THE MODULATION PRINCIPLE OF VACUUM ON THE SUPERCONDUCTIVITY OF YBCO

By neutron diffraction and other experiments, we have found that oxygen ions in YBCO can diffuse out of the sample in vacuo at room and low temperature, while the T(c) decreases greatly. We have also found that if the vacuum-deoxidation process lasts for several days there will be a damping oscillation of T(c) with time (t), and higher vacuum corresponds to a greater amplitude and a shorter period. We tentatively think that T(c) should satisfy the following function: T(c0) is-proportional-to T(c)e(-betat)cos (omegat + phi); it may be due to the diffusion of oxygen and the saturation of the valence state.

Artificial neural networks expecting more advanced microelectronics technology

　

Vacuum window of intermediate energy heavy-ion microbeam irradiation facility

The beam must be extracted into the air through the vacuum window to irradiate the living cell. In the window design, the material and thickness must be chosen to compromise the beam spot size broadening and the window safety. The structure-static analysis on the window of different structures and materials is done with the finite element analysis method, and the deformation and the equivalent stress axe simulated. The safety of these candidates is investigated using the intensity theory. In addition, the small angle scattering and the transverse range of ions are simulated using SRIM code, including all the effects on the beam spot size broadening, such as the incident ion energy, the material and the thickness of the window and the air composing. At last, the appropriate vacuum windows are presented, including the structure, material and thickness.

General SU(2)(L) x SU(2)(R) x U(1)(EM) sigma model with external sources, dynamical breaking and spontaneous vacuum symmetry breaking

We give a general SU(2)(L) x SU(2)(R) x U(1)(EM) sigma model with external sources, dynamical breaking and spontaneous vacuum symmetry breaking, and present the general formulation of the model. It is found that sigma and pi(0) without electric charges have electromagnetic interaction effects coming front the internal structures. A general Lorentz transformation relative to external sources J(gauge) - (J(A mu) J(A mu)(kappa)) derived, using the general Lorentz transformation and the four-dimensional current of nuclear matter of the ground si ate with J(gauge) = 0, we give the four-dimensional general relations between the different currents of nuclear matter systems with J(gauge) not equal 0 and those with J(gauge) = 0. The relation of the density's coupling with external magnetic field is derived, which conforms well to dense nuclear matter in a strong magnetic field. We show different condensed effects in strong interaction about fermions and antifermions, and give the concrete scalar and pseudoscalar condensed expressions of sigma(0) and pi(0) bosons. About different dynamical breaking and spontaneous vacuum symmetry breaking, the concrete expressions of different mass spectra are obtained in field theory. This paper acquires the running spontaneous vacuum breaking value sigma'(0), and obtains the spontaneous vacuum breaking in tenus of the running sigma'(0), which make nucleon, sigma, and pi particles gain effective masses. We achieve both the effect of external sources and nonvanishing value of the condensed scalar and pseudoscalar paticles. It is deduced that the masses of nucleons, sigma and pi generally depend on different external sources.

HIRFL大型真空系统；The vacuum system of HIRFL

HIRFL是兰州重离子加速器装置的英文首字母缩写,其真空系统是一个大型综合性系统。HIRFL由离子源、扇聚焦回旋加速器SFC、分离扇回旋加速器SSC和多用途的重离子冷却储存环(HIRFL-CSR)组成。多条束流运输线将这些加速器连接在一起,同时将各种重离子束流送往10多个实验终端。根据加速离子和束流寿命的需要,对各加速器真空度的要求是不同的:SFC已有50多年的历史,经过3次升级改造,真空度从10-4 Pa提高到10-6 Pa;建于上世纪八十年代的SSC真空度也为10-6 Pa;而两个重离子冷却储存环(CSRm和CSRe)的真空度达到10-10Pa以保证重离子有足够长的储存寿命。多条连接束运线根据不同实验终端的要求,其真空系统的设计方案也不同,文中列举了微束实验终端采取的防振措施;为充气反冲谱仪设计的清洁、大流量真空差分系统及为重离子治癌等终端设计的超薄壁扫描磁铁真空管道等。

Enlarged area A-type zeolite membranes prepared by vacuum seeding method

High quality A-type zeolite membranes, with enlarged area over 70 cm(2), were successfully synthesized on a tubular alpha-Al2O3 support by applying the vacuum seeding method.

