Formation of SnO2 supported porous membranes

In this work, the effect of the substrate microstructure on the formation of SnO2 membranes and of the sintering conditions on their porosity have been analysed. Samples have been prepared by colloidal suspensions cast on alumina or kaolin substrates. Supported membranes have been characterized by Hg porosimetry, MEV, XRD and N-2 adsorption-desorption isotherms. The results show that the narrower pore size distribution of alumina substrate allowed to prepare membranes more homogeneous and free of cracks than that supported on kaolin. The crystallite and pore sizes of the membranes could be controlled by adjusting the temperature of sintering, allowing materials with adequate microstructure with application for ultrafiltration process.

Influence of polymerization on the synthesis of SrTiO3: Part I. Characteristics of the polymeric precursors and their thermal decomposition

The influence of polymerization on the thermal decomposition of polymeric precursors and phase formation was investigated during synthesis of SrTiO3. The precipitation of polymeric precursor in acetone produced a more thermal stable precursor with lower weight loss during decomposition. This more stable precursor retarded the formation of the SrTiO3 phase. From thermal analysis, XRD and FT-IR the presence of an intermediate phase during decomposition of the precursors was observed. This is a mixed (Sr,Ti) carbonate phase with the proposed composition of Sr2Ti2O5.CO3. © 1995.

On the specific filtration mechanism of a mesoporous silica membrane, prepared with non-connecting parallel pores

We report the singular filtration properties of an ultrafiltration membrane made with mesoporous silica that exhibits cylindrical pores aligned mostly normal to the support. This membrane supported on tubular commercial macroporous alumina supports was prepared by the interfacial growth mechanism between stable silica-surfactant hybrid micelles made of the association of silica oligomers with polyethyleneoxide-based (PEO) surfactants and sodium fluoride, a well-known silica condensation catalyst [Boissière et al., An ultrafiltration membrane made with mesoporous MSU-X silica, Chem. Mater. 15 (2003) 460-463]. It appears that the combined effect of the silica nature of the membrane, whose surface charge can be easily adjusted by changing the pH and the non-connected cylindrical shape of the pores provides a new behavior in the retention properties, as proved by the filtration of polyoxyethylene polymers (PEO) with different molecular weights. Depending on the filtration conditions, a rejection rate of 80% and a steep cut-off at 2000 Da can be obtained or, on the reverse, polymers three times bigger than the pore diameter can diffuse through the membrane. This new filtration mechanism, which opens up new modes of separation modes, is explained in the light of both topology of the porous network and pH-dependent interactions between PEO polymers and silica porous media. © 2004 Elsevier B.V. All rights reserved.

Influence of apical enlargement in cleaning and extrusion in canals with mild and moderate curvatures

Optical microscopy and morphometric analysis were used in this study to evaluate, in vitro, the cleaning of the apical region in root canals with mild or moderate curvatures subjected to biomechanical preparation with a rotary system, as well as to assess the amount of extruded material to the periapical area. Lateral incisors (n = 32), 16 with curvature angles smaller or equal to 10° (GI) and 16 between 11° and 25° angles (GII) were submitted to Hero 642 rotary instrumentation with different surgical diameters: (A) 30.02 and (B) 45.02. Irrigation was performed at each change of instrument with 5 mL of ultrapure Milli-Q water and the extruded material through the apical foramen was collected. Root cross-sections were subjected to histological analysis by optical microscopy (×40) and the images were evaluated morphometrically using the Image Tool software. Quantification of the extruded material was performed by weighing after liquid evaporation. ANOVA showed no statistically significant differences (p>0.05) among the groups with respect to the procedures used to clean the apical region. Considering the amount of extruded material, the Tukey's HSD showed that canals with mild curvature prepared with the 45.02 surgical diameter showed significantly higher values (p<0.05) that those of the other groups, which were similar between themselves (p>0.05). In conclusion, the effect of cleaning the apical region did not differ in the groups, considering root curvature and the surgical diameter of instruments used for apical preparation. The amount of extruded material was greater in canals with mild curvature that were prepared with the 45.02 surgical instrument diameter.

