Kinetics and mechanism of hot corrosion of γ-Y 2Si 2O 7 in thin-film Na 2SO 4 molten salt

γ-Y 2Si 2O 7 is a promising candidate material both for hightemperature structural applications and as an environmental/thermal barrier coating material due to its unique properties such as high melting point, machinability, thermal stability, low linear thermal expansion coefficient (3.9×10 -6/K, 200°-1300°C), and low thermal conductivity (<3.0 W/ṁK above 300°C). The hot corrosion behavior of γ-Y 2Si 2O 7 in thin-film molten Na 2SO 4 at 850°-1000°C for 20 h in flowing air was investigated using a thermogravimetric analyzer (TGA) and a mass spectrometer (MS). γ-Y 2Si 2O 7 exhibited good resistance against Na 2SO 4 molten salt. The kinetic curves were well fitted by a paralinear equation: the linear part was caused by the evaporation of Na2SO4 and the parabolic part came from gas products evolved from the hotcorrosion reaction. A thin silica film formed under the corrosion scale was the key factor for retarding the hot corrosion. The apparent activation energy for the corrosion of γ-Y 2Si 2O 7 in Na 2SO 4 molten salt with flowing air was evaluated to be 255 kJ/mol.

Hot corrosion of γ-Y2Si2O7 in strongly basic Na2CO3 molten salt environment

γ-Y2Si2O7 is a promising candidate both for high temperature structural applications and as thermal barrier coatings due to its unique combination of properties, such as high melting point, good machinability, high thermal stability, low linear thermal expansion coefficient (3.9 × 10-6 K-1, 25-1400 °C) and low thermal conductivity (<3 W/m K above 300 °C). In this work, the hot corrosion behavior of γ-Y2Si2O7 in strongly basic Na2CO3 molten salt at 850-1000 °C for 20 h in flowing air was investigated. In the employed conditions, multi-layer corrosion scales with total thickness less than 90 μm were formed. At 850-900 °C, the outmost layer of the scale was composed of the reprecipitation of Y2O3, the bottom of a Si-rich Na2O·xSiO2 (x > 3.65) melt layer, and the middle of a NaYSiO4 layer. At 1000 °C, the corrosion products turned out to be a mixture of NaY9Si6O26 and Si-rich Na2O·xSiO2 (x > 3.65). In all cases, a thin layer of protective SiO2 formed under the Na2O·xSiO2 melt and protected the bulk material from further corrosion.

Is economic valuation of ecosystem services useful to decision-makers? Lessons learned from Australian coastal and marine management

Economic valuation of ecosystem services is widely advocated as a useful decision-support tool for ecosystem management. However, the extent to which economic valuation of ecosystem services is actually used or considered useful in decision-making is poorly documented. This literature blindspot is explored with an application to coastal and marine ecosystems management in Australia. Based on a nation-wide survey of eighty-eight decision-makers representing a diversity of management organizations, the perceived usefulness and level of use of ecosystem services economic valuation in support of coastal and marine management are examined. A large majority of decision-makers are found to be familiar with economic valuation and consider it useful - even necessary - in decision-making, although this varies across decision-makers groups. However, most decision-makers never or rarely use it. The perceived level of importance and trust in estimated dollar values differ across ecosystem services, and are especially high for values that relate to commercial activities. A number of factors are also found to influence respondent’s use of economic valuation. Such findings concur with conclusions from other existing works, and are instructive to reflect on the issue of the usefulness of ESV in environmental management decision-making. They also confirm that the survey-based approach developed in this application represents a sound strategy to examine this issue at various scales and management levels.

Building economic capability to improve the management of marine resources in Australia: Final report

