (13.04 ± 0.22). Although statistically different from those after 5,000 cycles, there was no statistically significant difference between volumes measured at 10,000 (12.87±0.21), 15,000 (12.92±0.24), and 20,000 (12.84±0.23) cycles. Conclusion: According to the video-imaging analysis, thermocycling caused a significant expansion in resin-composites tested, the volume increase was not able to...

Influência do tratamento clareador e envelhecimento induzido sobre o brilho, cor, dureza e rugosidade superficial de resinas compostas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência de união e estabilidade de um sistema adesivo universal à dentina erodida/abrasionada após desproteinização

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Eroded dentin does not jeopardize the bond strength of adhesive restorative materials

This in vitro study evaluated the bond strength of adhesive restorative materials to sound and eroded dentin. Thirty-six bovine incisors were embedded in acrylic resin and ground to obtain flat buccal dentin surfaces. Specimens were randomly allocated in 2 groups: sound dentin (immersion in artificial saliva) and eroded dentin (pH cycling model - 3x / cola drink for 7 days). Specimens were then reassigned according to restorative material: glass ionomer cement (Ketac (TM) Molar Easy Mix), resin-modified glass ionomer cement (Vitremer (TM)) or adhesive system with resin composite (Adper Single Bond 2 + Filtek Z250). Polyethylene tubes with an internal diameter of 0.76 mm were placed over the dentin and filled with the material. The microshear bond test was performed after 24 h of water storage at 37 degrees C. The failure mode was evaluated using a stereomicroscope (400x). Bond strength data were analyzed with two-way ANOVA and Tukey's post hoc tests (alpha = 0.05). Eroded dentin showed bond strength values similar to those for sound dentin for all materials. The adhesive system showed the highest bond strength values, regardless of the substrate (p < 0.0001). For all groups, the adhesive/mixed failure prevailed. In conclusion, adhesive materials may be used in eroded dentin without jeopardizing the bonding quality. It is preferable to use an etch-and-rinse adhesive system because it shows the highest bond strength values compared with the glass ionomer cements tested.

Finite element analysis of bonded model Class I 'restorations' after shrinkage

Objectives. The C-Factor has been used widely to rationalize the changes in shrinkage stress occurring at the tooth/resin-composite interfaces. Experimentally, such stresses have been measured in a uniaxial direction between opposed parallel walls. The situation of adjoining cavity walls has been neglected. The aim was to investigate the hypothesis that: within stylized model rectangular cavities of constant volume and wall thickness, the interfacial shrinkage-stress at the adjoining cavity walls increases steadily as the C-Factor increases. Methods. Eight 3D-FEM restored Class I 'rectangular cavity' models were created by MSC.PATRAN/MSC.Marc, r2-2005 and subjected to 1% of shrinkage, while maintaining constant both the volume (20 mm(3)) and the wall thickness (2 mm), but varying the C-Factor (1.9-13.5). An adhesive contact between the composite and the teeth was incorporated. Polymerization shrinkage was simulated by analogy with thermal contraction. Principal stresses and strains were calculated. Peak values of maximum principal (MP) and maximum shear (MS) stresses from the different walls were displayed graphically as a function of C-Factor. The stress-peak association with C-Factor was evaluated by the Pearson correlation between the stress peak and the C-Factor. Results. The hypothesis was rejected: there was no clear increase of stress-peaks with C-Factor. The stress-peaks particularly expressed as MP and MS varied only slightly with increasing C-Factor. Lower stress-peaks were present at the pulpal floor in comparison to the stress at the axial walls. In general, MP and MS were similar when the axial wall dimensions were similar. The Pearson coefficient only expressed associations for the maximum principal stress at the ZX wall and the Z axis. Significance. Increase of the C-Factor did not lead to increase of the calculated stress-peaks in model rectangular Class I cavity walls. (C) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effects of water flow on ablation rate and morphological changes in human enamel and dentin after Er:YAG laser irradiation

Purpose: To investigate the laboratory effect of Er:YAG laser on ablation rate and morphological changes in human enamel and dentin with varying water flow. Methods: 23 human third molars were sectioned in mesio-distal and buccal-lingual directions. The slabs were flattened and weighted on an analytical laboratory balance (control). A 4-mm(2) area was demarcated and the samples were randomly assigned into three groups according to water flow employed during the laser irradiation (1.0, 1.5, and 2.0 mL/minute). An Er:YAG laser was used to ablate enamel (80.22-J/cm(2), 300 mJ/4Hz) and dentin (96.26-J/cm(2), 250 mJ/4Hz). After irradiation, the samples were immersed in distilled water for 1 hour and then weighted again. The final mass was obtained and laser-irradiated substrate mass loss was calculated by the difference between the initial and final mass. Afterwards, specimens were prepared for SEM. Results: Data were submitted to ANOVA and Tukey's test (P< 0.05). It was observed that the 2.0 mL/minute resulted in a higher mass loss, 1.0 mL/minute showed a lower mass loss, and 1.5 mL/minute demonstrated intermediate results (P< 0.05). The increase of water flow promoted less melting areas and cracks. Furthermore, dentin was more ablated than enamel. It may be concluded that the water flow of Er:YAG laser and the substrates affected the ablation rate. Among the tested parameters, 2.0 mL/minute improved the ability of ablation in enamel and dentin, with less morphologic surface alteration. (Am J Dent 20 12;25:332-336).