Expression of 8-oxoguanine Glycosylase in Human Fetal Membranes

Problem The most common DNA lesion generated by oxidative stress (OS) is 7, 8-dihydro-8-oxoguanine (8-oxoG) whose excision repair is performed by 8-oxoguanine glycosylase (OGG1). We investigated OGG1 expression changes in fetal membranes from spontaneous preterm birth (PTB) and preterm premature rupture of the membranes (pPROM) and its changes in vitro in normal fetal membranes exposed to OS inducer water-soluble cigarette smoke extract (CSE). Method of study DNA damage was determined in amnion cells treated with CSE by comet and FLARE assays. OGG1 mRNA expression and localization in fetal membranes from clinical specimens and in normal term membranes exposed to CSE were examined by QRT-PCR and by immunohistochemistry. Results DNA strand and base damage was seen in amnion cells exposed to CSE. OGG1 expression was 2.5-fold higher in PTB samples compared with pPROM (P=0.045). No significant difference was seen between term and pPROM or PTB and term. CSE treatment showed a nonsignificant decrease in OGG1. OGG1 was localized to both amnion and chorion with less intense staining in pPROM and CSE-treated membranes. Conclusion Increased OS-induced DNA damage predominated by 8-oxoG is likely to persist in fetal cells due to reduced availability of base excision repair enzyme OGG1. This can likely lead to fetal cell senescence associated with some adverse pregnancy outcome.

Chitosan and alginate biopolymer membranes for remediation of contaminated water with herbicides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Court cleaning behavior of the white-bearded manakin (manacus manacus) and a test of the anti-predation hypothesis

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of the Etching Duration and Ultrasonic Cleaning on Microtensile Bond Strength Between Feldspathic Ceramic and Resin Cement

This study assessed the effect of different etching durations of feldspathic ceramic with hydrofluoric acid (HF) and ultrasonic cleaning of the etched ceramic surface on the microtensile bond strength stability of resin to a feldspathic ceramic. The research hypotheses investigated were: (1) different etching times would not affect the adhesion resistance and (2) ultrasonic cleaning would improve the adhesion. Ceramic blocks (6 x 6 x 5 mm) (N = 48) were obtained. The cementations surfaces were duplicated in resin composite. The six study groups (n = 8) were: G1Etching with 10% aqueous HF (30 s) + silane; G 210% HF (1 min) + silane; G3-10% HF (2 min) + silane; G4-10% HF (30 s) + ultrasonic cleaning (4 min) in distilled water + silane; G5-10% HF (1 min) + ultrasonic cleaning + silane; G6-10% HF (2 min) ultrasonic cleaning + silane. The cemented blocks were sectioned into microbars for the microtensile test. The etching duration did not create significant difference among the groups (p = .156) but significant influence of ultrasonic cleaning was observed (p = .001) (Two-way ANOVA and Tukey's test, p > 0.05). All the groups after ultrasonic cleaning presented higher bond strength (19.38-20.08 MPa) when compared with the groups without ultrasonic cleaning (16.2117.75 MPa). The bond strength between feldspathic ceramic and resin cement was not affected by different etching durations using HF. Ultrasonic cleaning increased the bond strength between ceramic surface and resin cement, regardless of the etching duration.

Characterization of natural rubber membranes using scaling laws analysis

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Development of organic-inorganic polymeric film formers for controlled drug release and wound care

Film forming polymeric systems represents a new and unexplored technology of systems forskin or wounds protection and for controlled drug release. The aim of this work was to study the use of polymeric organic-inorganic ureasil-polyether hybrids synthesized by the sol-gel process as film forming system containing silver sulfadiazine as model drug. The film formationtime can be controlled by changing the precursor/catalyst ratio used during the step of hydrolysis and condensations. The results showed that the precursor/catalyst proportion influences both the visual characteristics and time required to form the film. The precursor/catalyst ratio equal to 20.8 m/v was considered ideal due to promote the homogeneous and transparent film formation in less than 5 minutes. The release profile of sulfadiazine is dependent on the characteristics of the matrixes: matrix more hydrophobic as ureasil-POP provided a slowed released mainly due to the low swelling of the matrix. The more hydrophilic ureasil-POE matrix presents a large capacity to swell and favors the faster release of the drug. The set of results showed the possibility of future use of these systems for treating wounds caused by burns.