FRDC project 2008/306 Building economic capability to improve the management of marine resources in Australia was developed and approved in response to the widespread recognition and acknowledgement of the importance of incorporating economic considerations into marine management in Australia and of the persistent undersupply of suitably trained and qualified individuals capable of providing this input. The need to address this shortfall received broad based support and following widespread stakeholder consultation and building on previous unsuccessful State-based initiatives, a collaborative, cross-jurisdictional cross-institutional capability building model was developed. The resulting project sits within the People Development Program as part of FRDC’s ‘investment in RD&E to develop the capabilities of the people to whom the industry entrusts its future’, and has addressed its objectives largely through three core activities: 1. The Fisheries Economics Graduate Research Training Program which provides research training in fisheries/marine economics through enrolment in postgraduate higher degree studies at the three participating Universities; 2. The Fisheries Economics Professional Training Program which aims to improve the economic literacy of non-economist marine sector stakeholders and was implemented in collaboration with the Seafood Cooperative Research Centre through the Future Harvest Masterclass in Fisheries Economics; and, 3. The Australian Fisheries Economics Network (FishEcon) which aims to strengthen research in the area of fisheries economics by creating a forum in which fisheries economists, fisheries managers and Ph.D. students can share research ideas and results, as well as news of upcoming research opportunities and events. These activities were undertaken by a core Project team, comprising economic researchers and teachers from each of the four participating institutions (namely the University of Tasmania, the University of Adelaide, Queensland University of Technology and the Commonwealth Scientific and Industrial Research Organisation), spanning three States and the Commonwealth. The Project team reported to and was guided by a project Steering Committee. Commensurate with the long term nature of the project objectives and some of its activities the project was extended (without additional resources) in 2012 to 30th June 2015.

Influence of drying on the liquid limit behaviour of a marine clay

The possible mechanisms of particle aggregation and reduction in liquid limit of the Cochin marine clay on drying are investigated. Mineralogical analysis showed the absence of halloysite in the marine specimen. Experimental results also ruled out the possibility of cementitious material being responsible for particle aggregation and reduction in clay plasticity on drying. The presence of calcium and magnesium as the predominant exchangeable ions and of a high pore salt concentration facilitates strong interparticle attraction and small particle separations; the latter leads to development of significant capillary stresses that permits an intimate contact of particles and growth of strong van der Waals' and Coulombic bonds.

A study of geotechnical properties of Cochin Marine Clays

Most of the Greater Cochin area, which is undergoing rapid industrialisation, consists of extremely soft marine clay calling for expensive deep foundations. This paper presents a study on the physical properties and engeering characteristics of Cochin marine clays. These marine clays are characterised by high Atterberg limits and natural water contents. They are moderately sensitive with liquidity indices ranging over 0.46 to 0.87.The grain size distribution shows almost equal fractions of clay and silt size with sand content varying around 20%. Use of a dispersing agent in carrying out grain size distribution test plays an important role. The fabric of these clays had been identified as flocculant. The pore water has low salinity which results in marginal changes in properties on washing.Consolidation test results showed a preconsolidation pressure of up to about 0.5 kg/cm2 with high compression indices. Compression index vs liquid limit yielded a correlation comparable to that of published data. The undisturbed samples have a much larger coefficient of secondary consolidation as a result of flocculant fabric. These clays have very low undrained shear strength.

Measurement of the corrosion rate of aluminium in sodium hydroxide using holographic interferometry

The application of holographic interferometry to the measurement of the corrosion rate of aluminium in sodium hydroxide is investigated. Details of the fabrication of the corrosion cell and the experimental procedure are given. Thickness loss of aluminium was found for different dissolution times and compared with the conventional weight-loss method using a microbalance.

Engineering behavior of uplifted Smectite-rich Cochin and Mangalore marine clays

The present study aims to assess whether the smectite-rich Cochin and Mangalore clays, which were deposited in a marine medium and subsequently uplifted, exhibit consistency limits response typical of expanding lattice or nonexpanding (fixed) lattice-type clays on artificially changing the chemical environment. The chemical and engineering behaviors of Cochin and Mangalore marine clays are also compared with those of the smectite-rich Ariake Bay marine clay from Japan. Although Cochin, Mangalore, and Ariake clays contain comparable amounts of smectite (32-45%), Ariake clay exhibits lower consistency limits and much higher ranges of liquidity indices than the Indian marine clays. The lower consistency limits of the Ariake clay are attributed to the absence of well-developed, long-range, interparticle forces associated with the clay. Also, Ariake clay exhibits a significantly large (48-714 times) decrease in undrained strength on remolding in comparison to Cochin and Mangalore clays (sensitivity ranges between 1 and 4). A preponderance of long-range, interparticle forces reflected in the high consistency limits of Cochin and Mangalore clays (wL range from 75 to 180%) combined with low natural water contents yield low liquidity indices (typically <1) and high, remolded, undrained strengths and are considered to be responsible for the low sensitivity of the Indian marine clays.