Synthesis and properties of A-type zeolite membranes by secondary growth method with vacuum seeding

A-type zeolite membranes were successfully synthesized on tubular alpha-Al2O3 supports by secondary growth method with vacuum seeding In the seeding process, a thin, uniform and continuous seeding layer was closely attached to the support surface by the pressure difference between the two sides of the support wall. The effects of seed particle size, suspension concentration, coating pressure difference and coating time on the membrane and its pervaporation properties were investigated. The as-synthesized membranes were characterized by XRD and SEM. The quality of the membranes was evaluated by the pervaporation dehydration of 95 wt. % isopropanol/water mixture at 343 K. High quality A-type zeolite membranes can be reproducibly prepared by the secondary growth method with vacuum seeding under the conditions: seed particle size of 500-1200 nm, suspension concentration of 4-8 g/l, coating pressure difference of 0.0100-0.0250 MPa and coating time of 45-180 s. (C) 2004 Elsevier B.V. All rights reserved.

Luminescent properties of Mn2+ in hexagonal aluminates under ultraviolet and vacuum ultraviolet excitation

Mn2+-doped xBaO center dot 6Al(2)O(3) and BaMgAl10O17 phosphors were prepared by solid-state reaction. The investigation of vacuum ultraviolet (VUV) excitation spectra of these phosphors exhibits that 0.82BaO center dot 6Al(2)O(3):Mn2+ and BaMgAl10O17:Mn2+ have a stronger absorption than BaO center dot 6Al(2)O(3):Mn2+ at about 147 nm. The emission spectra under VUV excitation demonstrated that 0.82BaOBa center dot 6Al(2)O(3):Mn2+ and BaMgAl10O17:Mn2+ have a higher luminescent intensity than BaO center dot 6Al(2)O(3):Mn2+. The lifetime analysis indicates that they have similar decay times, indicating that 0.82BaOBa center dot 6Al(2)O(3):Mn2+ and BaMgAl10O17:Mn2+ can be used as luminescent materials for plasma display panels. We observed that the critical concentration of the Mn2+ ions by host excitation is different from that of Mn2+ direct excitation, revealing a different mechanism of energy transfer. The critical distance was calculated. A model was suggested to explain the process of the energy transfer from the host to the Mn2+ ions.

Thermal analysis of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) irradiated under vacuum

Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) was irradiated by Co-60 gamma-rays (doses of 50, 100 and 200kGy) under vacuum. The thermal analysis of control and irradiated PHBV, under vacuum was carried out by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The tensile properties of control and irradiated PHBV were examined by using an Instron tensile testing machine. In the thermal degradation of control and irradiated PHBV, a one-step weight loss was observed. The derivative thermogravimetric curves of control and irradiated PHBV confirmed only one weight-loss step change. The onset degradation temperature (T-o) and the temperature of maximum weight-loss rate (T-p) of control and irradiated PHBV were in line with the heating rate (degreesC min(-1)). T-o and T-p of PHBV decreased with increasing radiation dose at the same heating rate. The DSC results showed that Co-60 gamma-radiation significantly affected the thermal properties of PHBV. With increasing radiation dose, the melting temperature (T-m) of PHBV shifted to a lower value, due to the decrease in crystal size. The tensile strength and fracture strain of the irradiated PHBV decreased, hence indicating an increased brittleness.

Vacuum-deposited submonolayer thin films of a three-ring bent-core compound

Submonolayer thin films of a three-ring bent-core (that is, banana-shaped) compound, m-bis(4-n-octyloxystyryl)benzene (m-OSB), were prepared by the vacuum-deposition method, and their morphologies, structures, and phase behavior were investigated by atomic force microscopy (AFM) and transmission electron microscopy (TEM). The films have island shapes ranging from compact elliptic or circular patterns at low temperatures (below 40 degreesC) to branched patterns at high temperatures (above 60 degreesC). This shape evolution is contrary to the prediction based on the traditional diffusion-limited aggregation (DLA) theory. AFM observations revealed that two different mechanisms governed the film growth, in which the compact islands were formed via a dewetting-like behavior, while the branched islands diffusion-mediated. It is suggested m-OSB forms a two-dimensional, liquid crystal at the low-temperature substrate that is responsible for the unusual formation of compact islands. All of the monolayer islands are unstable and apt to transform to slender bilayer crystals at room temperature. This phase transition results from the peculiar molecular shape and packing of the bent-core molecules and is interpreted as escaping from macroscopic net polarization by the formation of an antiferroelectric alignment.