Radiographic evaluation of root canal cleaning, main and laterals, using different methods of final irrigation

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Removal of glyphosate herbicide from water using biopolymer membranes

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Polymeric Nanoparticles as Oral Delivery Systems for Encapsulation and Release of Polyphenolic Compounds: Impact on Quercetin Antioxidant Activity & Bioaccessibility

A delivery system containing polymeric (Eudragit) nanoparticles has been developed for encapsulation and controlled release of bioactive flavonoids (quercetin). Nanoparticles were fabricated using a solvent displacement method. Particle size, morphology, and charge were measured by light scattering, electron microscopy and zeta-potential. Encapsulation efficiency (EE) and release profiles were determined using electrochemical methods. Molecular interactions within the particle matrix were characterized by X-ray diffraction, differential scanning calorimetry, and infrared spectroscopy. Antioxidant properties of free and encapsulated quercetin were analyzed by TBARS and fluorescence spectroscopy. Bioaccessibility of quercetin was evaluated using an in vitro digestion model. Relatively small (d a parts per thousand aEuro parts per thousand 370 nm) anionic polymeric nanoparticles were formed containing quercetin in a non-crystalline form (EE a parts per thousand aEuro parts per thousand 67 %). The main interaction between quercetin and Eudragit was hydrogen bonding. Encapsulated quercetin remained stable during 6 months storage and maintained its antioxidant activity. Quercetin bioaccessibility within simulated small intestinal conditions was improved by encapsulation. The knowledge obtained from this study will facilitate the rational design and fabrication of polymeric nanoparticles as oral delivery systems for encapsulation, protection, and release of bioactive compounds.

In vitro cultivation of canine multipotent mesenchymal stromal cells on collagen membranes treated with hyaluronic acid for cell therapy and tissue regeneration

Support structures for dermal regeneration are composed of biodegradable and bioresorbable polymers, animal skin or tendons, or are bacteria products. The use of such materials is controversial due to their low efficiency. An important area within tissue engineering is the application of multipotent mesenchymal stromal cells (MSCs) to reparative surgery. The combined use of biodegradable membranes with stem cell therapy may lead to promising results for patients undergoing unsuccessful conventional treatments. Thus, the aim of this study was to test the efficacy of using membranes composed of anionic collagen with or without the addition of hyaluronic acid (HA) as a substrate for adhesion and in vitro differentiation of bone marrow-derived canine MSCs. The benefit of basic fibroblast growth factor (bFGF) on the differentiation of cells in culture was also tested. MSCs were collected from dog bone marrow, isolated and grown on collagen scaffolds with or without HA. Cell viability, proliferation rate, and cellular toxicity were analyzed after 7 days. The cultured cells showed uniform growth and morphological characteristics of undifferentiated MSCs, which demonstrated that MSCs successfully adapted to the culture conditions established by collagen scaffolds with or without HA. This demonstrates that such scaffolds are promising for applications to tissue regeneration. bFGF significantly increased the proliferative rate of MSCs by 63% when compared to groups without the addition of the growth factor. However, the addition of bFGF becomes limiting, since it has an inhibitory effect at high concentrations in culture medium.

Polymeric micelles and molecular modeling applied to the development of radiopharmaceuticals

Micelles composed of amphiphilic copolymers linked to a radioactive element are used in nuclear medicine predominantly as a diagnostic application. A relevant advantage of polymeric micelles in aqueous solution is their resulting particle size, which can vary from 10 to 100 nm in diameter. In this review, polymeric micelles labeled with radioisotopes including technetium (99mTc) and indium (111In), and their clinical applications for several diagnostic techniques, such as single photon emission computed tomography (SPECT), gamma-scintigraphy, and nuclear magnetic resonance (NMR), were discussed. Also, micelle use primarily for the diagnosis of lymphatic ducts and sentinel lymph nodes received special attention. Notably, the employment of these diagnostic techniques can be considered a significant tool for functionally exploring body systems as well as investigating molecular pathways involved in the disease process. The use of molecular modeling methodologies and computer-aided drug design strategies can also yield valuable information for the rational design and development of novel radiopharmaceuticals.